CN104790111A - Viscose rayon/coffee carbon blending knitted fabric - Google Patents
Viscose rayon/coffee carbon blending knitted fabric Download PDFInfo
- Publication number
- CN104790111A CN104790111A CN201510200780.9A CN201510200780A CN104790111A CN 104790111 A CN104790111 A CN 104790111A CN 201510200780 A CN201510200780 A CN 201510200780A CN 104790111 A CN104790111 A CN 104790111A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coffee carbon
- yarn
- knitted fabric
- viscose rayon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to viscose rayon/coffee carbon blending knitted fabric. The viscose rayon/coffee carbon blending knitted fabric is characterized by comprising the steps that fabric weave is adopted; plain weaving is carried out on a single face; the horizontal density is 62.5 longitudinal rows/10 cm, the longitudinal density is 44.5 horizontal rows/ 10 cm, and the needle size is 12 G; weaving is carried out on a computerized flat knitting machine; by adopting 40 s, 40% coffee carbon fibers and 60% viscose rayon fibers, yarn siro spinning is carried out, plying is conducted, yarns are obtained, and the doubling twist of yarn is 290 twists/m; the gram weight is 218 g/m<2>. According to the viscose rayon/coffee carbon blending knitted fabric, style and feel of traditional shell fabric are obtained, and functional characteristics such as moisture absorption, air permeability, bacteriostasis, deodorization, warming, heat insulating and far infrared ray launching are obtained, the fabric integrates the health care function and the comfortable function, and the fabric is ideal fabric used for producing socks, underwear, T-shirts and other personal clothes.
Description
Technical field
The present invention relates to a kind of viscose glue/coffee carbon blended knitted fabric.This fabric is mainly used in making the products next to the skin such as socks, underwear, T-shirt.
Background technology
In recent years, along with people's living standard improves day by day, consumption idea is constantly updated, and people more and more pay attention to quality of life and living environment, also more and more higher to the Functional Requirement of clothes, particularly the requirement of the aspect such as health care, feel, quality of clothes is also constantly improved.Simultaneously under the overall situation of economic internationalization and Market integrating, for meeting the demand of international market to high-grade fabric, need use technological means, upgrade traditional fabric, this is also that the development of China's hosiery industry provides a rare chance.
Although China becomes topmost textile production state and country of consumption in the world, its aggregate level lags far behind developed country.Mainly there is following problem: textiles class is confined to low and middle-grade, be functionally also confined to dull warming-type, added value, the scientific and technological content of textile product are also not high, and the market competitiveness is also not strong.Domestic and international market sweater tends to functionalization, raw material diversification, a style great variety of models day by day in addition.
For the production of dress-goods next to the skin such as underwear, socks and T sympathize, to the skin-friendly of fiber and sucting wet air permeability, there is high requirement, develop good spinnability, cost performance is high, moisture absorption is breathed freely, the functional fabric of bacteriostasis, and deodorization, become a developing direction.
Summary of the invention
The object of the invention is to overcome above-mentioned deficiency, provide that a kind of good spinnability, cost performance are high, moisture absorption is breathed freely, the viscose glue of bacteriostasis, and deodorization/coffee carbon blended knitted fabric.
The object of the present invention is achieved like this:
A kind of viscose glue/coffee carbon blended knitted fabric, adopts fabric tissue: one side plain weave.Horizontal close: 62.5 stringers/10cm; Vertical close: 44.5 lines/10cm.Pin number: 12G, Computerized flat knitting machine weaves.Adopt two 40
s, the coffee carbon fiber of 40% and the viscose siro-spinning yarn plying resultant yarn of 60%, and twist per unit is 290 twists/m.Grammes per square metre: 218 grams/m.
Product process flow
→ packaging → warehouse-in is scalded in two kinds of fibre sirospun yarn → doubling → rewindings → knit sheet → running-on → flatcar → hand seam → washing → dry → whole.
Two kinds of fibre sirospun yarn twists are at 920 ~ 1000 sth. made by twisting/m, and twist factor, between 360 ~ 400, can spin quality yarns.
