CN110341240A - 一种消防工程建设用高性能消防用品 - Google Patents
一种消防工程建设用高性能消防用品 Download PDFInfo
- Publication number
- CN110341240A CN110341240A CN201910622307.8A CN201910622307A CN110341240A CN 110341240 A CN110341240 A CN 110341240A CN 201910622307 A CN201910622307 A CN 201910622307A CN 110341240 A CN110341240 A CN 110341240A
- Authority
- CN
- China
- Prior art keywords
- fire
- flame retardant
- service inventory
- retardant coating
- engineering construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种消防工程建设用高性能消防用品，包括：基层，基层的外表面涂有防火涂料；耐火层，耐火层设于基层外表面，并与基层通过胶粘剂连接，耐火层上均匀布置有多个网状凹槽，网状凹槽内填充有阻燃材料；装饰层，装饰层设于耐火层的外表面，并与耐火层通过胶粘剂连接。本发明的一种消防工程建设用高性能消防用品通过在基层外部包覆一层网状结构的耐火层，并在网状结构内填充阻燃材料，极大地提升了该消防用品的防火性和耐火性，同时在耐火层的外表面包覆一层装饰层，使其外形更加美观。该消防用品结构简单，性能优越，安全环保，易于生产，成本低廉，质量稳定，防火耐火性强，适用范围较广，具有抗火的作用，有良好的市场应用前景。
Description
技术领域
本发明涉及消防用品技术领域，具体涉及一种消防工程建设用高性能消防用品。
背景技术
消防工程关系国计民生，关系到每个公民的人身和财产安全，因此，对消防工程建设用品的质量要求往往较高。现有技术中的消防用品大多为金属用品，金属类消防用品一般具有较强的硬度和较好的耐磨性和防火性能，但是，金属类消防用品也有其弊端，其往往密度大且制造成本较高，不适合大面积推广适用。
当前，市面上也逐渐出现了一些木质消防用品，虽然木质类消防用品的密度较小，制造成本相对于金属类消防用品也较为低廉，但是从使用的效果来看，现有的木质类消防用品防火性和耐火性较差，不能很好地满足消防工程建设用的要求。
因此，提供一种外形美观、防火耐火性强的高性能消防用品是本领域技术人员亟需解决的问题。
发明内容
有鉴于此，本发明提供了一种消防工程建设用高性能消防用品，通过在基层外部包覆有一层耐火层，并对耐火层采用网状结构设计，使耐火层内部填充大量的阻燃材料，同时配合涂有防火材料的基层，以及包覆于耐火层外表面的装饰层，使得该消防用品不仅外形美观，而且防火性好、耐火性强。
为了实现上述目的，本发明采用如下技术方案：
一种消防工程建设用高性能消防用品，包括：
基层，所述基层的外表面涂有防火涂料；
耐火层，所述耐火层分别设于所述基层的上表面和下表面，并与所述基层通过胶粘剂连接，所述耐火层上均匀布置有多个网状凹槽，所述网状凹槽内填充有阻燃材料；
装饰层，所述装饰层设于所述耐火层的外表面，并与所述耐火层通过胶粘剂连接。
经由上述的技术方案可知，与现有技术相比，本发明公开提供了一种消防工程建设用高性能消防用品，该消防用品是在木质基层外部包覆一层网状结构的耐火层，并在网状结构内填充有大量的阻燃材料，极大地提升了该消防用品的防火性，同时在耐火层的外表面包覆一层装饰层，使得该消防用品在防火性好的情况下，耐火时间长，耐火温度高，且外形美观。该高性能消防用品采用的材质不含甲醛、苯及其他有毒有害物质及放射性物质，从而遇火无烟、无毒、无异味，不会对空气造成污染，是一种防火性能极佳的高性能消防用品。
进一步的，所述基层为实木板、集成板、细木工板和刨花板中的一种，所述基层的厚度为5-20mm。
采用上述技术方案产生的有益效果是，不仅使得该消防用品的密度较小，重量较强，相对于现有技术中的金属类消防用品制造成本更为低廉，而且提高了该消防用品的质量稳定性，使得该消防用品更加结实耐用，拓宽了该消防用品的应用范围。
