CN105239183A - Aromatic home textile fabric and manufacturing method thereof - Google Patents
Aromatic home textile fabric and manufacturing method thereof Download PDFInfo
- Publication number
- CN105239183A CN105239183A CN201510684399.4A CN201510684399A CN105239183A CN 105239183 A CN105239183 A CN 105239183A CN 201510684399 A CN201510684399 A CN 201510684399A CN 105239183 A CN105239183 A CN 105239183A
- Authority
- CN
- China
- Prior art keywords
- fabric
- textile fabric
- low
- parts
- aromatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing an aromatic home textile fabric. The aromatic home textile fabric is composed, by weight parts, 100 parts of low-melting fiber, 10-20 parts of fragrance master batch, 5-10 parts of microcapsule fragrance finishing agent SCM, 2-3 parts of pigment printing paste, 15-20 parts of low-temperature adhesive SCP, 1-2 parts of thickener FAG, 5-10 parts of low-temperature fixing agent and an appropriate amount of softening agent. The method for manufacturing the aromatic home textile fabric comprises the steps of raw material preparation, composite spinning, aromatic fabric aftertreatment, padding method tidying, fabric drying, tentering and finished product obtaining. The method for manufacturing the aromatic home textile fabric has the advantages that the aromatic home textile fabric can improve sleep of the human body and is favorable for relieving fatigue and improving sleep quality; fragrance molecules are molten in ultrafine fibers, so that the fibers have natural aroma without being removed after long-time washing, and the aroma durability is achieved through a finishing process.
Description
Technical field
The present invention relates to a textile fabric technical field, particularly relate to the preparation method of a kind of fragrant family textile fabric.
Background technology
Family's textile fabric is conventional family expenses, hotel bedclothes fabric, and presents attractive in appearance, practical, high-grade, comfortable, the functional development trend of fashion band.Conventional home textile product fabric is interwoven by different weave specifications on equipment by warp thread and Wei yarn.Meet fabric national standard: GB18401-2010, industry standard: GB/T22796-2009.Along with the development trend of family's textile fabric, it should be the product that new and high technology combines with modern art.More practical, attractive in appearance, hommization has necessarily functional in addition.As: family's textile fabric has the families such as antibacterial, anti-mite, negative ion far-infrared and spins novel fabric now.
Summary of the invention
For the development trend of above-mentioned textile fabric, the invention provides a kind of family's textile fabric using various fragrance fiber to make, make it more can improve sleep quality, contribute to dispelling fatigue, improve sleep quality, technical scheme of the present invention is mainly first spices master batch and spinning material blend melt spinning, perfume molecules is melted in ultra-fine fibrous inside, fiber is had and washes the natural fragrance do not taken off for a long time, then realize the persistence of fragrance through finishing technique.
To achieve these goals, the technical solution adopted in the present invention is as follows:
A kind of fragrant family textile fabric, described fragrant family textile fabric is made up of following proportioning by weight: lowly melt fiber 100 parts, spices master batch 10-20 part, and microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG are appropriate.
Further, described spices master batch is selected from least one in Rose type essence, jasmine flower essence and lavender oil three kinds of raw materials, and the diameter made is the perfume particle of 0.5mm.
A preparation method for fragrant family textile fabric, comprises the following steps:
(1) raw material preparation: choose above-mentioned raw materials proportioning: low melt fiber 100 parts, spices master batch 10-20 part;
(2) composite spinning: first prepare cortex, first choose above-mentioned two kinds of mixing of materials even, fibrocortex is made by spinning equipment, choose the low and polymer of hydrolysis of fusing point again as sandwich layer, again spices master batch is added in process prepared by sandwich layer, form sandwich layer, finally by the above and below at sandwich layer all one machining state fibrocortex, finally form Aroma fabric crude product;
(3) Aroma fabric Final finishing: select microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG appropriate;
(4) padding method arranges: padding method comprises and pads, dries two steps, wherein pad in process the microcapsules perfumed finishing agent SCM first adding 1/3rd, the warm water adding equivalent again, stir, with become thin pulp, add the warm water with low temperature sticking agent equivalent again, finally add low temperature sticking agent, stir, after padding and softener SCG one-bath finishing process, add microcapsules perfumed finishing agent SCM and the softener SCG of 1/3rd in dip-dye equipment;
(5) Decal arranges: the Decal of indication comprises stamp, oven dry and first finished product three step, first in material bucket, described pigment printing paste is prepared in wherein said stamp process, microcapsules perfumed finishing agent SCM, low-temperature adhesive SCP and the thickener FAG of remaining 1/3rd is added successively in the process stirred, and carry out stamp by printing equipment, first finished product;
(6) fabric is dried: be transported in drying baker by the complete Aroma fabric of arrangement and carry out drying operation, bake out temperature 50-100 DEG C, drying time 2-5 minute, dry and adopt drying baker, the interior roof of drying baker arranges humidifier, the electrical heating elements of bottom set temperature change, transport tape runs through drying baker and arranges;
(7) tentering: tentering temperature is 100-120 DEG C;
(8) finished product.
