CN110205799A - A method of for cotton for wadding general-purpose glue and prepare Multifunctional spray glue cotton for wadding - Google Patents
A method of for cotton for wadding general-purpose glue and prepare Multifunctional spray glue cotton for wadding Download PDFInfo
- Publication number
- CN110205799A CN110205799A CN201910501795.7A CN201910501795A CN110205799A CN 110205799 A CN110205799 A CN 110205799A CN 201910501795 A CN201910501795 A CN 201910501795A CN 110205799 A CN110205799 A CN 110205799A
- Authority
- CN
- China
- Prior art keywords
- cotton
- wadding
- glue
- general
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method of for cotton for wadding general-purpose glue and prepare Multifunctional spray glue cotton for wadding, configure general-purpose glue: a, the multifunction finishing agent for successively weighing textile fabric to scale, HD-604 glue, water；B. the multifunction finishing agent of the textile fabric weighed up, HD-604 glue are added to the water, high speed dispersion stirs 20~30 minutes, until dispersing material substantially uniformity；Make Multifunctional spray glue cotton for wadding: a, selection cotton for wadding；B, in selected cotton for wadding surface even application general-purpose glue, 5--8g/ square metres of dosage；Another side even application HD-604 glue；C, it cotton for wadding has been sprayed, is sent into the dryer that temperature is 90 DEG C~110 DEG C and dries.With the fluffy of cotton for wadding, compression resilience is high, resistance to dry, wet washing, outside the performances such as warming, according further to certain frequency to human-body emitting far infrared, is radiated by flocculus and increases heat to human body far infrared, human body is allowed to bask.And anion is generated, form oxygen-enriched moist heat.Low surface charge, cotton for wadding do not generate electrostatic.
Description
Technical field
The invention belongs to composite material technical field, be related to a kind of high-efficiency thermal protection, microcirculation health care, anion, without quiet
Electricity cotton for wadding, and in particular to a method of for cotton for wadding general-purpose glue and prepare Multifunctional spray glue cotton for wadding.
Background technique
With the development of society and the progress of science and technology, the improvement of people's living standards, demand of the people to textile is from list
One resisting cold hides body, fast-developing to fashion-orientation, functionalization, lightening, personalized and health care functional textile direction, accelerates
Research and development new type functional new material is basis and the inexorable trend of textile development.
Heat insulating material refers to the raw material for constituting the wadding material that keeps warm, and is often used for clothes in the form of flocculus or wadding material, bedding, sleeps
Bag etc., maximum feature is light and fluffy insulation.In the fibrous raw material of Novel heat-preservation wadding material, generally all containing hollow or high
Heat insulating material is made by different production technologies in crimped polyester, acrylic staple fibre, superfine fibre.
American-European countries is to develop based on doughnut and superfine fibre flocculus and windproof laminated fabric.Russia develops
Using the non-woven cloth heat insulating material of the water jet process of ecology.This heat insulating material is made of polyester fiber net, is had on web
Water flow jet acts on the several rows of water needle to be formed, and water needle is in certain angle α (45 DEG C~89 DEG C) range with diagonal shape point
Cloth, eyelet is also installed on material, and regular eyelet makes material have good gas permeability and thermal diffusivity.Such heat insulating material is not
It is same that there is high-intensitive and high heat-retention using adhesive and composite layer.
The U.S. develops Dual-layer warming non-woven cloth, it is long by spun lacing Polyester Fibers layer and another layer of continuous polycondensation
Wire material is combined.DuPont Corporation is the needs for meeting each level dress designing and different prices, develops 5 kinds of batt layer
Heat insulating material: the good ThermoloftcM of novel fine-denier down-like Micro-loftcM, repeated washing conformality, dampness
Under wear well ThermolitecM, four pore structure fiber Hollofil and the good seven apertures in the human head structural fibers of fluffy degree of good performance
QuallofilcM.Thinsulate (Xin Xueli) thermal insulation material of 3M company has lightweight thermal, moisture-proof characteristic.