进一步的，所述耐火层采用的材质为玻璃纤维布，所述耐火层的厚度为3-10mm。
采用上述技术方案产生的有益效果是，采用玻璃纤维布不仅增强了该消防用品的坚韧度，防止消防用品在具体使用过程中出现破裂，而且，玻璃纤维布具有较好的耐热性，使得耐火层的物理特性不会因为外界温度的变化而发生明显的下降，从而提高了该消防用品的耐火性能，同时还提升了消防用品的结构稳定性，使其性能更加优越。
进一步的，所述阻燃材料为氮磷非卤阻燃剂。
进一步的，所述氮磷非卤阻燃剂由氢氧化铝、三聚氰胺和季戊四醇混合均匀而成，且各组分含量是氢氧化铝∶三聚氰胺∶季戊四醇为(3-5)∶(1-4)∶(0.5-2)。
采用上述技术方案产生的有益效果是，使得该消防用品在遇火后不会产生有毒烟雾及异味，不会对空气造成污染，从而进一步提升了该消防用品的安全环保性能。
进一步的，所述装饰层采用的材质为耐火板和PVC装饰膜中的一种。
采用上述技术方案产生的有益效果是，不仅增强了该消防用品的耐火性能，还使得该消防用品的外形更加美观，进一步拓宽了该消防用品的适用范围。
进一步的，所述装饰层的厚度为0.5-5mm。
采用上述技术方案产生的有益效果是，进一步增强了该消防用品的质量稳定性，使其不仅美观，而且韧度更高，更加结实耐用。
进一步的，所述胶粘剂为脲醛树脂和三聚氰胺组成的混合物。
进一步的，所述胶粘剂中脲醛树脂和三聚氰胺的质量比为(1-3)∶(0.5-2)。
采用上述技术方案产生的有益效果是，使得该消防用品的基层与耐火层、装饰层之间的粘合度好，各连接层之间不会随外界温度的变化而出现开裂的情形，进一步提升了该消防用品良好的结构稳定性。
进一步的，还包括耐磨层，所述耐磨层设于所述耐火层和所述装饰层之间，所述耐磨层采用的材质为矿粉、锯末和氯化镁溶液的混合物。
采用上述技术方案产生的有益效果是，耐磨层的设置不仅能够增强该消防用品的抗磨性，还能够保护耐火层，防止耐火层在使用过程中被磨损，避免该消防用品因磨损而导致韧度降低。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据提供的附图获得其他的附图。
图1附图为本发明提供的一种消防工程建设用高性能消防用品的结构示意图；
图2附图为本发明提供的一种消防工程建设用高性能消防用品的截面图；
图3附图为本发明提供的一种消防工程建设用高性能消防用品的侧视图；
图4附图为本发明提供的另一种消防工程建设用高性能消防用品的结构示意图。
其中：1-基层，2-耐火层，21-网状凹槽，3-胶粘剂，4-装饰层，5-耐磨层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整的描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明为一种消防工程建设用高性能消防用品，包括：
基层1，基层1的外表面涂有防火涂料；
耐火层2，耐火层2分别设于基层1的上表面和下表面，并与基层1通过胶粘剂3连接，耐火层2上均匀布置有多个网状凹槽21，网状凹槽21内填充有阻燃材料；
装饰层4，装饰层4设于耐火层2的外表面，并与耐火层2通过胶粘剂3连接。
如图1所示，根据本发明的一个可选实施例，基层1采用的材质为实木板，从而使得该消防用品的密度较小，重量较强，相对于现有技术中的金属类消防用品制造成本更为低廉。
如图2所示，根据本发明的一个可选实施例，基层1采用的材质为集成板，进一步扩大了该消防用品所选用材料的范围，同时使得该消防用品密度较小，重量较轻，制造成本更加低廉，有效降低了消防用品的生产成本。
如图3所示，根据本发明的一个可选实施例，基层1采用的材质为细木工板，进一步扩大了该消防用品所选用材料的范围，同时使得该消防用品密度较小，重量较轻，制造成本更加低廉，有效降低了消防用品的生产成本。
如图4所示，根据本发明的一个可选实施例，基层1采用的材质为刨花板，进一步扩大了该消防用品所选用材料的范围，同时使得该消防用品密度较小，重量较轻，制造成本更加低廉，有效降低了消防用品的生产成本。
根据本发明的一个可选实施例，基层1的厚度为15mm，保证了该消防用品的质量稳定性，使得该消防用品更加结实耐用，拓宽了该消防用品的应用范围。