Adopt straight-bar machines technique: when face weave, for fiber Problems existing, first yarn is lubricated and upper Lasaxing Oilfield, to improve the smoothness of yarn, avoid because yarn knotting causes broken yarn in weaving process, thus cause fabric to occur the flaws such as broken hole.
Common viscose fiber good hygroscopicity, is easy to dyeing, not easily plays electrostatic, have good spinning property.Be suitable for making underwear, coat and various adornment.Coffee carbon fiber major function is bacteriostasis, and deodorization, heat up and warming, emitting far-infraredly disperse anion and low-carbon environment-friendly.Water and nutrient are the hotbeds of bacterium, and bacterial reproduction speed depends on that environmental energy provides how many temperature, moisture and nutrient, and the porous adsorption effect of coffee carbon is effectively controlled by body surface moisture, and then play the effect of anti-bacteria breeding.And therefore the foul smell ammonia discharged during bacterial reproduction also significantly reduce, therefore coffee carbon also can effectively deodorizing.Meanwhile, coffee carbon fiber also has intensification warmth retention property, and increasing extent of temperature is high under light illumination than common PET fiber for coffee carbon fiber after tested, put on that coffee carbon dress ornament can enjoy that coffee brings from however warm comfortable sense.
The knit fabric of this project development is woven by the new type functional blended yarn developed and forms, this new type functional yarn utilizes SEILE textile technology blending plying resultant yarn to form, blending raw material adopts the viscose of 60% and the coffee carbon fiber of 40%, the fabric of exploitation is had moisture absorption is breathed freely, bacteriostasis, and deodorization, intensification are warming and emitting far-infrared functional characteristic.Project is mainly for the production of dress-goods next to the skin such as underwear, socks and T sympathize, therefore to the skin-friendly of fiber and sucting wet air permeability, there is high requirement, consider spinning property and the price situation of fiber simultaneously, therefore, project have employed the viscose of 60% and the coffee carbon fiber of 40% carries out blending, and the yarn that blending obtains is woven into through knitting has polyfunctional knit fabric.By trying discovery on, the functional characteristic that this knit fabric not only has that moisture absorption is breathed freely, bacteriostasis, and deodorization, intensification are warming and emitting far-infrared, effectively can also remove the peculiar smell such as tobacco and wine simultaneously.
The functional characteristic that this product has that good moisture absorption is breathed freely, bacteriostasis, and deodorization, intensification are warming and emitting far-infrared.Antibacterial inspection: all reach more than 92% to the bacteriostasis rate of Escherichia coli and staphylococcus aureus, through 20 durable tests, bacteriostasis rate still keeps more than 90%.Content of formaldehyde, far below standard, has environmental protection feature; Color fastness to washing, fastness to rubbing are all higher than standard.Reach standard regulation, meet Grade A requirement.It is the desirable fabric for making the products next to the skin such as socks, underwear, T-shirt.
Detailed description of the invention
The present invention relates to a kind of viscose glue/coffee carbon blended knitted fabric, this product adopts fabric tissue: one side plain weave.Horizontal close: 62.5 stringers/10cm; Vertical close: 44.5 lines/10cm.Pin number: 12G, Computerized flat knitting machine weaves.Adopt two 40
s, the coffee carbon fiber of 40% and the viscose siro-spinning yarn plying resultant yarn of 60%, and twist per unit is 290 twists/m.Grammes per square metre: 218 grams/m.
Not only there is the style of traditional fabric, feel, also have that moisture absorption is breathed freely, functional characteristic that bacteriostasis, and deodorization, intensification are warming and emitting far-infrared.Therefore this fabric collection health care, comfortable, function with integrally, there is the wide prospect of marketing.
Product process flow
→ packaging → warehouse-in is scalded in two kinds of fibre sirospun yarn → doubling → rewindings → knit sheet → running-on → flatcar → hand seam → washing → dry → whole.
The major technique that development process solves is crucial
(1) design of viscose glue/coffee carbon fiber yarn
For the characteristic of viscose and coffee carbon fiber, select respectively: the coffee carbon fiber of 30% and the viscose fiber blending of 70%, the coffee carbon fiber of 40% and the viscose fiber blending of 60% and the coffee carbon fiber of 50% and viscose three kinds of blended yarns of 50%, the fabric functional effect demand that final basis will reach selects the coffee carbon fiber of 40% and the viscose fiber blending scheme of 60%, reaches the requirement of fabric yarn and function thereof.
