CN110293696A - 一种已固化j型/工型长桁的加筋壁板封装方法 - Google Patents

一种已固化j型/工型长桁的加筋壁板封装方法 Download PDF

Info

Publication number
CN110293696A
CN110293696A CN201910478792.6A CN201910478792A CN110293696A CN 110293696 A CN110293696 A CN 110293696A CN 201910478792 A CN201910478792 A CN 201910478792A CN 110293696 A CN110293696 A CN 110293696A
Authority
CN
China
Prior art keywords
type
drum
stringer
cured
stiffened panel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910478792.6A
Other languages
English (en)
Other versions
CN110293696B (zh
Inventor
闫恩纬
刘琦
杨绍昌
王亚萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Aircraft Industry Group Co Ltd
Original Assignee
Xian Aircraft Industry Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Aircraft Industry Group Co Ltd filed Critical Xian Aircraft Industry Group Co Ltd
Priority to CN201910478792.6A priority Critical patent/CN110293696B/zh
Publication of CN110293696A publication Critical patent/CN110293696A/zh
Application granted granted Critical
Publication of CN110293696B publication Critical patent/CN110293696B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种已固化J型/工型长桁的加筋壁板封装方法，通过筒形透气织物能够形成稳定的真空通道。通过真空袋打褶位置的优化设计，平衡长桁左、右两侧固化压力，简化了加筋壁板的封装方法，提高了产品质量。

Description

一种已固化J型/工型长桁的加筋壁板封装方法
技术领域
本发明涉及复合材料零件制造领域，尤其适用于已固化J型/工型长桁的加筋壁板组件的制造。
背景技术
复合材料加筋壁板具有承载效率高，可设计性强等优点，在航空、航天等领域得到了广泛应用。
共固化、共胶接、二次胶接等是制造复合材料加筋壁板的常用工艺方法。其中，基于已固化长桁的共胶接、二次胶接方法由于能够分散制造风险，因而得到了制造部门的关注。相对于下料、铺贴等工序，由于封装工序涉及固化过程中次级零件的定位和压力的均匀传递，因而是加筋壁板制造的核心环节。
形成稳定、可靠的真空流动通路，均衡分布压力，尤其是长桁区域的压力分布，对加筋壁板的制造质量至关重要。加筋壁板常见的长桁截面形式包括T型，工型，J型等，其中，工型和J型长桁的截面形式最为复杂。在封装过程中，容易出现左、右压力不均衡，局部假真空的问题，从而引起长桁倾斜，导致轴线度超差，局部区域分层、脱粘等质量问题。
现有的封装方法需要使用辅助设施，增加了操作难度，且可能度产品质量带来不利影响。因而，迫切需要一种简单、可靠的封装方法，均衡长桁两侧压力，提高产品胶接质量。
发明内容
本发明公开了一种已固化J型/工型长桁的加筋壁板的封装方法，采用本方法能够均衡已固化J型/工型长桁腹板面左、右两侧的固化压力，避免在长桁腹板的C型凹槽部位形成架桥，导致长桁倾斜等问题，提高长桁与蒙皮的胶接质量。
一种已固化J型/工型长桁的加筋壁板封装方法，已固化J型/工型长桁的腹板面两侧均放置有卷成筒形的透气织物，其高度为J型/工型长桁腹板高度的1/2，其长度与已固化型/工型长桁等同。真空袋需在已固化J型/工型长桁的上缘条面两边及C型槽一侧腹板面1/2高度处打褶。封装方法包括以下步骤：
1在框架式成型模具的表面铺贴J型/工型加筋壁板的蒙皮；
2参考理论位置放置所有已固化J型/工型长桁；
3将透气织物卷成筒形；
4在已固化J型/工型长桁的腹板面两侧放置卷成筒形的透气织物，并用压敏胶带固定；
5制作真空袋，在已固化J型/工型长桁的上缘条面两边及C型槽一侧腹板面1/2高度处打褶；
6抽真空压实；
7组件进热压罐固化。
本发明的封装方法具备如下优点：1)将透气织物卷成筒形放置于已固化J型/工型长桁腹板面两侧，形成稳定的真空源，避免了假真空的出现；2)在已固化J型/工型长桁上缘条面两边及C型槽部位的腹板面打褶，自适应于已固化J型/工型长桁在固化过程中的姿态调整，平衡左、右两侧压力，提高胶接质量。
附图说明
图1已固化J型加筋壁板封装方法示意图
图2已固化工型加筋壁板封装方法示意图
图中编号说明：1、成型模具；2、蒙皮；3、J型长桁；4、透气织物；5、褶子；6、工型长桁。
具体实施方式
如图1－2，一种已固化J型/工型长桁的加筋壁板封装方法，在J型/工型长桁的腹板面两侧均放置有卷成筒形的透气织物，其高度应为J型/工型长桁腹板高度的1/2。卷成筒形的导气织物与J型/工型长桁等长度。真空袋需在J型/工型长桁的上缘条面两边及C型槽一侧腹板面1/2高度处打褶。
本发明以已固化J型长桁的加筋壁板封装为例，具体方法如下：
1在框架式成型模具1的表面铺贴J型/工型加筋壁板的蒙皮2；
2参考理论位置放置所有J型长桁3或工型长桁6；
3将透气织物4卷成筒形；
4在J型/工型长桁的腹板面两侧放置卷成筒形的透气织物4，并用压敏胶带固定；
5制作真空袋，在J型/工型长桁的上缘条面及C型槽一侧腹板面1/2高度处打出褶子5；
6抽真空压实；
7组件进热压罐固化。

Claims (6)

1.一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于在已固化J型/工型长桁的腹板面两侧均放置有卷成筒形的透气织物，其高度低于长桁腹板高度，其长度与已固化型/工型长桁等同，真空袋在已固化J型/工型长桁的上缘条面两边及低于C型槽一侧腹板面高度处打褶。
2.根据权利要求1所述的一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于封装步骤如下：
2－1在框架式成型模具的表面铺贴J型/工型加筋壁板的蒙皮；
2－2参考理论位置放置所有已固化J型/工型长桁；
2－3将透气织物卷成筒形；
2－4在已固化J型/工型长桁的腹板面两侧放置卷成筒形的透气织物，并用压敏胶带固定；
2－5制作真空袋，在已固化J型/工型长桁的上缘条面两边及C型槽一侧低于腹板面高度处打褶；
2－6抽真空压实；
2－7组件进热压罐固化。
3.根据权利要求1所述的一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于透气织物可采用聚酯纤维或尼龙材料。
4.根据权利要求1所述的一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于卷成筒形的透气织物用胶带固定在长桁两侧。
5.根据权利要求1所述的一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于透气织物的高度为J型/工型长桁腹板高度的1/2。
6.根据权利要求1所述的一种已固化J型/工型长桁的加筋壁板封装方法，其特征在于真空袋在低于C型槽一侧腹板面1/2高度处打褶。
CN201910478792.6A 2019-06-03 2019-06-03 一种已固化j型/工型长桁的加筋壁板封装方法 Active CN110293696B (zh)