CN110145076A - A kind of roof polychrome room temperature waterproof material and its construction technology - Google Patents
A kind of roof polychrome room temperature waterproof material and its construction technology Download PDFInfo
- Publication number
- CN110145076A CN110145076A CN201910398403.9A CN201910398403A CN110145076A CN 110145076 A CN110145076 A CN 110145076A CN 201910398403 A CN201910398403 A CN 201910398403A CN 110145076 A CN110145076 A CN 110145076A
- Authority
- CN
- China
- Prior art keywords
- basal plane
- cement
- polychrome
- construction
- room temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of roof polychrome room temperature waterproof materials and construction technology; including cement concrete basal plane; cement hardener cured layer is carried out on the cement concrete basal plane, and waterproof antiwear surface layer is set on water-proof binding bottom, weather-proof color protection layer is set in waterproof antiwear surface layer.The present invention does not need heating can construct at normal temperature; reduce generation, the discharge of the harmful substances such as exhaust gas, dust, noise, appearance multicolor is conducive to beautifying city, the conventional coagulating cement protective soil layer of Novel design scheme deduction and exemption; integrated engineering low cost, convenient later maintenance.
Description
Technical field
The invention belongs to building engineering fields, a kind of waterproof construction suitable for positions such as roof, balconies, and in particular to room
Very useful polychrome room temperature waterproof material and its construction technology.
Background technique
With the development of urbanization process, high-rise, small high-rise commercial house construction is its mainstream building.Roof water-proof is exploitation
The emphasis that quotient, unit in charge of construction or even owner, property are paid close attention to.The main form of construction work of roof water-proof is coiled material+microlith coagulation at present
Protective soil layer is conventional construction method.The easy leak in roof, balcony, infiltration, later period maintenance is difficult, at high cost.Annoying industry always
Main and property, thus also produces many contradictions.Main cause is as follows:
1, the preceding roof concrete surface out-of-flatness of coiled material construction, basal plane are cleared up unclean or coiled material heating temperature and are not reached
Mark is uneven, causes coiled material and cement basal plane bonding not firm, the joint treatment between irregular lead angle and coiled material and coiled material less than
Position, causes later period hollowing.
2, pea gravel concreten protective layer construction Thickness Strength, which is not achieved, causes to crack or flatness is not achieved and causes long-term product
Water infiltration.
3, after due to having carried out the construction covering of pea gravel concreten protective layer, later period maintenance is more difficult, and leakage point is difficult to really
It is fixed, it can be repaired after concrete need to be excluded.
4, in the maintenance in later period, since cell has been moved in, high altitude operation danger coefficient is larger, easily generates dust, makes an uproar
The pollution such as sound, toxic gas, and maintenance cost is high.
Summary of the invention
Goal of the invention: in order to solve the deficiencies in the prior art, the present invention provides a kind of roof polychrome room temperature waterproof materials
Material and its construction technology, it is reliable in quality, easy for construction for filtering out a kind of novel environment friendly construction waterproof material.
Technical solution: a kind of roof polychrome room temperature waterproof material, including cement concrete basal plane, the coagulating cement
Cement hardener cured layer is carried out on soil matrix face, and waterproof antiwear surface layer is set on water-proof binding bottom, in waterproof antiwear surface layer
The upper weather-proof color protection layer of setting.
As optimization: the waterproof antiwear surface layer mainly includes that following component is constituted according to parts by weight: by 4-8 parts
Water proofing asphalt made of composite modified emulsification decoloration pitch, 10-14 parts of high stiffness additive packages and 0.5-1.5 parts of water stirrings is mixed
Close mortar.
As optimization: the adhesion strength of the described composite modified emulsification decoloration pitch is greater than 1Mpa, softening point not in 78 DEG C,
5 degree of ductilities are greater than 80cm, 60% or more solid content.
As optimization: the high stiffness additive package mainly includes that following component is constituted according to parts by weight: by 70-
80 parts of gradation quartz sands, 15-25 parts of curing agent and 1-10 parts of filling powders.
