CN107513787A - A kind of length complex yarn and its production method - Google Patents
A kind of length complex yarn and its production method Download PDFInfo
- Publication number
- CN107513787A CN107513787A CN201610416491.7A CN201610416491A CN107513787A CN 107513787 A CN107513787 A CN 107513787A CN 201610416491 A CN201610416491 A CN 201610416491A CN 107513787 A CN107513787 A CN 107513787A
- Authority
- CN
- China
- Prior art keywords
- yarn
- filament
- rove
- long filament
- length
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of length complex yarn and its production method.The complex yarn is combined by long filament and spun yarn, and long filament is heart yarn, spun yarn is sheath yarn, and heart yarn and sheath yarn are eccentric structure, and wherein long filament is polypropylene filament yarn, accounts for the 10~50% of the complex yarn gross weight.Compared with the conventional spinning frame cored processing method of length composite yarn, cored effect is more superior, and uses polypropylene filament yarn to be incubated, the effect of water-absorbing fast-drying as heart yarn.
Description
Technical field
The present invention relates to a kind of new cotton yarn and its production method, and in particular to a kind of long and short fiber containing polypropylene fibre is answered
Yarns and its production method.
Background technology
As the improvement of people's living standards, everybody is for textile material, particularly functional material, from past
That body is covered in requirement, be slowly evolved into it is present to water-absorbing fast-drying, heating, insulation etc. functional demand, material more become
In diversification.
Wherein, people can prefer for cotton/Modal/viscose glue for the cellulose fibre class functional material of representative,
Because the sense of touch of this kind of material is more comfortable, and gentle non-stimulated, but all using the textile of this fibrid raw material, nothing
Method obtains water-absorbing fast-drying, insulation etc. feature；And strength is not too high, even by above-mentioned fiber and staple fibre
Blending, dimensional stability is simply also improved to a certain extent and controls the occurrence probability of broken hole, but anti-fluffing and anti-pilling
Problem still fails to solve.So it is highly desirable can develop one kind can be used for produce feel be enough and cellulose fibre face
Material matches in excellence or beauty, but also with water-absorbing fast-drying, the yarn of the fabric of heat insulation function.
Also occur the such yarn in part on the market at present, for example one kind is disclosed in patent document CN200310103660
Really twisted with the fingers by the chopped fiber beam being drafted and by the synthetic fibers multifilament of fibrillation on spinning frame by adding while the side wound
The length complex yarn that formula obtains, long filament after electric shredding at the front roller with the chopped fiber Shu Chonghe after drawing-off, twisting,
By the yarn that above-mentioned processing obtains due to being that chopped fiber beam looping lives synthetic fibers multifilament, or synthetic fibers multifilament and short fibre
Dimension mixing, although the strength of yarn is improved, the stability of production and processing needs further to be improved, particularly short fibre
Dimension is in covered filament, if the looping that can stablize lives to have a huge impact production below and dyeing, if bag
Cover and be not sufficiently stable, be then very easy to phenomena such as band occur.In addition, fibre-opening unit is installed at long filament end so that long filament script
Interlacing is opened, and so can more increase the difficulty of cladding.
The content of the invention
It is an object of the invention to provide one kind cladding stabilization, and with water-absorbing fast-drying, the length composite yarn of heat insulation function
Line and its production method.
The technical solution of the present invention：
In the length complex yarn of the present invention, long filament is heart yarn, spun yarn is sheath yarn, and heart yarn and sheath yarn are eccentric structure, its
Middle long filament is polypropylene filament yarn, accounts for the 10~50% of the complex yarn gross weight.
Compared with the conventional spinning frame cored processing method of length composite yarn, cored is carried out using two rove, and pass through
Self-criticism to reducing rove spacing, reaches the effect being evenly coated.In addition, using polypropylene filament yarn as heart yarn, using its light weight,
The characteristics of water guide, it is incubated, the effect of water-absorbing fast-drying.
