CN110025202A - A kind of casement and its production method - Google Patents
A kind of casement and its production method Download PDFInfo
- Publication number
- CN110025202A CN110025202A CN201910278596.4A CN201910278596A CN110025202A CN 110025202 A CN110025202 A CN 110025202A CN 201910278596 A CN201910278596 A CN 201910278596A CN 110025202 A CN110025202 A CN 110025202A
- Authority
- CN
- China
- Prior art keywords
- casement
- tpu
- lining
- film
- tpu film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of casement and its production methods comprising a casement ontology, casement ontology inside are equipped with shading lining, shading lining includes base fabric and TPU film, base fabric and TPU film are fit together by adhesive layer, also, the thickness of TPU film is not more than 0.04mm.Casement environmental protection, good shading effect and water-fastness free from extraneous odour, long service life.
Description
Technical field:
It is especially a kind of casement and its production method the present invention relates to home textile field.
Background technique:
At present, casement on the market is usually compounded with lining, lining in the side of casement to improve shaded effect
It is upper to coat three-layer coating repeatedly in base fabric using coating apparatus to realize shaded effect, since coating paste has centainly stupid
Range of solvents, therefore the slurry environment easy to pollute in production process, and the production time is long, and required place is more, and coating is easy
Aging can fall off, delamination, over time intolerant to washing;In addition, coating can give out peculiar smell under sunshine, feel is also poor, not enough
Softness, and quality weight, have seriously affected use.
Summary of the invention:
The technical problem to be solved by the invention is to provide a kind of environmental protection, good shading effect and water-fastness free from extraneous odour are used
The casement of service life length.
The technical solution of the invention is as follows, provides a kind of casement comprising a casement ontology, in casement ontology
Side is equipped with shading lining, and shading lining includes base fabric and TPU film, and base fabric and TPU film are fit together by adhesive layer, and
And the thickness of TPU film is not more than 0.04mm.
Preferably, adhesive layer is PU glue-line.
Preferably, casement ontology and shading lining are sewed together by adhesive bonding or suture.
Preferably, the left and right sides and top margin of casement ontology and shading lining are fixed together.
Preferably, casement and base fabric are any one of cotton, dacron or blended fabric of tender terylene.
Preferably, TPU film is the waterproof breathable membrane of the black with a thickness of 0.02mm.
The present invention also provides a kind of production methods of casement, include the following steps,
Step 1, the TPU film after the roller coating PU glue of base fabric side with thickness no more than 0.02mm are bonded, press through pressure roller
Form shading lining;
The two sides of casement ontology and lining are sewed together using sewing device, then cut, cut by step 2
One end is sewed together again afterwards.
Preferably, TPU film is prepared by film-blowing process.
Preferably, TPU film is entered by the way that TPU resin, TPU modifying agent and carbon black to be dosed into mixing machine after stirring
Heating plasticizing in screw extruder, then film extrusion, inflation, cooling and shaping, are then drawn and are surface-treated, then
Again draw after trimming, cut and cut open side, finally crimp scroll at.
Preferably, according to the mass fraction, TPU resin, TPU modifying agent and carbon black be respectively 100-120 parts, 4-6 parts,
0.3-1 parts, wherein TPU modifying agent graphene oxide, poly- rice type TPU and nano-titanium dioxide are mixed by 50:40:5.
Using after above scheme compared with prior art, the invention has the following advantages that by casement ontology side
Shading lining is set, and shading lining is that the TPU film of base fabric and thickness no more than 0.04mm is combined, and is ensuring that cost do not increase
Under the premise of adding, realize shading lining is soft, ventilative, waterproof, ageing-resistant, low temperature resistant, wear-resisting scratch resistance, tensile strength are good,
The features such as smell is small, environmentally friendly, good shading effect is, it can be achieved that 100% shading is suitble to the four seasons to use, service life convenient for washing
It is long, and simple process, high production efficiency, place needed for producing is few, environmentally friendly.
Detailed description of the invention:
The position Fig. 1 structural schematic diagram of the invention.
The sectional view of the position Fig. 2 shading lining of the invention.
