CN110195501A - A kind of wall multi-function decoration board and preparation method thereof - Google Patents
A kind of wall multi-function decoration board and preparation method thereof Download PDFInfo
- Publication number
- CN110195501A CN110195501A CN201910320289.8A CN201910320289A CN110195501A CN 110195501 A CN110195501 A CN 110195501A CN 201910320289 A CN201910320289 A CN 201910320289A CN 110195501 A CN110195501 A CN 110195501A
- Authority
- CN
- China
- Prior art keywords
- layer
- decoration board
- wall
- function decoration
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of wall multi-function decoration boards and preparation method thereof, the wall multi-function decoration board includes that multi-functional surface layer, basal layer, grid enhancement layer and anchor point reinforce enhancing point, the multi-functional surface layer is compound on the basal layer, the grid enhancement layer is preset between the multi-functional surface layer and the basal layer, the anchor point reinforces enhancing point and is distributed in the basic layer surface, and is embedded at grid enhancement layer bottom.The wall multifunctional veneer plate prepared using the method for the present invention, integrate waterproof, heat preservation, it is heat-insulated, mould proof, sterilization, except aldehyde, release anion, with the advantages such as clean surfaces, weather-proof, fire-retardant, cracking resistance, once tough, and there are the advantages such as structure is simple, construction is convenient, safe and environment-friendly, assembled architecture requirement is met, lithotome perfect can be substituted and cost is far below lithotome.
Description
Technical field
The present invention relates to building decoration area more particularly to a kind of external wall and interior wall wet combinings, the more function of dry hanging wall
Energy decorative panel and preparation method thereof.
Background technique
The country is very few for the research of wall decorative material fast-assembling, and Chinese utility model patent CN 208152440U is disclosed
The inorganic imitative stone decorative layered structure of exterior wall, the inorganic imitative stone decorative of exterior wall includes decorative layer and base, and the base sets
In the decorative layer bottom, the base is the one of which of asbestos-free calcium silicate board, cement fibre pressure plate, the decorative layer
Including cement, inorganic oxide iron pigment, color sand and mortar performance additive, the cement, inorganic oxide iron pigment, color sand and sand
Slurry performance additive is to be mutually mixed structure.This plate only proposes finish coat, base's layered structure, for structural reinforcement,
Anchor point is reinforced enhancing point and is not yet referred to, for finish coat waterproof, heat preservation, heat-insulated does not refer to.
Summary of the invention
The present invention for being currently related to the deficiency of decorative plate of outer wall content, provide a kind of wall multi-function decoration board and its
Preparation method, can effectively make up above-mentioned decorative plate of outer wall there are the problem of.
To achieve the above object, the invention adopts the following technical scheme:
The first aspect of the invention is to provide a kind of wall multi-function decoration board, including multi-functional surface layer, basal layer,
Grid enhancement layer and anchor point reinforce enhancing point, and the multi-functional surface layer is compound on the basal layer, and the grid enhancement layer is pre-
It being placed between the multi-functional surface layer and the basal layer, the anchor point reinforces enhancing point and is distributed in the basic layer surface, and
It is embedded at grid enhancement layer bottom.
Further, on the wall multi-function decoration board, the multi-functional surface layer is with hydraulicity gel rubber material
Or polymer is main component, complex mineral gathers materials, functional stuffing, inorganic pigment and multifunctional assistant, by spraying, polishing,
The techniques such as water mill, ball blast are prepared, and reach the expression effect of all kinds of lithotomes, collection waterproof, heat preservation, it is heat-insulated, mould proof, kill
Bacterium, except aldehyde, release anion be integrated, have the advantages such as clean surfaces, weather-proof, fire-retardant, cracking resistance, once tough.
