CN110373763A - Short fine packet polypropylene fiber yarn of one kind and preparation method thereof and a kind of fabric - Google Patents
Short fine packet polypropylene fiber yarn of one kind and preparation method thereof and a kind of fabric Download PDFInfo
- Publication number
- CN110373763A CN110373763A CN201910513797.8A CN201910513797A CN110373763A CN 110373763 A CN110373763 A CN 110373763A CN 201910513797 A CN201910513797 A CN 201910513797A CN 110373763 A CN110373763 A CN 110373763A
- Authority
- CN
- China
- Prior art keywords
- yarn
- polypropylene
- short fine
- fiber
- rove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of short fine packet polypropylene fiber yarn and preparation method thereof and a kind of fabrics, belong to field of textiles.Short fine packet polypropylene fiber yarn provided by the invention, is made of clad and sandwich layer, and the material of the clad is staple fiber, and the material of the sandwich layer is polypropylene filament yarn.The present invention enables short fine packet polypropylene fiber yarn provided by the invention to transmit vapor by the capillary in fabric under the collective effect of polypropylene filament yarn and staple fiber, and short fine packet polypropylene fiber yarn itself does not play any absorption, has preferable moisture absorbing and sweat releasing effect；In addition, the present invention is under the collective effect of polypropylene filament yarn and staple fiber, so that short fine packet polypropylene fiber yarn provided by the invention has preferable warmth retention property.Embodiment the result shows that, short fine packet polypropylene fiber yarn provided by the invention has apparent capillary effect, and clo value is higher, and warmth retention property is preferable.
Description
Technical field
The present invention relates to field of textiles, more particularly to a kind of short fine packet polypropylene fiber yarn and preparation method thereof and a kind of fabrics.
Background technique
Fabric in the prior art is generally formed by weaving by yarn, common yarn include natural fiber, terylene, nylon,
Cotton, fiber crops, polyester fiber etc..During the broiling summer, the wick effect of fabric directly affects the level of comfort of clothing, in addition cold
Cold winter, the warming effect of fabric also have great influence to severe cold is resisted.But the wick effect of fabric in the prior art
It is undesirable with warming effect, it is unable to satisfy requirement of the people to fabric wicking properties and thermal property.
Summary of the invention
The present invention provides a kind of short fine packet polypropylene fiber yarn and preparation method thereof and a kind of fabric, short fibres provided by the invention
Packet polypropylene fiber yarn has preferable wicking properties and thermal property.
The present invention provides a kind of short fine packet polypropylene fiber yarns, are made of clad and sandwich layer, the material of the clad is
Staple fiber, the material of the sandwich layer are polypropylene filament yarn.
Preferably, the line density of the short fine packet polypropylene fiber yarn is 9.7~150 Tekes.
Preferably, the material of the staple fiber includes one of cotton, fiber crops, polyester fiber and tencel or a variety of.
Preferably, the fineness of the polypropylene filament yarn is 10D~300D.
The present invention provides the preparation methods of short fibre packet polypropylene fiber yarn described in above-mentioned technical proposal, comprising the following steps:
(1) staple fiber is successively passed through to blowing, cotton carding, drafting and rove processing, obtains rove；
(2) rove and polypropylene filament yarn are subjected to drawing-off respectively, and the rove and polypropylene filament yarn are converged in front roller
It closes；
(3) after front roller exports, the rove obtains polypropylene filament yarn looping, twisting for the rove and polypropylene filament yarn
Short fibre packet polypropylene fiber yarn.
Preferably, the drafting multiple of rove and polypropylene filament yarn independently is 1.01~1.25 in the step (2).
Preferably, the length of staple fiber is 15~51mm after drawing-off.
The present invention also provides a kind of fabrics, including warp thread and weft yarn；The weft yarn is short fibre described in above-mentioned technical proposal
The short fine packet polypropylene fiber yarn that packet polypropylene fiber yarn or above-mentioned technical proposal the method are prepared.
Preferably, the filling density of the fabric is 20~100 pieces/inch.
Preferably, the fabric through it is close be 30~120 pieces/inch
The present invention provides a kind of short fine packet polypropylene fiber yarns, are made of clad and sandwich layer, the material of the clad is
Staple fiber, the material of the sandwich layer are polypropylene filament yarn.In the present invention, polypropylene fibre passes through staple fiber in the short fine packet polypropylene fiber yarn
Capillarity, enable short fine packet polypropylene fiber yarn provided by the invention to transmit vapor, and short fine packet polypropylene fiber yarn sheet
Body does not play any absorption, has preferable moisture absorbing and sweat releasing effect；In addition, the present invention is in the common of polypropylene filament yarn and staple fiber
Under effect, so that short fine packet polypropylene fiber yarn provided by the invention has preferable warmth retention property, staple fiber increases the comfortable of fabric
Degree, pliability.Embodiment the result shows that, short fine packet polypropylene fiber yarn provided by the invention has an apparent capillary effect, and gram
Sieve value is higher, and warmth retention property is preferable.
