CN110137553B - 液流电池和电池堆 - Google Patents
液流电池和电池堆 Download PDFInfo
- Publication number
- CN110137553B CN110137553B CN201810877624.XA CN201810877624A CN110137553B CN 110137553 B CN110137553 B CN 110137553B CN 201810877624 A CN201810877624 A CN 201810877624A CN 110137553 B CN110137553 B CN 110137553B
- Authority
- CN
- China
- Prior art keywords
- electrode
- slurry
- flow battery
- contralateral
- flow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
首次放电比容量(mAh/g) | 循环50次后的放电比容量(mAh/g) | |
实施例1 | 93.2 | 92.6 |
实施例2 | 89.5 | 89.0 |
实施例3 | 88.3 | 87.8 |
实施例4 | 80.2 | 79.6 |
实施例5 | 77.6 | 77.6 |
实施例6 | 74.5 | 74.3 |
实施例7 | 78.2 | 77.3 |
实施例8 | 81.1 | 80.9 |
实施例9 | 84.6 | 83.5 |
对比例1 | 30.2 | 29.8 |
Claims (56)