Further, on the wall multi-function decoration board, the hydraulicity gel rubber material is selected from cement, stone
One or more of cream, calcium hydroxide, waterglass；The polymer is selected from oiliness, water-based acrylic resin, modified acroleic acid
One or more of resin, epoxy resin, ethylene-vinyl acetate copolymer, styrene-butadiene copolymer, polyurethane, institute
It states mineral aggregate and is selected from the dusty materials and river sand, quartz sand, natural colour sand, sand burning etc. such as calcium powder, silica flour, kaolin carefully collection
One of material is a variety of；The inorganic pigment is in iron oxide, chromium oxide, titanium dioxide, hydrocarbon black powder and liquid color paste
One or more；The auxiliary agent be selected from polycarboxylate water-reducer, melamine water reducing agent, how based water reducer, hydroxypropyl cellulose,
Hydroxyethyl cellulose, lithium magnesium silicate, modified acroleic acid wetting agent, modified polyurethane dispersant, lithium metasilicate, calcium formate, tartaric acid
One of auxiliary agents such as sodium, sodium citrate, organic silicon defoamer, polyether antifoam agent are a variety of.
It is further preferred that the functional stuffing includes that insulation is filled out on the wall multi-function decoration board
Material, antisepsis and sterilization filler, except aldehyde powder, anion releasing agent and super-hydrophobic dose.
Further more, on the wall multi-function decoration board, the insulation filler is selected from hollow glass
One or more of glass microballon, glass bead, foamed ceramic particle, glue powder polyphenyl particle；The protection sterilization filler is selected from
One or more of hypochlorous acid class, organic sulfur, organic bromine, heterocyclic compound；It is described except aldehyde powder be selected from nano-titanium dioxide,
One or more of modified nano-titanium dioxide；The anion releasing agent include one of calcium carbide, calcium hydroxide or
It is several；Described super-hydrophobic dose selected from silane, polysiloxanes, the powder of silicon fluoride development, waterborne liquid, solvent based liquid addition
One or more of agent.
Further, on the wall multi-function decoration board, the basis is inorganic silicon scutum, modification is siliceous
One of plate, polymer flexibility plate.
It is further preferred that on the wall multi-function decoration board, described to have inorganic siliceous plate be with the hydraulicity
Gel rubber material, air-setting gel rubber material be main component, by be added all kinds of mineral aggregates for example calcium powder, flyash, anti-crack fiber,
Fiber dust, the inorganic silicon lumber formed by pressing process, casting craft；The modified silicon scutum is solidifying with the hydraulicity
Glue material, air-setting gel rubber material compound organic polymer such as acrylic resin, epoxy resin, polyurethane, ethene-vinyl acetate
Copolymer, styrene-butadiene copolymer are main component, by the way that all kinds of mineral aggregates such as calcium powder, flyash, cracking resistance fibre is added
Dimension, fiber dust, the modified silicon lumber formed by pressing process, casting craft；The polymer flexibility plate be with oiliness,
Water-based acrylic resin, acrylic resin modified, epoxy resin, ethylene-vinyl acetate copolymer, styrene butadiene copolymers
Object, polyurethane are that main component is passed through by the way that all kinds of mineral aggregate such as calcium powder, flyash, anti-crack fiber, fiber dusts are added
The polymer flexibility plate that pressing process, casting craft are formed.
Further, on the wall multi-function decoration board, the grid cloth is fiberglass gridding cloth, carbon fiber
Tie up the combination of one or more of grid cloth, polypropylene mesh cloth, polyvinyl alcohol grid cloth and Teflon fibrous mesh cloth.
Further, on the wall multi-function decoration board, the multi-functional surface layer with a thickness of 0.1-
30mm, the basal layer with a thickness of 0.1-30mm.
Further, on the wall multi-function decoration board, the anchor point is reinforced the enhancing point anchor point and is reinforced
The progress of one or more of the optional perforated metal steel disc of enhancing point, metal grill, wire is pre-buried, can also be in base layer side
Side fluting, is anchored by external anchoring piece, and being formed has the reinforcing enhancing point that prevents from sliding, fall off.
The second aspect of the invention is to provide the preparation method of wall multi-function decoration board described in one kind, including such as
Lower step (step S1, step S2 can be exchanged):
Basic laminate is placed on platform by step S1；
Step S2 reinforces enhancing point in basic lamina surface setting anchor point；
Step S3 places enhancing grid cloth；
Step S4 stirs multi-functional surface layer slurry；
Step S5 pours multi-functional surface layer slurry, strikes off, conserves to Surface hardened layer；
Step S6 passes through blasting craft, polishing process, ball blast technique processing or directly use, the more function of wall of formation
It can facing feature of the decorative panel with lithotome surface effect.
