CN101709187B - 一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法 - Google Patents

一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法 Download PDF

Info

Publication number
CN101709187B
CN101709187B CN2009101995923A CN200910199592A CN101709187B CN 101709187 B CN101709187 B CN 101709187B CN 2009101995923 A CN2009101995923 A CN 2009101995923A CN 200910199592 A CN200910199592 A CN 200910199592A CN 101709187 B CN101709187 B CN 101709187B
Authority
CN
China
Prior art keywords
powder
dry powder
coating
percent
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009101995923A
Other languages
English (en)
Other versions
CN101709187A (zh
Inventor
蔡东辉
谢丽青
李莹红
吕遐师
盛琳芳
陈颖
陆文雄
麻新闻
程启朝
郑爱新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beavin Chemical Building System Shanghai Co ltd
Shanghai Supe Chemical Co ltd
University of Shanghai for Science and Technology
Original Assignee
Beavin Chemical Building System Shanghai Co ltd
Shanghai Supe Chemical Co ltd
University of Shanghai for Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beavin Chemical Building System Shanghai Co ltd, Shanghai Supe Chemical Co ltd, University of Shanghai for Science and Technology filed Critical Beavin Chemical Building System Shanghai Co ltd
Priority to CN2009101995923A priority Critical patent/CN101709187B/zh
Publication of CN101709187A publication Critical patent/CN101709187A/zh
Application granted granted Critical
Publication of CN101709187B publication Critical patent/CN101709187B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法，属化学建筑材料及固体废弃物综合利用技术领域。本发明的原料配方如下：高炉矿渣微粉80～90wt％，钛白粉3～8wt％，灰钙粉3～8wt％，可再分散乳胶粉3～6wt％，保水剂0.2～0.6wt％，消泡剂0.05～0.2wt％。将上述各原料按上述配方称量配料，将所得配合料投入搅拌机中，充分搅拌15分钟，经充分混合均匀后，即得环保型干粉内墙涂料；使用时加入适量水分充分调和后即可进行涂饰和批刮墙面。本发明的涂料具有优良的施工性能和使用效能。该涂料粘结力强、耐擦洗、耐碱、耐水，涂膜不易开裂；另外，涂料无有机挥发物，无毒无味，对人体没有损害。

