CN110338981A - A kind of pro-skin antibacterial paper diaper - Google Patents
A kind of pro-skin antibacterial paper diaper Download PDFInfo
- Publication number
- CN110338981A CN110338981A CN201910502885.8A CN201910502885A CN110338981A CN 110338981 A CN110338981 A CN 110338981A CN 201910502885 A CN201910502885 A CN 201910502885A CN 110338981 A CN110338981 A CN 110338981A
- Authority
- CN
- China
- Prior art keywords
- paper diaper
- pro
- skin
- milliliters
- polymer membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to new function material technical fields, disclose a kind of pro-skin antibacterial paper diaper, human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side, high adsorption rapid-curing cutback precursor product is prepared using Material synthesis based on polyacrylate dispersion, organic reactant is added again to dissolve each other, then nano-titanium dioxide is added, carry out film formation reaction, the molding antibacterial polymer membrane material being prepared, it can be used safely using soaked in absolute ethyl alcohol drying, the antibacterial polymer membrane material has performance well using upper in paper diaper, the antibacterial polymer membrane material has performance well using upper in paper diaper, effectively kill all kinds of bacteriums, it is detached from dead bacterium from skin surface, the paper diaper surface being prepared can play the role of fabulous killing to bacterium and remove, to inhibit the breeding of bacterium, Gel is managed in surface formation immediately after absorbing urine, prevents the reverse osmosis of urine.
Description
Technical field
The invention belongs to new function material technical fields, and in particular to a kind of pro-skin antibacterial paper diaper.
Background technique
The user group of paper diaper mainly has baby and adult's two major classes.Wherein Chinese market is mainly baby's paper urine
Trousers, China have nearly 20,000,000 baby due every year, reach more than 4,000 ten thousand using 0 years old to 2 years old baby of urine pants.And according to state
The data of statistics bureau, family, 60 years old or more the population in the whole nation in 2008 reach 1.599 hundred million people, account for the 12% of total population;Over-65s it is old
Year population reaches 1.096 hundred million people account for total population 8.3%.
Diaper rash is the stimulation of mixture and cloth diaper (or paper diaper of poor quality) to skin because of urine and stool
With inflammation caused by friction, all occurs micro- red phenomenon from private parts to buttocks, skin can become coarse, or even occur superfine small
Acne.If the small long prickly heat of hip, while could also cause diaper using air-locked cloth diaper or the paper diaper of poor quality again
Rash.
As the promotion of living standard and science and technology strength develops, it is impossible to meet people for traditional diaper and paper diaper
Demand, the market competition of paper diaper is also more fierce.And to the promotion of paper diaper product nothing more than from use feeling and
Health environment-friendly angle is set out.Since paper diaper are directly contacted with human skin, the environment in urine is suitble to bacterial growth breeding, grows
Raw bacterium can be adsorbed on paper diaper surface, and then be adhered to skin, and the continuous breeding of bacterium is caused to accumulate.Existing anti-bacteria paper
The anti-biotic material that urine pants use either plant component or inorganic antiseptic all do not have anti-reflective osmosis, antibacterial effect
It cannot get effective guarantee.Therefore it provides a kind of have quick absorption, pro-skin antibacterial paper diaper is had a very important significance.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of pro-skin antibacterial paper diaper is provided, the paper urine being prepared
Trousers surface can play the role of fabulous kill except to inhibit the breeding of bacterium, immediately on surface after absorbing urine to bacterium
Physical gel is formed, the reverse osmosis of urine is prevented.