The novel heat-storing material that the companies such as Japanese Japan's spinning, Kuraray, You Nijika release one after another.On the one hand, by ZrC etc.
Ceramic particle is filled into wadding material, generates warm effect；On the other hand, the structure for adjusting heat insulating material finished product, learns from other's strong points to offset one's weaknesses, reaches
To multi-functional purpose.
The development of domestic flocculus is very fast, on raw material via the natural materials such as initial wool tire, cotton-wool, natural feather to
The extension of the synthesis materials such as acrylic fibers flocculus, polyester elastic flocculus.Imitative silk flosssilk wadding, super feather and down in recent years, metal coating composite flake,
Far-infrared warm fabric, natural feather chemical fibre insulation flocculus, chemical fibre mixing insulation flocculus, natural feather gum sprayed cotton composite heat insulation flocculus, antibacterial
Anion insulation flocculus, anion nonwoven cotton wool flake, flax flocculus, flaxen fiber nonwoven cotton wool flake, soybean fiber flocculus, soybean are fine
Tie up nonwoven cotton wool flake, bamboo fibre flocculus, bamboo fibre nonwoven cotton wool flake, zein fiber flocculus, zein fiber nonwoven cotton wool flake, Carbon fiber
Flocculus is tieed up, Carbon fibe acupuncture cotton flocculus adds charcoal nonwoven cotton wool flake, and the novel heat-preserving materials such as pearl cotton wool flake constantly come out.Wherein
Even more using non-woven insulation flocculus as major industry, these new materials are either all being constantly improve on fiber or technique
In the process, their light with its, warming, good permeabilities, radix saposhnikoviae, mould proof, mothproof, acid and alkali-resistance, the advantages that can directly washing, are a large amount of
It is widely used in producing instead of the natural fibers such as wool tire, cotton-wool wadding material.
It applies with the development of various new and high technologies and in textile industry and increasingly promotes, make heat insulating material increasingly towards multiple
The development of mould assembly multifunctional direction.It is so-called compound to refer to the different fiber such as various natural fibers, synthetic fibers and functional fiber
Between compound and heat insulating material and other fabrics between it is compound.Its object is to adjust the structure of heat insulating material finished product, inhale
The characteristics of taking various types of materials also has certain specific, excellent physically or chemically performances in addition to basic mechanical property,
Such as there is certain electric properties, magnetic performance, thermal property, the elasticity of compression, washing performance, permeability and water vapour permeability,
To reach multi-functional purpose, it is more in line with demand of the consumer to heat insulating material various aspects.Not with people's environmental consciousness
Disconnected enhancing, environmentally protective material also provide broader space for the development of heat insulating material.
A kind of textile fabric is more in the patent No. CN201210066454.X of Xi'an Huajie Technology Development Co., Ltd.
Nano-macromolecule material is used mentioned in functional finishing agent, cotton after post treatment, hair, silk, fiber crops, fiber product make
Dress ornament has the characteristics that microcirculation health care, warming, band anion, without electrostatic, clothing products can emit near-infrared, in it is infrared and
Far infrared, emission band is in 750~16000nm, emissivity > 96%, transmission power 456W/m2, negative ion concentration 2570/
cm3, absorption of UV > 99% can greatly improve microcirculation in human body, health care with super strength and heat-preserving function.
Summary of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the object of the present invention is to provide a kind of general-purpose glue for cotton for wadding and
The method for preparing Multifunctional spray glue cotton for wadding, a kind of high-efficiency thermal protection, microcirculation health care, anion, without electrostatic multifunctional glue spraying cotton for wadding,
It not only has the fluffy of conventional cotton for wadding, and compression resilience is high, resistance to dry, wet washing, and outside the performances such as light and warming, according further to
Certain frequency is radiated by flocculus and increases heat to human body far infrared to human-body emitting far infrared, to allow human body sense
To warm.A large amount of anion is generated simultaneously, oxygen-enriched moist heat is formed, does not generate the functions such as electrostatic.To fabricate cotton
The important new material of clothes and the bedding such as ski-wear, space suit and cotton-wadded quilt, sleeping bag and certain industrial goods.
