CN110129985A - A kind of vehicle wash resistant fire retardant elastic band and its manufacturing method - Google Patents
A kind of vehicle wash resistant fire retardant elastic band and its manufacturing method Download PDFInfo
- Publication number
- CN110129985A CN110129985A CN201910509945.9A CN201910509945A CN110129985A CN 110129985 A CN110129985 A CN 110129985A CN 201910509945 A CN201910509945 A CN 201910509945A CN 110129985 A CN110129985 A CN 110129985A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- warp thread
- elastic band
- retardant
- weft yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of vehicle wash resistant fire retardant elastic bands and its manufacturing method, including fabric upper layer and lower layer are weft yarn, and middle layer is warp thread, is connected between weft yarn and warp thread with chaining coil.Vehicle of the invention can be used as vehicle seat cloth harness fastener with fire retardant elastic band and use, can be on aircraft, high-speed rail and superior automobile, and elasticity is good, fire-retardant, after washing 20 times, still have good anti-flammability after tested.And there is good washing fastness, it is still not loose after washing 20 times, it can permanently use.
Description
Technical field
The present invention relates to a kind of elastic webbing and its manufacturing method, in particular to a kind of vehicle wash resistant fire retardant elastic band and
Its manufacturing method.
Background technique
The applicant has applied for a patent, topic in the past are as follows: a kind of vehicle flame-retardant elastic and its manufacturing method are (specially
Benefit number: CN-201510936608.X), the fire-retardant of ordinary elasticity band is solved the problems, such as, so that ordinary elasticity band is as vehicle seat
The use of cloth harness fastener, the especially use on aircraft, high-speed rail and superior automobile are achieved.But this method is done
Elastic webbing out, the anti-flammability after washing just decline quickly, can not use safely again.
Summary of the invention
An object of the present invention is to overcome defect of the existing technology, provides a kind of vehicle wash resistant fire retardant elastic
Band.
The second object of the present invention is to overcome defect of the existing technology, a kind of vehicle wash resistant fire retardant elastic is provided
Band and preparation method thereof.
These and other objects of the invention will further embody by the following detailed description and explanation.
A kind of vehicle of the invention wash resistant fire retardant elastic band, including fabric upper layer and lower layer are weft yarn, and middle layer is warp
Yarn is connected between weft yarn and warp thread with chaining coil.
Further, vehicle of the invention wash resistant fire retardant elastic band, weaving knitting chaining coil with ordinary polyester will
Upper layer weft yarns, middle layer warp thread and lower layer's weft yarn band together.
It is preferred that vehicle of the invention wash resistant fire retardant elastic band, a warp thread is clipped between upper and lower two weft yarns,
Upper and lower two weft yarns and a warp thread connection are banded together by chaining coil.
In vehicle of the invention in wash resistant fire retardant elastic band, weft yarn is ordinary polyester, line density 150-200dtex,
Warp thread is fire-retardant spandex monofilament, and line density 1400-1867dtex, chaining coil is 150-200dtex ordinary polyester.
The vehicle of the invention manufacturing method of wash resistant fire retardant elastic band, includes the following steps:
A, when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, the fire-retardant spandex monofilament of middle layer warp thread, then with ordinary polyester weave knitting chaining coil by upper layer weft yarns, middle layer warp thread and under
Layer weft yarn bands together, and forms elastic webbing；
B, the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
1) FR-510 type fire retardant, amount of flame-retardant agent 150-180g/l, bath raio 1:15-20, dipping temperature 60- are used
70 DEG C, time 2-3h.Dipping finishes dehydration 5-8mi n；
2) it is dried after being dehydrated, 100-120 DEG C of drying temperature, time 1-2mi n；
3) it is baked after drying, 190-195 DEG C of baking temperature, time 1-2mi n.
It is preferred that the vehicle of the invention manufacturing method of wash resistant fire retardant elastic band, includes the following steps:
A, when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 150-200dtex, (Yantai Tayho Advanced Materials Co., Ltd. is raw with fire-retardant spandex monofilament for middle layer warp thread
Produce), line density 1400-1867dtex, then knitting chaining coil is woven by upper layer with line density 150-200dtex ordinary polyester
Weft yarn, middle layer warp thread and lower layer's weft yarn band together, and form elastic webbing；
B, the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
1) FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd) is used, amount of flame-retardant agent is
150-180g/l, bath raio 1:15-20,60-70 DEG C of dipping temperature, time 2-3h.Dipping finishes dehydration 5-8min；
2) it is dried after being dehydrated, 100-120 DEG C of drying temperature, time 1-2min；
3) it is baked after drying, 190-195 DEG C of baking temperature, time 1-2min.