The present invention by adopting the above technical scheme, has the following technical effect that
1) the raw wall multi-function decoration board of the present invention is formed by multi-functional surface layer to basal layer in factory, simple process,
Structure safety and stability has reached the performance requirements such as lithotome expression effect, product strength, weather resistance be excellent；
2) the multi-functional surface layer of wall multi-function decoration board integrate waterproof, heat preservation, it is heat-insulated, decoration, have it is weather-proof,
The advantages such as fire-retardant, cracking resistance, once tough；Mass area ratio is quick and easy for installation no more than 20 kilograms；
3) by anchor point enhancing technique, meet decorated architectural development requirement, installation is safe and efficient, can effectively avoid plate
It slides, fall off in material installation process；
4) wall multi-function decoration board is prepared convenient, and molding is simple, can effectively push construction wall ornament materials city
Field Advantageous developments.
Detailed description of the invention
Fig. 1 is a kind of schematic cross-sectional view of wall multi-function decoration board of the present invention；
Fig. 2 is a kind of process flow chart of the preparation method of wall multi-function decoration board of the present invention；
Wherein, each appended drawing reference are as follows:
The multi-functional surface layer of 1-；2- basal layer；3- grid enhancement layer；4- anchor point reinforces enhancing point.
Specific embodiment
The present invention is described in more detail below by specific embodiment, for a better understanding of the present invention,
But following embodiments are not intended to limit the scope of the invention.
As shown in Figure 1, the present embodiment provides a kind of wall multi-function decoration board, including multi-functional surface layer 1, basal layer 2,
Grid enhancement layer 3 and anchor point reinforce enhancing point 4；The multi-functional surface layer 1 is compound on the basal layer 2, the grid enhancing
Layer 3 is preset between the multi-functional surface layer 1 and the basal layer 2；The anchor point reinforces enhancing point 4 and is distributed in the basal layer
It 5 surfaces and is covered by multi-functional surface layer 1, grid enhancement layer 3, and anchor point reinforces enhancing point 4 and is embedded at the grid enhancement layer
3 bottom.
As a preferred embodiment, the multi-functional surface layer 1 using hydraulicity gel rubber material or polymer as main component,
Complex mineral gathers materials, functional stuffing, inorganic pigment and multifunctional assistant, passes through the techniques such as spraying, polishing, water mill, ball blast and prepares
It forms, reaches the expression effect of all kinds of lithotomes, integrate waterproof, heat preservation, heat-insulated, decoration, have weather-proof, fire-retardant, anti-
The advantages such as split, be once tough.
In the present embodiment, the hydraulicity gel rubber material is selected from one of cement, gypsum, calcium hydroxide, waterglass
Or it is several；The polymer is selected from oiliness, water-based acrylic resin, acrylic resin modified, epoxy resin, ethyl vinyl acetate second
One or more of alkene copolymer, styrene-butadiene copolymer, polyurethane, the mineral aggregate are selected from calcium powder, quartz
One of fine aggregates such as the dusty materials such as powder, kaolin and river sand, quartz sand, natural colour sand, sand burning are a variety of；The face
Material is selected from one or more of iron oxide, chromium oxide, titanium dioxide, hydrocarbon black powder and liquid color paste；The auxiliary agent is selected from poly-
Carboxylic acid water reducer, melamine water reducing agent, how based water reducer, hydroxypropyl cellulose, hydroxyethyl cellulose, lithium magnesium silicate, modification
Acrylic acid wetting agent, lithium metasilicate, calcium formate, sodium tartrate, sodium citrate, organic silicon defoamer, gathers modified polyurethane dispersant
One of auxiliary agents such as ether defoaming agent or multiple combinations use.