Brief description of the drawings
（1）Fig. 1, Fig. 2, Fig. 3, Fig. 4 are the covering yarn structural representation of the present invention, and Fig. 5, Fig. 6, Fig. 7 are the bag of comparative example
Core yarn structure schematic diagram, whereinFor heart yarn,For sheath yarn.
Embodiment
In the length complex yarn of the present invention, long filament is heart yarn, spun yarn is sheath yarn, and from the point of view of fiber cross-sectional, heart yarn
It is eccentric structure with sheath yarn, i.e., heart yarn is not among sheath yarn, but the part beyond the centre of sheath yarn, wherein long filament are
Polypropylene filament yarn, account for the 10~50% of the complex yarn gross weight.Polypropylene fiber has lot of advantages, such as in general chemical fiber
Midst density is most light；With core sucting action, vapor can be transmitted by the capillary in fabric, water guide rapid-drying properties are better than other fibers
Deng.
In view of using polypropylene fibre full-drawn yarn（Abbreviation FDY）, filament is relatively sliding, it is possible to which core can not be completely covered by sheath yarn occur
The phenomenon of yarn；And FDY shrinkage factor is not as good as false twist processing yarn（Abbreviation DTY）, it is difficult to shrink into again after heart yarn exposes.Cause
This, polypropylene filament yarn used in the present invention is preferably polypropylene fibre DTY.
The fiber number of polypropylene filament yarn used in the present invention is preferably 30~75 Denier（Abbreviation D）.Within this range, it is easy to add
Work, and covered effect is good.
The fibrous raw material of spun yarn used in the present invention is preferably the one or more in viscose glue, polyester, acrylic fibers and cotton.
The length complex yarn of the present invention is twist yarn, and twist direction is Z twist directions or S twist directions.According to the sth. made by twisting of yarn
To, when for Z twist directions when, long filament is and to the right no more than right side rove diameter positioned at the center-right position of two rove beams
1/2 position.When for S twist directions when, long filament is positioned at the center-left position of two rove beams, and same to the left to be no more than left side rove straight
1/2 position in footpath., so can be advantageously in carrying when long filament particularly being inserted into the center-right position of rove it is preferred that Z twist directions
The stability of high clad structure.
We are by substantial amounts of experiment discovery repeatedly, the length complex yarn obtained using the cored processing method of routine, outside
The chopped fiber of side is difficult to encase the long filament of inner side completely.The production method of the length composite yarn of the present invention is as follows：Using spun yarn
Machine, first chopped fiber is formed after 2 rove beams successively by single hole horn mouth, buncher, ensure 2 rove interfasciculars every 0~
Long filament is fed among front roller and apron on the basis of 1mm, after then being twisted with rove beam in front roller exit
Compound, 1.5~2.0 times of spinning frame back zone drafting multiple, if back zone drafting multiple is less than 1.5, back zone tension in the roving is big, it is difficult to
Form cored structure.The bell-mouthed width of single hole is preferably 2~3mm；The width of buncher is preferably 2~4mm.
In the present invention, the tension force of long filament is preferably 20~60g.Here tension force locates as long filament creel to guide
Take turns the tension force of section.The tension force of long filament can effectively control the generation of the problems such as final products foaming, looping etc. within this range.
Embodiment
With reference to embodiment and comparative example, the invention will be further described.
The method of testing of each performance and parameter involved in the present invention is as follows.
（1）Clad ratio
30 root long degree 5cm complex yarn is taken, after being wrapped up with viscose staple fibre bar, fills in the copper coin with diameter 1.5mm holes
It is interior, observed after cutting off both ends with blade in microscope.When heart yarn exposes outside in sheath yarn, then it is judged as not coating；When not there is core
Yarn exposes outside in sheath yarn, then is judged as coating.Counted according to the result of 30, calculate cladding radical and account for the hundred of total radical
Ratio is divided to obtain clad ratio.