The present invention is achieved by the following technical solutions:
A kind of pro-skin antibacterial paper diaper, human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side
Material, the preparation of the antibacterial polymer membrane material the following steps are included:
(1) 12.5-13.0 grams of trimethoxy silane is weighed, 150-160 grams of polyacrylate dispersion is placed in a beaker, addition 70-
80 milliliters of saturated sodium carbonates-dehydrated alcohol mixed solvent place the beaker on magnetic stirring apparatus with 350-400 revs/min of speed
Degree stirring 40-50 minutes, obtains finely dispersed mixture and is transferred in round-bottomed flask, 35- is at the uniform velocity sequentially added into flask
40 milliliters of ethyl acrylates and 10-15 milliliters of triethylamines continue stirring 30-40 minutes, and for heating water bath to 80-85 DEG C, stirring is anti-
Answer 0.5-0.6 hours, obtain precipitation mixture, be filtered, obtain filtrate set in a round bottom flask using Rotary Evaporators into
Row evaporation, removes residual solvent, obtains precursor product;
(2) precursor product that step (1) is prepared is mixed with 120-130 milliliters of ethyl acetate, is added 80-90 milliliters and gathers
Glycol water is at the uniform velocity added dropwise to 4.5-5.0 milliliters of N, N- dimethyl using 50-60 DEG C of hot water heating water bath under stiring
Formamide is persistently dispersed with stirring 20-25 minutes after dripping, dispersion is transferred in round-bottomed flask, is added into flask
0.18-0.20 grams of nano-titanium dioxide and 1.2-1.4 grams of dispersing agent ultrasonic disperse 30-40 minutes, are passed through nitrogen and carry out instead
It answers, sets heating reaction temperature as 140-150 DEG C, the reaction time is 2.5-3.0 hours, stands 3-4 hours after reaction, adds
Enter 20-25 milliliters of saturated sodium chloride solutions, concussion is cleaned, and removes water phase after stratification, resultant product is added to polytetrafluoro
It is 10-12 hours dry in 55-60 DEG C of vacuum oven in ethylene mold, molding antibacterial polymer membrane material is obtained, nothing is used
Water-ethanol, which impregnates 4-5 hours, dries.
It is further described as to above scheme, the antibacterial polymer membrane material covers with a thickness of 0.20-0.24
Millimeter.
It is further described as to above scheme, step (1) the polyacrylate dispersion mass concentration is 65-67%.
It is further described as to above scheme, step (1) saturated sodium carbonate-dehydrated alcohol mixed solvent is embezzled
It is 3.5-4.0:18-20 with sodium carbonate and dehydrated alcohol mass ratio, saturated sodium carbonate is the saturated mode at 25 DEG C.
It is further described as to above scheme, step (2) the nano-titanium dioxide particle size is at 10-15 nanometers
Between.
It is further described as to above scheme, step (2) dispersing agent is living for polyoxyethylene-type non-ionic surface
Property agent.
It is further described as to above scheme, step (2) the Aqueous Solutions of Polyethylene Glycol mass concentration is 45-50%.
It is further described as to above scheme, step (2) saturated sodium chloride solution is the saturated mode at 25 DEG C.
It is further described as to above scheme, diaper body is by non-woven fabrics outer layer, high molecular material water suction internal layer
It is formed with flexible cotton air-permeable layer.
The present invention has the advantage that solve anti-biotic material that existing antibacterial paper diaper uses not compared with prior art
With the problem of anti-reflective osmosis, antibacterial effect cannot get effective guarantee, the present invention provides a kind of pro-skin antibacterial paper diaper,
Human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side, is using polyacrylate dispersion
Body material is synthetically prepared high adsorption rapid-curing cutback precursor product, then adds organic reactant and dissolve each other, and nano-silica is then added
Change titanium, carry out film formation reaction, the molding antibacterial polymer membrane material being prepared was dried using soaked in absolute ethyl alcohol 4-5 hours
It can use safely, the characteristics of this method prepares that antibacterial paper diaper is at low cost, properties of product are prominent, the antibacterial polymer membrane material
Broad-spectrum antiseptic, skin-friendly is good, stability is good, elasticity is good, reverse osmosis ability is strong, which answers in paper diaper
With having performance well, all kinds of bacteriums are effectively killed, are detached from dead bacterium from skin surface, the paper urine being prepared
Trousers surface can play the role of to bacterium it is fabulous kill except, to inhibit the breeding of bacterium, membrane material after absorbing urine immediately
Gel is managed in surface formation, prevents the reverse osmosis of urine, the pro-skin antibacterial paper diaper that the present invention uses solves existing antibacterial
The problem of anti-biotic material that paper diaper use all does not have anti-reflective osmosis, and antibacterial effect cannot get effective guarantee, is prepared into
This is low, easily accomplishes scale production, overcomes the short slab for the antibacterial paper diaper antibacterial material that existing method is prepared, and is antibacterial
The development and utilization of material provide new thinking and direction, improve the development and utilization of high-end anti-biotic material, can be realized promotion
High-quality paper diaper field industry development improves the realistic meaning in the application value of daily necessities field, is a kind of extremely worth
The technical solution of popularization and use.
