CN110128953A - A kind of fabric is compound to use glue - Google Patents
A kind of fabric is compound to use glue Download PDFInfo
- Publication number
- CN110128953A CN110128953A CN201910357860.3A CN201910357860A CN110128953A CN 110128953 A CN110128953 A CN 110128953A CN 201910357860 A CN201910357860 A CN 201910357860A CN 110128953 A CN110128953 A CN 110128953A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- tetrachloroethanes
- fabric
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound glues of fabric, include following weight item raw material: 58 parts of cycloaliphatic epoxy resin, 10 parts of tetrachloroethanes, 7 parts of black glue, 6 parts of Brazil wax, 3 parts of polyvinyl alcohol, 4 parts of alginic acid, 2 parts of disodium ethylene diamine tetraacetate, 2 parts of nano-graphene, 4 parts of aluminium powder, 5 parts of sodium nitrite, 12 parts of trichloroethanes, 7 parts of ethyl acrylate, 7 parts of nitromethane, 6 parts of isopropanol, 6 parts of amido silicon oil, 2 parts of difluoro tetrachloroethanes, 10 parts of acrylonitrile, 8 parts of tetrachloroethanes, 4 parts of amido silicon oil, 15 parts of silver-colored nickel zinc powder, 4 parts of dispersing agent, 9 parts of antistatic agent, 18 parts of organic solvent, 0.8 part of aromatic, 1.5 parts of antimicrobial fluid.The glue good permeability of preparation, water absorption rate is extremely low, so good to fabric combined strength bination, antistatic effect is splendid.And aromatic and antibacterial agent are added in preparation process, therefore make fabric have natural fragrance also there is preferable antibiotic property during composite material.
Description
Technical field
The present invention relates to a kind of compound glues of fabric, specially fabric complex technique field.
Background technique
In the clothes world, the fabric of clothes is multifarious, makes rapid progress.But generally, high-quality, high-grade
Fabric mostly has the characteristics that comfortable and easy to wear, sweat-absorbing breathable, the several respects such as pendency is well-pressed, vision is noble, tactile is soft and graceful.It is modern
It is produced on the clothes that formal social life is worn, the good blended yarn weaved fabric of multiselect.And pure cotton, pure wool, pure silk, pure fiber crops etc.
Natural fabric is less to be used as high-grade clothing materials because there is the shortcomings that easily natural fabric such as wrinkle, easily-deformable.With the modern times
The raising of living quality of patients, they oneself own dress is required it is also higher and higher, be no longer confined to be clothes moulding, style, more
Whether the fabric for focusing on clothes is comfortable, if environmental protection.
And the knitting fabric that tradition applies to Sports Series mostly uses common circular-section terylene low stretch yarn raw material, adopts
With manufacture craft after original dyeing, washing loose colour is more and light shine fastness is poor, and color becomes after long-term outdoor moves dressing
Must wither dark, feel hard and moisture absorption to lead sweat performance poor, wear sultry airtight, comfort is poor；Even if common people do not carry out any
In movable situation, still require that worn clothes must have the quality of high quality, in addition, as context pollution is increasingly tight
Weight, ciril disease also occur in succession, such as too coarse cloth textile will lead to some people skin and generate allergy, or externally
It is easy to produce the constitution of allergy in environment, modern is caused also gradually to pay attention to the idea of antibacterial, in the past only medical staff
Required antibacterial clothing and antibacterial utensil, is also gradually used in the articles of daily life.The breathable and waterproof and antibacterial of fabric
Property is particularly significant.
Summary of the invention
Glue is used the purpose of the present invention is to provide a kind of fabric is compound.
