CN110295432A - One kind can take fabric and its weaving process in the stamp aramid fiber blended fire prevention summer - Google Patents
One kind can take fabric and its weaving process in the stamp aramid fiber blended fire prevention summer Download PDFInfo
- Publication number
- CN110295432A CN110295432A CN201910646226.1A CN201910646226A CN110295432A CN 110295432 A CN110295432 A CN 110295432A CN 201910646226 A CN201910646226 A CN 201910646226A CN 110295432 A CN110295432 A CN 110295432A
- Authority
- CN
- China
- Prior art keywords
- fabric
- aramid fiber
- stamp
- yarn
- fire prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to take fabric and its weaving process in the stamp aramid fiber blended fire prevention summer, is related to textile technology field, and the fabric is double-layer fabric, upper layer uses 40 English branch doublet cords, is surface layer, and lower layer uses 40 English branch doublet cords, for inner layer, finished product grammes per square metre is about 193g/ ㎡.Weaving process of the present invention is easy to operate, first, viscose rayon and Fanglun l414 fiber are passed through into blowing, cotton carding, drafting, Roving Frames arrive spun yarn again, winder, using doubling, it is twisted strand again, upper layer yarn and underlying yarn spin respectively, then warping is distinguished in the upper and lower, sizing respectively, subsequently, denting woven fabric, it is weaved using upper and lower twin shaft loom, the fabric table inner layer is all plain weave, stitch weave in table, the comfort of dress is taken into account, aramid fiber content is up to 37.5% in the design fabric, not only with the flameproof effect of high fire-retardance, and fabric intensity is higher, printing quality is preferable, color fastness is preferable.
Description
Technical field
It is specifically a kind of to take fabric and its weaving work the stamp aramid fiber blended fire prevention summer the present invention relates to textile technology field
Skill.
Background technique
Fireproof garment be fireman and high-temperature operation personnel closely fiery operation when the protective clothes worn, be used to its upper and lower body
Dry, head, hand and foot are thermally shielded protection, including fire prevention jacket, fire prevention trousers, fire prevention headgear, fireproof glove and fire prevention
Footmuff has fire prevention, heat-insulated, wear-resisting, folding, the characteristics such as fire-retardant, antiradiation is hot, and the hot temperature of antiradiation is up to 1000 DEG C, because of season
Section is different, and fireproof garment can be divided into winter fireproof garment and summer fireproof garment.
It is blended with anti-flaming viscose and aramid fiber currently, summer fireproof garment generally uses fire resistance fibre yarn weaving, wherein aramid fiber
1414 have the characteristics that strength high fire-retardance effect is good, but there is the shortcomings that pigment dyeing can only being used when dyeing, poor color fastness, because making
Battle dress fabric does not require nothing more than fire prevention, also wants stamp, strength is more demanding, and when blended using aramid fiber, aramid fiber content is unsuitable
Greater than 20%, still, fireproof garment fabric strength woven in this way is just poor, and aramid fiber content is greater than after 20%, fabric printing quality
With regard to poor, and color fastness is also poor.Therefore, those skilled in the art provide one kind can take in the stamp aramid fiber blended fire prevention summer fabric and its
Weaving process, to solve the problems mentioned in the above background technology.
Summary of the invention
The purpose of the present invention is to provide one kind to take fabric and its weaving process in the stamp aramid fiber blended fire prevention summer, to solve
The problems mentioned above in the background art.
To achieve the above object, the invention provides the following technical scheme: one kind can take fabric in the stamp aramid fiber blended fire prevention summer,
The fabric is double-layer fabric, and upper layer uses 40 English branch doublet cords, is surface layer, and lower layer uses 40 English branch doublet cords, is inner layer, at
Product grammes per square metre is about 193g/ ㎡.
As a further solution of the present invention: the surface layer is different from inner layer fibre furnish.
As further scheme of the invention: the surface layer warp and weft is propped up bifilar using (80/20) 40 English of viscose glue/aramid fiber
Line, inner layer warp and weft use (90/10) 40 English branch doublet cord of aramid fiber/viscose glue.
As further scheme of the invention: the surface layer thread count is 51/48, and inner layer thread count is 17/16.
As further scheme of the invention: the surface layer and inner layer are all made of plain weave.