Embodiment 1
Using Modal fibre（Filament number 0.9D）Be made two rove beams, then by 30D polypropylene filament yarn from front roller with
Fed among apron, then long filament enters positioned at the position of two center-right sides of rove beam with rove beam in front roller exit
It is compound after the twisting of row Z-direction, the Z twist direction length composite yarns of 40 of the present invention are made.Wherein thread-tension 30g, rove interfascicular
Distance 0-1mm, single hole horn mouth width 2mm, buncher width 2mm, 1.9 times of back area draft.
Embodiment 2
Modal fibre is replaced with to filament number 1.2D viscose staple fibre, thread-tension 20g, remaining is made with embodiment 1
The Z twist direction length composite yarns of 50 of the present invention.
Embodiment 3
Mixing system is carried out according to 50/50 ratio using filament number 1.2D short rayon fiber peacekeeping 1.2D Modal chopped fiber
Blending sliver is obtained, then carries out drafting and viscose glue/Modal rove beam two is made, it is then that rove beam and polypropylene filament yarn is compound, it is long
Thread tension 40g, buncher width 3mm, 1.7 times of back area draft, with embodiment 1, the Z twist directions of 30 that the present invention is made are grown for remaining
Short composite yarn.
Embodiment 4
Rove beam two, then compound, the long filament by rove beam and polypropylene filament yarn are made using filament number 1.2D polyester staple fiber
Tension force 40g, buncher width 3mm, 1.7 times of back area draft, the Z twist direction length of 30 of the invention is made with embodiment 1 in remaining
Composite yarn.
Embodiment 5
Carry out according to 50/50 ratio being mixed to prepare two rove using 1.2D short rayon fiber peacekeeping 1.2D polyester staple fiber
Beam, then 50D polypropylene filament yarn is fed among front roller and apron, long filament is positioned at the position of two center-right sides of rove beam
Put, then with rove beam front roller exit carry out Z-direction twisting after it is compound, be made the present invention the Z twist direction length of 30 answer
Close yarn.Wherein thread-tension 40g, the distance 0-1mm of rove interfascicular, single hole horn mouth width 2mm, buncher width 3mm, back zone
1.7 times of drawing-off.
Embodiment 6
Using Modal chopped fiber（Filament number 1.2D）And polyester staple fiber（Filament number 1.2D）Enter according to 50/50 ratio
Row is mixed to prepare blending sliver, then carries out drafting and Modal/terylene rove beam two is made, then by rove beam and polypropylene filament yarn
Compound, the Z twist direction length composite yarns of 40 of the invention are made with embodiment 5 in remaining.
Embodiment 7
Drafting is carried out according to 50/50 ratio using polyester fiber sliver made from sliver made from combed cotton and embodiment 4, is made
Two combed cottons/terylene rove beam, then that rove beam and polypropylene filament yarn is compound, remaining is made the 30 of the present invention with embodiment 5
The Z twist direction length composite yarns of branch.
Embodiment 8
Carried out simultaneously according to 50/50 ratio using viscose rayon sliver made from combed cotton sliver made from embodiment 7 and embodiment 2
Bar, two combed cottons/viscose glue rove beam is made, then that rove beam and polypropylene filament yarn is compound, this is made with embodiment 5 in remaining
The Z twist direction length composite yarns of 30 of invention.
Embodiment 9
The distance of rove interfascicular is adjusted to 1-2mm, with embodiment 8, the length that the Z twist directions of 30 of the present invention are made is answered for remaining
Close yarn.
Embodiment 10
The combed cotton sliver obtained using embodiment 7 forms two rove beams, then by 30D polypropylene filament yarn from front roller and skin
Fed among circle, then long filament carries out Z with rove beam positioned at the position of two center-right sides of rove beam in front roller exit
It is compound after to twisting, the Z twist direction length composite yarns of 20 of the present invention are made.Wherein rove distance 0-1mm, single hole horn mouth
3mm, buncher 4mm, thread-tension 60g, 1.5 times of spun yarn back area draft.
