CN110106707A - PVC coating modification dacron thread and its production method - Google Patents
PVC coating modification dacron thread and its production method Download PDFInfo
- Publication number
- CN110106707A CN110106707A CN201910367829.8A CN201910367829A CN110106707A CN 110106707 A CN110106707 A CN 110106707A CN 201910367829 A CN201910367829 A CN 201910367829A CN 110106707 A CN110106707 A CN 110106707A
- Authority
- CN
- China
- Prior art keywords
- polyester filament
- pvc
- coating modification
- dacron thread
- plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of PVC coating modification dacron thread, include the following steps: the styrene solution for preparing SEBS, polyester filament is placed in previous solu impregnation 2-5 hours, takes out drying and obtain the modified polyester filament in surface;PVC plastic masterbatch is put into plastic extruder, is plasticized by plastic extruder extrusion system into improving uniformity of melt, and squeeze out head;The polyester filament outer layer for passing through head of plastic extruder, and keep squeezed out PVC melt coating modified on surface the modified polyester filament in surface, obtains the PVC coating modification dacron thread after cooling down.The PVC coating modification dacron thread produced using the method for the present invention, with bright in luster colour-fast, high-tension and elastic force, Waterproofing/oilproofing antiultraviolet, it is ageing-resistant, it is wear-resistant, resistance to rot, chemicals-resistant, it is nontoxic, the advantages that surface is smooth nice and cool, long service life, can be widely applied to the products such as carpet, wall paper, beach chair, curtain, seat cushions.
Description
Technical field
The present invention relates to PVC composite terylene field of material preparation, and in particular to a kind of PVC coating modification dacron thread and its life
Production method.
Background technique
Textilene is the extraordinary textile of no shuttle machine production, using the complex yarn of special packet complex structure, i.e. PVC/PET skin
Core pattern yarn.Core uses high-strength polyester industrial long filament, and cortex is ageing-resistant, polyvinyl chloride (PVC) material of ultra-violet radiation resisting
Material.Polyester filament is extended cladding, and Jing Laguang is cooled into smooth surface, Water-proof and oil-proof, nontoxic, cooling feeling recombination line.Warp thread
Beam of a loom is made by warping machine, directly weaving networking, then final products are organized into, such as beach chair, window blind, gardening, building
And protective fence, decoration, table mat, plate mat, coaster, tablecloth, carpet, tarpaulin of agricultural etc..Terylene has good resistance to
Hot, creep resistance, fatigue durability, rub resistance and abrasiveness, electrical insulating property and chemical resistance, but the brittleness of terylene compared with
Greatly, cause to apply and be restricted.
The structure of common PVC/PET core-skin type yarn is one layer of PVC material of polyester multifilament external sheath, the disadvantage is that should
Covering thread section seems rougher since polyester multifilament part is prominent, unsightly, and since polyester multifilament is relatively soft, product
It is not well-pressed.Its solution is found as covering thread through relevant test using PVC cladding polyester monofilament, and PVC coats terylene
The fibre section of monofilament is smooth, so that manufactured textile is beautiful.But there are problems that one is difficult to overcome because of terylene list
The surface of silk is more smooth, and roughness is inadequate, and bond stress is inadequate, preferable cladding is unable to reach, to affect product quality.
Polystyrene-Polyethylene-polybutene-polystyrene (SEBS) is a kind of multiduty novel thermoplastic elastomer,
It is thermoplastic block copolymers SBS molecule unsaturated double-bond by new modified elastomer prepared by selection plus hydrogen.With excellent
Different resistance to ozone, UV resistant, corrosion resistance, wearability, flexibility and electric insulating quality, and can reuse, mechanical property
Can also preferably, it has been more than vulcanized rubber that elongation at break, which is 0~150%,.How to make full use of the good characteristic of SEBS resin with
The low cost and high performance feature of polyester fiber prepares complex yarn, expands its application field, will hold out broad prospects.
Summary of the invention
The object of the present invention is to provide a kind of production methods of PVC coating modification dacron thread, to solve background technique presence
Drawbacks described above.
The present invention realizes by the following technical solutions:
A kind of production method of PVC coating modification dacron thread, includes the following steps:
Step 1 prepares the styrene solution of SEBS, and polyester filament is placed in previous solu impregnation 2-5 hours,
Drying removal solvent after taking-up, obtains the modified polyester filament in surface;
Step 2 puts into PVC plastic masterbatch in plastic extrusion machine inlet, and PVC plastic masterbatch passes through plastic extruder
Extrusion system and be plasticized into improving uniformity of melt, and squeeze out head;
The modified polyester filament in surface is passed through head of plastic extruder by step 3, and the PVC for squeezing out step 2 is molten
Body is coated on the modified polyester filament outer layer in surface, then obtains the PVC coating modification after cooling out of cooling trough
Dacron thread.