Further, in described step (3) " Aroma fabric Final finishing ", in the process contaminated, adopt bath raio 1:10-20, contaminate temperature 30-40 DEG C, immerged time 30 minutes.
Further, in described step (4) " fabric oven dry ", bottom drying baker, row's electrical heating elements is set, wherein electricity adds element and is divided into 3 groups, and the electrical heating elements of the right and left is symmetrical arranged, and the electrical heating elements quantity of middle one group is 2 times of left heating element heater or right heating element heater quantity.
The invention has the beneficial effects as follows: first the present invention devises and a kind ofly can make family's textile fabric with aroma type function, this aroma type man textile fabric mainly first by composite spinning by spices master batch and spinning material blend melt spinning, perfume molecules is melted in ultra-fine fibrous inside, fiber is had and washes the natural fragrance do not taken off for a long time, and produce the fragrant fiber fabric with core-skin three-decker, it has the excellent properties such as fragrance is pure, wash resistant, fragrance remaining time are long, and spices adds in the core.Spices master batch and sandwich layer copolymer binding strength high, and substantially can not through fibrocortex, but along fiber longitudinal Cong Transverse cross section effusion, reach lasting fragrance effect; Secondly, in order to better improve the fragrance of a textile fabric, improve its enduring quality, therefore carry out padding after composite spinning and the finishing technique of stamp, make the binding strength of spices and fiber and affinity reach the best.
Detailed description of the invention
In order to make those of ordinary skill in the art can better understand technical scheme of the present invention, below in conjunction with embodiment, technical scheme of the present invention is further described.
embodiment:a kind of fragrant family textile fabric, described fragrant family textile fabric is made up of following proportioning by weight: lowly melt fiber 100 parts, spices master batch 10-20 part, and microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG are appropriate.
Described spices master batch is selected from least one in Rose type essence, jasmine flower essence and lavender oil three kinds of raw materials, and the diameter made is the perfume particle of 0.5mm, namely one can be adopted separately exactly, also can be the combination of wherein combination between two or three, the equal spices master batch spices master batch making people pleasing of making adopts the perfume particle of 0.5mm can not only realize better stirring, and can also improve the permeability with fiber.
A preparation method for fragrant family textile fabric, comprises the following steps:
(1) raw material preparation: choose above-mentioned raw materials proportioning: low melt fiber 100 parts, spices master batch 10-20 part;
(2) composite spinning: first prepare cortex, first choose above-mentioned two kinds of mixing of materials even, fibrocortex is made by spinning equipment, choose the low and polymer of hydrolysis of fusing point again as sandwich layer, again spices master batch is added in process prepared by sandwich layer, form sandwich layer, upper finally by sandwich layer, all one machining states fibrocortex below, finally form Aroma fabric crude product, first by composite spinning by the spices master batch of a part with the common compound of fabric and together with melting altogether, form preliminary fragrant step, the fragrance of the Aroma fabric of subsequent production is distributed from inside to outside gradually, instead of the fragrance just remained on surface,
(3) Aroma fabric Final finishing: select microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG appropriate;
(4) padding method arranges: padding method comprises and pads, dries two steps, wherein pad in process the microcapsules perfumed finishing agent SCM first adding 1/3rd, the warm water adding equivalent again, stir, with become thin pulp, add the warm water with low temperature sticking agent equivalent again, finally add low temperature sticking agent, stir, after padding and softener SCG one-bath finishing process, microcapsules perfumed finishing agent SCM and the softener SCG of 1/3rd is added in dip-dye equipment, in the process contaminated, adopt bath raio 1:10-20, contaminate temperature 30-40 DEG C, immerged time 30 minutes;