A kind of weaving process that can take fabric the stamp aramid fiber blended fire prevention summer, the specific weaving process of the fabric includes following
Step:
(1) it is spare that viscose rayon, Fanglun l414 fiber preparation: are chosen；
(2) blowing: by viscose rayon and Fanglun l414 fiber reinforced cement composite at lesser cotton block or flock, big portion therein is removed
Point impurity, fault and the short flannel that should not be spinned, are made that constant weight, length, thickness be uniform, the good examination paper of shape；
(3) cotton carding: resolving into single fiber state for composite fibre, improve straightening of fibers parastate, removes thin in volume
Satisfactory strip is made in fiber further full and uniform mixing by small impurity and short flannel；
(4) drafting: being carried out and closed with 6~8 one threads, strip elongate take out carefully arrive defined weight, using and conjunction and lead
Stretching mixes fiber further uniformly；
(5) ripe bar: equably being elongated drawing-down by rove, and stretches fiber further in parallel, and the yarn after drawing-off is added
With turn appropriate, make sliver that there is certain strength；
(6) spun yarn: rove is drawn and attenuated to required fineness, keeps straightening of fibers parallel, yarn is subject to turn, is become with one
The spun yarn of dead twist degree, certain strength.
As further scheme of the invention: the weaving process is further comprising the steps of:
(7) winder: by incidental looping big, forming and with the bobbin of certain density at capacity, part on yarn is removed
Fault and impurity；
(8) above-mentioned mixed yarn doubling: is subjected to doubling；
(9) it twists thread: double twisting is carried out to the mixed yarn after doubling；
(10) warping: according to requiring to draw yarn from bobbin cradle, the piece yarn reel for being made into certain radical and length is wound on
In warp beam, with certain density, the warp beam of even tension, upper and lower axle distinguishes warping；
(11) sizing: upper and lower axle distinguishes sizing；
(12) it weaves: using twin shaft air-jet loom, by opening, wefting insertion, beat up, batch and match with warp let-off five big systems
It closes, warp and weft is made to interweave with forming fabric according to the requirement of design；
(13) dyeing and finishing: as needed pre-processing fabric, removes contained impurity on fiber, and in textile process process
The slurry of middle application and the greasy dirt etc. being stained with, then stamp and arrangement；
(14) coiled: to examine qualified coiled.
As further scheme of the invention: stock tank is put into the face that can be faded when lower layer's axoplasm yarn in the step (11)
Material.
As further scheme of the invention: further including denting process between the step (11) and step (12), press
Technique requires warp thread passing through menopause tablet, heald and reed.
As further scheme of the invention: being weaved in the step (12) using twin shaft, the whole top layer warp thread of an axis, one
The whole nexine warp thread of axis, table, inner layer are distinguished by color difference.
Compared with prior art, the beneficial effects of the present invention are: the present invention devise one kind can the blended fire prevention of stamp aramid fiber
Summer takes fabric and its weaving process, firstly, viscose rayon and Fanglun l414 fiber are passed through blowing, cotton carding, drafting, Roving Frames
Spun yarn, winder are arrived again, using doubling, are twisted strand again, upper layer yarn and underlying yarn spin respectively, then the upper and lower
Warping respectively, sizing, is put into the pigment that can fade when starching lower layer warp yarns in stock tank respectively, subsequently, denting woven fabric, using upper and lower
The weaving of twin shaft loom, the fabric table inner layer are all plain weaves, and stitch weave in table has taken into account the comfort of dress, the design
Aramid fiber content is up to 37.5% in fabric, and in actual use, fireproof garment fabric not only has the flameproof effect of high fire-retardance, and
And fabric intensity is higher, printing quality is preferable, color fastness is preferable.
Detailed description of the invention
Fig. 1 is a kind of organization chart that can take fabric and its weaving process the stamp aramid fiber blended fire prevention summer.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, one kind can take fabric in the stamp aramid fiber blended fire prevention summer, and fabric is dual-layer face in the embodiment of the present invention
Material, upper layer use 40 English branch doublet cords, are surface layer, and it is inner layer, finished product grammes per square metre is about 193g/ that lower layer, which uses 40 English branch doublet cords,
㎡。
Further, surface layer is different from inner layer fibre furnish.
