CN110396312A - 一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法 - Google Patents
一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法 Download PDFInfo
- Publication number
- CN110396312A CN110396312A CN201910737655.XA CN201910737655A CN110396312A CN 110396312 A CN110396312 A CN 110396312A CN 201910737655 A CN201910737655 A CN 201910737655A CN 110396312 A CN110396312 A CN 110396312A
- Authority
- CN
- China
- Prior art keywords
- preparation
- environment
- friendly type
- resisting
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，包括：氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝，其中氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝的加入比例为20%、40%、2%、12%、5%、1%、6%、2%、1.5%、2.5%、3%、3%、1%、1%、1%。该涂料具有杀菌几消除有害物质的功能，环保型好，具有耐水性、耐酸碱腐蚀好的功能，满足人们对于涂料环保型和安全性的要求。
Description
技术领域
本发明涉及到一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，属于无机涂料的领域。
背景技术
随着社会的发展，人们对于自身以及环境的保护越来越高，对于居住环境的涂料要求越来越高，但是现在使用的无机涂料耐腐蚀性较差。
为此，设计一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，通过在该涂料中添加氢氧化钙，可以提供杀菌防火以及耐水性的功能；通过在该涂料中添加氧化钴、氧化铬及氧化铝，提高涂料的防火以及耐高温的特性；通过在该涂料中添加硅溶胶，用于提高涂料的粘连性，并改善了氢氧化钙强度较差、容易脱落的情况，且硅溶胶具备抗酸碱腐蚀的功能；通过在该涂料中添加贝壳粉，可以消除室内产生的有害物质，提升环保效果；通过在该涂料中添加云母，可以提高涂料的附着能力，进一步防止出现脱落情况。
发明内容
为解决现有技术的不足，本发明的目的在于，提供一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，该涂料具有杀菌几消除有害物质的功能，环保型好，具有耐水性、耐酸碱腐蚀好的功能，满足人们对于涂料环保型和安全性的要求。
本发明解决其技术问题所采用的技术方案是：一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，包括：氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法中，氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝的加入比例为：20%、40%、2%、12%、5%、1%、6%、2%、1.5%、2.5%、3%、3%、1%、1%、1%。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，可以加工成粉末状。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，可以加工成乳液状。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其一种具体制备方法如下：
步骤1，准备原材料氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝；
步骤2，先添加40份水，然后加入20份氢氧化钙、2份云母粉、12份硅酸钾、1份氯化钠、5份贝壳粉、2.5份颜料、3份分散剂，搅拌混合；
步骤3，将步骤2中的混合物混合均匀后加入氧化钴、氧化铬、氧化铝、膨润土，进行搅拌；
步骤4，在步骤3中的混合物中加入增稠剂、硅溶胶，搅拌均匀，完成该无机涂料的制备过程。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其中在制备过程中所述的步骤2按照1200r/min的转速转动30分钟；所述的步骤3按照1200r/min的转速继续搅拌50分钟；所述的步骤4调制300r/min的转速搅拌30分钟。
本发明的有益效果是：
（1）通过在该涂料中添加氢氧化钙，可以提供杀菌防火以及耐水性的功能；
（2）通过在该涂料中添加氧化钴、氧化铬及氧化铝，提高涂料的防火以及耐高温的特性；
（3）通过在该涂料中添加硅溶胶，用于提高涂料的粘连性，并改善了氢氧化钙强度较差、容易脱落的情况，且硅溶胶具备抗酸碱腐蚀的功能；
（4）通过在该涂料中添加贝壳粉，可以消除室内产生的有害物质，提升环保效果；
（5）通过在该涂料中添加云母，可以提高涂料的附着能力，进一步防止出现脱落情况。
附图说明
图1为一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法流程示意图。
具体实施方式
下面结合附图对本发明作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，包括：氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法中，氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝的加入比例为：20%、40%、2%、12%、5%、1%、6%、2%、1.5%、2.5%、3%、3%、1%、1%、1%。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，可以加工成粉末状。
上述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，可以加工成乳液状。
实施例1
本实施例一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，步骤如下：
步骤1，准备原材料氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝；
步骤2，先添加40份水，然后加入20份氢氧化钙、2份云母粉、12份硅酸钾、1份氯化钠、5份贝壳粉、2.5份颜料、3份分散剂，搅拌混合；
步骤3，将步骤2中的混合物混合均匀后加入氧化钴、氧化铬、氧化铝、膨润土，进行搅拌；
步骤4，在步骤3中的混合物中加入增稠剂、硅溶胶，搅拌均匀，完成该无机涂料的制备过程。
进一步地，所述的步骤2按照1200r/min的转速转动30分钟；所述的步骤3按照1200r/min的转速继续搅拌50分钟；所述的步骤4调制300r/min的转速搅拌30分钟。
综上所述，本发明一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，该涂料具有杀菌几消除有害物质的功能，环保型好，具有耐水性、耐酸碱腐蚀好的功能，满足人们对于涂料环保型和安全性的要求，具有良好的应用前景。
Claims (5)
1.一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其特征在于：包括氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝，其中氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝的加入比例为：20%、40%、2%、12%、5%、1%、6%、2%、1.5%、2.5%、3%、3%、1%、1%、1%。
2.根据权利要求1所述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其特征在于：可以加工成粉末状。
3.根据权利要求1所述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其特征在于：可以加工成乳液状。
4.一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其特征在于：其一种具体制备方法如下：
步骤1，准备原材料氢氧化钙、水、云母、硅酸钾、贝壳粉、氯化钠、硅溶胶、膨润土、消泡石、颜料、分散剂、增稠剂、氧化钴、氧化铬、氧化铝；
步骤2，先添加40份水，然后加入20份氢氧化钙、2份云母粉、12份硅酸钾、1份氯化钠、5份贝壳粉、2.5份颜料、3份分散剂，搅拌混合；
步骤3，将步骤2中的混合物混合均匀后加入氧化钴、氧化铬、氧化铝、膨润土，进行搅拌；
步骤4，在步骤3中的混合物中加入增稠剂、硅溶胶，搅拌均匀，完成该无机涂料的制备过程。
5.根据权利要求4所述的一种环保型水性耐碱、耐腐蚀无机涂料及其制备方法，其特征在于：其中在制备过程中所述的步骤2按照1200r/min的转速转动30分钟；所述的步骤3按照1200r/min的转速继续搅拌50分钟；所述的步骤4调制300r/min的转速搅拌30分钟。