Description

一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法
技术领域
本发明涉及一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法，属化学建筑材料及固体废弃物综合利用技术领域。
背景技术
随着当前科学技术的发展，人民生活水平的提高，对自己居住环境提出了越来越高的要求，同时随着人们环保意识的增强，对室内污染和VOC越来越受到公众的关注。而当前用作内墙的建筑装饰涂料广泛使用的是乳胶漆，乳胶涂料以水为分散介质，其在环保方面具有一定的优势，但是为了改善乳胶漆的性能，在涂料配方中还需要加入一定量的助剂，在涂料成膜过程中，会迁移至涂料表面并挥发出VOC，此外乳液中残余的单体也构成VOC，对人们的身体健康具有危害性。(VOC是有机挥发物简称)
发明内容
本发明的目的是利用高炉矿渣微粉作为主要原料制备一种环保型干粉内墙涂料。
本发明一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法，其特征在于具有以下的过程和步骤：
a.确定原料配方，选定所用的原料及其重量百分配比；各原料组分及其重量百分比如下：
高炉矿渣微粉    80～90％；
钛白粉          3～8％；
灰钙粉          3～8％；
可再分散乳液粉  3～6％；
保水剂          0.2～0.6％；
消泡剂          0.05～0.2％；
所述的高炉矿渣微粉为白色，其化学成分为：(wt％)Fe2O3 0.4，CaO 40.9，SiO2 30.5，Al2O3 13.9，MgO 8.6，TiO2 0.7，P2O5 0.02，S 2.5，MnO 0.2；其余2.28；比表面积≥500m2/kg；
所述的钛白粉为锐钛型钛白粉；
所述的灰钙粉是一种混合型活性填料，由氧化钙、氢氧化钙和少量碳酸钙按一定比例混合而成，细度为325目；CaO∶Ca(OH)2∶CaCO3＝1∶1∶0.1；
所述的可由分散乳胶粉为苯乙烯-丙烯酸乳胶粉，丙烯酸酯乳胶粉、酯酸乙烯-乙烯乳胶粉中的任一种；
所述的保水剂为甲基纤维素、乙基纤维素、羟乙类纤维素、羟乙基甲基纤维素，羟丙基甲基纤维素中的任一种；细度为100目；
所述的消泡剂为干粉消泡剂；
b.按照上述配方分别称量配料，将配合料放入混合机中，经充分均匀混合，得到干粉内墙涂料；使用时加入适量水即可使用。
本发明的方法制得的环保型干粉内墙涂料具有良好的施工性能和使用效能；具有很高的粘结力和耐擦洗性；涂膜不易开裂。另外该涂料具有耐碱、耐水性能；而且涂料没有有机挥发物成分，无毒无味，故降低了制造成本；也为固体废弃物高炉水淬矿渣的利用开辟了一条新途径。本发明涂料为固体干粉，其贮存期长，且能够以包装形式运输和销售，可降低生产运输环节的费用。本发明的干粉内墙涂料使用方便，只需加入一定量的水，搅拌均匀即可使用。本发明制备干粉涂料的工艺方法极为简单，操作方便，便于推广。
具体实施方式
现将本发明的具体实施例叙述于后。
实施例1
本实施例制备100kg环保型干粉内墙涂料为例，制备过程如下：
按规定的原料配方称量，用量如下：
Figure GSB00000640789300021
将上述各原料依次投入搅拌机中，充分搅拌15分钟，经充分混合均匀后，即得环保型干粉内墙涂料；使用时加入适量水充分调和后即可涂饰和批刮。
实施例2
本实施例制备100kg高炉矿渣基干粉内墙涂料为例，制备过程如下：
按规定的原料配方称量，用量如下：
Figure GSB00000640789300031
将上述各原料依次投入搅拌机中，充分搅拌15分钟，经充分混合均匀后，即得高炉矿渣基内墙干粉涂料；使用时加入适量水充分调和后即可涂饰和批刮。

Claims (1)

1.一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法，其特征在于具有以下的过程和步骤：
a.确定原料配方，选定所用的原料及其重量百分配比；各原料组分及其重量百分比如下：
高炉矿渣微粉    80～90％；
钛白粉          3～8％；
灰钙粉          3～8％；
可再分散乳液粉  3～6％；
保水剂          0.2～0.6％；
消泡剂          0.05～0.2％；
所述的高炉矿渣微粉为白色，其化学成分为：(wt％)Fe2O3 0.4，CaO 40.9，SiO2 30.5，Al2O3 13.9，MgO 8.6，TiO2 0.7，P2O5 0.02，S 2.5，MnO 0.2；其余2.28；比表面积≥500m2/kg；
所述的钛白粉为锐钛型钛白粉；
所述的灰钙粉是一种混合型活性填料，由氧化钙、氢氧化钙和少量碳酸钙按一定比例混合而成，细度为325目；CaO∶Ca(OH)2∶CaCO3＝1∶1∶0.1；
所述的可由分散乳胶粉为苯乙烯-丙烯酸乳胶粉，丙烯酸酯乳胶粉、酯酸乙烯-乙烯乳胶粉中的任一种；
所述的保水剂为甲基纤维素、乙基纤维素、羟乙类纤维素、羟乙基甲基纤维素，羟丙基甲基纤维素中的任一种；细度为100目；
所述的消泡剂为干粉消泡剂；
b.按照上述配方分别称量配料，将配合料放入混合机中，经充分均匀混合，得到干粉内墙涂料；使用时加入适量水即可使用。
CN2009101995923A 2009-11-26 2009-11-26 一种以高炉矿渣微粉为主要原料的环保型干粉内墙涂料的制备方法 Expired - Fee Related CN101709187B (zh)