CN110256988A - A kind of ceramic tile stone material gum and preparation method thereof - Google Patents
A kind of ceramic tile stone material gum and preparation method thereof Download PDFInfo
- Publication number
- CN110256988A CN110256988A CN201910633693.0A CN201910633693A CN110256988A CN 110256988 A CN110256988 A CN 110256988A CN 201910633693 A CN201910633693 A CN 201910633693A CN 110256988 A CN110256988 A CN 110256988A
- Authority
- CN
- China
- Prior art keywords
- parts
- gum
- lotion
- buna
- ceramic tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic tile stone material gum, by weight score meter, raw material composition includes: 25~30 parts of VAE lotion, 20~25 parts of buna lotion, 30~50 parts of quartz sand, 25~35 parts of coarse whiting, 0.4~0.6 part of dispersing agent, 0.2~0.4 part of fungicide, 0.1~0.3 part of mill base.In addition, the invention also discloses the methods for preparing above-mentioned gum, comprising the following steps: 1) VAE lotion, buna lotion investment dispersion machine are stirred to get mixed emulsion；2) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion and obtains gum.The problems such as gum prepared by the present invention fully achieves the bonding requirement of vitrified tile, efficiently solves the hollowing occurred when vitrified tile bonds, flakes, falls off；Have the characteristics that waterproof, adhesion are good, cold resistance is preferable, higher tensile strength by the mixed emulsion of acrylic emulsion, buna lotion, the preparation of isoprene rubber lotion.
Description
Technical field
The invention belongs to building material technical fields, more particularly to a kind of ceramic tile stone material gum and preparation method thereof.
Background technique
Vitrified tile is fired according to a certain percentage by quartz sand, mud, is then polished bright but does not need to polish,
Surface is smooth bright as glass-mirror.Its water absorption rate, straightness of sides, bending strength, in terms of it is better than general
Logical glazed tile, polished bricks and general marble.Vitrified tile is a kind of good ornament materials, is used for interior decoration, is had very
Good decorative effect.But since the water absorption rate of vitrified tile itself is lower than 5 ‰, so that very tired when it is pasted to cement layer surface
It is difficult.Ceramic tile gum can effectively improve the adhesion strength at the vitrified tile back side and cement layer surface, be that current most effective interface is viscous
Tie reinforcing material.However, ceramic tile gum is various in style currently on the market, quality is very different, will appear hollowing after use, rises
Shell, the problems such as falling off, such as: the vitrified tile after bonding is easy to appear the phenomenon that falling off by after the etch of rainwater；Weather it is cold
Thermal change makes cementitious material by the influence deformed, and cementitious material and vitrified tile interface is caused parting occur, and causes vitreous
Brick falls off.
Summary of the invention
The present invention is directed to overcome one of the problems of the above-mentioned prior art, a kind of ceramic tile stone material gum is provided, by weight
Number meter, raw material composition include:
Preferably, according to parts by weight, the buna lotion is by 10~13 parts of buna, 10~12 parts of toluene systems
At.
Preferably, the mesh number of the quartz sand is 40~70 mesh.
Further further include:
0.2~0.4 part of fungicide,
0.1~0.3 part of mill base.
Preferably, the mill base is middle yellow pulp.
In addition, the present invention also provides a kind of methods for preparing above-mentioned ceramic tile stone material gum, comprising the following steps:
1) VAE lotion, buna lotion investment dispersion machine are stirred 25~35 minutes and obtains mixed emulsion, dispersion machine
Revolving speed is 800~900 revs/min；
2) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 15
Gum is obtained within~25 minutes, the revolving speed of dispersion machine is 850~900 revs/min.
Ceramic tile stone material gum prepared by the present invention fully achieves the bonding requirement of vitrified tile, efficiently solves glass
The problems such as changing the hollowing occurred when brick bonds, flaking, fall off.
Specific embodiment
For a better understanding of the present invention, below with reference to the embodiment content that the present invention is furture elucidated, but it is of the invention
Content is not limited solely to the following examples.
Embodiment 1:
A kind of ceramic tile stone material gum, according to parts by weight, raw material composition includes:
Wherein, according to parts by weight, the buna lotion is made of 10 parts of buna, 10 parts of toluene.The stone
The mesh number of sand is 40 mesh；The mill base is middle yellow pulp.
