CN110284286B - Method for reducing pattern print of foaming curtain fabric - Google Patents
Method for reducing pattern print of foaming curtain fabric Download PDFInfo
- Publication number
- CN110284286B CN110284286B CN201910618991.2A CN201910618991A CN110284286B CN 110284286 B CN110284286 B CN 110284286B CN 201910618991 A CN201910618991 A CN 201910618991A CN 110284286 B CN110284286 B CN 110284286B
- Authority
- CN
- China
- Prior art keywords
- foaming
- fabric
- treatment
- feeding
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for reducing the pattern print of a foaming curtain fabric, which comprises the following steps: s1, adopting the plain oxford fabric as the base fabric of the foaming curtain fabric; s2, feeding the base fabric into a setting machine for setting treatment; adopting prepared foaming slurry to carry out sizing treatment on the base fabric; sending the sized fabric into a drying device for sectional drying treatment; feeding the dried fabric into a foaming compression roller device for carrying out foaming treatment; feeding the fabric subjected to the foam pressing treatment into a cold water roller for cooling treatment; feeding the cooled fabric into a winding machine for winding; the foaming curtain fabric manufactured by the method greatly reduces the irregular pattern degree on the surface of the foaming coating, thereby improving the aesthetic feeling of the curtain and ensuring the plump hand feeling of the foaming layer.
Description
Technical Field
The invention relates to the technical field of curtain fabric processing, in particular to a method for reducing the pattern print of a foaming curtain fabric.
Background
The curtain fabric is various, and the foaming layer of the foaming curtain fabric is soft and has good shading property, so that the foaming curtain fabric is popular with consumers.
However, in the process of producing the foamed curtain fabric, the fabric base fabric is usually made of a plain oxford base fabric. The plain oxford base fabric is arranged in the warp and weft directions, the foaming layer is made on the back surface of the base fabric, the foaming layer can be attached to the fabric surface, and the different tissue positions of the coating surface are recessed to different degrees due to different tensions applied to the warp and weft directions in the later rolling process, so that an irregular concave-convex pattern can be formed on the surface of the coating, and the aesthetic feeling of the curtain is affected.
Disclosure of Invention
The technical problem to be solved by the invention is as follows: in the existing production process of the foaming curtain fabric, in the winding process, due to the uneven bonding tension of the foaming coating layer surface and the cloth surface, irregular patterns can be generated on the surface of the foaming coating layer, so that the aesthetic feeling of the curtain is influenced.
The technical scheme adopted by the invention for solving the technical problems is as follows:
a method for reducing the pattern print of the foaming curtain fabric comprises the following steps:
s1, adopting plain oxford cloth as the base cloth of the foaming curtain fabric;
s2, feeding the base fabric into a setting machine for setting treatment;
s3, sizing the base fabric by using pre-prepared foaming sizing agent;
s4, feeding the sized fabric into a drying device for sectional drying treatment;
s5, feeding the dried fabric into a foaming compression roller device for carrying out foaming treatment; wherein the foaming pressure of the foaming roller device is set to 9kg/cm2;
S6, feeding the fabric subjected to the foam pressing treatment into a cold water roller for cooling treatment;
s7, feeding the fabric subjected to cooling treatment into a winding machine for winding treatment; wherein the winding tension of the winding machine is set to be 11 nm.
Further preferably, the setting temperature of the setting machine is set to be 120-160 ℃.
According to a further preferable technical scheme, the foaming slurry is prepared from 15 parts by weight of titanium dioxide solution, 15 parts by weight of foam stabilizer, 1 part by weight of cross-linking agent, 2 parts by weight of thickening agent, 80 parts by weight of acrylate emulsion and 0.5 part by weight of ammonia water.
According to a further preferable technical scheme, the solid content of the acrylate emulsion is 50%.
Further preferably, the sectional drying treatment is performed in a specific drying manner: the first section drying temperature is 80 ℃, and the drying time is 25 seconds; the second section drying temperature is 120 ℃, and the drying time is 25 seconds; the third section drying temperature is 160 ℃, and the drying time is 25 seconds.
Further optimizing the technical scheme, the cooling treatment also comprises a finishing treatment; and the finishing treatment comprises the steps of brushing a layer of hard glue on the foaming coating and drying.
Further preferably, the technical scheme is that the hard glue is prepared by mixing 97% of acrylic emulsion with the solid content of 50% and 3% of a stiffening glue agent according to the weight ratio.
Further preferably, the sizing amount of the foaming sizing agent is 40g/m2。
The invention has the beneficial effects that: the foaming curtain fabric manufactured by the method greatly reduces the irregular pattern degree on the surface of the foaming coating, thereby improving the aesthetic feeling of the curtain and ensuring the plump hand feeling of the foaming layer.
Drawings
FIG. 1 is a schematic flow diagram of the present invention.
Detailed Description
The present invention will be further described with reference to the accompanying drawings.
