CN110204986A - A kind of raw material of environmental protection boccaro inner-outer wall - Google Patents
A kind of raw material of environmental protection boccaro inner-outer wall Download PDFInfo
- Publication number
- CN110204986A CN110204986A CN201910551322.8A CN201910551322A CN110204986A CN 110204986 A CN110204986 A CN 110204986A CN 201910551322 A CN201910551322 A CN 201910551322A CN 110204986 A CN110204986 A CN 110204986A
- Authority
- CN
- China
- Prior art keywords
- boccaro
- raw material
- agent
- parts
- environmentally friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of raw material of environmentally friendly boccaro inner-outer wall, the purple soil coating material is naturally to calcine boccaro as raw material, cooperate environment-friendlyacrylic acrylic acid lotion, auxiliary agent, it is ground through high speed dispersion, purple soil coating material is made, contained raw material includes hydroxyethyl cellulose, dispersing agent, wetting agent, defoaming agent, propylene glycol, calcining boccaro, coalescing agent, ordor removing lotion, thickener, wherein the ingredient for calcining boccaro is SiO2、AI2O3、Fe2O3, CaO, MgO deviate from all liq in material, powder particle avoided to bond through cold stage and hot phase process, do not add any chemical industry pigment, the calcining boccaro powder of abundant mobility is made in sintering under high temperature.
Description
Technical field
The present invention relates to coating and its preparation technical field, more particularly to a kind of original of environmentally friendly boccaro inner-outer wall
Material.
Background technique
Coating is to be coated in the body surface protected or decorated, and can form the continuous thin of firm attachment with coated article
Film adds or does not add pigment, filler usually based on resin or oil or lotion, adds corresponding additive, uses organic solvent
Or the thick liquid that water is formulated.Coating belongs to organic chemical industry's macromolecular material, is formed by film and belongs to macromolecule chemical combination
Species type.According to the classification for the chemical products that the modern times pass through, coating belongs to fine chemical product.Modern coating gradually at
It is an important industry in chemical industry for a kind of multi-functional engineering material.It, which is acted on, mainly at 4 points: protection, dress
Decorations cover up the defect and other special roles of product, promote the value of product.
Wherein, building coating is an important class in coating, in China, will generally be used for inner wall of building, exterior wall,
The coating of ceiling, ground, toilet is known as building coating.There is building coating decoration functions, defencive function and livability to improve
Function.
Boccaro is a kind of ceramic between pottery and porcelain, its main feature is that compact structure, close to porcelain, intensity
Larger, particle is tiny, and fracture is conchoidal or stone shape, but does not have the translucence of porcelain body.Yixing purple sand device tire matter has this
Kind characteristic, moreover, among device mass color is very smooth, the variation containing fine granularity shows a kind of chiltern effect.Boccaro has
The palm of product colour may be implemented by the temperature in control cellar on the basis of not adding any chemical industry pigment for natural colour
Control.
Therefore, in conjunction with the above problem, the raw material for providing a kind of environmentally friendly boccaro inner-outer wall are that those skilled in the art need
It solves the problems, such as.
Summary of the invention
In view of this, the present invention provides a kind of raw material of environmentally friendly boccaro inner-outer wall, this method simple possible is not adding
Add in the temperature stored on the basis of any chemical industry pigment by natural colour and control and grasps product colour.
To achieve the goals above, the present invention adopts the following technical scheme:
A kind of raw material of environmental protection boccaro inner-outer wall, according to parts by weight, including following components: boccaro 40-55 parts of calcining,
10-30 parts of deionized water, 0.1-0.2 parts of hydroxyethyl cellulose, 0.5-0.8 parts of dispersing agent, 0.1-0.2 parts of wetting agent, defoaming agent
0.3-0.4 parts, 2-3 parts of propylene glycol, 2-3 parts of coalescing agent, 30-35 parts of acrylic emulsion, 0.5-0.7 parts of thickener.