A method of preparing ceramic tile stone material gum, comprising the following steps:
1) buna lotion will be prepared in buna, toluene investment reaction kettle；
2) VAE lotion, buna lotion investment dispersion machine are stirred 25 minutes and obtains mixed emulsion, the revolving speed of dispersion machine
It is 800 revs/min；
3) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 15
Minute obtains gum, and the revolving speed of dispersion machine is 850 revs/min.
Embodiment 2:
A kind of ceramic tile stone material gum, according to parts by weight, raw material composition includes:
Wherein, according to parts by weight, the buna lotion is made of 12 parts of buna, 11 parts of toluene.The stone
The mesh number of sand is 40 mesh；The mill base is middle yellow pulp.
A method of preparing ceramic tile stone material gum, comprising the following steps:
2) buna lotion will be prepared in buna, toluene investment reaction kettle；
2) VAE lotion, buna lotion investment dispersion machine are stirred 30 minutes and obtains mixed emulsion, the revolving speed of dispersion machine
It is 850 revs/min；
3) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 20
Minute obtains gum, and the revolving speed of dispersion machine is 880 revs/min.
Embodiment 3:
A kind of ceramic tile stone material gum, according to parts by weight, raw material composition includes:
Wherein, according to parts by weight, the buna lotion is made of 13 parts of buna, 12 parts of toluene.The stone
The mesh number of sand is 40 mesh；The mill base is middle yellow pulp.
A method of preparing ceramic tile stone material gum, comprising the following steps:
1) buna lotion will be prepared in buna, toluene investment reaction kettle；
2) VAE lotion, buna lotion investment dispersion machine are stirred 35 minutes and obtains mixed emulsion, the revolving speed of dispersion machine
It is 900 revs/min；
3) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 25
Minute obtains gum, and the revolving speed of dispersion machine is 900 revs/min.
Embodiment 4:
A kind of ceramic tile stone material gum, according to parts by weight, raw material composition includes:
Wherein, according to parts by weight, the buna lotion is made of 13 parts of buna, 12 parts of toluene.The stone
The mesh number of sand is 40 mesh；The mill base is middle yellow pulp.
A method of preparing ceramic tile stone material gum, comprising the following steps:
1) buna lotion will be prepared in buna, toluene investment reaction kettle；
2) VAE lotion, buna lotion investment dispersion machine are stirred 30 minutes and obtains mixed emulsion, the revolving speed of dispersion machine
It is 850 revs/min；
3) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 25
Minute obtains gum, and the revolving speed of dispersion machine is 850 revs/min.
Embodiment 5:
Ceramic tile stone material gum made from above-described embodiment 1~4 is tested for the property, referring to JC/T547-2017 " ceramics
Brick adhesive " criterion ceramic tile stone material gum is tested for the property, result is as shown in table 1 below:
Table 1
As can be seen from the above table, the present invention mentions prepared ceramic tile stone material gum, fully achieves the bonding of vitrified tile
It is required that the problems such as efficiently solving the hollowing occurred when vitrified tile bonds, flaking, fall off, and construction is simple.
Although an embodiment of the present invention has been shown and described, it will be understood by those skilled in the art that: not
A variety of change, modification, replacement and modification can be carried out to these embodiments in the case where being detached from the principle of the present invention and objective, this
The range of invention is defined by the claims and their equivalents.
Claims (6)
1. a kind of ceramic tile stone material gum, which is characterized in that according to parts by weight, raw material composition includes:
。
2. ceramic tile stone material gum according to claim 1, which is characterized in that according to parts by weight, the buna cream
Liquid is made of 10~13 parts of buna, 10~12 parts of toluene.
3. ceramic tile stone material gum according to claim 2, which is characterized in that the mesh number of the quartz sand is 40~70 mesh.
4. according to any ceramic tile stone material gum of claim 1-4, which is characterized in that according to parts by weight, raw material composition
Further include:
0.2~0.4 part of fungicide,
0.1~0.3 part of mill base.
5. ceramic tile stone material gum according to claim 3, which is characterized in that the mill base is middle yellow pulp.
6. a kind of method for preparing any ceramic tile stone material gum of claim 1 to 5, which is characterized in that including following step
It is rapid:
1) VAE lotion, buna lotion investment dispersion machine are stirred 25~35 minutes and obtains mixed emulsion, the revolving speed of dispersion machine
It is 800~900 revs/min；
2) quartz sand, coarse whiting, dispersing agent, fungicide, mill base are put into above-mentioned mixed emulsion, dispersion machine continues stirring 15~25
Minute obtains gum, and the revolving speed of dispersion machine is 850~900 revs/min.