To achieve the above object, the invention provides the following technical scheme: a kind of fabric is compound to include following weight with glue
Component materials: 55-60 parts of cycloaliphatic epoxy resin, 6-8 parts of black glue, 5-7 parts of Brazil wax, gathers 8-12 parts of tetrachloroethanes
2-4 parts of vinyl alcohol, 3-5 parts of alginic acid, 1-3 parts of disodium ethylene diamine tetraacetate, 1-3 parts of nano-graphene, 3-6 parts of aluminium powder, nitrous
Sour sodium 3-6 parts, 10-13 parts of trichloroethanes, 6-8 parts of ethyl acrylate, 6-8 parts of nitromethane, 4-7 parts of isopropanol, amido silicon oil
4-8 parts, 1-3 parts of difluoro tetrachloroethanes, 8-12 parts of acrylonitrile, 6-10 parts of tetrachloroethanes, 2-5 parts of amido silicon oil, silver-colored nickel zinc powder
10-20 parts, 3-5 parts of dispersing agent, 8-10 parts of antistatic agent, 15-20 parts of organic solvent, aromatic 0.5-1
Part, 1-2 parts of antimicrobial fluid.
Further preferably, the fabric is compound includes following weight item raw material: cycloaliphatic epoxy resin 58 with glue
Part, 10 parts of tetrachloroethanes, 7 parts of black glue, 6 parts of Brazil wax, 3 parts of polyvinyl alcohol, 4 parts of alginic acid, ethylenediamine tetra-acetic acid two
2 parts of sodium, 2 parts of nano-graphene, 4 parts of aluminium powder, 5 parts of sodium nitrite, 12 parts of trichloroethanes, 7 parts of ethyl acrylate, nitromethane 7
Part, 6 parts of isopropanol, 6 parts of amido silicon oil, 2 parts of difluoro tetrachloroethanes, 10 parts of acrylonitrile, 8 parts of tetrachloroethanes, 4 parts of amido silicon oil,
15 parts of silver-colored nickel zinc powder, 4 parts of dispersing agent, 9 parts of antistatic agent, 18 parts of organic solvent, 0.8 part of aromatic, 1.5 parts of antimicrobial fluid.
Preferably, the antimicrobial fluid is increased by plant extracts, citric acid, usnic acid sodium, enzyme antibacterial agent, antibacterial
Effect agent mixes.
It further preferably, include the raw material of following mass fraction: plant extracts 30%, lemon in terms of very by antimicrobial fluid
Lemon acid 30%, usnic acid sodium 35%, enzyme antibacterial agent 2%, Trimethoprim 3%.
Preferably, the aromatic is the peppermint oil of microcapsule coated.
A kind of fabric it is compound with glue the preparation method comprises the following steps: Step 1: matching according to the composition of raw materials of the compound glue of fabric
Than by cycloaliphatic epoxy resin, tetrachloroethanes, black glue, Brazil wax, polyvinyl alcohol, alginic acid, ethylenediamine tetra-acetic acid two
Sodium, nano-graphene, sodium nitrite, trichloroethanes, ethyl acrylate, nitromethane, isopropanol, amido silicon oil, difluoro tetrachloro
Ethane, acrylonitrile, tetrachloroethanes, amido silicon oil are added in reaction kettle, and temperature of reaction kettle is increased to 55-70 DEG C；
Step 2: being subsequently added into dispersing agent and organic solvent after mixing evenly, 75-90 DEG C are raised the temperature to, it is lasting to stir
Silver-colored nickel zinc powder is added after 30-40 minutes, aluminium powder stirs evenly；
Step 3: being cooled to room temperature after being finally slowly added to antistatic agent, aromatic, stirring 20-30 minutes, it is added anti-
Bacterium solution stirs 15 minutes can be up to adhesive.
Preferably, the mixing speed of blender is 150-200r/min in the step three.
Compared with prior art, beneficial effects of the present invention are as follows: prepare glue method of the present invention is simple, and the glue prepared
Liquid good permeability, water absorption rate is extremely low, thus it is good to fabric combined strength bination, and also antistatic effect is splendid, is also equipped with certain resist
Thermal impact.And aromatic and antibacterial agent are added in preparation process, therefore have fabric naturally during composite material
Fragrance also has preferable antibiotic property, substantially increases the performance of composite material.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction in the embodiment of the present invention, it is clear that institute
The embodiment of description is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention,
Every other embodiment obtained by those of ordinary skill in the art without making creative efforts, belongs to this hair
The range of bright protection.