(5) Decal arranges: the Decal of indication comprises stamp, oven dry and first finished product three step, first in material bucket, described pigment printing paste is prepared in wherein said stamp process, microcapsules perfumed finishing agent SCM, low-temperature adhesive SCP and the thickener FAG of remaining 1/3rd is added successively in the process stirred, and carry out stamp by printing equipment, first finished product;
Can find out that from step (4) and step (5) method carries out spice finish to Aroma fabric in two steps in the further finishing technique of Aroma fabric, come mainly through padding machine and printing equipment, pad with stamp in all adopt microcapsules perfumed finishing agent SCM to improve odor prolongation, and adopt the various additive cooperatively interacted to add, further improve adhesion-tight degree and the affinity of fragrance;
(6) fabric is dried: be transported in drying baker by the complete Aroma fabric of arrangement and carry out drying operation, bake out temperature 50-100 DEG C, drying time 2-5 minute, dry and adopt drying baker, the interior roof of drying baker arranges humidifier, the electrical heating elements of bottom set temperature change, transport tape runs through drying baker and arranges, one row's electrical heating elements is set bottom drying baker, wherein electricity adds element and is divided into 3 groups, the electrical heating elements of the right and left is symmetrical arranged, the electrical heating elements quantity of middle one group is 2 times of left heating element heater or right heating element heater quantity, the temperature provided in oven dry of middle electrical heating elements is 100 DEG C, and two of both sides groups of low temperature that electrical heating elements provides are 50 DEG C, in drying unit, the hyperthermia drying at middle part and the low temperature drying on both sides are mainly realized to the above-mentioned set-up mode of electrical heating elements, so the fragrance phenomenon that part is scattered and disappeared due to the rising of temperature in drying course can be reduced, in order to further reduce scattering and disappearing of fragrance in drying course, therefore humidifier is set when oven dry, part moisture in humidifier can by fragrance to pressing down, and do not think externally to scatter and disappear, in the drying course of low temperature, fragrance can be got back to again in Aroma fabric, scattering and disappearing of fragrance can be reduced to a certain extent,
(7) tentering: tentering temperature is 100-120 DEG C;
(8) finished product.
Below various additive is specifically described:
Microcapsules perfumed finishing agent SCM is a kind of full capsule type microcapsule fragrance, discharges fragrance by modes such as frictions.Be applicable to the spice finish of cotton, hair, silk, fiber crops, chemical & blended fabric.Perfumed finishing agent SCM is to human non-toxic, non-stimulated to skin, without allergic reaction, easy to use, technique simple possible.The outward appearance of perfumed finishing agent SCM is oyster white paste liquid, and pH value is 7, and granularity is less than 1 μm, and active constituent content is 40%, dispersibles in water.
The Main Ingredients and Appearance of low temperature sticking agent SCJ-939 low temperature sticking agent SCJ-939 is the copolymer of isocyanates and acrylate, be applicable to cotton, hair, silk, fiber crops, chemical & blended fabric set process also can be applicable in printing technology, there is good anchor effect.SCJ-939 is easy to use for low temperature sticking agent, technique simple possible.The outward appearance of low temperature sticking agent SCJ-939 is outer wall of a city white slurry liquid, anionic, density 0.98g/cm3, can mix with any ratio with water, pH value is 6.5 ~ 7.5, good with other after-treating auxiliary compatibility, to the brute force of fabric, coloured light, feel without any harmful effect.
The specific macromolecular compound of softener SCG system.Outward appearance is pale yellow transparent liquid, water-soluble, proportion: 1.02, flash-point: >160 DEG C, active constituent content: 60%, refraction index: 1.445(25 DEG C), pH value is about 7, ionic: nonionic, can be miscible with water.This product is nontoxic, do not fire, not quick-fried, to human-body safety, non-stimulated to skin, without allergic reaction, free from environmental pollution.Soft finishing agent SCG usage is easy, with antibiotic finish, anti-uv finishing, RESIN FINISH with bathing, arrange body lotion shear stability high, not affecting color and luster and the brute force of fabric.This product can be used for the fabrics such as cotton, fiber crops, wool, silk broadcloth, terylene, nylon, cotton/wash, hair/wash.
