CN110229576A - A kind of quick-dry type anticorrosive antirust primer and preparation method thereof - Google Patents
A kind of quick-dry type anticorrosive antirust primer and preparation method thereof Download PDFInfo
- Publication number
- CN110229576A CN110229576A CN201910519314.5A CN201910519314A CN110229576A CN 110229576 A CN110229576 A CN 110229576A CN 201910519314 A CN201910519314 A CN 201910519314A CN 110229576 A CN110229576 A CN 110229576A
- Authority
- CN
- China
- Prior art keywords
- parts
- quick
- dry type
- agent
- adhesive force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of quick-dry type anticorrosive antirust primers, are made of the component of following portions by weight: 25 parts of acrylic resin, 15 parts of dimethylbenzene, 1.5 parts of iron oxide red, 0.13 part of high-carbon black pigment, 3 parts of medium chrome yellow, 8 parts of titanium dioxide, 6 parts of lithopone, 5 parts of talcum powder, 10 parts of modified resin, 2 parts of butanol, 0.5 part of dispersing agent, 0.1 part of levelling agent, 1 part of adhesive force auxiliary agent, 0.2 part of drier, 0.5 part of preservative；Compared with prior art, the present invention can be under normal temperature state equipped with drier, rapid draing, and entirety has the characteristics that good anti-corrosive properties, good antirust property, grinability is good, cost performance is high, is suitble to large-scale pipeline production；Increase preservative, it can be ensured that coating by the infringement of bacterium and algae, does not considerably increase service life and the corrosion resistance of paint；Using the modified resin and adhesive force auxiliary agent of certain component, the composition formed with other components increases adhesive force, further improves antiseptic property.
Description
Technical field
The present invention relates to industrial coating technical field, specially a kind of quick-dry type anticorrosive antirust primer and preparation method thereof.
Background technique
Priming paint is the first layer of paint system, for improving the adhesive force of finishing coat, the richness for increasing finishing coat, providing alkali resistant
Property, anti-corrosion function etc. is provided, while can guarantee the uniform pickup of finishing coat, paint system is made to play optimum efficiency.Surface paint quality
Priming paint can not be had to well, this saying is not right, because finishing coat is different from the function of priming paint, finishing coat more lays particular emphasis on final dress
Decorations and apparent effect, and priming paint then lays particular emphasis on and improves adhesive force, anti-corrosion function, alkali resistance etc..
Existing priming paint, it is poor that there are antiseptic properties, and service life is short, and technical process is cumbersome, and causing cannot extensive flowing water
Line production, economic cost are high.
Summary of the invention
The purpose of the present invention is to provide a kind of quick-dry type anticorrosive antirust primers and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
The purpose of the present invention is be achieved by following technical proposals: a kind of quick-dry type anticorrosive antirust primer, by following
The component of parts by weight is made: 25-35 parts of acrylic resin, 15~20 parts of dimethylbenzene, 1.5-5 parts of iron oxide red, high pigment charcoal
0.1-0.3 parts black, 3-5 parts of medium chrome yellow, 8-12 parts of titanium dioxide, 6-12 parts of lithopone, 5-10 parts of talcum powder, modified resin 10-15
Part, is prevented 2-5 parts of butanol, 0.5-1 parts of dispersing agent, 0.1-0.3 parts of levelling agent, 1-2 parts of adhesive force auxiliary agent, 0.2-0.5 parts of drier
Rotten agent 0.5-1 parts.
Preparation method of the invention, comprising the following steps:
Step 1: acrylic resin being added in slack tank and is stirred by opening dispersion machine, stirring after five minutes, is being stirred
Iron oxide red, high-carbon black pigment, medium chrome yellow, titanium dioxide, lithopone, talcum powder and one third point are slowly added into during mixing
The dimethylbenzene of amount is mixed；
Step 2: the dispersing speed in set-up procedure (1) makes revolving speed reach 1500-2100 per minute turns, to mixing material
It is sufficiently stirred, is sent into grinder and is ground after dispersion 30 minutes, be ground to fineness less than 30 μm；
Step 3: the ground mixing material of step (2) is put into paint mixing tank, be added modified resin, butanol, dispersing agent,
Levelling agent, adhesive force auxiliary agent, drier, preservative and remaining dimethylbenzene, are stirred.
In the present invention, the fineness of the iron oxide red, high-carbon black pigment and medium chrome yellow is 300~500 mesh.
In the present invention, the adhesive force auxiliary agent is silane coupling agent or propyl trimethoxy silicane.
In the present invention, the drier is the mixing of one or more of cobalt iso-octoate, isooctoate of rare earth metal, calcium iso-octoate
Object.
In the present invention, the preservative is isothiazolinone derivatives, benzimidazole esters, Dao Weixier -75,1,2- benzene
And the compounding intermixture of isothiazoline -3- ketone and other preservatives.