(2) Spinning Process Design
The mentality of designing of yarn process determines according to the feature of fiber, Yang Qichang, keeps away that it is short, designs and meet fiber bodies characteristic sum self-law, and can make its maximum advantage, can make again the high-quality new type yarn of its minimize shorts.Finally, for the problem that fibre cohesion is poor, determine the spinning method using SEILE textile.In addition, for the problem that yarn easily fluffs, the spinning twist and twist factor is strengthened.Determine that the twist is at 920 ~ 1000 sth. made by twisting/m, twist factor, between 360 ~ 400, can spin quality yarns.
(3) straight-bar machines technique: when face weave, for fiber Problems existing, first lubricates yarn and upper Lasaxing Oilfield, to improve the smoothness of yarn, avoids because yarn knotting causes broken yarn in weaving process, thus causes fabric to occur the flaws such as broken hole.
The level that product reaches
1, technological innovation
(1) innovation of raw material: for ensureing the characteristic that the moisture absorption of yarn is ventilative, have selected the viscose of 60%, simultaneously in order to make fabric have bacteriostasis, and deodorization, heat up warming and emitting far-infrared function, adds the coffee carbon fiber of 40%, to reach required fabric effect.
(2) innovation of spinning method, with SEILE textile technology, solves the problem that fibre cohesion is poor.
(3) optimization of spinning process, by choose reasonable yarn twist, reduces the fluffing of yarn; Rational weaving condition, decreases the breakage phenomena in process.
2, quality level
Through national textile product Quality Supervision and Inspection Center (Jiangyin), authority detects: according to GB18401-2010 " national general safety technical code for textile products ", FZ/T 73005-2012 " low containing wool blend and anti-woollen knitwear ", GB/T 7742.1-2005 " textile fabric bursts performance Part I: bursting strength and burst the mensuration hydraulic method of expansion ratio ", FZ/T73023-2006 " antibiosis knitting product " regulation, meets Grade A that FZ/T 73005-2012 standard specifies and the category-B requirement that GB18401-2010 standard specifies.Specific as follows:
This product color fastness to washing: 4-5 level (technical requirement 3 grades); Color fastness to water: 4-5 level (technical requirement 3 grades); Acidproof PERSPIRATION COLOR FASTNESS: 4-5 level (technical requirement 3 grades); Alkaline-resisting PERSPIRATION COLOR FASTNESS: 4-5 level (technical requirement 3 grades).Fastness to rubbing: dry friction: 4-5 level (technical requirement 3 grades); Wet friction: 4-5 level (technical requirement 2-3 level).Content of formaldehyde is less than 20mg/kg (technical requirement 75mg/kg).Antibacterial inspection: all reach more than 92% to the bacteriostasis rate of Escherichia coli and staphylococcus aureus, through 20 durable tests, bacteriostasis rate still keeps more than 90%.
Claims (3)
1. viscose glue/coffee carbon blended knitted fabric, is characterized in that: adopt fabric tissue: one side plain weave; Horizontal close: 62.5 stringers/10cm; Vertical close: 44.5 lines/10cm; Pin number: 12G, Computerized flat knitting machine weaves; Adopt two 40
s, the coffee carbon fiber of 40% and the viscose siro-spinning yarn plying resultant yarn of 60%, and twist per unit is 290 twists/m; Grammes per square metre: 218 grams/m.
2. viscose glue according to claim 1/coffee carbon blended knitted fabric, it is characterized in that, the fabrication processing of described fabric is as follows: → packaging → warehouse-in is scalded in two kinds of fibre sirospun yarn → doubling → rewindings → knit sheet → running-on → flatcar → hand seam → washing → dry → whole.
3. viscose glue according to claim 2/coffee carbon blended knitted fabric, is characterized in that: two kinds of fibre sirospun yarns, the twist is at 920 ~ 1000 sth. made by twisting/m, and twist factor is between 360 ~ 400.