Specific embodiment
To make the purpose of the present invention, technical solution and effect clearer, clear and definite, combined with specific embodiments below to this hair
It is bright to be described further, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, is not used to limit
Technical solution provided by the present invention.
Embodiment 1
A kind of pro-skin antibacterial paper diaper, human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side
Material, the preparation of the antibacterial polymer membrane material the following steps are included:
(1) 12.5 grams of trimethoxy silanes are weighed, 150 grams of polyacrylate dispersions are placed in a beaker, 70 milliliters of saturated carbons are added
Sour sodium-dehydrated alcohol mixed solvent is placed the beaker and is stirred 40 minutes on magnetic stirring apparatus with 350 revs/min of speed, obtained
Finely dispersed mixture is transferred in round-bottomed flask, and 35 milliliters of ethyl acrylates and 10 milliliters are at the uniform velocity sequentially added into flask
Triethylamine continues stirring 30 minutes, and heating water bath is stirred to react 0.5 hour to 80 DEG C, obtains precipitation mixture, be filtered,
It obtains filtrate and sets to be evaporated using Rotary Evaporators in a round bottom flask, remove residual solvent, obtain precursor product;
(2) precursor product that step (1) is prepared is mixed with 120 milliliters of ethyl acetate, 80 milliliters of polyethylene glycol is added
Aqueous solution is at the uniform velocity added dropwise to 4.5 milliliters of n,N-Dimethylformamide under stiring, is dripped using 50 DEG C of hot water heating water baths
It is persistently dispersed with stirring afterwards 20 minutes, dispersion is transferred in round-bottomed flask, 0.18 gram of nano-titanium dioxide is added into flask
And 1.2 grams of dispersing agents, it ultrasonic disperse 30 minutes, is passed through nitrogen and is reacted, set heating reaction temperature as 140 DEG C, react
Time is 2.5 hours, stands 3 hours after reaction, and 20 milliliters of saturated sodium chloride solutions, concussion cleaning, stratification is added
After remove water phase, resultant product is added in Teflon mould, dry 10 hours in 55 DEG C of vacuum ovens, is obtained
Antibacterial polymer membrane material is formed, was dried using soaked in absolute ethyl alcohol 4 hours.
It is further described as to above scheme, the antibacterial polymer membrane material covers with a thickness of 0.20 millimeter.
It is further described as to above scheme, step (1) the polyacrylate dispersion mass concentration is 65%.
It is further described as to above scheme, step (1) saturated sodium carbonate-dehydrated alcohol mixed solvent is embezzled
It is 3.5:18 with sodium carbonate and dehydrated alcohol mass ratio, saturated sodium carbonate is the saturated mode at 25 DEG C.
It is further described as to above scheme, step (2) the nano-titanium dioxide particle size is at 10-15 nanometers
Between.
It is further described as to above scheme, step (2) dispersing agent is living for polyoxyethylene-type non-ionic surface
Property agent.
It is further described as to above scheme, step (2) the Aqueous Solutions of Polyethylene Glycol mass concentration is 45%.
It is further described as to above scheme, step (2) saturated sodium chloride solution is the saturated mode at 25 DEG C.
It is further described as to above scheme, diaper body is by non-woven fabrics outer layer, high molecular material water suction internal layer
It is formed with flexible cotton air-permeable layer.