Further, surface layer warp and weft uses (80/20) 40 English branch doublet cord of viscose glue/aramid fiber, and inner layer warp and weft uses
(90/10) 40 English branch doublet cord of aramid fiber/viscose glue.
Further, surface layer thread count is 51/48, and inner layer thread count is 17/16.
Further, surface layer and inner layer are all made of plain weave.
A kind of weaving process that can take fabric the stamp aramid fiber blended fire prevention summer, the specific weaving process of the fabric includes following
Step:
(1) it is spare that viscose rayon, Fanglun l414 fiber preparation: are chosen；
(2) blowing: by viscose rayon and Fanglun l414 fiber reinforced cement composite at lesser cotton block or flock, big portion therein is removed
Point impurity, fault and the short flannel that should not be spinned, are made that constant weight, length, thickness be uniform, the good examination paper of shape；
(3) cotton carding: resolving into single fiber state for composite fibre, improve straightening of fibers parastate, removes thin in volume
Satisfactory strip is made in fiber further full and uniform mixing by small impurity and short flannel；
(4) drafting: being carried out and closed with 6~8 one threads, and improvement strip long segment is irregular, strip is elongated to take out carefully to arrive providing
Weight, and further increase fiber stretches parallel degree, using and closing mixes fiber further uniformly with drawing-off；
(5) ripe bar: equably being elongated drawing-down by rove, and stretches fiber further in parallel, and the yarn after drawing-off is added
With turn appropriate, make sliver that there is certain strength, is unwound with sharp reeling roving and spun yarn；
(6) spun yarn: rove is drawn and attenuated to required fineness, keeps straightening of fibers parallel, yarn is subject to turn, is become with one
The spun yarn of dead twist degree, certain strength.
Further, the weaving process is further comprising the steps of:
(7) winder: by incidental looping big, forming and with the bobbin of certain density at capacity, part on yarn is removed
Fault and impurity, to improve the quality of yarn；
(8) above-mentioned mixed yarn doubling: is subjected to doubling；
(9) it twists thread: double twisting is carried out to the mixed yarn after doubling；
(10) warping: according to requiring to draw yarn from bobbin cradle, the piece yarn reel for being made into certain radical and length is wound on
In warp beam, with certain density, the warp beam of even tension, upper and lower axle distinguishes warping；
(11) sizing: upper and lower axle distinguishes sizing, and warp thread makes yarn have certain wearability convenient for weaving by starching；
(12) it weaves: using twin shaft air-jet loom, by opening, wefting insertion, beat up, batch and match with warp let-off five big systems
It closes, warp and weft is made to interweave with forming fabric according to the requirement of design；
(13) dyeing and finishing: as needed pre-processing fabric, removes contained impurity on fiber, and in textile process process
The slurry of middle application and the greasy dirt etc. being stained with, then stamp and arrangement；
(14) coiled: to examine qualified coiled.
Further, stock tank is put into the pigment that can be faded when lower layer's axoplasm yarn in step (11).
Further, further include denting process between step (11) and step (12), pass through warp thread by technique requirement
Menopause tablet, heald and reed.
Further, it is weaved using twin shaft in step (12), the whole top layer warp thread of an axis, the whole nexine warp thread of an axis, it is table, inner
Layer is distinguished by color difference.
This process flow is easy to operate, firstly, viscose rayon and Fanglun l414 fiber are passed through blowing, cotton carding, drafting, thick
Yarn process arrives spun yarn, winder again, using doubling, is twisted strand again, upper layer yarn and underlying yarn spin respectively, then upper layer
Warping is distinguished with lower layer, and sizing, is put into the pigment that can fade when starching lower layer warp yarns, subsequently, denting woven fabric is adopted in stock tank respectively
It is weaved with upper and lower twin shaft loom, which is all plain weave, and stitch weave in table has taken into account the comfort of dress,
Aramid fiber content is up to 37.5% in the design fabric, and in actual use, fireproof garment fabric not only has the fire prevention of high fire-retardance
Effect, and fabric intensity is higher, printing quality is preferable, color fastness is preferable.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (10)
1. one kind can take fabric in the stamp aramid fiber blended fire prevention summer, which is characterized in that the fabric is double-layer fabric, and upper layer uses 40
English branch doublet cord is surface layer, and it is inner layer, finished product grammes per square metre is about 193g/ ㎡ that lower layer, which uses 40 English branch doublet cords,.