根据本发明的一个可选实施例，耐火层2采用的材质为玻璃纤维布，玻璃纤维布不仅增强了该消防用品的坚韧度，防止消防用品在具体使用过程中出现破裂，而且，玻璃纤维布还具有较好的耐热性，使得耐火层的物理特性不会因为外界温度的变化而发生明显的下降，从而提高了该消防用品的耐火性能。
根据本发明的一个可选实施例，耐火层2的厚度为6mm，从而不仅增强了该消防用品的韧度和抗拉伸性能，还提升了消防用品的结构稳定性，使其性能更加优越。
根据本发明的一个可选实施例，阻燃材料为氮磷非卤阻燃剂；具体地，氮磷非卤阻燃剂为由氢氧化铝、三聚氰胺和季戊四醇混合均匀组成的阻燃混合物，且各组分含量是氢氧化铝∶三聚氰胺∶季戊四醇为4∶2∶1，从而使得该消防用品在遇火后不会产生有毒烟雾及异味，不会对空气造成污染，进一步提升了该消防用品的安全环保性能。
根据本发明的一个可选实施例，装饰层4采用的材质为耐火板，不仅进一步增强了该消防用品的耐火性能，还使得消防用品的外形更加美观，拓宽了该消防用品的适用范围。
根据本发明的一个可选实施例，装饰层4的厚度为2mm，从而进一步增强了该消防用品的质量稳定性，使其不仅美观，而且韧度更高，更加结实耐用。
根据本发明的一个可选实施例，胶粘剂3为脲醛树脂和三聚氰胺组成的混合物，且脲醛树脂和三聚氰胺的质量比为1∶1，从而使得该消防用品的基层与耐火层、装饰层之间的粘合度好，进一步提升了该消防用品良好的结构稳定性。
如图4所示，根据本发明的一个可选实施例，还包括耐磨层5，耐磨层5设于耐火层2和装饰层4之间，耐磨层5采用的材质为矿粉、锯末和氯化镁溶液的混合物，耐磨层的设置不仅能够增强该消防用品的抗磨性，还能够保护耐火层，防止耐火层在使用过程中被磨损，避免该消防用品因磨损而导致韧度降低。
本发明的一种消防工程建设用高性能消防用品通过在木质基层外部包覆一层网状结构的耐火层，并在网状结构内填充有大量的阻燃材料，极大地提升了该消防用品的防火性，同时在耐火层的外表面包覆一层装饰层，使得该消防用品在防火性好的情况下，耐火时间长，耐火温度高，且外形美观。该高性能消防用品结构简单，性能优越，安全环保，易于生产，成本低廉，质量稳定，防火耐火性强，适用范围较广，具有良好的市场应用前景。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种消防工程建设用高性能消防用品，其特征在于，包括：
基层(1)，所述基层(1)的外表面涂有防火涂料；
耐火层(2)，所述耐火层(2)分别设于所述基层(1)的上表面和下表面，并与所述基层(1)通过胶粘剂(3)连接，所述耐火层(2)上均匀布置有多个网状凹槽(21)，所述网状凹槽(21)内填充有阻燃材料；
装饰层(4)，所述装饰层(4)设于所述耐火层(2)的外表面，并与所述耐火层(2)通过胶粘剂(3)连接。
2.根据权利要求1所述的一种消防工程建设用高性能消防用品，其特征在于，所述基层(1)为实木板、集成板、细木工板和刨花板中的一种，所述基层(1)的厚度为5-20mm。
3.根据权利要求1所述的一种消防工程建设用高性能消防用品，其特征在于，所述耐火层(2)采用的材质为玻璃纤维布，所述耐火层(2)的厚度为3-10mm。
4.根据权利要求1所述的一种消防工程建设用高性能消防用品，其特征在于，所述阻燃材料为氮磷非卤阻燃剂。
5.根据权利要求4所述的一种消防工程建设用高性能消防用品，其特征在于，所述氮磷非卤阻燃剂由氢氧化铝、三聚氰胺和季戊四醇混合均匀而成，且各组分含量是氢氧化铝∶三聚氰胺∶季戊四醇为(3-5)∶(1-4)∶(0.5-2)。
6.根据权利要求1所述的一种消防工程建设用高性能消防用品，其特征在于，所述装饰层(4)采用的材质为耐火板和PVC装饰膜中的一种。
7.根据权利要求6所述的一种消防工程建设用高性能消防用品，其特征在于，所述装饰层(4)的厚度为0.5-5mm。
8.根据权利要求1所述的一种消防工程建设用高性能消防用品，其特征在于，所述胶粘剂(3)为脲醛树脂和三聚氰胺组成的混合物。
9.根据权利要求8所述的一种消防工程建设用高性能消防用品，其特征在于，所述胶粘剂(3)中脲醛树脂和三聚氰胺的质量比为(1-3)∶(0.5-2)。
10.根据权利要求1-9任一项所述的一种消防工程建设用高性能消防用品，其特征在于，还包括耐磨层(5)，所述耐磨层(5)设于所述耐火层(2)和所述装饰层(4)之间，所述耐磨层(5)采用的材质为矿粉、锯末和氯化镁溶液的混合物。