As a preferred embodiment, the functional stuffing includes insulation filler, antisepsis and sterilization filler, except aldehyde powder
End, anion releasing agent and super-hydrophobic dose.Specifically, the insulation filler is selected from hollow glass micropearl, glass bead, hair
Steep one or more of ceramic particle, glue powder polyphenyl particle；The protection sterilization filler is selected from hypochlorous acid class, organic sulfur, has
One or more of machine bromine, heterocyclic compound；The aldehyde powder that removes is in nano-titanium dioxide, modified nano-titanium dioxide
One or more；The anion releasing agent is selected from one or more of calcium carbide, calcium hydroxide；Super-hydrophobic dose include with
The combination of one or more of silane, polysiloxanes, the powder of silicon fluoride development, waterborne liquid, solvent based liquid additive makes
With.
As a preferred embodiment, the optional inorganic silicon scutum of the basal layer 2, modified silicon scutum, polymer flexibility plate
One of.In the present embodiment, the inorganic silicon scutum be with hydraulicity gel rubber material, air-setting gel rubber material be mainly at
Divide, by the way that all kinds of mineral aggregate such as calcium powder, flyash, anti-crack fiber, fiber dusts are added, passes through pressing process, casting craft
The inorganic silicon lumber of formation；The modified silicon scutum is organic with hydraulicity gel rubber material, air-setting gel rubber material compounding
Polymer such as acrylic resin, epoxy resin, polyurethane, ethylene-vinyl acetate copolymer, styrene-butadiene copolymer are
Main component passes through addition all kinds of mineral aggregate such as calcium powder, flyash, anti-crack fiber, fiber dusts, by pressing process, pours
The modified silicon lumber that building technology is formed；The polymer flexibility plate is with oiliness, water-based acrylic resin, modified acroleic acid tree
Rouge, epoxy resin, ethylene-vinyl acetate copolymer, styrene-butadiene copolymer, polyurethane are main component, pass through addition
All kinds of mineral aggregates such as calcium powder, flyash, anti-crack fiber, fiber dust, the polymer formed by pressing process, casting craft
Flexible board.
By adopting the above technical scheme, by selecting different basal layers, it is ensured that multi-function decoration board meets flexible, toughness,
Meet the demands such as outdoor wall, indoor intensity, meets the design requirement and cost requirement of various schemes.
As another preferred embodiment, the grid enhancement layer 3 using fiberglass gridding cloth, carbon fiber mesh fabric,
The combination of one or more of polypropylene mesh cloth, polyvinyl alcohol grid cloth or Teflon fibrous mesh cloth.Using above-mentioned skill
The anti-of multi-function decoration board can be improved by the way that grid enhancement layer is arranged between multifunctional veneer layer and basal layer in art scheme
It splits, peel off, can make that multi-function decoration board stable structure, intensity are high, alkaline resistance properties is good, anti-corrosion, cracking resistance, make multi-function decoration board
The stress being subject to is evenly dispersed, and the impact of external force or extruding is avoided to lead to malformation.
In the installation process of the wall multi-function decoration board, anchor point is selected to reinforce enhancing point, improves product construction peace
Convenience is filled, prevents product sliding, falling off increases product installation and the safety of use process.The anchor point reinforces enhancing point 4
It is pre-buried using the progress of one or more of perforated metal steel disc, metal grill, wire, or opened in the basal layer side
Slot is anchored by external anchoring piece, and being formed has the reinforcing enhancing point that prevents from sliding, fall off.
As another preferred embodiment, as shown in Fig. 2, also providing a kind of preparation method of wall multi-function decoration board
(step S1, step S2 can be exchanged), has and includes the following steps:
Basic laminate is placed on platform by step S1；
Step S2 reinforces enhancing point in basic lamina surface setting anchor point；
Step S3 places enhancing grid cloth；
Step S4 stirs multi-functional surface layer slurry；
Step S5 pours multi-functional surface layer slurry, strikes off, conserves to Surface hardened layer；
Step S6, by blasting craft, polishing process, ball blast technique processing or directly use, the wall of shape is with multi-functional
Decorative panel is at the facing feature with lithotome surface effect.
In order to verify the preparation method of wall multi-function decoration board, inventor has carried out following pilot production:
Pilot production 1:
Step S1, the inorganic silicon scutum that standard specification is 1200mm*1200mm*10mm is placed on levelling bench；
Step S2, it uses polyurethane adhesive to paste punching steel disc as anchor point in inorganic silicon scutum specific position and reinforces enhancing point；
Step S3, paving alkali-proof glass fiber mesh；
Step S4, mix cement base Multifunctional sizing agent；
Step S5, cement base Multifunctional sizing agent is scraped on grid cloth surface batch, strikes off, conserves to Surface hardened layer；
Step S6, using ball blast technique, the wall multi-function decoration board of natural gold fiber crops effect is formed.