2. one kind according to claim 1 can take fabric in the stamp aramid fiber blended fire prevention summer, which is characterized in that the surface layer with
Inner layer fibre furnish is different.
3. one kind according to claim 1 can take fabric in the stamp aramid fiber blended fire prevention summer, which is characterized in that the surface layer warp
Weft yarn uses (80/20) 40 English branch doublet cord of viscose glue/aramid fiber, and inner layer warp and weft is propped up bifilar using (90/10) 40 English of aramid fiber/viscose glue
Line.
4. one kind according to claim 1 can take fabric in the stamp aramid fiber blended fire prevention summer, which is characterized in that the surface layer warp
Weft density is 51/48, and inner layer thread count is 17/16.
5. one kind according to claim 1 can take fabric in the stamp aramid fiber blended fire prevention summer, which is characterized in that the surface layer and
Inner layer is all made of plain weave.
6. the weaving process that one kind according to claim 1 can take fabric the stamp aramid fiber blended fire prevention summer, which is characterized in that
The specific weaving process of the fabric the following steps are included:
(1) it is spare that viscose rayon, Fanglun l414 fiber preparation: are chosen；
(2) by viscose rayon and Fanglun l414 fiber reinforced cement composite at lesser cotton block or flock, it is miscellaneous blowing: to remove major part therein
Matter, fault and the short flannel that should not be spinned, are made that constant weight, length, thickness be uniform, the good examination paper of shape；
(3) cotton carding: resolving into single fiber state for composite fibre, improve straightening of fibers parastate, removes tiny miscellaneous in volume
Satisfactory strip is made in fiber further full and uniform mixing by matter and short flannel；
(4) drafting: being carried out and closed with 6~8 one threads, and strip is elongated to take out and carefully arrive defined weight, using and conjunction make with drawing-off
Fiber further uniformly mixes；
(5) ripe bar: equably being elongated drawing-down by rove, and stretches fiber further in parallel, and the yarn after drawing-off is fitted
When turn, make sliver have certain strength；
(6) spun yarn: rove being drawn and attenuated to required fineness, keeps straightening of fibers parallel, yarn is subject to turn, is become with a dead twist
The spun yarn of degree, certain strength.
7. the weaving process that one kind according to claim 1 can take fabric the stamp aramid fiber blended fire prevention summer, which is characterized in that
The weaving process is further comprising the steps of:
(7) winder: by incidental looping big, forming and with the bobbin of certain density at capacity, part fault on yarn is removed
And impurity；
(8) above-mentioned mixed yarn doubling: is subjected to doubling；
(9) it twists thread: double twisting is carried out to the mixed yarn after doubling；
(10) warping: according to requiring to draw yarn from bobbin cradle, the piece yarn reel for being made into certain radical and length is wound on warp beam
On, with certain density, the warp beam of even tension, upper and lower axle distinguishes warping；
(11) sizing: upper and lower axle distinguishes sizing；
(12) it weaves: using twin shaft air-jet loom, by opening, wefting insertion, beat up, batch cooperation with warp let-off five big systems, make
Warp and weft interweaves with forming fabric according to the requirement of design；
(13) dyeing and finishing: as needed pre-processing fabric, removes contained impurity on fiber, and apply during textile process
The slurry added and the greasy dirt etc. being stained with, then stamp and arrangement；
(14) coiled: to examine qualified coiled.
8. the weaving process that one kind according to claim 7 can take fabric the stamp aramid fiber blended fire prevention summer, which is characterized in that
Stock tank is put into the pigment that can be faded when lower layer's axoplasm yarn in the step (11).
9. the weaving process that one kind according to claim 7 can take fabric the stamp aramid fiber blended fire prevention summer, which is characterized in that
Further include denting process between the step (11) and step (12), warp thread is passed through into menopause tablet, heald and steel by technique requirement
Reed.
10. one kind according to claim 7 can take the weaving process of fabric the stamp aramid fiber blended fire prevention summer, feature exists
In using twin shaft weaving in the step (12), the whole top layer warp thread of an axis, the whole nexine warp thread of an axis, table, inner layer pass through color not
With difference.