To achieve the goals above, the technical solution adopted by the present invention is that:
A kind of general-purpose glue for cotton for wadding includes consisting of by mass fraction ratio:
The multifunction finishing agent of textile fabric: 3~5wt%；
HD-604 glue: 9~11wt%；
Water=88~84wt%.
A method of preparing Multifunctional spray glue cotton for wadding, comprising the following steps:
(1) general-purpose glue is configured:
A, multifunction finishing agent, the HD-604 glue, water of textile fabric are successively weighed to scale；
B. the multifunction finishing agent of the textile fabric weighed up, HD-604 glue are added to the water, high speed dispersion stirs 20~30 points
Clock, until dispersing material substantially uniformity；
(2) Multifunctional spray glue cotton for wadding is made:
A, cotton for wadding is selected；
B, in selected cotton for wadding surface even application general-purpose glue, 5--8g/ square metres of dosage；Another side even application
HD-604 glue；
C, it cotton for wadding has been sprayed, is sent into the dryer that temperature is 90 DEG C~110 DEG C and dries.
The multifunction finishing agent of the textile fabric uses the textile fabric of Xi'an Huajie Technology Development Co., Ltd.
Multifunction finishing agent.
The beneficial effects of the present invention are:
1. spraying is to wad a quilt with cotton with " microcirculation health care, warming, anion, without electrostatic multifunctional finishing agent " content in general-purpose glue
The microcirculation health care of cotton, warming, anion, the key realized without antistatic property.This project passes through a large amount of scientific experiment, selects
HJN-01 nano-far-infrared keeps warm multifunction finishing agent, 3~5wt% of dosage.
2. every square metre of multi-functional glue amount of spraying, is to realize the multi-functional guarantee of cotton-wool.Dosage 5--8g/ is determined after experiment
Square metre.
3. high-efficiency thermal protection, microcirculation health care, anion, without electrostatic multifunctional cotton for wadding functional structure design.Multi-functional cotton for wadding
Functional structure design are as follows: spray general-purpose glue on one side, another side sprays conventional glue.
4. general-purpose glue and cotton for wadding have excellent binding strength, keep the fluffy of cotton for wadding, compression resilience it is high, it is resistance to it is dry,
The performances such as wet washing, light and warming, and there is excellent microcirculation health care, warming, anion, without electrostatic function.
5. Application of micron development technique is innovated, microcirculation health care, warming, anion have been started, without electrostatic multifunctional
Heat insulating material frontier.
6. high-efficiency thermal protection, microcirculation health care, anion, without electrostatic multifunctional cotton for wadding performance study innovate.It solves long-term
Since chemical fibre class textile can only be made of ceramic powders, absorbing sweat, poor air permeability, electrostatic are big, dress is uncomfortable, product is single,
Infrared emitting rate is low, does not have the problems such as natural fibre product and disadvantage.
7. high-efficiency thermal protection, microcirculation health care, anion, without electrostatic multifunctional cotton for wadding functional structure design innovation.
8. process method for finishing is innovated.
9. nano material high fastness technological innovation in conjunction with textile surface.
Xi'an Huajie Technology Development Co., Ltd. uses nano-macromolecule material, micro- the following through high-tech means processing
Ring health care, high-efficiency thermal protection, microcirculation health care, anion, without electrostatic multifunctional glue spraying cotton for wadding, it not only has the fluffy of conventional cotton for wadding
Pine, compression resilience height, resistance to dry, wet washing, and outside the performances such as light and warming, it is remote to human-body emitting according further to certain frequency
Infrared ray, emission band is in 750~16000nm, emissivity >=0.87, transmission power 456W/m2, radiated by flocculus to human body
Far infrared increases heat, 4-6 DEG C of far infrared radiation surface temperature rise, so that human body be allowed to bask.It generates simultaneously a large amount of negative
Ion, 2900/cm of negative ion concentration3, oxygen-enriched moist heat is formed, does not generate the functions such as electrostatic.Surface charge density≤
1.2μC/m2.Briefly, there is fluffy insulation flocculus stopping the loss of human body thermal energy outside human body, while having high intensity again
Infrared radiation is sat near the fireplace, heat-preserving function with super strength just as we wear wadded jacket winter.
