CN110196357A - A kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method - Google Patents
A kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method Download PDFInfo
- Publication number
- CN110196357A CN110196357A CN201910531137.2A CN201910531137A CN110196357A CN 110196357 A CN110196357 A CN 110196357A CN 201910531137 A CN201910531137 A CN 201910531137A CN 110196357 A CN110196357 A CN 110196357A
- Authority
- CN
- China
- Prior art keywords
- sample
- electrode foil
- tested
- single side
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electrode foil for aluminum electrolytic capacitors single side specific volume test methods, include the following steps: the sample that electrode foil to be measured is cut into effective area, if etched foil, first carry out static pre- chemical conversion, clean after voltage-withstand test and dry sample;Using having the substance of solidification filling sealing function to seal the side corrosion holes filling of electrode foil, filling one guarantees good leakproofness to twice.The present invention can be very good characterization specific volume of electrode foil amount, intuitive to reflect electrode foil performance indicator.
Description
Technical field
The present invention relates to the surveys of the performance of a kind of test of specific volume of electrode foil in use for aluminium electrolytic capacitor, especially electrode foil single side
Method for testing.
Background technique
Electrode foil is the key raw material of aluminium electrolutic capacitor manufacture, and the quality of electrode foil will directly influence aluminium electricity
The quality of electrolysis condenser.The performance of the core material electrode foil of aluminium electrolutic capacitor mainly uses electrical property, physical property, chemistry
Performance is measured, and wherein electrical property can be described with parameters such as specific capacity, oxidation film pressure resistance, oxidation film pressure resistance pressure-resistant times,
Specific capacity parameter is to describe the important indicator of electrode foil properties of oxide-film.Electrode foil for aluminum electrolytic capacitors is by up of three-layer, just
Face and reverse side corrosion layer, intermediate residual sandwich layer, positive and negative corrosion layer have porous structure, to increase its specific surface area, but because raw material,
The factors such as manufacturing process influence, and the microstructures such as positive and negative corrosion layer aperture, hole density are different, show macro property upper body
Now for specific volume, the sample after pressure resistance is immersed the ammonium pentaborate test fluid centainly matched by difference, traditional specific volume test method
In, fail to show specific specific volume front and back.
Summary of the invention
It is an object of the invention to overcome disadvantages described above, a kind of electrode foil for aluminum electrolytic capacitors single side specific volume test is provided
Method improves the validity of electrode foil assessment.
The purpose of the present invention is achieved through the following technical solutions:
A kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method, the specific steps are as follows:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm size;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one or two layers with solidification filling
The substance of sealing function, and keep to drying regime;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
A further improvement of the present invention is that: the substance with solidification filling sealing function in step D is acrylic acid tree
Rouge, alkyd resin, epoxy resin, liquid glue, adhesive tape or transparent nail polish.
Compared with the prior art, the present invention has the following advantages:
Because the microstructures such as positive and negative corrosion layer aperture, hole density are different, show and be presented as on macro property than having
Institute's difference, traditional specific volume test method fail to show specific specific volume front and back.The present invention can be very good characterization electrode
Foil single side specific capacity, it is intuitive to reflect electrode foil performance indicator, and operation is simple.Know electrode foil single side specific capacity, for
Process management and control, equipment Design in production can provide strong foundation.
Specific embodiment:
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be to the skill in the embodiment of the present invention
Art scheme is clearly and completely described, it is clear that and described embodiments are some of the embodiments of the present invention, rather than all
Embodiment.The elements and features described in one embodiment of the invention can be with one or more other embodiment party
Elements and features shown in formula combine.It should be noted that being omitted for purposes of clarity, in explanation unrelated to the invention
, the expression and description of component known to persons of ordinary skill in the art and processing.Based on the embodiments of the present invention, this field
Those of ordinary skill's every other embodiment obtained under the premise of not making the creative labor, belongs to guarantor of the present invention
The range of shield.
A kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method, which includes the following steps: will be to
Survey electrode foil and cut into effective area (50 ± 0.25) mm*(10 ± 0.05) sample of mm.Etched foil in this way, according to National Electrical
Professional standard SJ/T11140-2012 first carries out static pre- chemical conversion, cleans after voltage-withstand test and dries sample;Use acrylic acid tree
Rouge, alkyd resin or the substance with solidification filling sealing function guarantee the side corrosion holes filling sealing of electrode foil good
Good leakproofness.The test method can be very good characterization electrode foil single side specific capacity, intuitive to reflect electrode foil performance indicator.
Embodiment 1:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one layer of colorless and transparent nail polish, and protected
It holds to drying regime, is coated with upper one layer of nail polish, and keep to drying regime;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Embodiment 2:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one layer of epoxy resin, and is kept to dry
Dry state;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Embodiment 3:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one layer of liquid glue, and is kept to drying
State;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Embodiment 4:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with layer of transparent adhesive plaster;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Embodiment 5:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one layer of acrylic resin, and kept
To drying regime;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Embodiment 6:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one layer of alkyd resin, and is kept extremely
Drying regime;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
Finally, it should be noted that although the present invention and its advantage have been described in detail above it should be appreciated that not
Can be carried out in the case where beyond the spirit and scope of the present invention being defined by the claims appended hereto various changes, substitution and
Transformation.Moreover, the scope of the present invention is not limited only to the specific reality of process, equipment described in specification, means, method and steps
Apply example.One of ordinary skilled in the art holds from the disclosure it will be readily understood that can be used according to the present invention
The row function essentially identical to corresponding embodiment described herein obtains the result essentially identical with it, existing and future
Process, equipment, means, method or step to be developed.Therefore, the attached claims are intended to wrap in the range of them
Include such process, equipment, means, method or step.
Claims (2)
1. a kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method, it is characterised in that: specific step is as follows:
A, sample to be tested is cut into (50 ± 0.25) mm*(10 ± 0.05) mm size;
B, voltage-withstand test is carried out in the boric acid test fluid of 70g/L, pressure stabilizing 3 minutes;
C, after the sample after voltage-withstand test being cleaned with ultrapure water, 100 DEG C oven 3 minutes;
D, sample to be tested is taken out, after placing room temperature, is integrally applied at the sample to be tested back side and is covered with one or two layers with solidification filling
The substance of sealing function, and keep to drying regime;
E, sample is put into the ammonium pentaborate test fluid of 80g/L and carries out volume test, gained capacity is sample to be tested single side appearance
Amount.
2. a kind of electrode foil for aluminum electrolytic capacitors single side specific volume test method according to claim 1, it is characterised in that: institute
State in step D have solidification filling sealing function substance be acrylic resin, alkyd resin, epoxy resin, liquid glue, thoroughly
Gelatin band or transparent nail polish.