A kind of quick-dry type anticorrosive antirust primer of the invention and preparation method thereof has the beneficial effect that:
(1) present invention can be under normal temperature state equipped with drier, rapid draing, and the whole good, antirust with anti-corrosive properties
The features such as performance is good, grinability is good, cost performance is high is suitble to large-scale pipeline production.
(2) invention increases preservatives, it can be ensured that coating by the infringement of bacterium and algae, does not considerably increase paint
Service life and corrosion resistance.
(3) modified resin and adhesive force auxiliary agent of certain component, the composition formed with other components are used in the present invention
Adhesive force is increased, antiseptic property is further improved.
Specific embodiment
Further instruction With reference to embodiment, but following detailed description should not be done and be managed
Solution is the limitation invented ontology.Those of ordinary skill in the art can apparently make various on the basis of the present invention
Change and change, it should within the scope of invention.
Embodiment 1
A kind of quick-dry type anticorrosive antirust primer, is made of the component of following portions by weight: 25 parts of acrylic resin, dimethylbenzene
15 parts, 1.5 parts of iron oxide red, 0.13 part of high-carbon black pigment, 3 parts of medium chrome yellow, 8 parts of titanium dioxide, 6 parts of lithopone, 5 parts of talcum powder,
10 parts of modified resin, 2 parts of butanol, 0.5 part of dispersing agent, 0.1 part of levelling agent, 1 part of adhesive force auxiliary agent, 0.2 part of drier, preservative
0.5 part.
Preparation method of the invention, comprising the following steps:
Step 1: acrylic resin being added in slack tank and is stirred by opening dispersion machine, stirring after five minutes, is being stirred
Iron oxide red, high-carbon black pigment, medium chrome yellow, titanium dioxide, lithopone, talcum powder and one third point are slowly added into during mixing
The dimethylbenzene of amount is mixed；
Step 2: the dispersing speed in set-up procedure (1) makes revolving speed reach 1500-2100 per minute turns, to mixing material
It is sufficiently stirred, is sent into grinder and is ground after dispersion 30 minutes, be ground to fineness less than 30 μm；
Step 3: the ground mixing material of step (2) is put into paint mixing tank, be added modified resin, butanol, dispersing agent,
Levelling agent, adhesive force auxiliary agent, drier, preservative and remaining dimethylbenzene, are stirred.
In the present invention, the fineness of the iron oxide red, high-carbon black pigment and medium chrome yellow is 300~500 mesh.
In the present invention, the adhesive force auxiliary agent is silane coupling agent or propyl trimethoxy silicane.
In the present invention, the drier is the mixing of one or more of cobalt iso-octoate, isooctoate of rare earth metal, calcium iso-octoate
Object.
In the present invention, the preservative is isothiazolinone derivatives, benzimidazole esters, Dao Weixier -75,1,2- benzene
And the compounding intermixture of isothiazoline -3- ketone and other preservatives.
Embodiment 2
A kind of quick-dry type anticorrosive antirust primer, is made of the component of following portions by weight: 35 parts of acrylic resin, dimethylbenzene
20 parts, 5 parts of iron oxide red, 0.3 part of high-carbon black pigment, 5 parts of medium chrome yellow, 12 parts of titanium dioxide, 12 parts of lithopone, 10 parts of talcum powder,
15 parts of modified resin, 5 parts of butanol, 1 part of dispersing agent, 0.3 part of levelling agent, 2 parts of adhesive force auxiliary agent, 0.5 part of drier, preservative 1
Part.
Preparation method of the invention, comprising the following steps:
Step 1: acrylic resin being added in slack tank and is stirred by opening dispersion machine, stirring after five minutes, is being stirred
Iron oxide red, high-carbon black pigment, medium chrome yellow, titanium dioxide, lithopone, talcum powder and one third point are slowly added into during mixing
The dimethylbenzene of amount is mixed；
Step 2: the dispersing speed in set-up procedure (1) makes revolving speed reach 1500-2100 per minute turns, to mixing material
It is sufficiently stirred, is sent into grinder and is ground after dispersion 30 minutes, be ground to fineness less than 30 μm；
Step 3: the ground mixing material of step (2) is put into paint mixing tank, be added modified resin, butanol, dispersing agent,
Levelling agent, adhesive force auxiliary agent, drier, preservative and remaining dimethylbenzene, are stirred.
In the present invention, the fineness of the iron oxide red, high-carbon black pigment and medium chrome yellow is 300~500 mesh.
In the present invention, the adhesive force auxiliary agent is silane coupling agent or propyl trimethoxy silicane.
In the present invention, the drier is the mixing of one or more of cobalt iso-octoate, isooctoate of rare earth metal, calcium iso-octoate
Object.
In the present invention, the preservative is isothiazolinone derivatives, benzimidazole esters, Dao Weixier -75,1,2- benzene
And the compounding intermixture of isothiazoline -3- ketone and other preservatives.