Embodiment 1: a kind of fabric it is compound with glue the preparation method comprises the following steps: Step 1: according to the compound glue of fabric original
Material formula proportion；By 55 parts of cycloaliphatic epoxy resin, 8 parts of tetrachloroethanes, 6 parts of black glue, 5 parts of Brazil wax, polyvinyl alcohol 2
Part, 3 parts of alginic acid, 1 part of disodium ethylene diamine tetraacetate, 1 part of nano-graphene, 3 parts of sodium nitrite, 10 parts of trichloroethanes, propylene
6 parts of acetoacetic ester, 6 parts of nitromethane, 4 parts of isopropanol, 4 parts of amido silicon oil, 1 part of difluoro tetrachloroethanes, 8 parts of acrylonitrile, four chloroethenes
In 2 parts of 6 parts of alkane, amido silicon oil addition reaction kettles, temperature of reaction kettle is increased to 55 DEG C；
Step 2: being subsequently added into 15 parts of 3 parts of dispersing agent and organic solvent after mixing evenly, 75 DEG C are raised the temperature to, is held
Continuous stirring is added silver-colored 10 parts, 3 parts of aluminium powder of powder of nickel zinc and stirs evenly after 30 minutes；
Step 3: be cooled to room temperature after being finally slowly added to 8 parts of antistatic agent, 0.5 part of aromatic, 20 minutes of stirring,
Being added 1 part of antimicrobial fluid stirring 15 minutes can be up to adhesive.
Embodiment 2: a kind of fabric it is compound with glue the preparation method comprises the following steps: Step 1: according to the compound glue of fabric original
Material formula proportion；By 60 parts of cycloaliphatic epoxy resin, 12 parts of tetrachloroethanes, 8 parts of black glue, 7 parts of Brazil wax, polyvinyl alcohol
4 parts, 5 parts of alginic acid, 3 parts of disodium ethylene diamine tetraacetate, 3 parts of nano-graphene, 6 parts of sodium nitrite, 13 parts of trichloroethanes, propylene
8 parts of acetoacetic ester, 8 parts of nitromethane, 7 parts of isopropanol, 8 parts of amido silicon oil, 3 parts of difluoro tetrachloroethanes, 12 parts of acrylonitrile, tetrachloro
In 5 parts of 10 parts of ethane, amido silicon oil addition reaction kettles, temperature of reaction kettle is increased to 70 DEG C；
Step 2: being subsequently added into 20 parts of 5 parts of dispersing agent and organic solvent after mixing evenly, 90 DEG C are raised the temperature to, is held
Silver-colored 20 parts, 6 parts of aluminium powder of powder of nickel zinc is added after forty minutes and stirs evenly for continuous stirring；
Step 3: be cooled to room temperature after being finally slowly added to 10 parts of antistatic agent, 1 part of aromatic, 30 minutes of stirring,
Being added 2 parts of antimicrobial fluid stirrings 15 minutes can be up to adhesive.
Embodiment 3: a kind of fabric it is compound with glue the preparation method comprises the following steps: Step 1: according to the compound glue of fabric original
Material formula proportion；By 58 parts of cycloaliphatic epoxy resin, 10 parts of tetrachloroethanes, 7 parts of black glue, 6 parts of Brazil wax, polyvinyl alcohol
3 parts, 4 parts of alginic acid, 2 parts of disodium ethylene diamine tetraacetate, 2 parts of nano-graphene, 4 parts of sodium nitrite, 12 parts of trichloroethanes, propylene
7 parts of acetoacetic ester, 7 parts of nitromethane, 6 parts of isopropanol, 7 parts of amido silicon oil, 2 parts of difluoro tetrachloroethanes, 10 parts of acrylonitrile, tetrachloro
In 4 parts of 9 parts of ethane, amido silicon oil addition reaction kettles, temperature of reaction kettle is increased to 60 DEG C；
Step 2: being subsequently added into 18 parts of 4 parts of dispersing agent and organic solvent after mixing evenly, 80 DEG C are raised the temperature to, is continued
Silver-colored 15 parts, 5 parts of aluminium powder of powder of nickel zinc is added after stirring 35 minutes to stir evenly；
Step 3: be cooled to room temperature after being finally slowly added to 9 parts of antistatic agent, 0.8 part of aromatic, 25 minutes of stirring,
Being added 1.5 parts of antimicrobial fluid stirrings 15 minutes can be up to adhesive.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of fabric is compound to use glue, it is characterised in that: the compound same glue includes following weight item raw material: alicyclic ring
Epoxy resin 55-60 parts of race, 8-12 parts of tetrachloroethanes, 6-8 parts of black glue, 5-7 parts of Brazil wax, 2-4 parts of polyvinyl alcohol, sea
3-5 parts of alginic acid, 1-3 parts of disodium ethylene diamine tetraacetate, 1-3 parts of nano-graphene, 3-6 parts of aluminium powder, 3-6 parts of sodium nitrite, trichlorine
10-13 parts of ethane, 6-8 parts of ethyl acrylate, 6-8 parts of nitromethane, 4-7 parts of isopropanol, 4-8 parts of amido silicon oil, difluoro tetrachloro
1-3 parts of ethane, 8-12 parts of acrylonitrile, 6-10 parts of tetrachloroethanes, 2-5 parts of amido silicon oil, silver-colored 10-20 parts of nickel zinc powder, dispersion
3-5 parts of agent, 8-10 parts of antistatic agent, 15-20 parts of organic solvent, 0.5-1 parts of aromatic, 1-2 parts of antimicrobial fluid.