A kind of construction technology of the polychrome room temperature waterproof material of the roof according to, including the solidification of roof cement basal plane
Layer, water-proof binding bottom, waterproof antiwear surface layer, weather-proof four working procedure of color protection layer；
Step 1: cement basal plane cured layer is constructed
Basal plane is cement concrete basal plane, carries out the processing of cement hardener infiltration solidification to basal plane, cement basal plane is cleaned
Completely, dry tack free, using roller roller coating cement seal curing agent, 0.1-0.3 kilograms of roller coating amount/square meter, after roller coating half an hour
It can carry out next procedure construction；
Step 2: water-proof binding bottom is constructed
Basal plane is cleaned up, no ponding, using roller roller coating water-proof tack coat, 0.1-0.3 kilograms of dosage of constructing/flat
Meter, between 0 to 30 DEG C of construction temperature；
Step 3: waterproof antiwear surface construction
Basal plane is cleaned up, no ponding, is scratched using rake is scraped, 1.1-1.3 kilograms of dosage/square meter of constructing, construction temperature 0
To between 30 DEG C, enters lower road working procedure after maintenance 12 hours, must not drench with rain, endure cold during maintenance；
Step 4: weather-proof color protection layer construction
Basal plane is cleaned up, is dried, using roller roller coating, 0.1-0.3 kilograms of dosage/square meter of constructing, construction temperature 0 to
Between 30 DEG C, conserves 12 hours, must not drench with rain, endure cold during maintenance.
As optimization: the cement basal plane cured layer with a thickness of 0.2mm.
As optimization: the water-proof binding underlayer thickness is 0.5mm.
As optimization: the scratch resistance layer is with a thickness of 2mm.
As optimization: the weather-proof color protection layer is constructed with a thickness of 0.2mm.
The utility model has the advantages that the operation principle of the present invention is that: due to having carried out cement seal curing agent to cement basal plane cured layer
Curing process improves the intensity of cement basal plane, avoids the layering because of cement basal plane and water-proof system caused by running ash race sand.Using
Primary roofing material of the composite modified emulsification decoloration pitch as water-proof binding bottom, that is, avoid high-temperature heating construction, and can
Beautify the color of roof by adding mill base/toner, waterproof antiwear surface layer plays covering protective effect to existing waterproof layer, together
When have the function of assist waterproof.Weather-proof color protection layer then solves the colour fading problem of the color of roof.
The present invention does not need heating can construct at normal temperature, reduce the production of the harmful substances such as exhaust gas, dust, noise
Raw, discharge, appearance multicolor are conducive to beautifying city, and the conventional coagulating cement protective soil layer of Novel design scheme deduction and exemption is whole
Project cost is low, convenient later maintenance.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can better understand advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, those of ordinary skill in the art's every other implementation obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment
With reference to the accompanying drawings and examples, further description of the specific embodiments of the present invention.Following embodiment is only
For clearly illustrating technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Specific embodiment 1
As shown in Figure 1, a kind of roof polychrome room temperature waterproof material and construction technology, including cement basal plane cured layer 1, water
1 top roller coating water-proof binding bottom 2 of mud basal plane cured layer scratches waterproof antiwear surface layer 3, resistance in waterproof on water-proof binding bottom 2
The weather-proof color protection layer 4 of roller coating in wear layer 3.
The waterproof antiwear surface layer mainly includes that following component is constituted according to parts by weight: by 4 parts of composite modified emulsifications
Water proofing asphalt mixed mortar made of decoloration pitch, 10 parts of high stiffness additive packages and 0.5 part of water stirring.
The adhesion strength of the described composite modified emulsification decoloration pitch is greater than 1Mpa, and softening point is not in 78 DEG C, 5 degree of ductilities
Greater than 80cm, 60% or more solid content.
The high stiffness additive package mainly includes that following component is constituted according to parts by weight: by 70 parts of gradation quartz
Sand, 15 parts of curing agent and 1 part of filling powder.
The construction technology of roof polychrome room temperature waterproof material, including roof cement basal plane cured layer, waterproof are viscous
Tie bottom, waterproof antiwear surface layer, weather-proof four working procedure of color protection layer；
Step 1: cement basal plane cured layer is constructed
Basal plane is cement concrete basal plane, carries out the processing of cement hardener infiltration solidification to basal plane, cement basal plane is cleaned
Completely, dry tack free, using roller roller coating cement seal curing agent, 0.1 kilogram/square meter of roller coating amount, after roller coating half an hour
Carry out next procedure construction；
Step 2: water-proof binding bottom is constructed
Basal plane is cleaned up, no ponding, using roller roller coating water-proof tack coat, 0.1 kilogram/square meter of dosage of constructing is applied
Between 0 to 30 DEG C of work temperature；
Step 3: waterproof antiwear surface construction
Basal plane is cleaned up, no ponding, is scratched using rake is scraped, 1.1 kilograms/square meter of dosage of constructing, construction temperature 0 to 30
Between DEG C, enters lower road working procedure after maintenance 12 hours, must not drench with rain, endure cold during maintenance；
Step 4: weather-proof color protection layer construction
Basal plane is cleaned up, is dried, using roller roller coating, 0.1 kilogram/square meter of dosage of constructing, 0 to 30 DEG C of construction temperature
Between, it conserves 12 hours, must not drench with rain, endure cold during maintenance.