Specific embodiment
The present invention provides a kind of short fine packet polypropylene fiber yarns, are made of clad and sandwich layer, the material of the clad is
Staple fiber, the material of the sandwich layer are polypropylene filament yarn.
In the present invention, the line density of the short fine packet polypropylene fiber yarn is preferably 9.7~150 Tekes, further preferably
For 20~130 Tekes, more preferably 50~100 Tekes.
In the present invention, the clad material of the short fine packet polypropylene fiber yarn is staple fiber, and the material of the staple fiber is excellent
Choosing includes one of cotton, fiber crops, polyester fiber and tencel or a variety of.
In the present invention, the sandwich layer material of the short fine packet polypropylene fiber yarn is polypropylene filament yarn, the fineness of the polypropylene filament yarn
Preferably 10D~300D, further preferably 50~250D, more preferably 100~200D.
Short fine packet polypropylene fiber yarn provided by the invention, using polypropylene filament yarn as sandwich layer, is effectively improved using staple fiber as clad
The Plug design and warmth retention property of short fine packet polypropylene fiber yarn.
The present invention provides the preparation methods of short fibre packet polypropylene fiber yarn described in above-mentioned technical proposal, comprising the following steps:
(1) staple fiber is successively passed through to blowing, cotton carding, drafting and rove processing, obtains rove；
(2) rove and polypropylene filament yarn are subjected to drawing-off respectively, and the rove and polypropylene filament yarn are converged in front roller
It closes；
(3) after front roller exports, the rove obtains polypropylene filament yarn looping, twisting for the rove and polypropylene filament yarn
Short fibre packet polypropylene fiber yarn.
Staple fiber is successively passed through blowing, cotton carding, drafting and rove processing by the present invention, obtains rove.The present invention to blowing,
The specific embodiment of cotton carding, drafting and rove does not specially require, using mode well-known to those skilled in the art.
In carding process, sliver exporting speed is preferably 120~160m/min, further preferably 130~150m/min, carded sliver Dry Weight per Unit
Preferably 18~22g/5m, further preferably 19~21g/5m.During drafting, present invention preferably employs twice merging,
Specifically include head and and two simultaneously, the head and during, Dry Weight per Unit is preferably 18~21g/5m, further preferably 20g/5m,
Back zone drafting multiple is preferably 1.8~1.95 times, preferably 6 and is closed；Described two and during, Dry Weight per Unit is preferably 18~
20g/5m, back zone drafting multiple are preferably 1.3~1.4 times, preferably 8 and are closed.During rove, the rove Dry Weight per Unit
Preferably 5.5~7.2g/5m, the design twist is preferably 3.9~5.5, and more preferably 4.0~5.0, back area draft is preferably 1.13
~1.45, more preferably 1.13~1.20, roller gauge is preferably 10mm*22mm*33mm.
After obtaining rove, the rove and polypropylene filament yarn are carried out drawing-off by the present invention respectively, and by the rove and polypropylene fibre
Long filament converges in front roller.In the present invention, the drafting multiple of the rove and polypropylene filament yarn independently be preferably 1.01~
1.25, further preferably 1.05~1.2, more preferably 1.1~1.15, present invention preferably employs the modes of roller draft to thick
Yarn and polypropylene filament yarn carry out drawing-off.In the present invention, the staple length after drawing-off is preferably 15~51mm, further preferably
20~50mm, more preferably 30~40mm.After drawing-off, the present invention converges rove and polypropylene filament yarn in front roller.
For the present invention by rove and polypropylene filament yarn after front roller exports, the rove obtains polypropylene filament yarn looping, twisting
Short fibre packet polypropylene fiber yarn.The present invention does not specially require looping, the specific embodiment of twisting, using those skilled in the art
Known mode.
The present invention also provides a kind of fabric, the fabric includes warp thread and weft yarn；The weft yarn is above-mentioned technical proposal
The short fine packet polypropylene fiber yarn that the short fine packet polypropylene fiber yarn or above-mentioned technical proposal the method are prepared.
In the present invention, the filling density of the fabric is preferably 20~100 pieces/inch, further preferably 40~80/English
It is very little, more preferably 50~70 pieces/inch.
In the present invention, the fabric through it is close preferably 30~120 pieces/inch, further preferably 50~100/
Inch, more preferably 70~80 pieces/inch.
In the present invention, it is fine to preferably include cotton, hair, silk, fiber crops, bamboo fibre, soybean fiber, corn for the material of the warp thread
One or more scribbled in dimension, acrylic fibers, terylene, tencel or above-mentioned substance.
