CN110083022A - A kind of preparation method of ink powder coloured silk powder - Google Patents
A kind of preparation method of ink powder coloured silk powder Download PDFInfo
- Publication number
- CN110083022A CN110083022A CN201910347827.2A CN201910347827A CN110083022A CN 110083022 A CN110083022 A CN 110083022A CN 201910347827 A CN201910347827 A CN 201910347827A CN 110083022 A CN110083022 A CN 110083022A
- Authority
- CN
- China
- Prior art keywords
- organic
- parts
- pigment
- additive
- coloured silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation methods of ink powder coloured silk powder, according to parts by weight, it is made by following raw material: 70-80 parts of polyester resin, 2-4 parts of organic black pigments, organic yellow uitramarine 2-4 parts, organic magenta pigments 3-5 parts, organic green pigment 2-3 parts, 1-2 parts of additive, the organic black pigments use carbon dust, organic yellow uitramarine uses pigment Yellow 12, organic magenta pigments are mixed to get using pigment red 122 and pigment blue 60 in 1:1 ratio, organic green pigment is mixed to get using pigment green 36 and pigment blue 60 in 1:1 ratio, the additive uses processing-type silica, processing-type silica includes following one: CAB-O-SIL TG-C321, CAB-O-SIL TG-C4 25, CAB-O-SIL TG-C493.The prepared ink powder adsorption capacity of the present invention is stronger, and has the relatively thin advantage of printing layer in the case where guaranteeing adsorption capacity.
Description
Technical field
The present invention relates to ink powder preparation field, in particular to a kind of preparation method of ink powder coloured silk powder.
Background technique
The main component of ink powder (also known as carbon dust) is not carbon, and most of is by the groups such as resin and carbon black, charge agent, magnetic powder
At and ink powder coloured silk powder is one of ink powder, by increasing various pigment in ink powder, guarantees that ink powder can carry out colour
Color, however the paper printed currently on the market by ink powder coloured silk powder is fast by time of tide fading rate, and printing layer is thicker, leads to it
More wasteful ink powder when printing.
Summary of the invention
The main purpose of the present invention is to provide a kind of preparation methods of ink powder coloured silk powder, have solved existing in the prior art
The paper printed by ink powder coloured silk powder is fast by time of tide fading rate, and printing layer is thicker, more wasteful ink when leading to its printing
The problem of powder.
To achieve the above object, the technical scheme adopted by the invention is as follows:
The invention discloses a kind of preparation methods of ink powder coloured silk powder, according to parts by weight, are made by following raw material: poly-
70-80 parts of ester resin, 2-4 parts of organic black pigments, yellow uitramarine 2-4 parts organic, magenta pigments 3-5 parts organic, You Jiqing
2-3 parts of color pigment, 1-2 parts of additive.
As preferred: the organic black pigments use carbon dust, and organic yellow uitramarine uses pigment Yellow 12, described to have
Machine magenta pigments are mixed to get using pigment red 122 and pigment blue 60 in 1:1 ratio, and organic green pigment uses pigment
Green 36 and pigment blue 60 be mixed to get in 1:1 ratio, the additive use processing-type silica, processing-type silica packet
Include following one: CAB-O-SIL TG-C321, CAB-O-SIL TG-C425, CAB-O-SIL TG-C493.
Preferably, according to parts by weight, being made by following raw material: 70 parts of polyester resin, organic black pigments 2
Part, 2 parts of organic yellow uitramarine, 3 parts of organic magenta pigments, 2 parts of organic green pigment, 1 part of additive, the additive use
CAB-O-SIL TG-C321。
Preferably, it is described according to parts by weight, be made by following raw material: 75 parts of polyester resin, organic black face
Expect 3 parts, 3 parts of organic yellow uitramarine, 4 parts of organic magenta pigments, 2.5 parts of organic green pigment, 1.5 parts of additive, it is described to add
Add agent using CAB-O-SIL TG-C425.
Preferably, it is described according to parts by weight, be made by following raw material: 80 parts of polyester resin, organic black face
Expect 4 parts, 4 parts of organic yellow uitramarine, 5 parts of organic magenta pigments, 3 parts of organic green pigment, 2 parts of additive, the additive
Using CAB-O-SIL TG-C493.
Preferably, the preparation method of the ink powder coloured silk powder, the specific steps are as follows:
(1), feedstock processing:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic green pigment and add
Agent is added to cross 1000 meshes；
(2), raw material mixes:
By the polyester resin after screening, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic cyan
Pigment and additive, which are added in blender, to be stirred；
(3), mixture fuses:
It is fused being added in fuse machine by the material for being stirred generation in step (2)；
(4), fusion material processing:
(4.1), it will be dried by the fusion material fused in step (3)；
(4.2), the fusion material after drying is added in pulverizer and is crushed；
(4.3), 1200 meshes are crossed to smashed material, obtains color powder.