In the implementation of the scheme, the following slurry needs to be prepared in advance:
foaming slurry: the foaming slurry is prepared from 15 parts by weight of titanium dioxide solution, 15 parts by weight of foam stabilizer, 1 part by weight of cross-linking agent, 2 parts by weight of thickening agent, 80 parts by weight of acrylic ester emulsion with solid content of 50% and 0.5 part by weight of ammonia water.
Hard glue: is prepared by mixing 97 percent of acrylic emulsion with solid content of 50 percent and 3 percent of stiffening agent according to the weight ratio.
The following is a specific implementation flow of the scheme, as shown in fig. 1: a method for reducing the pattern print of a foaming curtain fabric is disclosed, wherein the foaming curtain fabric is made of a foamed material; the method specifically comprises the following steps:
adopting plain oxford as the base fabric of the foaming curtain fabric;
feeding the base cloth into a setting machine, and carrying out setting treatment at the temperature of 120-160 ℃;
adopting prepared foaming slurry to carry out sizing treatment on the base fabric; the sizing amount of the foaming sizing agent is 40g/m2. If multiple foaming processes exist, the directions of the two adjacent pulp scraping are opposite;
sending the sized fabric into a drying device for sectional drying treatment: the first section drying temperature is 80 ℃, and the drying time is 25 seconds; the second section drying temperature is 120 ℃, and the drying time is 25 seconds; the third section drying temperature is 160 ℃, and the drying time is 25 seconds.
Feeding the dried fabric into a foaming compression roller device for carrying out foaming treatment; wherein the foaming pressure of the foaming roller device is set to 9kg/cm2(ii) a The pressure bubble pressure here is obtained through numerous debugging experiments.
In order to protect the foaming coating, the fabric after the foaming treatment is subjected to finishing treatment, namely: brushing a layer of hard glue on the foaming coating and drying.
Feeding the fabric subjected to the top facing treatment into a cold water roller for cooling treatment; the cooling treatment enables the fabric coating to shrink, so that the adhesion degree of the coating and the cloth cover is reduced, and the elasticity of the cloth cover is improved;
feeding the cooled fabric into a winding machine for winding; wherein the winding tension of the winding machine is set to be 11 nm. The rolling tension is obtained through numerous debugging experiments.
Some experimental comparison data are listed below:
conclusion of experimental data: the comparison shows that when the pressure of the pressure bubble is 9 kilograms per square centimeter and the rolling tension is 11 newtons, the coating surface can be smoother and the irregular patterns on the coating surface can be obviously reduced on the premise of not changing the hand feeling of the foam coating.
The basic principles and the main features of the solution and the advantages of the solution have been shown and described above. It will be understood by those skilled in the art that the present solution is not limited to the embodiments described above, which are described in the specification and illustrated only to illustrate the principles of the solution, but that various changes and modifications may be made to the solution without departing from the spirit and scope of the solution, and these changes and modifications are intended to be within the scope of the claimed solution. The scope of the present solution is defined by the appended claims and equivalents thereof.
Claims (3)
1. A method for reducing the pattern print of a foaming curtain fabric is characterized by comprising the following steps:
s1, adopting plain oxford cloth as the base cloth of the foaming curtain fabric;
s2, feeding the base fabric into a setting machine for setting treatment;
s3, sizing the base fabric by using pre-prepared foaming sizing agent; the foaming slurry is prepared from 15 parts by weight of titanium dioxide solution, 15 parts by weight of foam stabilizer, 1 part by weight of cross-linking agent, 2 parts by weight of thickening agent, 80 parts by weight of acrylic ester emulsion with the solid content of 50% and 0.5 part by weight of ammonia water; the sizing amount of the foaming sizing agent is 40g/m 2;
s4, feeding the sized fabric into a drying device for sectional drying treatment;
s5, feeding the dried fabric into a foaming compression roller device for carrying out foaming treatment; wherein the foaming pressure of the foaming pressure roller device is set to be 9kg/cm 2;
s6, performing finishing treatment on the fabric subjected to the foam pressing treatment, wherein the finishing treatment is to brush a layer of hard glue on the foam coating and dry the hard glue; the hard glue is prepared by mixing 97% of acrylic emulsion with solid content of 50% and 3% of hard glue agent according to weight ratio;
s7, feeding the fabric subjected to the foam pressing treatment into a cold water roller for cooling treatment;
s8, feeding the fabric subjected to cooling treatment into a winding machine for winding treatment; wherein the winding tension of the winding machine is set to be 11 nm.
2. The method for reducing the fabric print of the foamed curtain fabric as claimed in claim 1, wherein the setting temperature of the setting machine is set to 120 ℃ to 160 ℃.
3. The method for reducing the pattern print of the foaming curtain fabric as claimed in claim 1, wherein the specific drying manner of the sectional drying treatment is as follows: the first section drying temperature is 80 ℃, and the drying time is 25 seconds; the second section drying temperature is 120 ℃, and the drying time is 25 seconds; the third section drying temperature is 160 ℃, and the drying time is 25 seconds.