Pilot production 2:
Step S1, metal is pasted in the modified silicon scutum specific position that specification is 600mm*900mm*8mm with epoxy glue glue
Net reinforces enhancing point as anchor point；
Step S2, modified silicon scutum is placed on levelling bench；
Step S3, the paving grid cloth of resistance to pp；
Step S4, waterglass base Multifunctional sizing agent is stirred；
Step S5, waterglass base mortar is scraped on grid cloth surface batch, strikes off, conserves to Surface hardened layer；
Step S6, using technique for grinding, the wall multi-function decoration board of natural English Brown effect is formed.
Pilot production 3:
Step S1, the flexible silicon scutum that standard specification is 600mm*1200mm*4mm is placed on levelling bench；
Step S2, it uses polyurethane adhesive to paste wire as anchor point in flexible silicon scutum specific position and reinforces enhancing point；
Step S3, the paving grid cloth of resistance to Teflon；
Step S4, polymer Multifunctional sizing agent is stirred；
Step S5, polymer Multifunctional sizing agent is scraped on grid cloth surface batch, strikes off, conserves to Surface hardened layer；
Step S6, the wall multi-function decoration board of natural hemp effect is formed.
Pilot production 4:
Step S1, the modified silicon scutum that standard specification is 1200mm*200mm*6mm is placed on levelling bench；
Step S2,100mm*50mm*3mm notch is outputed in modified silicon scutum side；
Step S3, paving polyvinyl alcohol grid cloth；
Step S4, gypsum base Multifunctional sizing agent is stirred；
Step S5, gypsum base Multifunctional sizing agent is scraped on grid cloth surface batch, strikes off, conserves to Surface hardened layer；
Step S6, the wall multi-function decoration board of natural sandstone effect is formed.
By above-mentioned 4 pilot productions, the good wall multi-function decoration board of surface effect, testing result can get
Meet product standard.Pilot production step is succinct, easy to operate, is convenient for large-scale serial production, is conducive to control and is produced into
This, changes environmental pollution caused by previous in-situ spraying, also reduces the exploitation of lithotome, easy to promote and utilize.
Specific embodiments of the present invention are described in detail above, but it is merely an example, the present invention is simultaneously unlimited
It is formed on particular embodiments described above.To those skilled in the art, any couple of present invention carries out equivalent modifications and
Substitution is also all among scope of the invention.Therefore, without departing from the spirit and scope of the invention made by equal transformation and
Modification, all should be contained within the scope of the invention.
Claims (11)
1. a kind of wall multi-function decoration board, which is characterized in that including multi-functional surface layer, basal layer, grid enhancement layer and anchor
Point reinforces enhancing point, and the multi-functional surface layer is compound on the basal layer, and the grid enhancement layer is preset in described multi-functional
Between surface layer and the basal layer；The anchor point reinforces enhancing point and is distributed in the basic layer surface.
2. wall multi-function decoration board according to claim 1, which is characterized in that the multi-functional surface layer is with the hydraulicity
Gel rubber material or polymer are main component, and complex mineral gathers materials, functional stuffing, inorganic pigment and multifunctional assistant form.
3. wall multi-function decoration board according to claim 2, which is characterized in that the hydraulicity gel rubber material is selected from
One or more of cement, gypsum, calcium hydroxide, waterglass；The polymer is selected from oiliness, water-based acrylic resin, changes
One of property acrylic resin, epoxy resin, ethylene-vinyl acetate copolymer, styrene-butadiene copolymer, polyurethane
Or it is several；The mineral aggregate is selected from dusty materials and river sand, quartz sand, natural colour sand, the burnings such as calcium powder, silica flour, kaolin
Tie one of sand or a variety of；The inorganic pigment is selected from iron oxide, chromium oxide, titanium dioxide, hydrocarbon black powder and liquid color paste
One or more of；The multifunctional assistant be selected from polycarboxylate water-reducer, melamine water reducing agent, how based water reducer, hydroxypropyl
Base cellulose, hydroxyethyl cellulose, lithium magnesium silicate, modified acroleic acid wetting agent, modified polyurethane dispersant, lithium metasilicate, formic acid
One of calcium, sodium tartrate, sodium citrate, organic silicon defoamer, polyether antifoam agent are a variety of.