The function cotton for wadding can be used as warm-up, sleeping bag etc., pass through the infrared ray and sunlight and nature of absorption human-body emitting
In infrared ray, by the storage of the infrared ray of absorption and with 87% emissivity to human-body emitting, coincide with human body starting wave, easily
It is absorbed by the body, human body 70mm can be penetrated, can greatly improve microcirculation in human body, there are certain health care functions.
Multifunctional efficient keeps warm cotton-wool, cotton, hair, chemical fibre can be used and be made, not only with moisture absorption, perspire, breathe freely
Performance, and have more energy storage, heat accumulation, anion releasing effect.
Under the premise of meeting warming, clothes, sleeping bag bulking value can be made to reduce 1/3, which has been equipped with People's Armed Police's special type
8000 sets of army's sleeping bag, greatly reduce sleeping bag volume, weight, meeting army is requirement of the soldier by gram loss of weight." liberation army
Report " with " liberation army tests novel field operation sleeping bag, and subzero 26 degree outdoor soldiers safely sleep soundly " etc. for topic, made special topic three times and reported
Road is made that contribution for the promotion of liberation army logistical equipment.
Technical indicator
1) infrared emitting rate: >=0.87；
2) launch wavelength: 750~16000nm；
3) power emission rate: 456W/m2(at 37 DEG C)；
4) surface charge density≤1.2 μ C/m2；
5) 4-6 DEG C of far infrared radiation temperature rise；
6) negative ion concentration: 2900/cm3。
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
The present invention is further discussed below below in conjunction with attached drawing and principle.
A kind of general-purpose glue for cotton for wadding includes consisting of by mass fraction ratio:
The multifunction finishing agent of textile fabric: 3~5wt%；
HD-604 glue: 9~11wt%；
Water=88~84wt%.
As shown in Figure 1, a kind of method for preparing Multifunctional spray glue cotton for wadding, comprising the following steps:
(1) general-purpose glue is configured:
A, multifunction finishing agent, the HD-604 glue, water of textile fabric are successively weighed to scale；
B. the multifunction finishing agent of the textile fabric weighed up, HD-604 glue are added to the water, high speed dispersion stirs 20~30 points
Clock, until dispersing material substantially uniformity；
(2) Multifunctional spray glue cotton for wadding is made:
A, cotton for wadding is selected；
B, in selected cotton for wadding surface even application general-purpose glue, 5--8g/ square metres of dosage；Another side even application
HD-604 glue；
C, it cotton for wadding has been sprayed, is sent into the dryer that temperature is 90 DEG C~110 DEG C and dries.Application range
1. being suitable for the insulation flocculus that cotton, hair, chemical fibre etc. are raw material, the winters such as processing sleeping bag, cotton bedding, cotton dress is suitble to protect
Warm product.
2. being suitable for other fields improves microcirculation in human body and clothes for health care.
3. cotton for wadding spraying function glue surface is skin-proximal face.
Basic principle
Quantum theory thinks that substance is under the irradiation of incident light, after molecule absorption luminous energy, will great-jump-forward increase oneself
Energy, i.e. the variation of matter energy be it is quantized, the energy hv of each photon depends on the energy difference Δ between two energy levels
E。
Δ E=E2-E1=hV
In formula, h is Planck's constant, and υ is light frequency, E2、E1For the energy of first energy level and whole energy level.
Infra-red radiation is derived from the change of material molecule internal motion.The form of internal motions of molecule is extremely complex, mainly has
The electronics vibration of each atomic nucleus near its equilbrium position in nuclear movement, the translation of molecule, molecule, and it is entire
Rotation of the molecule around certain symmetry axis.Since translational energy is the function of temperature, therefore molecule translational motion does not have with electromagnetic radiation
Selective interaction relationship does not generate discrete infrared spectroscopy.Mainly consider to be transported by intramolecular electronics in research
Nuclear vibration and the generated molecular spectrum of rotation in dynamic, molecule.