Preferably, the mass concentration of the styrene solution of the SEBS is 10-20%.
Preferably, the fineness of the polyester filament is 35-40tex, strength 970-1000cN, elongation 18-20.
The polyester filament is selected from one of HT type polyester filament, HMLS type polyester filament and LS type polyester filament, excellent
Select HT type polyester filament.
It is further preferred that the number of impregnation is no less than 2 times in step 1.
It further include as a preferred technical solution, pigment in the PVC plastic masterbatch, it, can by adding different pigment
To obtain different colors, the pigment mainly common Masterbatch of plastics in the prior art.
It is further preferred that in the PVC plastic masterbatch, also containing the EVA for accounting for PVC plastic masterbatch quality 5%-10%.
Inventor is found surprisingly that, a small amount of EVA is added, and can be very good the elasticity and pliability that promote PVC coating modification dacron thread.
In step 3, temperature of plate is 150-170 DEG C, and extruder screw revolving speed is 30-40rpm, winding speed 110-
120rpm。
The present invention also provides the PVC coating modification dacron threads that the above method produces, successively by inner core to outer layer
Are as follows: polyester filament inner core, SEBS coat, PVC clad.
PVC coating modification dacron thread of the present invention, wherein polyester filament after SEBS is composite modified, the ultimate strength of yarn and
Elongation at break significantly improves, and solves the problems, such as that polyester filament brittleness is larger.And further improve PVC cladding polyester filament
The defect of common covering property difference, improves product quality.Present invention process method is simple, without adding extras, existing
Having can directly implement on the basis of production line.The PVC coating modification dacron thread produced using method of the invention has color fresh
Gorgeous colour-fast, high-tension, Waterproofing/oilproofing antiultraviolet is ageing-resistant, wear-resistant, and resistance to rot, chemicals-resistant is nontoxic, surface light
The advantages that cunning is nice and cool, long service life, can be widely applied to the products such as carpet, wall paper, beach chair, curtain, seat cushions.
Specific embodiment
The present invention is illustrated below by specific embodiment, but is not intended to limit the present invention.
In embodiment unless otherwise instructed, polyester filament selects HT type polyester filament, fineness 35-40tex, strength
970-1000cN, elongation 18-20.
Embodiment 1:
Entire technical process includes the following steps:
Step 1 is prepared the styrene solution for the SEBS that mass concentration is 15%, polyester filament is sufficiently placed in aforementioned molten
Impregnation 5 hours in liquid, drying removal solvent after taking-up, obtain the modified polyester filament in surface;
Step 2 by PVC plastic masterbatch, accounts in the EVA investment plastic extrusion machine inlet of PVC plastic masterbatch quality 7%
It is blended, PVC plastic masterbatch is plasticized into improving uniformity of melt by the extrusion system of plastic extruder, and squeezes out head;
Step 3, the modified polyester filament in the surface that step 1 is obtained passes through head of plastic extruder, and makes step 2
The PVC melt coating squeezed out the polyester filament outer layer modified on surface, temperature of plate are 165 ± 2 DEG C, extruder screw revolving speed
It is 115 ± 5rpm for 35 ± 5rpm, winding speed.Then the PVC coating modification is obtained after cooling out of cooling trough
Dacron thread.
Embodiment 2:
Entire technical process includes the following steps:
Step 1 is prepared the styrene solution for the SEBS that mass concentration is 10%, polyester filament is sufficiently placed in aforementioned molten
Impregnation 2 hours in liquid, drying removal solvent after taking-up, obtain the modified polyester filament in surface;
Step 2, by PVC plastic masterbatch, the EVA that accounts for PVC plastic masterbatch quality 5%, appropriate pigment Masterbatch investment plastics
It squeezes out and is blended in machine inlet, PVC plastic masterbatch is plasticized into improving uniformity of melt by the extrusion system of plastic extruder, and squeezes out
Head;
Step 3, the modified polyester filament in the surface that step 1 is obtained passes through head of plastic extruder, and makes step 2
The PVC melt coating squeezed out the polyester filament outer layer modified on surface, temperature of plate are 165 ± 2 DEG C, extruder screw revolving speed
It is 115 ± 5rpm for 35 ± 5rpm, winding speed.Then the PVC coating modification is obtained after cooling out of cooling trough
Dacron thread.
Embodiment 3:
Entire technical process includes the following steps:
Step 1 prepares the styrene solution for the SEBS that mass concentration is 15%, polyester filament is placed in previous solu
Impregnation 5 hours, drying removal solvent after taking-up obtained the modified polyester filament in surface;
PVC plastic masterbatch is put into plastic extrusion machine inlet and is blended by step 2, and PVC plastic masterbatch is squeezed by plastics
Out the extrusion system of machine and be plasticized into improving uniformity of melt, and squeeze out head;
Step 3, the modified polyester filament in the surface that step 1 is obtained passes through head of plastic extruder, and makes step 2
The PVC melt coating squeezed out the polyester filament outer layer modified on surface, temperature of plate are 165 ± 2 DEG C, extruder screw revolving speed
It is 115 ± 5rpm for 35 ± 5rpm, winding speed.Then the PVC coating modification is obtained after cooling out of cooling trough
Dacron thread.