4. wall multi-function decoration board according to claim 2, which is characterized in that the functional stuffing includes thermal insulation separation
Hot filler, antisepsis and sterilization filler, except aldehyde powder, anion releasing agent and super-hydrophobic dose.
5. wall multi-function decoration board according to claim 4, which is characterized in that the insulation filler is selected from sky
One or more of heart glass microballoon, glass bead, foamed ceramic particle, glue powder polyphenyl particle；Filler is sterilized in the protection
Selected from one or more of hypochlorous acid class, organic sulfur, organic bromine, heterocyclic compound；The aldehyde powder that removes is selected from nano-silica
Change one or more of titanium, modified nano-titanium dioxide；The anion releasing agent in calcium carbide, calcium hydroxide one
Kind is several；Described super-hydrophobic dose selected from silane, polysiloxanes, the powder of silicon fluoride development, waterborne liquid, solvent based liquid
One or more of additive.
6. wall multi-function decoration board according to claim 1, which is characterized in that the basal layer is inorganic siliceous
One of plate, modified silicon scutum, polymer flexibility plate.
7. wall multi-function decoration board according to claim 6, which is characterized in that the inorganic silicon scutum is with hydraulic
Property gel rubber material, air-setting gel rubber material be main component, it is fine by the way that all kinds of mineral aggregates such as calcium powder, flyash, cracking resistance is added
Dimension, fiber dust, the inorganic silicon lumber formed by pressing process, casting craft；The modified silicon scutum is with the hydraulicity
Gel rubber material, air-setting gel rubber material compound organic polymer such as acrylic resin, epoxy resin, polyurethane, ethyl vinyl acetate second
Alkene copolymer, styrene-butadiene copolymer are main component, by the way that all kinds of mineral aggregate such as calcium powder, flyash, cracking resistances are added
Fiber, fiber dust, the modified silicon lumber formed by pressing process, casting craft；The polymer flexibility plate is with oil
Property, water-based acrylic resin, acrylic resin modified, epoxy resin, ethylene-vinyl acetate copolymer, styrene-butadiene are total
Polymers, polyurethane are main component, by the way that all kinds of mineral aggregate such as calcium powder, flyash, anti-crack fiber, fiber dusts are added, are led to
Cross pressing process, casting craft formed change polymer flexibility plate.
8. wall multi-function decoration board according to claim 1, which is characterized in that the grid enhancement layer is glass fibers
Tie up one of grid cloth, carbon fiber mesh fabric, polypropylene mesh cloth, polyvinyl alcohol grid cloth and Teflon fibrous mesh cloth or
Several combinations.
9. wall multi-function decoration board according to claim 1, which is characterized in that the multi-functional surface layer with a thickness of
0.1-30mm, the basal layer with a thickness of 0.1-30mm.
10. wall multi-function decoration board according to claim 1, which is characterized in that the anchor point is reinforced enhancing point and adopted
Carried out with one or more of perforated metal steel disc, metal grill, wire it is pre-buried, or the basal layer side slot,
It is anchored by external anchoring piece, being formed has the reinforcing enhancing point that prevents from sliding, fall off.
11. a kind of preparation method of wall multi-function decoration board, which is characterized in that include the following steps (step S1, step S2
Can exchange):
Basic laminate is placed on platform by step S1；
Step S2 reinforces enhancing point in basic lamina surface setting anchor point；
Step S3 places enhancing grid cloth；
Step S4 stirs multi-functional surface layer slurry；
Step S5 pours multi-functional surface layer slurry, strikes off, conserves to Surface hardened layer；
Step S6 passes through blasting craft, polishing process, ball blast technique processing or directly use, the wall multifunctional assembling of formation
Plaque has the facing feature of lithotome surface effect.