Preferably, blender revolving speed is 1600r/min in the step (2).
Preferably, fuse machine temperature is 250 DEG C in the step (3).
Compared with prior art, the invention has the following beneficial effects:
By using CAB-O-SIL TG-C321 type additive, so that the bonding strength of ink powder and paper greatly increases, this
Sample allows for ink powder after the completion of printing, and when paper is by the time of tide, the fading rate of paper is slower；
It reduces ink powder so that printing layer of the ink powder in printing is thinner by certain ratio mixed raw material and is printing
When loss so that the paper that the ink powder can print is more；
From the foregoing, it will be observed that the ink powder adsorption capacity that the present invention is prepared is stronger, and has print in the case where guaranteeing adsorption capacity
The relatively thin advantage of brush layer, while the ink powder asepsis environment-protecting being prepared through the invention, have higher market prospects.
Detailed description of the invention
Fig. 1 is a kind of flow chart of the preparation method of ink powder coloured silk powder of the present invention；
Fig. 2 is 100 paper coloring degree attenuation curve figures of 1-3 of embodiment of the present invention printing；
Fig. 3 is the soaked fade curves figure of 100 paper of 1-3 of embodiment of the present invention printing.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
A kind of preparation method of ink powder coloured silk powder is made by following raw material according to parts by weight: polyester resin 70-80
Part, 2-4 parts of organic black pigments, it is yellow uitramarine 2-4 parts organic, magenta pigments 3-5 parts organic, green pigment 2-3 parts organic,
1-2 parts of additive.
The organic black pigments use carbon dust, and organic yellow uitramarine uses pigment Yellow 12, organic carmetta
Pigment is mixed to get using pigment red 122 and pigment blue 60 in 1:1 ratio, and organic green pigment uses pigment green 36 and face
Material basket 60 is mixed to get in 1:1 ratio, the additive use processing-type silica, processing-type silica include it is following it
One: CAB-O-SIL TG-C321, CAB-O-SIL TG-C425, CAB-O-SIL TG-C493.
Embodiment 1
The invention discloses a kind of preparation methods of ink powder coloured silk powder, according to parts by weight, are made by following raw material: poly-
70 parts of ester resin, 2 parts of organic black pigments, 2 parts of organic yellow uitramarine, 3 parts of organic magenta pigments, 2 parts of organic green pigment,
1 part of additive, the additive uses CAB-O-SIL TG-C321.
The preparation method of the ink powder coloured silk powder, the specific steps are as follows:
(1), feedstock processing:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic green pigment and add
Agent is added to cross 1000 meshes；
(2), raw material mixes:
By the polyester resin after screening, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic cyan
Pigment and additive, which are added in blender, to be stirred；
(3), mixture fuses:
It is fused being added in fuse machine by the material for being stirred generation in step (2)；
(4), fusion material processing:
(4.1), it will be dried by the fusion material fused in step (3)；
(4.2), the fusion material after drying is added in pulverizer and is crushed；
(4.3), 1200 meshes are crossed to smashed material, obtains color powder.
Preferably, blender revolving speed is 1600r/min in the step (2).
Preferably, fuse machine temperature is 250 DEG C in the step (3).
Embodiment 2
The invention discloses a kind of preparation methods of ink powder coloured silk powder, according to parts by weight, are made by following raw material: poly-
75 parts of ester resin, 3 parts of organic black pigments, 3 parts of organic yellow uitramarine, 4 parts of organic magenta pigments, organic green pigment 2.5
Part, 1.5 parts of additive, the additive use CAB-O-SIL TG-C425.
The preparation method of ink powder coloured silk powder, the specific steps are as follows:
(1), feedstock processing:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic green pigment and add
Agent is added to cross 1000 meshes；
(2), raw material mixes:
By the polyester resin after screening, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic cyan
Pigment and additive, which are added in blender, to be stirred；
(3), mixture fuses:
It is fused being added in fuse machine by the material for being stirred generation in step (2)；
(4), fusion material processing:
(4.1), it will be dried by the fusion material fused in step (3)；
(4.2), the fusion material after drying is added in pulverizer and is crushed；
(4.3), 1200 meshes are crossed to smashed material, obtains color powder.
Preferably, blender revolving speed is 1600r/min in the step (2).
Preferably, fuse machine temperature is 250 DEG C in the step (3).
Embodiment 3
The invention discloses a kind of preparation methods of ink powder coloured silk powder, according to parts by weight, are made by following raw material: poly-
80 parts of ester resin, 4 parts of organic black pigments, 4 parts of organic yellow uitramarine, 5 parts of organic magenta pigments, 3 parts of organic green pigment,
2 parts of additive, the additive uses CAB-O-SIL TG-C493.