Comparative example 1:
Entire technical process includes the following steps:
PVC plastic masterbatch is put into plastic extrusion machine inlet and is blended by step 1, and PVC plastic masterbatch is squeezed by plastics
Out the extrusion system of machine and be plasticized into improving uniformity of melt, and squeeze out head;
Polyester filament is passed through head of plastic extruder by step 3, and the PVC melt coating for squeezing out step 1 is being washed
Synthetic fibre long filament outer layer, temperature of plate are 165 ± 2 DEG C, and extruder screw revolving speed is 35 ± 5rpm, winding speed is 115 ± 5rpm.So
Afterwards out of cooling trough after cooling, the PVC cladding polyester filament is obtained.
Comparative example 2:
Entire technical process includes the following steps:
Step 1, by PVC plastic masterbatch, account for PVC plastic masterbatch quality 5%-10% EVA investment plastic extruder charging
It is blended in mouthful, PVC plastic masterbatch is plasticized into improving uniformity of melt by the extrusion system of plastic extruder, and squeezes out head;
Polyester filament is passed through head of plastic extruder by step 3, and the PVC melt coating for squeezing out step 1 is being washed
Synthetic fibre long filament outer layer, temperature of plate are 165 ± 2 DEG C, and extruder screw revolving speed is 35 ± 5rpm, winding speed is 115 ± 5rpm.So
Afterwards out of cooling trough after cooling, the PVC cladding polyester filament is obtained.
" yarn single yarn ultimate strength and elongation at break is wrapped in textile to GB/T3916-2013 according to national standards
Measurement " as defined in test method, to each embodiment and comparative example carry out Mechanics Performance Testing.Testing result is as shown in table 1.
Table 1
From testing result as can be seen that PVC coating modification dacron thread of the present invention and the PVC not being modified to polyester filament
Coating cotton thread is compared, and ultimate strength, elongation are significantly increased.In addition, adding a small amount of EVA in PVC, can be very good to mention
The elasticity of coating modification polyester filament is risen, and is added to the PVC (comparative example 2) of EVA in unmodified polyester filament outer cladding, and
It is not added with the PVC (embodiment 3) of EVA in unmodified polyester filament outer cladding, the elasticity of the two is not apparent from raising, shows EVA
There may be certain synergistic functions between SEBS, and the elasticity and pliability of material are remarkably improved when existing simultaneously.
The above shows and describes the basic principle, main features and advantages of the invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (10)
1. a kind of production method of PVC coating modification dacron thread, which comprises the steps of:
Step 1 prepares the styrene solution of SEBS, and polyester filament is placed in previous solu impregnation 2-5 hours, takes out
Drying removal solvent afterwards obtains the modified polyester filament in surface;
Step 2 puts into PVC plastic masterbatch in plastic extrusion machine inlet, and PVC plastic masterbatch is squeezed by plastic extruder
Pressure system and be plasticized into improving uniformity of melt, and squeeze out head;
The modified polyester filament in surface is passed through head of plastic extruder, and the PVC melt packet for squeezing out step 2 by step 3
The modified polyester filament outer layer in surface is overlayed on, then obtains the PVC coating modification terylene after cooling out of cooling trough
Silk.
2. the method as described in claim 1, which is characterized in that the mass concentration of the styrene solution of the SEBS is 10-
20%.
3. the method as described in claim 1, which is characterized in that the fineness of the polyester filament is 35-40tex, strength 970-
1000cN, elongation 18-20.
4. method as claimed in claim 3, which is characterized in that the polyester filament is selected from HT type polyester filament, HMLS type is washed
One of synthetic fibre long filament and LS type polyester filament.
5. the method as described in claim 1, which is characterized in that the polyester filament is HT type polyester filament.
6. the method as described in claim 1, which is characterized in that the number of impregnation is no less than 2 times in step 1.
7. the method as described in claim 1, which is characterized in that further include pigment in the PVC plastic masterbatch.
8. the method as described in claim 1, which is characterized in that in the PVC plastic masterbatch, also contain and account for PVC plastic masterbatch
The EVA of quality 5%-10%.
9. the method as described in claim 1, which is characterized in that the temperature of plate in step 3 is 150-170 DEG C, extruder spiral shell
Bar revolving speed is 30-40rpm, winding speed 110-120rpm.
10. such as the PVC coating modification dacron thread of any one of claim 1-9 the method preparation, which is characterized in that extremely by inner core
Outer layer is successively are as follows: polyester filament inner core, SEBS coat, PVC clad.