Low-temperature adhesive take acrylate as base stock, has synthesized a kind of Environment-friendlylow-temperature low-temperature pigment printing binding agent by the method for pre-emulsification semi-continuous emulsion polymerizing.Formaldehydeless, without (APEO) carcinogenic arylamine, not containing heavy metal ion, have the good characteristic of acrylate and polyurethane concurrently, rub resistance and the fastness to washing of COAT PRINTING DYED FABRICS can be improved, and there is the performances such as good feel, antifouling and weather resisteant.The feel, the Dry Sack that solve pattern-printing and dyeing fabric are bright, the key problem such as COLOR FASTNESS and environmental protection.
Thickener FAG is acrylic acid series synthetic high polymer.Outward appearance: oyster white thick liquid is ionic: cloudy pH value: 6-7 solid content: 80% performance characteristics and purposes: thickening effect is suitable with import thickening agent PTF, but one-tenth is stuck with paste fast, separately need not add ammoniacal liquor, furnishing stability of pigment paste is good, stable storing, good with coating, adhesive compatibility, tinctorial yield is high.
Claims (5)
1. a fragrant family textile fabric, it is characterized in that, described fragrant family textile fabric is made up of following proportioning by weight: lowly melt fiber 100 parts, spices master batch 10-20 part, and microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG are appropriate.
2. one according to claim 1 fragrant family textile fabric, is characterized in that, described spices master batch is selected from least one in Rose type essence, jasmine flower essence and lavender oil three kinds of raw materials, and the diameter made is the perfume particle of 0.5mm.
3. a preparation method for fragrant family textile fabric, is characterized in that, comprise the following steps:
(1) raw material preparation: choose above-mentioned raw materials proportioning: low melt fiber 100 parts, spices master batch 10-20 part;
(2) composite spinning: first prepare cortex, first choose above-mentioned two kinds of mixing of materials even, fibrocortex is made by spinning equipment, choose the low and polymer of hydrolysis of fusing point again as sandwich layer, again spices master batch is added in process prepared by sandwich layer, form sandwich layer, finally by the above and below at sandwich layer all one machining state fibrocortex, finally form Aroma fabric crude product;
(3) Aroma fabric Final finishing: select microcapsules perfumed finishing agent SCM5-10 part, pigment printing paste 2-3 part, low-temperature adhesive SCP15-20 part, thickener FAG1-2 part, low temperature sticking agent 5-10 part and softener SCG appropriate;
(4) padding method arranges: padding method comprises and pads, dries two steps, wherein pad in process the microcapsules perfumed finishing agent SCM first adding 1/3rd, the warm water adding equivalent again, stir, with become thin pulp, add the warm water with low temperature sticking agent equivalent again, finally add low temperature sticking agent, stir, after padding and softener SCG one-bath finishing process, add microcapsules perfumed finishing agent SCM and the softener SCG of 1/3rd in dip-dye equipment;
(5) Decal arranges: the Decal of indication comprises stamp, oven dry and first finished product three step, first in material bucket, described pigment printing paste is prepared in wherein said stamp process, microcapsules perfumed finishing agent SCM, low-temperature adhesive SCP and the thickener FAG of remaining 1/3rd is added successively in the process stirred, and carry out stamp by printing equipment, first finished product;
(6) fabric is dried: be transported in drying baker by the complete Aroma fabric of arrangement and carry out drying operation, bake out temperature 50-100 DEG C, drying time 2-5 minute, dry and adopt drying baker, the interior roof of drying baker arranges humidifier, the electrical heating elements of bottom set temperature change, transport tape runs through drying baker and arranges;
(7) tentering: tentering temperature is 100-120 DEG C;
(8) finished product.
4. the preparation method of a kind of fragrant family according to claim 3 textile fabric, is characterized in that: in described step (3) " Aroma fabric Final finishing ", in the process contaminated, adopt bath raio 1:10-20, contaminates temperature 30-40 DEG C, immerged time 30 minutes.
5. the preparation method of a kind of fragrant family according to claim 3 textile fabric, it is characterized in that: in described step (4) " fabric oven dry ", bottom drying baker, row's electrical heating elements is set, wherein electricity adds element and is divided into 3 groups, the electrical heating elements of the right and left is symmetrical arranged, and the electrical heating elements quantity of middle one group is 2 times of left heating element heater or right heating element heater quantity.