CN110423091A - A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate - Google Patents
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate Download PDFInfo
- Publication number
- CN110423091A CN110423091A CN201910824379.0A CN201910824379A CN110423091A CN 110423091 A CN110423091 A CN 110423091A CN 201910824379 A CN201910824379 A CN 201910824379A CN 110423091 A CN110423091 A CN 110423091A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- water
- conditioning function
- magnesium cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, the alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate is made of the raw material of following parts by weight: 100 parts of light calcined magnesia, 30-70 parts of epsom salt, 0.1-5 parts of composite modifier, 5-10 parts of aromatic insect repellent agent, 5-30 parts of conditioning agent, 1-10 parts of catalytic antimicrobial agent, 10-50 parts of agricultural crop straw, 10-200 parts of mineral filler, water-reducing agent 0.5-5, adjustable solidification agent 1-10,0.5-5 parts of defoaming agent, 1-10 parts of toughener, 20-300 parts of water.The present invention is by being added to mineral humidity adjusting material diatomite; with humidity conditioning function; plate fire-proof and water-proof, high-strength damp-proof, the antibacterial and mouldproof of preparation; it is the ideal material for substituting conventional wood panels, glued board, wood-plastic board; using inorganic coagulation material, zero content of formaldehyde is added to a large amount of forest and agricultural biomass; also there is very big benefit to environmental protection, can be widely applied to the field of furniture such as wardrobe, wine cabinet, bookcase.
Description
Technical field
The present invention relates to furniture building materials technology field, specially a kind of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate
Preparation method.
Background technique
Wardrobe plate is exactly the plate for making wardrobe, and wardrobe plate includes cabinet board and cabinet door plate, common clothing
Cabinet plate has particieboard, density board, moist-proof board, lumber core, Chinese fir board, multi-layer solid wood plate, Australia's deals, Europe deals, decoration panel, horse
Pregnancy plate etc..
Existing wardrobe plate is all solid wood board, particieboard, density board, wood-plastic clad plate either chlorine oxygen currently on the market
The composite board of magnesium cement, plate made of the prior art are easily deformed, and formaldehyde, does not prevent fires and cockroach proof, plate do not have
There is humidity conditioning function, the big clothing of plum rain season air humidity is easy dampness, although the composite board of magnesia oxychloride cement is prevented fires, by
In being easy damp suction surface halide accumulation containing chloride ion, contact steel and iron parts are easy to cause its corrosion, in view of the deficiencies of the prior art, be badly in need of one kind
High performance plate solves the above problems.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, tools
The advantages of zero formaldehyde of slave board material, largely consumes forest and agricultural biomass, the no pollution to the environment that can be recycled, solves the prior art
Manufactured plate is easily deformed, formaldehyde, does not prevent fires and cockroach proof, plate do not have humidity conditioning function, plum rain season air is wet
It spends big clothing and is easy dampness, the composite board of magnesia oxychloride cement contains chloride ion and is easy damp suction surface halide accumulation, and contact steel and iron parts are easy to lead
The problem of causing its corrosion.
To achieve the above object, the cockroach proof humidity conditioning function the invention provides the following technical scheme: a kind of alkali magnesium cement is prevented fires
Wardrobe plate, the alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate are made of the raw material of following parts by weight: light-burned oxidation
100 parts of magnesium, 0.1-5 parts of composite modifier, 5-10 parts of aromatic insect repellent agent, 5-30 parts of conditioning agent, is urged at 30-70 parts of epsom salt
Change antibacterial agent 1-10 parts, 10-50 parts of agricultural crop straw, 10-200 parts of mineral filler, water-reducing agent 0.5-5, adjustable solidification agent 1-10, defoaming
0.5-5 parts of agent, 1-10 parts of toughener, 20-300 parts of water.
Preferably, the light calcined magnesia, content 85%, commonly using active quantities is 60~65.
Preferably, the composite modifier includes that enhancing component and water resistant component, the two ratio are preferred are as follows: 2 (3:1): 1.
Preferably, the aromatic insect repellent agent includes one kind of wormwood, lemon grass (Cymbopogon citratus), camphorwood leaf or bits, lavender, bay leaf
Or it is several.
Preferably, the conditioning agent includes calcined diatomite, and the adjustable solidification agent includes portland cement, gypsum, caustic soda, sulphur
The one or several kinds of hydrochlorate, chlorate, lime, the defoaming agent include silicone oil, organosilicon, polyethers, phosphate one kind or
Several, the toughener includes the one or more of acrylic emulsion, re-dispersible glue powder, epoxy resin, phenolic resin.
Preferably, the catalytic antimicrobial agent include titanium dioxide, zinc oxide, nano-silver powder, zirconium oxide, titanium-containing blast furnace slag,
The one or more of modified verdelite powder.