Vehicle of the invention with fire retardant elastic band can be used as vehicle seat cloth harness fastener use, can be used in aircraft,
In high-speed rail and superior automobile, elasticity is good, fire-retardant, after washing 20 times, still has good anti-flammability after tested.And have good
Good washing fastness, it is still not loose after washing 20 times, it can be used for a long time.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of vehicle wash resistant fire retardant elastic band of the present invention.Symbol 1 represents upper layer weft yarns, symbol 2
Lower layer's weft yarn is represented, symbol 3 represents chaining coil, and symbol 4 represents warp thread.
By the following specific examples further illustrate the invention, but embodiment is merely to illustrate, and can not limit this
The range of invention.
In the present invention, it is refered in particular to as non-, all amounts, part are unit of weight, and all raw materials can be purchased from market
?.
Embodiment 1
It manufactures according to the following steps:
1: when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 150dtex, for middle layer warp thread with fire-retardant spandex monofilament (Yantai Tayho Advanced Materials Co., Ltd.'s production), line is close
1400dtex is spent, then weaves knitting chaining coil with 150dtex ordinary polyester and ties upper layer weft yarns, middle layer warp thread and lower layer's weft yarn
It binds together, is formed elastic webbing (institutional framework is as shown in Fig. 1).
2: the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
Using FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd), amount of flame-retardant agent 150g/
L, bath raio 1:15,60 DEG C of dipping temperature, time 2h, dipping finishes dehydration 5min.
It is dried after dehydration, 100 DEG C of drying temperature, time 1min.
It is baked after drying, 190 DEG C of baking temperature, time 1min.
Embodiment 2
It manufactures according to the following steps:
1: when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 180dtex, for middle layer warp thread with fire-retardant spandex monofilament (Yantai Tayho Advanced Materials Co., Ltd.'s production), line is close
1600dtex is spent, then weaves knitting chaining coil with 180dtex ordinary polyester and ties upper layer weft yarns, middle layer warp thread and lower layer's weft yarn
It binds together, is formed elastic webbing (institutional framework is as shown in Fig. 1).
2: the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
Using FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd), amount of flame-retardant agent 160g/
L, bath raio 1:15,60 DEG C of dipping temperature, time 2.5h, dipping finishes dehydration 5min.
It is dried after dehydration, 100 DEG C of drying temperature, time 1.5min.
It is baked after drying, 190 DEG C of baking temperature, time 1.5min.
Embodiment 3
It manufactures according to the following steps:
1: when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 200dtex, for middle layer warp thread with fire-retardant spandex monofilament (Yantai Tayho Advanced Materials Co., Ltd.'s production), line is close
1867dtex is spent, then weaves knitting chaining coil with 200dtex ordinary polyester and ties upper layer weft yarns, middle layer warp thread and lower layer's weft yarn
It binds together, is formed elastic webbing (institutional framework is as shown in Fig. 1).
2: the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
Using FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd), amount of flame-retardant agent 180g/
L, bath raio 1:20,70 DEG C of dipping temperature, time 3h, dipping finishes dehydration 8min.
It is dried after dehydration, 120 DEG C of drying temperature, time 2min.
It is baked after drying, 195 DEG C of baking temperature, time 2min.
Comparative example 1
It manufactures according to the following steps:
1: when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 120dtex, third layer warp thread spandex monofilament (Yantai Tayho Advanced Materials Co., Ltd.'s production), line density
1300dtex, then weave knitting chaining coil with 100dtex ordinary polyester and tie up upper layer weft yarns, middle layer weft yarn and lower layer warp yarns
Together, elastic webbing is formed.
2: the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
Using FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd), amount of flame-retardant agent 120g/
L, bath raio 1:10,50 DEG C of dipping temperature, time 1.5h, dipping finishes dehydration 4min.
It is dried after dehydration, 90 DEG C of drying temperature, time 3min.
It is baked after drying, 150 DEG C of baking temperature, time 3min.