Short fibre packet polypropylene fiber yarn is weft yarn described in fabric techniques described above scheme provided by the invention, effectively increases fabric
Plug design and warmth retention property.
In the present invention, the fabric preferably includes spring and summer knitted T-shirt, Polo shirt, socks, gym suit and autumn and winter ox
The fabrics such as son.
The present invention does not specially require the preparation method of fabric, is using method well-known to those skilled in the art
Can, such as jet openpore manufacturing process or cowboy's manufacturing process.
Below in conjunction with the embodiment in the present invention, the technical solution in the present invention is clearly and completely described.
Embodiment 1
(1) polypropylene filament yarn (being abbreviated as 100DPP) that fineness is 100D is introduced into front roller, polypropylene fibre by feeding unit
Filament drawing multiple is 1.1 times, to ensure that polypropylene filament yarn is fed with certain tension；
(2) by short cellucotton, principal length, successively through blowing, cotton carding, drafting, Roving Frames, is prepared into 29mm
The rove of 5.5g/10m；
(3) cotton carding speed 130m/min in step (2), quantitative 20g/5m；
(4) head and speed 600m/min in step (2), quantitative 21g/5m, back area draft 1.85；
(5) two and speed 600m/min in step (2), quantitative 20g/5m, back area draft 1.35；
(6) rove ingot speed 950r/min in step (2), the twist 4.87, quantitative 5.5g/10m；Roller gauge 10mm*22mm*
33mm；
(7) rove that step (2) obtains is converged by drawing-off and the single polypropylene filament yarn of fineness 100D in front roller, together
When, it is ensured that the yarn position accurate positioning of fiber；
(8) rove passes through twisting for polypropylene filament yarn looping, clamping after front roller exports, and short fine packet polypropylene fiber yarn is made,
It is abbreviated as JC20S+100DPP.
The short fibre packet polypropylene fiber yarn JC20S+100DPP that embodiment 1 is prepared weaves weft-knitting on circular weft knitting machine
Single jersey.
Comparative example 1
Using traditional ring spinning yarn JC20S as yarn, weft-knitting single jersey is weaved on circular weft knitting machine.
Embodiment 2
According to the preparation method of embodiment 1, using cotton short fiber TSC10S as clad；It is the polypropylene filament yarn of 100D with fineness
For sandwich layer, cotton staple packet polypropylene fiber yarn TSC10S+100DPP is prepared；Using C58.3tex ring as warp thread, with short fine packet polypropylene staple fibre spun yarn
Line TSC10S+100DPP is weft yarn, 1 in use 2 under twill-weave, weaved on rapier loom, it is woven through it is close be 45/
Inch, filling density is 42 pieces/inch.
Comparative example 2
It is tested according to the method for embodiment 2, difference is polypropylene filament yarn replacing with terylene, and short fine packet is prepared
Spun polyester thread TSC10S+100DDTY；
Using C10S ring as warp thread, using TSC10S+100DDTY as weft yarn, 1 in use 2 under twill-weave, knitted in arrow shaft
Weaved on machine, it is woven through it is close be 45 pieces/inch, filling density is 42 pieces/inch.
Embodiment 3
It prepares respectively according to the method for embodiment 1:
(sandwich layer is the polypropylene filament yarn of fineness 50D to JC40S+50DPP；Staple fiber is JC40S)；(sandwich layer is JC32S+75DPP
The polypropylene filament yarn of fineness 75D；Staple fiber is JC32S)；(sandwich layer is the polypropylene filament yarn of fineness 100D to JC20S+100DPP；Staple fiber
For JC20S)；(sandwich layer is the polypropylene filament yarn of fineness 100D to JC16S+100DPP；Staple fiber is JC16S)；C21S+75DPP (sandwich layer
For the polypropylene filament yarn of fineness 75D；Staple fiber is C21S)；(sandwich layer is the polypropylene filament yarn of fineness 100D to C20S+100DPP；Staple fiber
For C20S)；(sandwich layer is the polypropylene filament yarn of fineness 100D to C16S+100DPP；Staple fiber is C16S)；(sandwich layer is C12S+100DPP
The polypropylene filament yarn of fineness 100D；Staple fiber is C12S)；(sandwich layer is the polypropylene filament yarn of fineness 150D to C10S+150DPP；Staple fiber
For C10S).
Performance test
The knitting single jersey wicking properties obtained to embodiment 1 and comparative example 1 are tested, and test result is as shown in table 1:
The wicking properties test result of table 1 embodiment 1 and 1 yarn of comparative example
By 1 test result of table it is found that short fibre packet polypropylene fiber yarn JC20S+100DPP provided by the invention and traditional JC20S
Yarn is compared, and the present invention provides short fibre packet polypropylene fiber yarn JC20S+100DPP with excellent wick effect, and capillary effect is remote
Much higher than traditional JC20S yarn, illustrate that short fine packet polypropylene fiber yarn provided by the invention has excellent wicking wet transmitting performance.
