CN110406238A - A kind of preparation method of the full shade fabric of water-impervious - Google Patents

A kind of preparation method of the full shade fabric of water-impervious Download PDF

Info

Publication number
CN110406238A
CN110406238A CN201910663515.2A CN201910663515A CN110406238A CN 110406238 A CN110406238 A CN 110406238A CN 201910663515 A CN201910663515 A CN 201910663515A CN 110406238 A CN110406238 A CN 110406238A
Authority
CN
China
Prior art keywords
fabric
water
impervious
full
full shade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910663515.2A
Other languages
Chinese (zh)
Inventor
李群芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Heqian Textile Finishing Co Ltd
Original Assignee
Suzhou Heqian Textile Finishing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Heqian Textile Finishing Co Ltd filed Critical Suzhou Heqian Textile Finishing Co Ltd
Priority to CN201910663515.2A priority Critical patent/CN110406238A/en
Publication of CN110406238A publication Critical patent/CN110406238A/en
Pending legal-status Critical Current

Abstract

The present invention relates to fabric technical field more particularly to a kind of preparation methods of the full shade fabric of water-impervious.The full shade fabric of the water-impervious is just with full coating technique, so that fabric is combined together with TPU film, so that fabric has the function of waterproof, impermeable, shading and antiultraviolet, while enabling to fabric soft, smooth, more durable, the fabric free from extraneous odour prepared is more environmentally-friendly.In addition, the full shade fabric method and process of the water-impervious is simple and easy to control, glue is combined with TPU film with better shaded effect, and fabric has better unfading, efficiently solves the embrittlement issue of fabric, suitable to promote the use of.

Description

A kind of preparation method of the full shade fabric of water-impervious
Technical field
The present invention relates to fabric technical field more particularly to a kind of preparation methods of the full shade fabric of water-impervious.
Background technique
The full shade fabric of water-impervious use in modern society it is very universal, in umbrella fabric, tent material and curtain face Even more relatively common in material, the coating process majority of the complex manufacturing technology of traditional shading waterproof fabrics, fabric uses spot printing Technique, the seepage of water of fabric cannot access effective holding, and the brittleness for side's infiltration shade fabric that tradition is prepared is larger, prevents Water shade fabric is easy to be broken from folding line.
The present invention devises a kind of preparation method of full shade fabric of water-impervious, and the full shade fabric of the water-impervious is just with completely covering Membrane process, so that fabric is combined together with TPU film, so that fabric has the function of waterproof, impermeable, shading and antiultraviolet Can, while enabling to fabric soft, smooth, more durable, the fabric free from extraneous odour prepared is more environmentally-friendly.In addition, should The full shade fabric method and process of water-impervious is simple and easy to control, and glue is combined with TPU film with better shaded effect, fabric With better unfading, the embrittlement issue of fabric is efficiently solved, is suitble to promote the use of.
Summary of the invention
In order to overcome defect present in background technique, the technical solution adopted by the present invention to solve the technical problems is: A kind of preparation method of the full shade fabric of water-impervious, it is characterised in that the steps include: uniformly to brush the one side of spare fabric Upper one layer of glue, using coating technique in the spare fabric side of cementing, heat is covered with one layer of TPU film, using full coat method, Coated temperature is 115-125 degrees Celsius, and overlay film speed is 20 meters per minute.
The preferred spare fabric is knitting fabric, shuttle-woven fabric, non-woven material or elastic fabric.
The preferred glue has ethyl acetate, bridging agent, stock white and polyurethanes to be prepared.
A kind of preparation method of the full shade fabric of water-impervious according to the present invention, the full shade fabric of the water-impervious is just with full Coating technique, so that fabric is combined together with TPU film, so that fabric has waterproof, impermeable, shading and antiultraviolet Function, while enabling to fabric soft, smooth, more durable, the fabric free from extraneous odour prepared is more environmentally-friendly.In addition, The full shade fabric method and process of the water-impervious is simple and easy to control, and glue is combined with TPU film with better shaded effect, face Material has better unfading, efficiently solves the embrittlement issue of fabric, is suitble to promote the use of.
Specific embodiment
Specific embodiment one, a kind of preparation method of the full shade fabric of water-impervious, it is characterised in that the steps include: will be spare The one side of fabric is uniformly brushed on one layer of glue, and using coating technique in the spare fabric side of cementing, heat is covered with one layer TPU film, using full coat method, coated temperature is 120 degrees Celsius, and overlay film speed is 20 meters per minute, and the spare fabric is It is knitted fabric, shuttle-woven fabric, non-woven material or elastic fabric, the glue have ethyl acetate, bridging agent, stock white and poly- ammonia Carbamate is prepared.
Specific embodiment two, a kind of preparation method of the full shade fabric of water-impervious, it is characterised in that the steps include: will be spare The one side of fabric is uniformly brushed on one layer of glue, and using coating technique in the spare fabric side of cementing, heat is covered with one layer TPU film, using full coat method, coated temperature is 125 degrees Celsius, and overlay film speed is 20 meters per minute, and the spare fabric is It is knitted fabric, shuttle-woven fabric, non-woven material or elastic fabric, the glue have ethyl acetate, bridging agent, stock white and poly- ammonia Carbamate is prepared.
A kind of preparation method of the full shade fabric of water-impervious according to the present invention, the full shade fabric of the water-impervious is just with full Coating technique, so that fabric is combined together with TPU film, so that fabric has waterproof, impermeable, shading and antiultraviolet Function, while enabling to fabric soft, smooth, more durable, the fabric free from extraneous odour prepared is more environmentally-friendly.In addition, The full shade fabric method and process of the water-impervious is simple and easy to control, and glue is combined with TPU film with better shaded effect, face Material has better unfading, efficiently solves the embrittlement issue of fabric, is suitble to promote the use of.
Obviously, the above embodiments are merely examples for clarifying the description, and does not limit the embodiments.It is right For those of ordinary skill in the art, can also make on the basis of the above description it is other it is various forms of variation or It changes.There is no necessity and possibility to exhaust all the enbodiments.And it is extended from this it is obvious variation or It changes still within the protection scope of the invention.

Claims (3)

1. a kind of preparation method of the full shade fabric of water-impervious, it is characterised in that the steps include: by the one side of spare fabric, Even to be brushed on one layer of glue, using coating technique in the spare fabric side of cementing, heat is covered with one layer of TPU film, using full Coating method, coated temperature are 115-125 degrees Celsius, and overlay film speed is 20 meters per minute.
2. a kind of preparation method of the full shade fabric of water-impervious according to claim 1, which is characterized in that the spare face Material is knitting fabric, shuttle-woven fabric, non-woven material or elastic fabric.
3. a kind of preparation method of the full shade fabric of water-impervious according to claim 1, which is characterized in that the glue has Ethyl acetate, bridging agent, stock white and polyurethanes are prepared.
CN201910663515.2A 2019-07-23 2019-07-23 A kind of preparation method of the full shade fabric of water-impervious Pending CN110406238A (en)