Preferably, the agricultural crop straw includes one kind or several of straw stalk, straw, kaoliang stalk, sugarcane stem, peanut bar
Kind, the agricultural crop straw is handled by lye desugar, dries pulverizing to partial size 50-200 mesh.
Preferably, the mineral filler includes solid sulfur ash, flyash, silicon ash, the one or more of light calcium carbonate powder, silica flour,
The mesh number of the mineral filler is 200-400 mesh.
Preferably, the water-reducing agent include Lignins water-reducing agent, naphthalene sulfonic acids based water reducer, naphthalene water reducer one kind or
Several, the water-reducing agent is water-soluble resin water-reducing agent or polycarboxylate water-reducer.
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, comprising the following steps:
1) epsom salt and water mixed dissolution in proportion, it is mixed that composite modifier, water-reducing agent and defoaming agent is then added
It is stand-by to close investment blender；
2) light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, catalytic antimicrobial agent, virtue are sequentially added in blender
Fragrant pest repellant, straw powder and toughener stir to obtain slurry；
3) slurry is poured into template, is laid with glass fiber net by roller of roller press and is rolled into slab, is cut to size and loads onto mould
Frame is sent into fog room and conserves 20-40h in the environment of 20-40 ° of temperature, humidity 60%-90%；
4) template is removed, continues maintenance 3-5 days in the environment of 20-40 ° of temperature, humidity 60%-90%, cutting plate passes through
Abrasive finishing machine abrasive finishing, the technology finally transferred in plate surface thermal transfer or water make plate surface have a wood grain, stone material, pattern,
Obtain alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe board finished product.
Compared with prior art, beneficial effects of the present invention are as follows:
1, plate fire-proof and water-proof prepared by the present invention, high-strength damp-proof, antibacterial and mouldproof are substitution conventional wood panels, glued board, wood
The ideal material of mould plate, using inorganic coagulation material, zero content of formaldehyde is added to a large amount of forest and agricultural biomass, to environmental protection
Also there is very big benefit, can be widely applied to the field of furniture such as wardrobe, wine cabinet, bookcase.
2, the present invention is compared with the plate of magnesia oxychloride cement material, due to not chloride ion-containing, will not the moisture absorption return, corrode steel
Connector substantially prolongs the service life of product, by being added to natural drive cockroach plant, has plate and drives cockroach
Effect makes plate have toughness, collision is not easy defect corner when beating, improves inorganic glue by being added to toughening material
Brittleness problems existing for gel material, plate are added to mineral humidity adjusting material diatomite, have humidity conditioning function.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
A kind of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate
Be made of the raw material of following parts by weight: 100 parts of light calcined magnesia, 30-70 parts of epsom salt, 0.1-5 parts of composite modifier,
5-10 parts of aromatic insect repellent agent, 5-30 parts of conditioning agent, 1-10 parts of catalytic antimicrobial agent, 10-50 parts of agricultural crop straw, mineral filler 10-
200 parts, water-reducing agent 0.5-5, adjustable solidification agent 1-10,0.5-5 parts of defoaming agent, 1-10 parts of toughener, 20-300 parts of water.
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, comprising the following steps:
1) epsom salt and water mixed dissolution in proportion, it is mixed that composite modifier, water-reducing agent and defoaming agent is then added
It is stand-by to close investment blender；
2) light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, catalytic antimicrobial agent, virtue are sequentially added in blender
Fragrant pest repellant, straw powder and toughener stir to obtain slurry；
3) slurry is poured into template, is laid with glass fiber net by roller of roller press and is rolled into slab, is cut to size and loads onto mould
Frame is sent into fog room and conserves 20-40h in the environment of 20-40 ° of temperature, humidity 60%-90%；
4) template is removed, continues maintenance 3-5 days in the environment of 20-40 ° of temperature, humidity 60%-90%, cutting plate passes through
Abrasive finishing machine abrasive finishing, the technology finally transferred in plate surface thermal transfer or water make plate surface have a wood grain, stone material, pattern,
Obtain alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe board finished product.
Embodiment 1
A kind of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, is calculated with mass fraction, includes following composition: light-burned
100 parts of magnesia powder, 70 parts of epsom salt, 3 parts of composite modifier, 5 parts of aromatic insect repellent agent, 5 parts of conditioning agent, catalytic antimicrobial agent
5 parts, 35 parts of agricultural crop straw, 30 parts of mineral filler, 0.5 part of water-reducing agent, 8 parts of adjustable solidification agent, 0.5 part of defoaming agent, 10 parts of toughener,
107 parts of water.