The thermal property for the fabric that embodiment 2 and comparative example 2 are prepared is tested, test result is as shown in table 2:
The thermal property test result of table 2 embodiment 2 and 2 fabric of comparative example
| Kind | Capillary effect cm (broadwise) | Clo value DEG C ㎡/W | Heat preservation rate % |
| Embodiment 2 | 8.9 | 0.208 | 26.8 |
| Comparative example 2 | 7.3 | 0.139 | 19.8 |
By 2 test result of table it is found that the fabric that the embodiment of the present invention 2 provides has better thermal insulation property, thus illustrate
Short fine packet polypropylene fiber yarn provided by the invention has preferable thermal insulation property.In the present invention, clo value is description clothes or knits
The engineering unit of object heat-insulation warm keeping performance (i.e. thermal resistance), at 20~21 DEG C of room temperature, relative humidity is no more than 50%, air velocity
In environment no more than 10cm/s (the indoor normal airflow speed for being equivalent to ventilation equipment), a people sits quietly or is engaged in slightly
Mental labour, the insulation value for keeping worn clothes when comfort conditions are 1 clo value；The size of clo value illustrate fabric it is warming every
The height of hot degree, clo value is higher, illustrates that heat retention of the fabric is better.
The JC40S+50DPP that embodiment 3 is provided；JC32S+75DPP；JC20S+100DPP；JC16S+100DPP；C21S
+75DPP；C20S+100DPP；C16S+100DPP；C12S+100DPP and C10S+150DPP weave latitude on circular weft knitting machine respectively
Knitting single jersey is compiled, wicking properties are carried out to obtained knitting single jersey and are tested, test result is as shown in table 3:
The wicking properties for the short fine packet polypropylene fiber yarn that 3 embodiment 3 of table provides
The JC40S+50DPP that embodiment 3 is provided；JC32S+75DPP；JC20S+100DPP；JC16S+100DPP；C21S
+75DPP；C20S+100DPP；C16S+100DPP；The thermal insulation property of C12S+100DPP and C10S+150DPP is tested, with
C58.3tex ring is warp thread, the short fine packet polypropylene fiber yarn obtained respectively using embodiment 3 as weft yarn, 1 in use 2 under twill group
Knit, weaved on rapier loom, it is woven through it is close be 45 pieces/inch, filling density is 42 pieces/inch.The fabric that weaving is obtained
Thermal property is tested, and test result is as shown in table 4:
The thermal property for the short fine packet polypropylene fiber yarn that 4 embodiment 3 of table provides
It follows that the short fine packet polypropylene fiber yarn that embodiment 3 provides all has preferable wicking wet transmitting performance and warmth retention property
Energy.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (10)
1. a kind of short fine packet polypropylene fiber yarn, is made of, the material of the clad is staple fiber, the sandwich layer clad and sandwich layer
Material be polypropylene filament yarn.
2. short fine packet polypropylene fiber yarn according to claim 1, which is characterized in that the line density of the short fine packet polypropylene fiber yarn
For 9.7~150 Tekes.
3. short fine packet polypropylene fiber yarn according to claim 1 or 2, which is characterized in that the material of the staple fiber include cotton,
One of fiber crops, polyester fiber and tencel are a variety of.
4. short fine packet polypropylene fiber yarn according to claim 1 or 2, which is characterized in that the fineness of the polypropylene filament yarn is 10D
~300D.
5. the preparation method of any one of Claims 1 to 4 short fine packet polypropylene fiber yarn, comprising the following steps:
(1) staple fiber is successively passed through to blowing, cotton carding, drafting and rove processing, obtains rove；
(2) rove and polypropylene filament yarn are subjected to drawing-off respectively, and the rove and polypropylene filament yarn are converged in front roller；
(3) after front roller exports, polypropylene filament yarn looping, twisting are obtained short fibre by the rove for the rove and polypropylene filament yarn
Packet polypropylene fiber yarn.
6. preparation method according to claim 5, which is characterized in that rove and polypropylene filament yarn leads in the step (2)
It stretches multiple and independently is 1.01~1.25.
7. preparation method according to claim 5 or 6, which is characterized in that the length of staple fiber is 15~51mm after drawing-off.
8. a kind of fabric, including warp thread and weft yarn；The weft yarn is any one of Claims 1 to 4 short fine packet polypropylene fiber yarn
Or the short fine packet polypropylene fiber yarn that any one of claim 5~7 the method is prepared.
9. fabric according to claim 8, which is characterized in that the filling density of the fabric is 20~100 pieces/inch.
10. fabric according to claim 8 or claim 9, which is characterized in that the fabric through it is close be 30~120 pieces/inch.