Preferably, it is raw material that the calcining boccaro, which selects boccaro raw ore,.
Preferably, the ingredient of the calcining boccaro is SiO2、AI2O3、Fe2O3、CaO、MgO。
Preferably, the hydroxyethyl cellulose is Aksu hydroxyethyl cellulose 451.
Preferably, the dispersing agent is Nuo Puke dispersing agent 5040.
Preferably, the wetting agent is Nuo Puke wetting agent DX200.
Preferably, the defoaming agent is break Thailand defoaming agent 610.
Preferably, the coalescing agent is Yi Shiman coalescing agent.
Preferably, the acrylic emulsion is SHIN-ETSU HANTOTAI's ordor removing lotion.
Preferably, the thickener is SHIN-ETSU HANTOTAI's ordor removing thickener.
A kind of preparation method of the raw material of environmental protection boccaro inner-outer wall, the specific steps are as follows:
S1, weighs boccaro raw ore, and broken, aging, sieving deviates from all liquid in material through cold stage, hot phase process
Body avoids powder particle from bonding, and the calcining boccaro powder of abundant mobility is made in sintering under 900-1350 DEG C of high temperature；
Deionized water is put into container by S2, opens dispersion machine, and setting revolving speed is 300-400r/min, is slowly added to hydroxyl
Revolving speed is adjusted to 800-1000r/min, disperses 5-10min, grain dissolution by ethyl cellulose；
S3 is slowly added to dispersing agent, wetting agent, defoaming agent, propylene glycol, coalescing agent, thickener, disperses 10min；
S4 is slowly added to calcine Red Stone Ware obtained by step S1, and setting revolving speed is that 1200r/min disperses 30-45min, surveys thin
Degree is 30 μm；
S5, reduction of speed to 500-600r/min are added surplus material, are uniformly dispersed, and adjust viscosity, obtain inside and outside environmentally friendly boccaro
The raw material finished product of wall.
As can be seen from the above technical solutions, compared with prior art, beneficial effects of the present invention are as follows:
The boccaro raw ore that the present invention selects originates in dyas and Cambrian strata, the predominantly middle Carboniferous System and two of raw material
Repeatedly it is stratum and upper Jurassic system and Quaternary Strata Red Stone Ware mine, natural colour is relied on the basis of not adding any chemical industry pigment
Product colour is grasped in color and control cellar temperature, filtering out the different demands mesh numbers such as 40 mesh to 400 mesh is material, Jing Lengjie
Duan Yure phase process deviates from all liq in material, powder particle is avoided to bond, and abundant mobility is made in sintering under high temperature
Calcining boccaro powder.Raw material are according to different use needs, and sintering (900 degree to 1350 degree) makes particle at high temperature for selection
Sufficient mobility powder occurs.Purple soil coating material prepared by the present invention is led in building and the natural boccaro wall material of household inner, external wall
Domain has development prospect.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1:
The embodiment of the present invention 1 discloses a kind of raw material of environmentally friendly boccaro inner-outer wall, the technical solution adopted is as follows:
A kind of raw material of environmental protection boccaro inner-outer wall, according to parts by weight, including following components:
Calcining boccaro is 40 parts, deionized water is 24 parts, Aksu hydroxyethyl cellulose 451 is 0.1 part, Nuo Puke dispersion
Agent 5040 is 0.8 part, Nuo Puke wetting agent DX200 is 0.2 part, break Thailand defoaming agent 610 is 0.4 part, propylene glycol is 2 parts, her scholar
Graceful coalescing agent is 2 parts, SHIN-ETSU HANTOTAI's ordor removing lotion is 30 parts, SHIN-ETSU HANTOTAI's ordor removing thickener is 0.5 part.