Embodiment 2
A kind of pro-skin antibacterial paper diaper, human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side
Material, the preparation of the antibacterial polymer membrane material the following steps are included:
(1) 12.8 grams of trimethoxy silanes are weighed, 155 grams of polyacrylate dispersions are placed in a beaker, 75 milliliters of saturated carbons are added
Sour sodium-dehydrated alcohol mixed solvent is placed the beaker and is stirred 45 minutes on magnetic stirring apparatus with 380 revs/min of speed, obtained
Finely dispersed mixture is transferred in round-bottomed flask, and 38 milliliters of ethyl acrylates and 12 milliliters are at the uniform velocity sequentially added into flask
Triethylamine continues stirring 35 minutes, and heating water bath is stirred to react 0.55 hour to 83 DEG C, obtains precipitation mixture, carried out
Filter obtains filtrate and sets to be evaporated using Rotary Evaporators in a round bottom flask, removes residual solvent, obtains precursor product;
(2) precursor product that step (1) is prepared is mixed with 125 milliliters of ethyl acetate, 85 milliliters of polyethylene glycol is added
Aqueous solution is at the uniform velocity added dropwise to 4.8 milliliters of n,N-Dimethylformamide under stiring, is dripped using 55 DEG C of hot water heating water baths
It is persistently dispersed with stirring afterwards 23 minutes, dispersion is transferred in round-bottomed flask, 0.19 gram of nano-titanium dioxide is added into flask
And 1.3 grams of dispersing agents, it ultrasonic disperse 35 minutes, is passed through nitrogen and is reacted, set heating reaction temperature as 145 DEG C, react
Time is 2.8 hours, stands 3.5 hours after reaction, and 22 milliliters of saturated sodium chloride solutions, concussion cleaning, standing point is added
Water phase is removed after layer, resultant product is added in Teflon mould, it is 11 hours dry in 58 DEG C of vacuum ovens, it obtains
To molding antibacterial polymer membrane material, dried using soaked in absolute ethyl alcohol 4.5 hours.
It is further described as to above scheme, the antibacterial polymer membrane material covers with a thickness of 0.22 millimeter.
It is further described as to above scheme, step (1) the polyacrylate dispersion mass concentration is 66%.
It is further described as to above scheme, step (1) saturated sodium carbonate-dehydrated alcohol mixed solvent is embezzled
It is 3.8:19 with sodium carbonate and dehydrated alcohol mass ratio, saturated sodium carbonate is the saturated mode at 25 DEG C.
It is further described as to above scheme, step (2) the nano-titanium dioxide particle size is at 10-15 nanometers
Between.
It is further described as to above scheme, step (2) dispersing agent is living for polyoxyethylene-type non-ionic surface
Property agent.
It is further described as to above scheme, step (2) the Aqueous Solutions of Polyethylene Glycol mass concentration is 48%.
It is further described as to above scheme, step (2) saturated sodium chloride solution is the saturated mode at 25 DEG C.
It is further described as to above scheme, diaper body is by non-woven fabrics outer layer, high molecular material water suction internal layer
It is formed with flexible cotton air-permeable layer.
Embodiment 3
A kind of pro-skin antibacterial paper diaper, human skin is contacted in diaper body covers one layer of antibacterial polymer membrane material on one side
Material, the preparation of the antibacterial polymer membrane material the following steps are included:
(1) 13.0 grams of trimethoxy silanes are weighed, 160 grams of polyacrylate dispersions are placed in a beaker, 80 milliliters of saturated carbons are added
Sour sodium-dehydrated alcohol mixed solvent is placed the beaker and is stirred 50 minutes on magnetic stirring apparatus with 400 revs/min of speed, obtained
Finely dispersed mixture is transferred in round-bottomed flask, and 40 milliliters of ethyl acrylates and 15 milliliters are at the uniform velocity sequentially added into flask
Triethylamine continues stirring 40 minutes, and heating water bath is stirred to react 0.6 hour to 85 DEG C, obtains precipitation mixture, be filtered,
It obtains filtrate and sets to be evaporated using Rotary Evaporators in a round bottom flask, remove residual solvent, obtain precursor product;
(2) precursor product that step (1) is prepared is mixed with 130 milliliters of ethyl acetate, 90 milliliters of polyethylene glycol is added
Aqueous solution is at the uniform velocity added dropwise to 5.0 milliliters of n,N-Dimethylformamide under stiring, is dripped using 60 DEG C of hot water heating water baths
It is persistently dispersed with stirring afterwards 25 minutes, dispersion is transferred in round-bottomed flask, 0.20 gram of nano-titanium dioxide is added into flask
And 1.4 grams of dispersing agents, it ultrasonic disperse 40 minutes, is passed through nitrogen and is reacted, set heating reaction temperature as 150 DEG C, react
Time is 3.0 hours, stands 4 hours after reaction, and 25 milliliters of saturated sodium chloride solutions, concussion cleaning, stratification is added
After remove water phase, resultant product is added in Teflon mould, dry 12 hours in 60 DEG C of vacuum ovens, is obtained
Antibacterial polymer membrane material is formed, was dried using soaked in absolute ethyl alcohol 5 hours.