Specific embodiment 2
As shown in Figure 1, a kind of roof polychrome room temperature waterproof material and construction technology, including cement basal plane cured layer 1, water
1 top roller coating water-proof binding bottom 2 of mud basal plane cured layer scratches waterproof antiwear surface layer 3, resistance in waterproof on water-proof binding bottom 2
The weather-proof color protection layer 4 of roller coating in wear layer 3.
The waterproof antiwear surface layer mainly includes that following component is constituted according to parts by weight: by 8 parts of composite modified emulsifications
Water proofing asphalt mixed mortar made of decoloration pitch, 14 parts of high stiffness additive packages and 1.5 parts of water stirrings.
The adhesion strength of the described composite modified emulsification decoloration pitch is greater than 1Mpa, and softening point is not in 78 DEG C, 5 degree of ductilities
Greater than 80cm, 60% or more solid content.
The high stiffness additive package mainly includes that following component is constituted according to parts by weight: by 80 parts of gradation quartz
Sand, 25 parts of curing agent and 10 parts of filling powders.
The construction technology of roof polychrome room temperature waterproof material, including roof cement basal plane cured layer, waterproof are viscous
Tie bottom, waterproof antiwear surface layer, weather-proof four working procedure of color protection layer；
Step 1: cement basal plane cured layer is constructed
Basal plane is cement concrete basal plane, carries out the processing of cement hardener infiltration solidification to basal plane, cement basal plane is cleaned
Completely, dry tack free, using roller roller coating cement seal curing agent, 0.3 kilogram/square meter of roller coating amount, after roller coating half an hour
Carry out next procedure construction；
Step 2: water-proof binding bottom is constructed
Basal plane is cleaned up, no ponding, using roller roller coating water-proof tack coat, 0.3 kilogram/square meter of dosage of constructing is applied
Between 0 to 30 DEG C of work temperature；
Step 3: waterproof antiwear surface construction
Basal plane is cleaned up, no ponding, is scratched using rake is scraped, 1.3 kilograms/square meter of dosage of constructing, construction temperature 0 to 30
Between DEG C, enters lower road working procedure after maintenance 12 hours, must not drench with rain, endure cold during maintenance；
Step 4: weather-proof color protection layer construction
Basal plane is cleaned up, is dried, using roller roller coating, 0.3 kilogram/square meter of dosage of constructing, 0 to 30 DEG C of construction temperature
Between, it conserves 12 hours, must not drench with rain, endure cold during maintenance.
Specific embodiment 3
As shown in Figure 1, a kind of roof polychrome room temperature waterproof material and construction technology, including cement basal plane cured layer 1, water
1 top roller coating water-proof binding bottom 2 of mud basal plane cured layer scratches waterproof antiwear surface layer 3, resistance in waterproof on water-proof binding bottom 2
The weather-proof color protection layer 4 of roller coating in wear layer 3.
The waterproof antiwear surface layer mainly includes that following component is constituted according to parts by weight: by 6 parts of composite modified emulsifications
Water proofing asphalt mixed mortar made of decoloration pitch, 12 parts of high stiffness additive packages and 1 part of water stirring.
The adhesion strength of the described composite modified emulsification decoloration pitch is greater than 1Mpa, and softening point is not in 78 DEG C, 5 degree of ductilities
Greater than 80cm, 60% or more solid content.
The high stiffness additive package mainly includes that following component is constituted according to parts by weight: by 75 parts of gradation quartz
Sand, 20 parts of curing agent and 5 parts of filling powders.
The construction technology of roof polychrome room temperature waterproof material, including roof cement basal plane cured layer, waterproof are viscous
Tie bottom, waterproof antiwear surface layer, weather-proof four working procedure of color protection layer；
Step 1: cement basal plane cured layer is constructed
Basal plane is cement concrete basal plane, carries out the processing of cement hardener infiltration solidification to basal plane, cement basal plane is cleaned
Completely, dry tack free, using roller roller coating cement seal curing agent, 0.2 kilogram/square meter of roller coating amount, after roller coating half an hour
Carry out next procedure construction；
Step 2: water-proof binding bottom is constructed
Basal plane is cleaned up, no ponding, using roller roller coating water-proof tack coat, 0.2 kilogram/square meter of dosage of constructing is applied
Between 0 to 30 DEG C of work temperature；
Step 3: waterproof antiwear surface construction
Basal plane is cleaned up, no ponding, is scratched using rake is scraped, 1.2 kilograms/square meter of dosage of constructing, construction temperature 0 to 30
Between DEG C, enters lower road working procedure after maintenance 12 hours, must not drench with rain, endure cold during maintenance；
Step 4: weather-proof color protection layer construction
Basal plane is cleaned up, is dried, using roller roller coating, 0.2 kilogram/square meter of dosage of constructing, 0 to 30 DEG C of construction temperature
Between, it conserves 12 hours, must not drench with rain, endure cold during maintenance.