Embodiment 2:
The embodiment of the present invention 2 discloses a kind of raw material of environmentally friendly boccaro inner-outer wall, the technical solution adopted is as follows:
A kind of raw material of environmental protection boccaro inner-outer wall, according to parts by weight, including following components:
Calcining boccaro is 47 parts, deionized water is 10 parts, Aksu hydroxyethyl cellulose 451 is 0.2 part, Nuo Puke dispersion
Agent 5040 is 0.7 part, Nuo Puke wetting agent DX200 is 0.1 part, break Thailand defoaming agent 610 is 0.3 part, propylene glycol is 3 parts, her scholar
Graceful coalescing agent is 3 parts, SHIN-ETSU HANTOTAI's ordor removing lotion is 35 parts, SHIN-ETSU HANTOTAI's ordor removing thickener is 0.7 part.
Embodiment 3:
The embodiment of the present invention 3 discloses a kind of raw material of environmentally friendly boccaro inner-outer wall, the technical solution adopted is as follows:
A kind of raw material of environmental protection boccaro inner-outer wall, according to parts by weight, including following components:
Calcining boccaro is 41 parts, deionized water is 21 parts, Aksu hydroxyethyl cellulose 451 is 0.2 part, Nuo Puke dispersion
Agent 5040 is 0.5 part, Nuo Puke wetting agent DX200 is 0.2 part, break Thailand defoaming agent 610 is 0.4 part, propylene glycol is 3 parts, her scholar
Graceful coalescing agent is 3 parts, SHIN-ETSU HANTOTAI's ordor removing lotion is 30 parts, SHIN-ETSU HANTOTAI's ordor removing thickener is 0.7 part.
Each embodiment in this specification is described in a progressive manner, the highlights of each of the examples are with other
The difference of embodiment, the same or similar parts in each embodiment may refer to each other.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (10)
1. a kind of raw material of environmental protection boccaro inner-outer wall, which is characterized in that according to parts by weight, including following components: calcining is purple
40-55 parts of sand, 10-30 parts of deionized water, 0.1-0.2 parts of hydroxyethyl cellulose, 0.5-0.8 parts of dispersing agent, wetting agent 0.1-0.2
Part, 0.3-0.4 parts of defoaming agent, 2-3 parts of propylene glycol, 2-3 parts of coalescing agent, 30-35 parts of acrylic emulsion, thickener 0.5-0.7
Part.
2. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the calcining boccaro
Ingredient is SiO2、AI2O3、Fe2O3、CaO、MgO。
3. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the hydroxy ethyl fiber
Element is Aksu hydroxyethyl cellulose 451.
4. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the dispersing agent is promise
General section's dispersing agent 5040.
5. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the wetting agent is promise
General section's wetting agent DX200.
6. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the defoaming agent is break
Safe defoaming agent 610.
7. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the coalescing agent is
Yi Shiman coalescing agent.
8. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the acrylic emulsion
For SHIN-ETSU HANTOTAI's ordor removing lotion.
9. a kind of raw material of environmentally friendly boccaro inner-outer wall according to claim 1, which is characterized in that the thickener is letter
More ordor removing thickener.
10. a kind of preparation method of the raw material of environmental protection boccaro inner-outer wall, which is characterized in that specific step is as follows:
S1, weighs boccaro raw ore, broken, aging, sieving, through cold stage, hot phase process, deviate from all liq in material,
Powder particle is avoided to bond, the calcining boccaro powder of abundant mobility is made in sintering under 900-1350 DEG C of high temperature；
Deionized water is put into container by S2, opens dispersion machine, and setting revolving speed is 300-400r/min, is slowly added to ethoxy
Revolving speed is adjusted to 800-1000r/min, disperses 5-10min, grain dissolution by cellulose；
S3 is slowly added to dispersing agent, wetting agent, defoaming agent, propylene glycol, coalescing agent, thickener, disperses 10min；
S4 is slowly added to calcine Red Stone Ware obtained by step S1, and setting revolving speed is that 1200r/min disperses 30-45min, surveys fineness and is
30μm；
S5, reduction of speed to 500-600r/min are added surplus material, are uniformly dispersed, and adjust viscosity, obtain environmentally friendly boccaro inner-outer wall
Raw material finished product.