It is further described as to above scheme, the antibacterial polymer membrane material covers with a thickness of 0.24 millimeter.
It is further described as to above scheme, step (1) the polyacrylate dispersion mass concentration is 67%.
It is further described as to above scheme, step (1) saturated sodium carbonate-dehydrated alcohol mixed solvent is embezzled
It is 4.0:20 with sodium carbonate and dehydrated alcohol mass ratio, saturated sodium carbonate is the saturated mode at 25 DEG C.
It is further described as to above scheme, step (2) the nano-titanium dioxide particle size is at 10-15 nanometers
Between.
It is further described as to above scheme, step (2) dispersing agent is living for polyoxyethylene-type non-ionic surface
Property agent.
It is further described as to above scheme, step (2) the Aqueous Solutions of Polyethylene Glycol mass concentration is 50%.
It is further described as to above scheme, step (2) saturated sodium chloride solution is the saturated mode at 25 DEG C.
It is further described as to above scheme, diaper body is by non-woven fabrics outer layer, high molecular material water suction internal layer
It is formed with flexible cotton air-permeable layer.
Comparative example 1
Difference with embodiment 1 is only that, in the preparation of antibacterial polymer membrane material, omits step (1) described trimethoxy silane
Addition, remaining is consistent.
Comparative example 2
Difference with embodiment 2 is only that, in the preparation of antibacterial polymer membrane material, omits the addition of step (1) described triethylamine
It uses, remaining is consistent.
Comparative example 3
Difference with embodiment 3 is only that, in the preparation of antibacterial polymer membrane material, step (1) the heating in water bath for reaction temperature
It is 90 DEG C, is stirred to react 0.4 hour, remaining is consistent.
Comparative example 4
Difference with embodiment 3 is only that, in the preparation of antibacterial polymer membrane material, omits step (2) described N, N- dimethyl methyl
The addition of amide, remaining is consistent.
Comparative example 5
Difference with embodiment 3 is only that, in the preparation of antibacterial polymer membrane material, omit in step (2) nano-titanium dioxide and
The addition of dispersing agent, remaining is consistent.
Comparative example 6
Difference with embodiment 3 is only that, in the preparation of antibacterial polymer membrane material, step (1) the heating reaction temperature is 120
DEG C, the reaction time is 5.0 hours, remaining is consistent.
Comparative experiments
Pro-skin antibacterial paper diaper is prepared using the method for embodiment 1-3 and comparative example 1-6 respectively.It is with patent publication No.
A kind of method that novel antibacterial lateral leakage protection paper diaper are related to disclosed in CN108066069A as a control group, in identical test bar
Each group paper diaper sample is tested for the property under part, when data reach stable, acquires representative data, gained experiment
Data are the average value of 5 groups of samples, and irrelevant variable is consistent in holding test, count effective average value and (utilize statistics before experiment
Method carries out experimental design, is then tested and recorded test data, and analysis obtains test result, makes full use of system in the process
Meter tool explains result to the greatest extent), as a result as shown in the table:
(antibiotic property is tested using GB/T 20944.3-2008 " the evaluation succusion of antibacterial textile performance ": this antibacterial is real
In testing, reagent mainly has PBS buffer solution, meat soup and culture medium.After related medicine allocation, buffer PBS is divided in 2
In a 5OO milliliters of conical flask, and meat soup, culture medium are completely dissolved ingredient after being both needed to heating, and selected strain is large intestine
Bacillus;The measurement of wet guilding: being tested according to national standard GB/T12704-91, using the computermatic fabric moisture transmission instrument of YG601-II,
Using vapor transfer rate as deliberated index;)
The pro-skin antibacterial paper diaper that the present invention uses solves the anti-biotic material that existing antibacterial paper diaper uses and does not all have anti-reflective
The problem of osmosis, antibacterial effect cannot get effective guarantee, preparation cost is low, easily accomplishes scale production, and overcomes existing
The short slab for the antibacterial paper diaper antibacterial material that method is prepared provides new thinking and side for the development and utilization of anti-biotic material
To, improve the development and utilization of high-end anti-biotic material, can be realized promote high-quality paper diaper field industry development, improve in day
The realistic meaning of the application value in articles field is a kind of technical solution being extremely worth of widely use.