Specific embodiment:
With regard to specific embodiment, the invention will be further described below:
Embodiment 1
As illustrated in fig. 1 and 2, a kind of casement comprising a casement ontology 1 is equipped in shading on the inside of casement ontology 1
Cloth 2, shading lining 2 include base fabric 21 and TPU film 23, and base fabric 21 and TPU film 23 are fit together by adhesive layer 22, and
And TPU film 23 is the waterproof breathable membrane of the black with a thickness of 0.02mm.The TPU film is prepared by film-blowing process, is glued
Connecing layer is that PU glue-line, casement ontology and shading lining are sewed together by adhesive bonding or suture, is in the present embodiment
Suture, specifically, the left and right sides and top margin of casement ontology and shading lining are sewed together, and casement and base
Cloth is any one of cotton, dacron or blended fabric of tender terylene.By the waterproof and breathable for selecting the black of 0.02mm
TPU film, it can be achieved that 100% shaded effect.Also, it is not more than the TPU film of 0.04mm thickness due to using, so that whole
Cost is not higher than the cost of coating shading lining, has curtain body and shading lining knot with 2.4m specification common on the market
The casement of structure is calculated, and with the cost of the casement of coating way realization shaded effect at 12 yuan or so, and uses the TPU of 0.02mm
The casement for the shading lining preparation that Film laminated base fabric is formed, totle drilling cost is at 10 yuan or so, it is clear that just has in simple price
Advantage moreover needs coating operation repeatedly for three times compared to coating lining, and occupied ground is more, and time-consuming, and slurry contamination is big etc.
Defect, shading lining of the invention completely solve the above problem.
Specifically, the production method of casement, includes the following steps,
Step 1, the TPU film after the roller coating PU glue of base fabric side with thickness no more than 0.02mm are bonded, press through pressure roller
Form shading lining;
The two sides of casement ontology and lining are sewed together using sewing device, then cut, cut by step 2
One end is sewed together again afterwards.
Among these, TPU film enters spiral shell by the way that TPU resin, TPU modifying agent and carbon black to be dosed into mixing machine after stirring
Heating plasticizing in bar extruder, then film extrusion, inflation, cooling and shaping, are then drawn and are surface-treated, then again
Side is cut and is cutd open in trimming after secondary traction, finally crimp scroll at.
Further, according to the mass fraction, TPU resin, TPU modifying agent and carbon black be respectively 100-120 parts, 4-6 parts,
0.3-1 parts, wherein TPU modifying agent graphene oxide, poly- rice type TPU and nano-titanium dioxide are mixed by 50:40:5.
This product can prepare the TPU film of different-thickness, control according to the fabric component of different base fabrics and casement ontology
Under the premise of cost, preferable using effect is realized.
In conclusion the present invention is by being arranged shading lining in casement ontology side, shading lining is base fabric and thickness
TPU film no more than 0.04mm is combined, under the premise of ensuring that cost is not increased, realize shading lining it is soft,
Ventilative, waterproof, ageing-resistant, low temperature resistant, wear-resisting scratch resistance, the features such as tensile strength is good, smell is small, environmentally friendly, good shading effect can be real
Existing 100% shading is suitble to the four seasons to use convenient for washing, long service life, and simple process, high production efficiency, needed for production
Place is few, environmentally friendly.
Only the preferred embodiment of the present invention has been described above, but is not to be construed as limiting the scope of the invention.It is all
The equivalent structure or equivalent flow shift done using description of the invention, be included in scope of patent protection of the invention it
It is interior.
Claims (10)
1. a kind of casement comprising a casement ontology, casement ontology inside are equipped with shading lining, it is characterised in that: hide
Light lining includes base fabric and TPU film, and base fabric and TPU film are fit together by adhesive layer, also, the thickness of TPU film
No more than 0.04mm.
2. casement according to claim 1, it is characterised in that: adhesive layer is PU glue-line.
3. casement according to claim 1, it is characterised in that: casement ontology and shading lining are bonded by adhesive
Or suture is sewed together.
4. casement according to claim 3, it is characterised in that: the left and right sides of casement ontology and shading lining with
And top margin is fixed together.
5. casement according to claim 1, it is characterised in that: casement and base fabric are cotton, dacron or tender wash
Any one of blended fabric of synthetic fibre.
6. casement according to claim 1, it is characterised in that: TPU film is the waterproof of the black with a thickness of 0.02mm
Breathable films.
7. a kind of production method of casement, it is characterised in that: include the following steps,
Step 1, the TPU film after the roller coating PU glue of base fabric side with thickness no more than 0.02mm are bonded, press to be formed through pressure roller
Shading lining;
The two sides of casement ontology and lining are sewed together using sewing device, then cut into pre- scale by step 2
It is very little, one end is sewed together again after cutting.
8. the production method of casement according to claim 7, it is characterised in that: TPU film by film-blowing process prepare and
At.
9. the production method of casement according to claim 8, it is characterised in that: TPU film is by by TPU resin, TPU
Modifying agent and carbon black are dosed into stirred in mixing machine after enter heating plasticizing in screw extruder, then film extrusion, inflation, cold
But be formed, then drawn and be surface-treated, then again draw after trimming, cut and cut open side, finally crimp scroll
At.
10. the production method of casement according to claim 9, it is characterised in that: according to the mass fraction, TPU resin,
TPU modifying agent and carbon black are respectively 100-120 parts, 4-6 parts, 0.3-1 parts, wherein TPU modifying agent graphene oxide, poly- rice type
TPU and nano-titanium dioxide are mixed by 50:40:5.