The preparation method of ink powder coloured silk powder, the specific steps are as follows:
(1), feedstock processing:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic green pigment and add
Agent is added to cross 1000 meshes；
(2), raw material mixes:
By the polyester resin after screening, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic cyan
Pigment and additive, which are added in blender, to be stirred；
(3), mixture fuses:
It is fused being added in fuse machine by the material for being stirred generation in step (2)；
(4), fusion material processing:
(4.1), it will be dried by the fusion material fused in step (3)；
(4.2), the fusion material after drying is added in pulverizer and is crushed；
(4.3), 1200 meshes are crossed to smashed material, obtains color powder.
Preferably, blender revolving speed is 1600r/min in the step (2).
Preferably, fuse machine temperature is 250 DEG C in the step (3).
Example 1, embodiment 2 and embodiment 3 powder of prizing are put into duplicator and carry out copy test, and average every kind color powder is beaten
Print 100, Fig. 2 are 100 paper coloring degree attenuation curve figures that embodiment 1- embodiment 3 prints, and Fig. 3 is embodiment 1- embodiment
The soaked fade curves figure of 100 paper of 3 printings.
It obviously can be seen that the growth with print paper quantity by Fig. 2, the degree of staining of paper is gradually reduced, and embodiment
The degree of staining decrease speed of paper is significantly lower than the degree of staining decrease speed of paper in embodiment 2 and embodiment 3 in 1, bright by Fig. 3
It is aobvious to can be seen that paper degree of staining when soaked is gradually reduced, and the degree of staining decline reduction of speed degree of paper is obviously low in embodiment 1
The degree of staining decrease speed of paper in embodiment 2 and embodiment 3；
In summary, the printable number of paper of the ink powder being prepared through the invention is more, fast being faded by the time of tide
Degree is slow, and embodiment 1 is optimal selection.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. a kind of preparation method of ink powder coloured silk powder, it is characterised in that: according to parts by weight, be made by following raw material: polyester
70-80 parts of resin, 2-4 parts of organic black pigments, yellow uitramarine 2-4 parts organic, magenta pigments 3-5 parts organic, organic cyan
2-3 parts of pigment, 1-2 parts of additive.
2. a kind of preparation method of ink powder coloured silk powder according to claim 1, it is characterised in that: the organic black pigments are adopted
With carbon dust, organic yellow uitramarine uses pigment Yellow 12, and organic magenta pigments use pigment red 122 and pigment blue 60
It is mixed to get in 1:1 ratio, organic green pigment is mixed to get using pigment green 36 and pigment blue 60 in 1:1 ratio, institute
Additive is stated using processing-type silica, processing-type silica includes following one: CAB-O-SIL TG-C321, CAB-
O-SIL TG-C425、CAB-O-SIL TG-C493。
3. a kind of preparation method of ink powder coloured silk powder according to claim 1, it is characterised in that: according to parts by weight, by with
Lower raw material is made: 70 parts of polyester resin, 2 parts of organic black pigments, 2 parts of organic yellow uitramarine, organic magenta pigments 3
Part, 2 parts of organic green pigment, 1 part of additive, the additive use CAB-O-SIL TG-C321.
4. a kind of preparation method of ink powder coloured silk powder according to claim 1, it is characterised in that: according to parts by weight, by with
Lower raw material is made: 75 parts of polyester resin, 3 parts of organic black pigments, 3 parts of organic yellow uitramarine, organic magenta pigments 4
Part, 2.5 parts of organic green pigment, 1.5 parts of additive, the additive use CAB-O-SIL TG-C425.
5. a kind of preparation method of ink powder coloured silk powder according to claim 1, it is characterised in that: according to parts by weight, by with
Lower raw material is made: 80 parts of polyester resin, 4 parts of organic black pigments, 4 parts of organic yellow uitramarine, organic magenta pigments 5
Part, 3 parts of organic green pigment, 2 parts of additive, the additive use CAB-O-SIL TG-C493.
6. according to a kind of preparation method of ink powder coloured silk powder any in claim 3-5, the specific steps are as follows:
(1), feedstock processing:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, organic green pigment and additive
Cross 1000 meshes；
(2), raw material mixes:
By polyester resin, organic black pigments, organic yellow uitramarine, organic magenta pigments, the organic green pigment after screening
It is added in blender and is stirred with additive；
(3), mixture fuses:
It is fused being added in fuse machine by the material for being stirred generation in step (2)；
(4), fusion material processing:
(4.1), it will be dried by the fusion material fused in step (3)；
(4.2), the fusion material after drying is added in pulverizer and is crushed；
(4.3), 1200 meshes are crossed to smashed material, obtains ink powder coloured silk powder.
7. a kind of preparation method of ink powder coloured silk powder according to claim 6, it is characterised in that: stirring in the step (2)
Machine revolving speed is 1600r/min.
8. a kind of preparation method of ink powder coloured silk powder according to claim 6, it is characterised in that: hot melt in the step (3)
Machine temperature is 250 DEG C.