A kind of production method of high-purity high rigidity gold Download PDFInfo
- Publication number
- CN110179226A CN110179226A CN201910301934.1A CN201910301934A CN110179226A CN 110179226 A CN110179226 A CN 110179226A CN 201910301934 A CN201910301934 A CN 201910301934A CN 110179226 A CN110179226 A CN 110179226A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- gold
- raw material
- production method
- crucible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of high-purity high rigidity gold, comprising the following steps: S1: raw material is chosen: gold raw material required for purchasing in regular shop；S2: raw material cleaning: gold raw material described in S1 is placed in service sink and is cleaned；S3: it air-dries processing: gold raw material described in S2 being placed on draughty place and carries out natural air drying；S4: molten gold: gold raw material air-dried described in S3 is placed in crucible, is burnt crucible using acetylene torch, is smelt the ingredient A of suitable processing ornaments.Present invention production is simple, not only gold can be made to reach mirror effect by polishing, also substantially increase the aesthetics of gold jewelry.
Description
Technical field
The present invention relates to Technology for Gold field more particularly to a kind of production methods of high-purity high rigidity gold.
Background technique
Gold jewelry refers to the jewellery made using gold as primary raw material, and in order to overcome, price of gold lattice are high, hardness is low, color list
One, some other metallic elements is added in proof gold usually to increase the hard of jewellery gold in the inexquisite disadvantage of easy to wear, decorative pattern
Degree converts its tone and reduces its fusing point, occurs as soon as different, the visibly different billon jewellery of gold content of quality height in this way.
Common gold jewelry, simple process do not promote the hardness of gold, but maintain the relatively soft characteristic of gold,
The partially soft vehicle mill that not can be carried out of gold jewelry quality is beaten, and surface can not generate mirror effect, to limit the beauty of gold jewelry
Property.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of production sides of high-purity high rigidity gold
Method.
A kind of production method of high-purity high rigidity gold proposed by the present invention, comprising the following steps:
S1: raw material is chosen: gold raw material required for purchasing in regular shop；
S2: raw material cleaning: gold raw material described in S1 is placed in service sink and is cleaned；
S3: it air-dries processing: gold raw material described in S2 being placed on draughty place and carries out natural air drying；
S4: molten gold: gold raw material air-dried described in S3 is placed in crucible, burns crucible, refining using acetylene torch
At the ingredient A of suitable processing ornaments；
S5: reverse mould: ingredient A described in S4 is poured into plaster mold using high frequency centrifugal casting machine and pours out workpiece B；
S6: it holds mould: workpiece B described in S5 is beaten, be trimmed to workpiece C；
S7: frosted: workpiece C described in S6 is placed on polishing table, using high frequency sand-blasting machine to the surface of workpiece C into
Row processing recycles dedusting rifle to be dusted cleaning to by polishing table to obtain workpiece D；
S8: vehicle mill is beaten: workpiece D described in S7 is placed on polishing table, is polished using polishing machine workpiece D,
Until stopping polishing and obtaining workpiece E, be dusted cleaning to by polishing table using dedusting rifle when workpiece surface generates gloss；
S9: press polish: workpiece E described in S8 is placed on polishing table, simultaneously using the surface agate pen slow contact workpiece E
Rub, until stop friction after workpiece E surface-brightening, to obtain workpiece F, finally using dedusting rifle to by polishing table into
Row dedusting cleaning；
S10: Che Hua: the machine that workpiece F described in S10 is equipped with diamond vehicle flower knife is made into pattern in workpiece surface
Batch high-grade Shaoxing wine carve, obtain finished product G.
Preferably, when the gold raw material in the S2 cleans in clear water reserviors, cleaning box, cleaning box are placed in service sink
Gold raw material is put into box and impregnates 10 minutes by the water for inside pouring into 40 DEG C, then is cleaned with hairbrush to gold raw material surface.
Preferably, the crucible in the S4 be silica crucible, acetylene torch burn crucible when, make silica crucible bottom uniformly by
Heat.
Preferably, when beating workpiece B in the S6, workpiece B is carried out repeating to beat using hammer, until finishing
At the shape of needs.
Preferably, the model wH1010 of the S7 medium-high frequency sand-blasting machine, the model SQ-12 of dedusting rifle.
Preferably, in the S8 polishing machine model GWS6-100E, need to guarantee that light is good in bruting process, with
It is illuminated if light is not sufficient enough using headlamp convenient for observation lustrous surface situation.
Preferably, when agate pen carries out mantle friction to workpiece E in the S9, it is desirable to provide sufficient illumination, if any need
It to be assisted rubbing to workpiece E using magnifying glass.
Preferably, finished product G is needed to be placed into packing box and is stored after completing in the S10.