Embodiment 3
A kind of quick-dry type anticorrosive antirust primer, is made of the component of following portions by weight: 30 parts of acrylic resin, dimethylbenzene
18 parts, 3.5 parts of iron oxide red, 0.2 part of high-carbon black pigment, 4 parts of medium chrome yellow, 10 parts of titanium dioxide, 9 parts of lithopone, 8 parts of talcum powder,
13 parts of modified resin, 0.8 part of dispersing agent, 0.2 part of levelling agent, 1.5 parts of adhesive force auxiliary agent, 0.35 part of drier, is prevented 3 parts of butanol
0.8 part of rotten agent.
Preparation method of the invention, comprising the following steps:
Step 1: acrylic resin being added in slack tank and is stirred by opening dispersion machine, stirring after five minutes, is being stirred
Iron oxide red, high-carbon black pigment, medium chrome yellow, titanium dioxide, lithopone, talcum powder and one third point are slowly added into during mixing
The dimethylbenzene of amount is mixed；
Step 2: the dispersing speed in set-up procedure (1) makes revolving speed reach 1500-2100 per minute turns, to mixing material
It is sufficiently stirred, is sent into grinder and is ground after dispersion 30 minutes, be ground to fineness less than 30 μm；
Step 3: the ground mixing material of step (2) is put into paint mixing tank, be added modified resin, butanol, dispersing agent,
Levelling agent, adhesive force auxiliary agent, drier, preservative and remaining dimethylbenzene, are stirred.
In the present invention, the fineness of the iron oxide red, high-carbon black pigment and medium chrome yellow is 300~500 mesh.
In the present invention, the adhesive force auxiliary agent is silane coupling agent or propyl trimethoxy silicane.
In the present invention, the drier is the mixing of one or more of cobalt iso-octoate, isooctoate of rare earth metal, calcium iso-octoate
Object.
In the present invention, the preservative is isothiazolinone derivatives, benzimidazole esters, Dao Weixier -75,1,2- benzene
And the compounding intermixture of isothiazoline -3- ketone and other preservatives.
Above description is only the preferred embodiment of the application and the explanation to institute's application technology principle.Those skilled in the art
Member is it should be appreciated that invention scope involved in the application, however it is not limited to technology made of the specific combination of above-mentioned technical characteristic
Scheme, while should also cover in the case where not departing from the inventive concept, it is carried out by above-mentioned technical characteristic or its equivalent feature
Any combination and the other technical solutions formed.Such as features described above has similar function with (but being not limited to) disclosed herein
Can technical characteristic replaced mutually and the technical solution that is formed.
Claims (6)
1. a kind of quick-dry type anticorrosive antirust primer, it is characterised in that: be made of the component of following portions by weight: acrylic resin
25-35 parts, 15~20 parts of dimethylbenzene, 1.5-5 parts of iron oxide red, 0.1-0.3 parts of high-carbon black pigment, 3-5 parts of medium chrome yellow, titanium dioxide
8-12 parts, 6-12 parts of lithopone, 5-10 parts of talcum powder, 10-15 parts of modified resin, 2-5 parts of butanol, 0.5-1 parts of dispersing agent, levelling
0.1-0.3 parts of agent, 1-2 parts of adhesive force auxiliary agent, 0.2-0.5 parts of drier, 0.5-1 parts of preservative.
2. a kind of preparation method of quick-dry type anticorrosive antirust primer according to claim 1, it is characterised in that: including following
Step:
Step 1: acrylic resin being added in slack tank and is stirred by opening dispersion machine, is stirred after five minutes, stirred
Iron oxide red, high-carbon black pigment, medium chrome yellow, titanium dioxide, lithopone, talcum powder and one third component are slowly added into journey
Dimethylbenzene is mixed；
Step 2: the dispersing speed in set-up procedure (1) makes revolving speed reach 1500-2100 per minute turns, carries out to mixing material
It is sufficiently stirred, is sent into grinder and is ground after dispersion 30 minutes, be ground to fineness less than 30 μm；
Step 3: the ground mixing material of step (2) being put into paint mixing tank, modified resin, butanol, dispersing agent, levelling is added
Agent, adhesive force auxiliary agent, drier, preservative and remaining dimethylbenzene, are stirred.
3. a kind of quick-dry type anticorrosive antirust primer according to claim 1, it is characterised in that: the iron oxide red, high color
The fineness of plain carbon black and medium chrome yellow is 300~500 mesh.
4. a kind of quick-dry type anticorrosive antirust primer according to claim 1, it is characterised in that: the adhesive force auxiliary agent is silicon
Alkane coupling agent or propyl trimethoxy silicane.
5. a kind of quick-dry type anticorrosive antirust primer according to claim 1, it is characterised in that: the drier is isooctyl acid
The mixture of one or more of cobalt, isooctoate of rare earth metal, calcium iso-octoate.
6. a kind of quick-dry type anticorrosive antirust primer according to claim 1, it is characterised in that: the preservative is isothiazole
Quinoline ketone derivatives, benzimidazole esters, Dao Weixier -75, the compounding of 1,2-benzisothiazolin-3-one and other preservatives are mixed
Mixture.