Embodiment 11
Combing sliver made from filament number 1.5D acrylic staple fibre sliver and embodiment 7 is carried out according to 50/50 ratio
Silver mixing, drafting is then carried out again two acrylic fibers/cotton rove beam is made.
Then 75D polypropylene filament yarn is fed among front roller and apron, it is center-left that long filament is located at two rove beams
Side, S is then carried out in front roller exit with rove beam to compound after twisting, the S twist direction length of 20 that the present invention is made is answered
Close yarn.Wherein thread-tension 60g, the distance 0-1mm of rove interfascicular, single hole horn mouth 3mm, buncher 4mm, back area draft 1.5
Times.
Embodiment 12
Twist direction is changed to Z twist directions, the Z twist direction length composite yarns of 20 of the invention are made with embodiment 11 in remaining.
Embodiment 13
Carried out using filament number 1.2D short rayon fiber peacekeeping filament number 0.9D acrylic staple fibre according to 40/60 ratio
Blending sliver is mixed to prepare, then carries out drafting and viscose glue/acrylic fibers rove beam two is made, then the polypropylene filament yarn with 30D is answered
Close, the Z twist direction length composite yarns of 40 of the invention are made with embodiment 1 in remaining.
Embodiment 14
Mixing system is carried out according to 40/60 ratio using filament number 1.2D Modal chopped fiber and 0.9D acrylic staple fibre
Blending sliver is obtained, then carries out drafting and Modal/acrylic fibers rove beam two, then compound with polypropylene filament yarn, thread-tension is made
20g, the Z twist direction length composite yarns of 50 of the invention are made with embodiment 1 in remaining.
Comparative example 1
Two rove beams are made using filament number 1.2D viscose rayons, then carry out compound, rove with 100D polypropylene filament yarns again
The distance 5-6mm of interfascicular, single hole horn mouth 5mm, not using buncher, length composite yarn is made with embodiment 1 in remaining.
Gained composite yarn is parallel construction, does not form the eccentric cored structure of the present invention.
Comparative example 2
Two rove beams are made using filament number 1.2D viscose rayons, then carry out compound, long filament with 30D polypropylene filament yarns again
Power 20g, 1.15 times of back area draft, length composite yarn is made with embodiment 1 in remaining.
Gained composite yarn is parallel construction, does not form the eccentric cored structure of the present invention.
Table 1
Claims (7)
1. a kind of length complex yarn, is combined by long filament and spun yarn, it is characterized in that：The long filament is heart yarn, spun yarn
For sheath yarn, and heart yarn and sheath yarn are eccentric structure, wherein the long filament is polypropylene filament yarn, account for the complex yarn gross weight 10~
50%。
2. length complex yarn according to claim 1, it is characterized in that：The polypropylene filament yarn is polypropylene fibre false twist processing yarn.
3. length complex yarn according to claim 2, it is characterized in that：The fiber number of the polypropylene filament yarn is 30~75 denier Buddhist nuns
You.
4. length complex yarn according to claim 1, it is characterized in that：The fibrous raw material of the spun yarn is viscose glue, gathered
One or more in ester, acrylic fibers and cotton.
5. according to length complex yarn according to any one of claims 1 to 4, it is characterized in that：The length complex yarn is to add
Twisted yarn, and twist direction is Z twist directions or S twist directions.
6. a kind of production method of the length complex yarn described in claim 1, it is characterized in that：Using spinning frame, first by short fibre
Dimension is formed after 2 rove beams successively by single hole horn mouth, buncher, is ensureing 2 rove Shu Binglie 0~2mm of interval base
Long filament is fed among front roller and apron on plinth, it is compound after then being twisted with rove beam in front roller exit, carefully
1.5~2.0 times of yarn machine back area draft.
7. the production method of length complex yarn according to claim 6, it is characterized in that：The tension force of long filament is 20~60g.