2. a kind of fabric according to claim 1 is compound to use glue, it is characterised in that: the compound glue packet of the fabric
Containing following weight item raw material: 58 parts of cycloaliphatic epoxy resin, 7 parts of black glue, 6 parts of Brazil wax, gathers 10 parts of tetrachloroethanes
3 parts of vinyl alcohol, 4 parts of alginic acid, 2 parts of disodium ethylene diamine tetraacetate, 2 parts of nano-graphene, 4 parts of aluminium powder, 5 parts of sodium nitrite, three
12 parts of chloroethanes, 7 parts of ethyl acrylate, 7 parts of nitromethane, 6 parts of isopropanol, 6 parts of amido silicon oil, 2 parts of difluoro tetrachloroethanes, third
10 parts of alkene nitrile, 8 parts of tetrachloroethanes, 4 parts of amido silicon oil, silver-colored 15 parts of nickel zinc powder, 4 parts of dispersing agent, 9 parts of antistatic agent, You Jirong
18 parts of agent, 0.8 part of aromatic, 1.5 parts of antimicrobial fluid.
3. a kind of fabric according to claim 1 is compound to use glue, it is characterised in that: the antimicrobial fluid is by plant extract
Object, citric acid, usnic acid sodium, enzyme antibacterial agent, Trimethoprim mix.
4. a kind of fabric according to claim 3 is compound to use glue, it is characterised in that: include in terms of very by antimicrobial fluid
The raw material of following mass fraction: plant extracts 30%, citric acid 30%, usnic acid sodium 35%, enzyme antibacterial agent 2%, antibacterial synergy
Agent 3%.
5. a kind of fabric according to claim 1 is compound to use glue, it is characterised in that: the aromatic is microcapsule coated
Peppermint oil.
6. a kind of compound preparation method with glue of fabric, it is characterised in that: specifically the preparation method comprises the following steps: Step 1: according to fabric
The compound composition of raw materials with glue matches, by cycloaliphatic epoxy resin, tetrachloroethanes, black glue, Brazil wax, polyethylene
Alcohol, alginic acid, disodium ethylene diamine tetraacetate, nano-graphene, sodium nitrite, trichloroethanes, ethyl acrylate, nitromethane,
Isopropanol, amido silicon oil, difluoro tetrachloroethanes, acrylonitrile, tetrachloroethanes, amido silicon oil are added in reaction kettle, will react kettle temperature
Degree is increased to 55-70 DEG C；
Step 2: being subsequently added into dispersing agent and organic solvent after mixing evenly, 75-90 DEG C are raised the temperature to, it is lasting to stir
Silver-colored nickel zinc powder is added after 30-40 minutes, aluminium powder stirs evenly；
Step 3: being cooled to room temperature after being finally slowly added to antistatic agent, aromatic, stirring 20-30 minutes, it is added anti-
Bacterium solution stirs 15 minutes can be up to adhesive.
7. the compound preparation method with glue of a kind of fabric according to claim 6, it is characterised in that:, the step
The mixing speed of blender is 150-200r/min in three.