For the molecule of a certain determining state, energy is electron energy Ee, vibrational energy EvWith rotational energy EyThree it
With that is,
E=Ee+Ev+Ey
When molecule transits to low-lying level E ' from high level E ", photon, frequency will be given off outward are as follows:
H is Planck's constant in formula.
Quantum theory is studies have shown that material absorbing and the essence for emitting infrared light are the variation of molecular dipole moment and the vibration of light
Swing the result of electric field interaction.The reason of material radiates is since its composed atom, molecule or ionic system are in difference
It is mainly related with the transition of its electronics in shortwave area produced by transition between energy level, and then vibrated with crystal lattices in long-wavelength region
Characteristic is related.Radiation caused by variation when vibration or rotation occur for molecule with dipole moment is the mechanism that material radiates
Place.There is extremely strong infrared activation polarization vibration in simple material, such as metal oxide, nitride, carbide, meanwhile,
In its infrared spectral region, there are extremely strong absorption of vibrations bands.The presence of this absorbability vibration decides the infra-red radiation of material
Performance.The infrared high radiation wave band of simple material is often in the two phonons combination absorption band of moderate absorption intensity, including part
Multi-phonon combination zone is the combination frequency absorption of two phonons or multi-phonon, and radiation wave band is 5~10um, and spectrum is about
The entire two phonons sum of fundamental frequencies area of shortwave is extended to from strong resonance long wave.
Infrared ray between visible light and microwave, can be subdivided into near-infrared, in infrared and far infrared.It is generally believed that
Heated by Far-Infrared Radiation technology medium wavelength is known as far ultraviolet infrared ray between 4~1000um.Light quantum has characteristic and effect, wave
When to grow infrared ray energy of a quantum between 2.5~30um be 0.04~0.5eV, chemical action is not almost played, and can only
Play the grid vibration of acceleration molecular vibration or crystallization.Constitute the fundamental particle of substance, electronics, atom or molecule, even place
It is also all ceaselessly moving-is vibrating or rotating in ground state, these movements have the intrinsic frequency of oneself.
When encountering the infrared irridiation of some wave number, if the intrinsic frequency of the wave number of infrared ray transmission and fundamental particle
It is equal, then can there is a situation where with vibration center shake kinematic similitude, particle can absorb infrared ray and make movement further intensifies.
That is, molecule, atomic energy attract comparable infrared with itself proper motion frequency to the substance of infrared ray responsive
Line not only occurs the transition for carrying kinetic energy grade, the various motion amplitudes centered on equilbrium position, the self-energy of particle has also been enlarged
It increases, the macroscopic view reflection of microstructure particle movement aggravation is exactly that object temperature increases.If the two frequency phase-difference is larger, that
Infrared ray would not be absorbed and may be reflection or pass through.Absorption of the material to incident radiation heat is heated it can be seen that improving
Rate is closely related with spectral frequency, should establish and radiate actual effect spectrum section with reasonable infrared heating, to reach and heating product
Best match (here it is " optimal spectrum matching principles ").
So-called " matching ", exactly " radiation window " alignment heating object " absorbing window " are opened very big, and no pair
On " radiation window " close to obtain very little.Since the monochromatic spectrum of radiation and the monochromatic spectrum of absorption can not accomplish absolute matches,
Therefore the optimal selection to far infrared radiator and radiation temperature is taken in practical applications, makes " the section radiance " of radiator
Be heated product, " section absorptivity " corresponding with the incidence section matches, this is both the machine of heating by infrared radiation
Reason.
Nano material quantum size effect and tunnel-effect due to caused by its special structure, leads in certain size range
It is caused to generate good infrared ray absorbing property, nano material refers to material of the characteristic size in 1-100nm range of material component
Material.When the size of a particle is small to nanometer order of magnitude, its microstructure and properties be both different from the microcosmic body of atom, molecule
System, also different from the bulky grain material meta system of display eigen property, a but transition system therebetween.