Comparative example 2
It manufactures according to the following steps:
1: when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is commonly to wash
Synthetic fibre, line density 220dtex, third layer warp thread spandex monofilament (Yantai Tayho Advanced Materials Co., Ltd.'s production), line density
2100dtex, then weave knitting chaining coil with 220dtex ordinary polyester and tie up upper layer weft yarns, middle layer weft yarn and lower layer warp yarns
Together, elastic webbing is formed.
2: the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates fire-retardant whole
Science and engineering skill are as follows:
Using FR-510 type fire retardant (production of changzhou Di textile technology Co., Ltd), amount of flame-retardant agent 200g/
L, bath raio 1:25,80 DEG C of dipping temperature, time 3.5h, dipping finishes dehydration 10min.
It is dried after dehydration, 130 DEG C of drying temperature, time 0.5min.
It is baked after drying, 210 DEG C of baking temperature, time 0.5min.
Vehicle is with common fire retardant elastic band such as table 1 compared with vehicle of the present invention wash resistant fire retardant elastic band performance:
Table 1
As can be seen from the comparative examples, the technique of the raw material selection of elastic webbing, braiding structure and fire-retardant processing is for product
Flame retardant property has a great impact.
Claims (8)
1. a kind of vehicle wash resistant fire retardant elastic band, it is characterised in that including fabric upper layer and lower layer be weft yarn, middle layer be warp
Yarn is connected between weft yarn and warp thread with chaining coil.
2. vehicle according to claim 1 wash resistant fire retardant elastic band, it is characterised in that woven and be knitted with ordinary polyester
Chaining coil bands together upper layer weft yarns, middle layer warp thread and lower layer's weft yarn.
3. vehicle according to claim 1 or 2 wash resistant fire retardant elastic band, it is characterised in that between upper and lower two weft yarns
A warp thread is clipped, is banded together upper and lower two weft yarns and a warp thread connection by chaining coil.
4. vehicle according to any one of claims 1 to 3 wash resistant fire retardant elastic band, it is characterised in that weft yarn is commonly to wash
Synthetic fibre, line density 150-200dtex.
5. vehicle according to any one of claims 1 to 3 wash resistant fire retardant elastic band, it is characterised in that warp thread is fire-retardant ammonia
Synthetic fibre monofilament, line density 1400-1867dtex.
6. vehicle according to any one of claims 1 to 3 wash resistant fire retardant elastic band, it is characterised in that chaining coil is
150-200dtex ordinary polyester.
7. the vehicle according to any one of claims 1 to 6 manufacturing method of wash resistant fire retardant elastic band, it is characterised in that packet
Include following steps:
A, when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is ordinary polyester, in
The layer fire-retardant spandex monofilament of warp thread, then knitting chaining coil is woven by upper layer weft yarns, middle layer warp thread and lower layer's latitude with ordinary polyester
Yarn bands together, and forms elastic webbing；
B, the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates flame-proof treatment work
Skill are as follows:
1) FR-510 type fire retardant, amount of flame-retardant agent 150-180g/l, bath raio 1:15-20, dipping temperature 60-70 are used
DEG C, time 2-3h.Dipping finishes dehydration 5-8min；
2) it is dried after being dehydrated, 100-120 DEG C of drying temperature, time 1-2min；
3) it is baked after drying, 190-195 DEG C of baking temperature, time 1-2min.
8. the vehicle according to claim 7 manufacturing method of wash resistant fire retardant elastic band, it is characterised in that including as follows
Step:
A, when design flexibility band institutional framework, using woven composite construction is knitted, fabric upper layer and lower layer weft yarn is ordinary polyester, line
Density is 150-200dtex, the fire-retardant spandex monofilament of middle layer warp thread, line density 1400-1867dtex, then with line density 150-
200dtex ordinary polyester braiding knitting chaining coil bands together upper layer weft yarns, middle layer warp thread and lower layer's weft yarn, forms bullet
Property band；
B, the elastic webbing completed to weaving carries out dipping flame-proof treatment, forms inflaming retarding membrane on terylene surface, impregnates flame-proof treatment work
Skill are as follows:
1) FR-510 type fire retardant, amount of flame-retardant agent 150-180g/l, bath raio 1:15-20, dipping temperature 60-70 are used
DEG C, time 2-3h.Dipping finishes dehydration 5-8min；
2) it is dried after being dehydrated, 100-120 DEG C of drying temperature, time 1-2min；
3) it is baked after drying, 190-195 DEG C of baking temperature, time 1-2min.