Claims (9)
1. a kind of pro-skin antibacterial paper diaper, which is characterized in that contact human skin in diaper body covers one layer on one side
Antibacterial polymer membrane material, the preparation of the antibacterial polymer membrane material the following steps are included:
(1) 12.5-13.0 grams of trimethoxy silane is weighed, 150-160 grams of polyacrylate dispersion is placed in a beaker, addition 70-
80 milliliters of saturated sodium carbonates-dehydrated alcohol mixed solvent place the beaker on magnetic stirring apparatus with 350-400 revs/min of speed
Degree stirring 40-50 minutes, obtains finely dispersed mixture and is transferred in round-bottomed flask, 35- is at the uniform velocity sequentially added into flask
40 milliliters of ethyl acrylates and 10-15 milliliters of triethylamines continue stirring 30-40 minutes, and for heating water bath to 80-85 DEG C, stirring is anti-
Answer 0.5-0.6 hours, obtain precipitation mixture, be filtered, obtain filtrate set in a round bottom flask using Rotary Evaporators into
Row evaporation, removes residual solvent, obtains precursor product;
(2) precursor product that step (1) is prepared is mixed with 120-130 milliliters of ethyl acetate, is added 80-90 milliliters and gathers
Glycol water is at the uniform velocity added dropwise to 4.5-5.0 milliliters of N, N- dimethyl using 50-60 DEG C of hot water heating water bath under stiring
Formamide is persistently dispersed with stirring 20-25 minutes after dripping, dispersion is transferred in round-bottomed flask, is added into flask
0.18-0.20 grams of nano-titanium dioxide and 1.2-1.4 grams of dispersing agent ultrasonic disperse 30-40 minutes, are passed through nitrogen and carry out instead
It answers, sets heating reaction temperature as 140-150 DEG C, the reaction time is 2.5-3.0 hours, stands 3-4 hours after reaction, adds
Enter 20-25 milliliters of saturated sodium chloride solutions, concussion is cleaned, and removes water phase after stratification, resultant product is added to polytetrafluoro
It is 10-12 hours dry in 55-60 DEG C of vacuum oven in ethylene mold, molding antibacterial polymer membrane material is obtained, nothing is used
Water-ethanol, which impregnates 4-5 hours, dries.
2. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that the antibacterial polymer membrane material covers
With a thickness of 0.20-0.24 millimeters.
3. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (1) described polyacrylate dispersion
Mass concentration is 65-67%.
4. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (1) described saturated sodium carbonate-is anhydrous
Saturated sodium carbonate and dehydrated alcohol mass ratio are 3.5-4.0:18-20 in alcohol mixed solvent, and saturated sodium carbonate is at 25 DEG C
Saturated mode.
5. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (2) the nano-titanium dioxide grain
Diameter size is between 10-15 nanometers.
6. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (2) dispersing agent is polyoxy second
Ene-type nonionic surfactant.
7. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (2) described Aqueous Solutions of Polyethylene Glycol
Mass concentration is 45-50%.
8. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that step (2) described saturated sodium chloride solution
For the saturated mode at 25 DEG C.
9. a kind of pro-skin antibacterial paper diaper as described in claim 1, which is characterized in that diaper body is high by non-woven fabrics outer layer
Molecular material water suction internal layer and flexible cotton air-permeable layer composition.