Nanoparticle size is small, large specific surface area, has very high surface energy, to have a significant impact to its chemical property.Experiment card
It is bright, after particle dispersion degree improves to a certain extent, with the reduction of particle diameter, positioned at the atomicity and total atom of particle surface
Several ratios increased dramatically, and when partial size is reduced to 5nm, surface atom proportion is up to 50%.Since surface atom number increases,
Atomicity is reduced in particle, and the electron energy level in enabled band divides, and the level spacing after division is in the energy of infrared ray
It measures (1 × 12 in range-2-1×10-5EV), so as to cause new infrared ray absorbing channel.Nano material is due to its own structure
On feature and have small-size effect, surface-interface effect, quantum size effect and macro quanta tunnel effect, thus with
Compared with the conventional material of component, catalysis, optics, magnetism, in terms of have many unusual performances, infrared ray inhale
It receives and shows good development prospect with transmitting aspect.
The total radiant power M (T) for all wavelengths that object per surface area emits to entire hemispherical space is with its temperature
Changing rule.
M (T)=ελσT4
σ=5.6697 × 10-8w/ (m in formula2·k4)
Above formula shows that all temperature all can spontaneously launch outward infrared emanation higher than the object of Kelvin zero degree, moreover,
The total radiant power of object per surface area transmitting is directly proportional to the biquadratic of emissivity and Kelvin.As long as moreover, when temperature
When degree has small change, it will just cause the radiant power great changes of object emission.
With the rapid development of infrared technique, the research of high radiant rate material is at hot spot, far infrared product fundamental wavelength
Selection it is quite important, the wavelength for radiating product is consistent with the absorbing wavelength of radiation phenomenon object (i.e. Spectral matching),
Resonance effects could be generated, this is the key point of product quality.
The warming energy of the infrared cotton for wadding of nanometer should include two parts, and a part is that the fluffy flocculus of cotton for wadding itself generates
Warming energy, it is by increasing the air layer of flocculus, the flowing of reduction air layer air, to the greatest extent may be used using the methods of heat insulating material
The thermal resistance that cotton for wadding can be improved, it is actually exactly to reduce human body that the thermal energy for reducing human body, which will not quickly conduct warming to realize,
Heat-energy losses, measurement index are clo value, warming rate, thermal resistance.Another part is exactly the infrared energy of cotton for wadding, it is will to wad a quilt with cotton
Piece has carried out the infrared arrangement of nanometer, and flocculus, according further to certain frequency to human-body emitting infrared ray, leads to other than above-mentioned function
It crosses extraneous radiation and increases heat to human body, so that human body be allowed to bask.Like under cold environment, human body is infrared in receiving
The irradiation of lamp, measurement index are infra red energy densities.
The principle of this cotton for wadding is briefly exactly: having fluffy insulation flocculus in the damage for stopping human body thermal energy outside human body
It loses, while having high-intensitive infrared radiation again, sat near the fireplace just as we wear wadded jacket winter.
Claims (2)
1. a kind of general-purpose glue for cotton for wadding, which is characterized in that by mass fraction ratio include consisting of:
The multifunction finishing agent of textile fabric: 3~5wt%；
HD-604 glue: 9~11wt%；
Water=88~84wt%.
2. a kind of method for preparing Multifunctional spray glue cotton for wadding, which comprises the following steps:
(1) general-purpose glue is configured:
A, multifunction finishing agent, the HD-604 glue, water of textile fabric are successively weighed to scale；
B. the multifunction finishing agent of the textile fabric weighed up, HD-604 glue are added to the water, high speed dispersion stirs 20~30 minutes, makes
Until material substantially uniformity is dispersed；
(2) Multifunctional spray glue cotton for wadding is made:
A, cotton for wadding is selected；
B, in selected cotton for wadding surface even application general-purpose glue, 5--8g/ square metres of dosage；Another side even application HD-
604 glue；
C, it cotton for wadding has been sprayed, is sent into the dryer that temperature is 90 DEG C~110 DEG C and dries.