Beneficial effects of the present invention: by being cleaned, being air-dried to gold raw material, molten gold gold hardness can be made to be mentioned
Rise, by reverse mould, hold mould, frosted, vehicle mill are beaten and the processing of press polish, the surface generation mirror effect of gold can be made, pass through vehicle
Gold can be carved by spending, and obtain more beautiful and light and handy gold product, and process is free of harmful substance；This hair
Bright production is simple, not only gold can be made to reach mirror effect by polishing, also substantially increase the aesthetics of gold jewelry.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment
A kind of production method of high-purity high rigidity gold is proposed in the present embodiment, comprising the following steps:
S1: raw material is chosen: gold raw material required for purchasing in regular shop；
S2: raw material cleaning: gold raw material described in S1 is placed in service sink and is cleaned；
S3: it air-dries processing: gold raw material described in S2 being placed on draughty place and carries out natural air drying；
S4: molten gold: gold raw material air-dried described in S3 is placed in crucible, burns crucible, refining using acetylene torch
At the ingredient A of suitable processing ornaments；
S5: reverse mould: ingredient A described in S4 is poured into plaster mold using high frequency centrifugal casting machine and pours out workpiece B；
S6: it holds mould: workpiece B described in S5 is beaten, be trimmed to workpiece C；
S7: frosted: workpiece C described in S6 is placed on polishing table, using high frequency sand-blasting machine to the surface of workpiece C into
Row processing recycles dedusting rifle to be dusted cleaning to by polishing table to obtain workpiece D；
S8: vehicle mill is beaten: workpiece D described in S7 is placed on polishing table, is polished using polishing machine workpiece D,
Until stopping polishing and obtaining workpiece E, be dusted cleaning to by polishing table using dedusting rifle when workpiece surface generates gloss；
S9: press polish: workpiece E described in S8 is placed on polishing table, simultaneously using the surface agate pen slow contact workpiece E
Rub, until stop friction after workpiece E surface-brightening, to obtain workpiece F, finally using dedusting rifle to by polishing table into
Row dedusting cleaning；
S10: Che Hua: the machine that workpiece F described in S9 is equipped with diamond vehicle flower knife is made into pattern in workpiece surface
Batch high-grade Shaoxing wine carve, obtain finished product G.
In the present embodiment, when the gold raw material in S2 cleans in clear water reserviors, cleaning box, cleaning box are placed in service sink
Gold raw material is put into box and impregnates 10 minutes by the water for inside pouring into 40 DEG C, then is cleaned with hairbrush to gold raw material surface,
Crucible in S4 is silica crucible, when acetylene torch burns crucible, makes silica crucible bottom thermally equivalent, carries out in S6 to workpiece B
When beating, workpiece B is carried out repeating to beat using hammer, until being trimmed to the shape of needs, the model of S7 medium-high frequency sand-blasting machine
For wH1010, the model GWS6-100E of polishing machine in the model SQ-12, S8 of dedusting rifle needs to guarantee light in bruting process
Line is good, in order to observe lustrous surface situation, if light is not sufficient enough, is illuminated using headlamp, agate pen in S9
When carrying out mantle friction to workpiece E if needed, it is desirable to provide sufficient illumination is assisted using magnifying glass to workpiece E
It rubs, finished product G is needed to be placed into packing box and be stored after completing in S11, clear by carrying out to gold raw material
Wash, air-dry, molten gold can make gold hardness get a promotion, by reverse mould, hold mould, frosted, vehicle mill is beaten and the processing of press polish, can be with
The surface of gold is set to generate mirror effect, gold can be carved by spending by vehicle, obtain more beautiful and light and handy gold
Product, and process is free of harmful substance；Present invention production is simple, not only gold can be made to reach mirror surface effect by polishing
Fruit also substantially increases the aesthetics of gold jewelry.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of production method of high-purity high rigidity gold, which comprises the following steps:
S1: raw material is chosen: gold raw material required for purchasing in regular shop；
S2: raw material cleaning: gold raw material described in S1 is placed in service sink and is cleaned；
S3: it air-dries processing: gold raw material described in S2 being placed on draughty place and carries out natural air drying；
S4: molten gold: gold raw material air-dried described in S3 is placed in crucible, is burnt crucible using acetylene torch, is smelt suitable
Close the ingredient A of processing ornaments；
S5: reverse mould: ingredient A described in S4 is poured into plaster mold using high frequency centrifugal casting machine and pours out workpiece B；
S6: it holds mould: workpiece B described in S5 is beaten, be trimmed to workpiece C；
S7: frosted: workpiece C described in S6 is placed on polishing table, using high frequency sand-blasting machine to the surface of workpiece C at
Reason recycles dedusting rifle to be dusted cleaning to by polishing table to obtain workpiece D；
S8: vehicle mill is beaten: workpiece D described in S7 is placed on polishing table, is polished using polishing machine workpiece D, until
When workpiece surface generates gloss, stops polishing and obtain workpiece E, be dusted cleaning to by polishing table using dedusting rifle；
S9: press polish: workpiece E described in S8 is placed on polishing table, using the agate pen surface slow contact workpiece E and is carried out
Friction, to obtain workpiece F, is finally removed using dedusting rifle to by polishing table until stopping friction after workpiece E surface-brightening
Dirt cleaning；
S11: Che Hua: the machine that workpiece F described in S9 is equipped with diamond vehicle flower knife is done into criticizing for pattern in workpiece surface
High-grade Shaoxing wine is carved, and finished product G is obtained.
2. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that in the S2
When gold raw material cleans in clear water reserviors, it is placed with cleaning box in service sink, 40 DEG C of water is poured into cleaning box, by gold raw material
It is put into box and impregnates 10 minutes, then gold raw material surface is cleaned with hairbrush.
3. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that in the S4
Crucible is that silica crucible makes silica crucible bottom thermally equivalent when acetylene torch burns crucible.
4. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that right in the S6
When workpiece B is beaten, workpiece B is carried out repeating to beat using hammer, until being trimmed to the shape of needs.
5. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that high in the S7
The model wH1010 of frequency sand-blasting machine, the model SQ-12 of dedusting rifle.
6. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that thrown in the S8
The model GWS6-100E of ray machine needs to guarantee that light is good in bruting process, in order to observe lustrous surface situation, if light
Line is not sufficient enough, then is illuminated using headlamp.
7. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that Ma in the S9
Nao to workpiece E carry out mantle friction when, it is desirable to provide sufficient illumination is assisted using magnifying glass to work if needed
Part E rubs.
8. a kind of production method of high-purity high rigidity gold according to claim 1, which is characterized in that in the S10
Finished product G needs to be placed into packing box after completing to be stored.