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, comprising the following steps: 1) seven water
It is stand-by that magnesium sulfate and water are dissolved into Adlerika, and composite modifier is successively added in a reservoir in the process, water-reducing agent, disappears
Infusion mixing investment blender is stand-by；2) it then sequentially adds light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, urge
Change antibacterial agent, aromatic insect repellent agent, straw powder, toughener, stir to obtain slurry；3) slurry is poured into template, be laid with
Glass fiber net is rolled into slab by roller of roller press, is cut to size and loads onto mould bases, is sent into fog room at 20 ° of temperature, humidity
20h is conserved in the environment of 60%；4) template is removed, continues maintenance 3 days in the environment of 20 ° of temperature, humidity 60%, cutting plate leads to
Abrasive finishing machine abrasive finishing is crossed, the technology finally transferred in plate surface thermal transfer or water makes plate surface have wood grain, stone material, figure
Case obtains alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe panel products.
Embodiment 2
In embodiment 1, following steps are added:
Light calcined magnesia, content 85%, commonly using active quantities is 60~65；Composite modifier include enhancing component and
Water resistant component, the two ratio are preferred are as follows: 2 (3:1): 1；Aromatic insect repellent agent include wormwood, lemon grass (Cymbopogon citratus), camphorwood leaf or bits, lavender,
The one or more of bay leaf；Conditioning agent includes calcined diatomite, and adjustable solidification agent includes portland cement, gypsum, caustic soda, sulfuric acid
The one or several kinds of salt, chlorate, lime, defoaming agent include silicone oil, organosilicon, polyethers, phosphate, and toughener includes propylene
The one or more of yogurt liquid, re-dispersible glue powder, epoxy resin, phenolic resin.
A kind of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, is calculated with mass fraction, includes following composition: light-burned
100 parts of magnesia, 60 parts of epsom salt, 2 parts of composite modifier, 10 parts of aromatic insect repellent agent, 10 parts of conditioning agent, catalytic antimicrobial agent
10 parts, 45 parts of agricultural crop straw, 20 parts of mineral-filled material, 1 part of water-reducing agent, 6 parts of adjustable solidification agent, 0.8 part of defoaming agent, 8 parts of toughener,
90 parts of water.
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, comprising the following steps: 1) seven water
It is stand-by that magnesium sulfate and water are dissolved into Adlerika, and composite modifier is successively added in a reservoir in the process, water-reducing agent, disappears
Infusion mixing investment blender is stand-by；2) it then sequentially adds light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, urge
Change antibacterial agent, aromatic insect repellent agent, straw powder, toughener, stir to obtain slurry；3) slurry is poured into template, be laid with
Glass fiber net is rolled into slab by roller of roller press, is cut to size and loads onto mould bases, is sent into fog room at 40 ° of temperature, humidity
40h is conserved in the environment of 90%；4) template is removed, continues maintenance 3 days in the environment of 40 ° of temperature, humidity 90%, cutting plate leads to
Abrasive finishing machine abrasive finishing is crossed, the technology finally transferred in plate surface thermal transfer or water makes plate surface have wood grain, stone material, figure
Case obtains alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe panel products.
Embodiment 3
In example 2, following steps are added:
Catalytic antimicrobial agent includes titanium dioxide, zinc oxide, nano-silver powder, zirconium oxide, titanium-containing blast furnace slag, modified verdelite powder
One or more；Agricultural crop straw includes the one or more of straw stalk, straw, kaoliang stalk, sugarcane stem, peanut bar, farming
Object stalk is handled by lye desugar, dries pulverizing to partial size 50-200 mesh；Mineral filler include solid sulfur ash, flyash, silicon ash,
The one or more of light calcium carbonate powder, silica flour, the mesh number of mineral filler are 200-400 mesh；Water-reducing agent include Lignins water-reducing agent,
The one or more of naphthalene sulfonic acids based water reducer, naphthalene water reducer, water-reducing agent are water-soluble resin water-reducing agent or polycarboxylate water-reducer.
A kind of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, is calculated with mass fraction, includes following composition: light-burned
100 parts of magnesia, 52 parts of epsom salt, 1 part of composite modifier, 10 parts of aromatic insect repellent agent, 15 parts of conditioning agent, catalytic antimicrobial agent
5 parts, 30 parts of agricultural crop straw, 30 parts of mineral-filled material, 2 parts of water-reducing agent, 5 parts of adjustable solidification agent, 1 part of defoaming agent, 7 parts of toughener, water
106 parts.
A kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, comprising the following steps: 1) seven water
It is stand-by that magnesium sulfate and water are dissolved into Adlerika, and composite modifier is successively added in a reservoir in the process, water-reducing agent, disappears
Infusion mixing investment blender is stand-by；2) it then sequentially adds light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, urge
Change antibacterial agent, aromatic insect repellent agent, straw powder, toughener, stir to obtain slurry；3) slurry is poured into template, be laid with
Glass fiber net is rolled into slab by roller of roller press, is cut to size and loads onto mould bases, is sent into fog room at 40 ° of temperature, humidity
40h is conserved in the environment of 90%；4) template is removed, continues maintenance 3 days in the environment of 40 ° of temperature, humidity 90%, cutting plate leads to
Abrasive finishing machine abrasive finishing is crossed, the technology finally transferred in plate surface thermal transfer or water makes plate surface have wood grain, stone material, figure
Case obtains alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe panel products.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (10)
- A kind of cockroach proof humidity conditioning function wardrobe plate 1. alkali magnesium cement is prevented fires, it is characterised in that: the alkali magnesium cement fire prevention cockroach proof Humidity conditioning function wardrobe plate is made of the raw material of following parts by weight: 100 parts of light calcined magnesia, 30-70 parts of epsom salt, compound 0.1-5 parts of modifying agent, 5-10 parts of aromatic insect repellent agent, 5-30 parts of conditioning agent, 1-10 parts of catalytic antimicrobial agent, agricultural crop straw 10-50 Part, 10-200 parts of mineral filler, water-reducing agent 0.5-5, adjustable solidification agent 1-10,0.5-5 parts of defoaming agent, 1-10 parts of toughener, water 20- 300 parts.
- The cockroach proof humidity conditioning function wardrobe plate 2. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Light calcined magnesia, content 85%, commonly using active quantities is 60~65.
- The cockroach proof humidity conditioning function wardrobe plate 3. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Composite modifier includes that enhancing component and water resistant component, the two ratio are preferred are as follows: 2 (3:1): 1.
- The cockroach proof humidity conditioning function wardrobe plate 4. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Aromatic insect repellent agent includes the one or more of wormwood, lemon grass (Cymbopogon citratus), camphorwood leaf or bits, lavender, bay leaf.
- The cockroach proof humidity conditioning function wardrobe plate 5. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Conditioning agent includes calcined diatomite, and the adjustable solidification agent includes portland cement, gypsum, caustic soda, sulfate, chlorate, lime One or several kinds, the defoaming agent include silicone oil, organosilicon, polyethers, phosphate, the toughener include acrylic emulsion, The one or more of re-dispersible glue powder, epoxy resin, phenolic resin.
- The cockroach proof humidity conditioning function wardrobe plate 6. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Catalytic antimicrobial agent include titanium dioxide, zinc oxide, nano-silver powder, zirconium oxide, titanium-containing blast furnace slag, modified verdelite powder one kind or It is several.
- The cockroach proof humidity conditioning function wardrobe plate 7. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Agricultural crop straw includes the one or more of straw stalk, straw, kaoliang stalk, sugarcane stem, peanut bar, and the agricultural crop straw passes through Lye desugar processing, dries pulverizing to partial size 50-200 mesh.
- The cockroach proof humidity conditioning function wardrobe plate 8. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Mineral filler includes solid sulfur ash, flyash, silicon ash, the one or more of light calcium carbonate powder, silica flour, and the mesh number of the mineral filler is 200-400 mesh.
- The cockroach proof humidity conditioning function wardrobe plate 9. a kind of alkali magnesium cement according to claim 1 is prevented fires, it is characterised in that: described Water-reducing agent includes the one or more of Lignins water-reducing agent, naphthalene sulfonic acids based water reducer, naphthalene water reducer, and the water-reducing agent is water Soluble resin water-reducing agent or polycarboxylate water-reducer.
- 10. a kind of preparation method of alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe plate, it is characterised in that: including following step It is rapid:1) epsom salt and water mixed dissolution in proportion, composite modifier, water-reducing agent and defoaming agent mixing is then added and throws It is stand-by to enter blender；2) light-magnesite powder, mineral filler, conditioning agent, adjustable solidification agent, catalytic antimicrobial agent, fragrance drive are sequentially added in blender Worm agent, straw powder and toughener stir to obtain slurry；3) slurry is poured into template, is laid with glass fiber net by roller of roller press and is rolled into slab, is cut to size and loads onto mould bases, send Enter in fog room and conserves 20-40h in the environment of 20-40 ° of temperature, humidity 60%-90%；4) template is removed, continues maintenance 3-5 days in the environment of 20-40 ° of temperature, humidity 60%-90%, cutting plate passes through sanding Machine sanding, the technology finally transferred in plate surface thermal transfer or water make plate surface have wood grain, stone material, and pattern obtains Alkali magnesium cement fire prevention cockroach proof humidity conditioning function wardrobe board finished product.