In this patent, the cement basal plane cured layer with a thickness of 0.2mm.The water-proof binding underlayer thickness is
0.5mm.The scratch resistance layer is with a thickness of 2mm.The weather-proof color protection layer is constructed with a thickness of 0.2mm.
The operation principle of the present invention is that: due to having carried out cement seal curing agent curing process to cement basal plane cured layer 1,
The intensity for improving cement basal plane avoids the layering because of cement basal plane and water-proof system caused by running ash race sand.Using composite modified
Primary roofing material of the emulsification decoloration pitch as water-proof binding bottom 2, that is, avoid high-temperature heating construction, and can be by adding
Additive color slurry/toner beautifies the color of roof, and waterproof antiwear surface layer 3 plays covering protective effect to existing waterproof layer, has simultaneously
Assist the effect of waterproof.Weather-proof color protection layer 4 then solves the colour fading problem of the color of roof.
The present invention does not need heating can construct at normal temperature, reduce the production of the harmful substances such as exhaust gas, dust, noise
Raw, discharge, appearance multicolor are conducive to beautifying city, and the conventional coagulating cement protective soil layer of Novel design scheme deduction and exemption is whole
Project cost is low, convenient later maintenance.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of roof polychrome room temperature waterproof material, it is characterised in that: including cement concrete basal plane, the coagulating cement
Cement hardener cured layer is carried out on soil matrix face, and waterproof antiwear surface layer is set on water-proof binding bottom, in waterproof antiwear surface layer
The upper weather-proof color protection layer of setting.
2. roof according to claim 1 polychrome room temperature waterproof material, it is characterised in that: the waterproof antiwear surface layer
Mainly include that following component is constituted according to parts by weight: being mixed by 4-8 parts of composite modified emulsification decoloration pitches, 10-14 parts of high stiffness
Close water proofing asphalt mixed mortar made of additive and 0.5-1.5 parts of water stirrings.
3. roof according to claim 1 polychrome room temperature waterproof material, it is characterised in that: the composite modified emulsification
The adhesion strength of decoloration pitch is greater than 1Mpa, and for softening point not in 78 DEG C, 5 degree of ductilities are greater than 80cm, 60% or more solid content.
4. roof according to claim 1 polychrome room temperature waterproof material, it is characterised in that: the high stiffness mixing adds
Adding agent mainly includes that following component is constituted according to parts by weight: by 70-80 parts of gradation quartz sands, 15-25 parts of curing agent and 1-10
Part filling powder.
5. a kind of construction technology of roof according to claim 1 polychrome room temperature waterproof material, it is characterised in that: including
Roof cement basal plane cured layer, water-proof binding bottom, waterproof antiwear surface layer, weather-proof four working procedure of color protection layer；
Step 1: cement basal plane cured layer is constructed
Basal plane is cement concrete basal plane, carries out the processing of cement hardener infiltration solidification to basal plane, cement basal plane is cleaned up,
Dry tack free, using roller roller coating cement seal curing agent, 0.1-0.3 kilograms of roller coating amount/square meter can be into after roller coating half an hour
Row next procedure construction；
Step 2: water-proof binding bottom is constructed
Basal plane is cleaned up, no ponding, using roller roller coating water-proof tack coat, 0.1-0.3 kilograms of dosage/square meter of constructing is applied
Between 0 to 30 DEG C of work temperature；
Step 3: waterproof antiwear surface construction
Basal plane is cleaned up, no ponding, is scratched using rake is scraped, 1.1-1.3 kilograms of dosage/square meter of constructing, construction temperature 0 to 30
Between DEG C, enters lower road working procedure after maintenance 12 hours, must not drench with rain, endure cold during maintenance；
Step 4: weather-proof color protection layer construction
Basal plane is cleaned up, is dried, using roller roller coating, 0.1-0.3 kilograms of dosage/square meter of constructing, 0 to 30 DEG C of construction temperature
Between, it conserves 12 hours, must not drench with rain, endure cold during maintenance.
6. the roof according to claim 1 construction technology of polychrome room temperature waterproof material, it is characterised in that: the water
Mud basal plane cured layer with a thickness of 0.2mm.
7. the roof according to claim 1 construction technology of polychrome room temperature waterproof material, it is characterised in that: described is anti-
Water bond coating is with a thickness of 0.5mm.
8. the roof according to claim 1 construction technology of polychrome room temperature waterproof material, it is characterised in that: described is resistance to
Scratch layers are with a thickness of 2mm.
9. the roof according to claim 1 construction technology of polychrome room temperature waterproof material, it is characterised in that: described is resistance to
The construction of color protection layer is waited with a thickness of 0.2mm.