CN103105749A - Preparation method of color ink powder for printers - Google Patents
Preparation method of color ink powder for printers Download PDFInfo
- Publication number
- CN103105749A CN103105749A CN 201210524873 CN201210524873A CN103105749A CN 103105749 A CN103105749 A CN 103105749A CN 201210524873 CN201210524873 CN 201210524873 CN 201210524873 A CN201210524873 A CN 201210524873A CN 103105749 A CN103105749 A CN 103105749A
- Authority
- CN
- China
- Prior art keywords
- ink powder
- comprised
- yellow uitramarine
- following component
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of color ink powder for printers, belonging to the field of pigments. The preparation method is simple in process and is easy to operate. The color ink powder is yellow ink powder which contains a yellow pigment, wherein the yellow pigment comprises the following components in parts by weight: 20-40 parts of La2O3, 10-40 parts of MoO3, 5-10 parts of Pr6O11 and 5-10 parts of Nd1.8Sm0.2O3. The color ink powder adopts an inorganic oxide as the pigment; and the yellow ink powder has bright color and stable properties, can still give play to functions stably after long-term storage and is especially suitable for vast quick printing.
Description
Technical field
The present invention relates to a kind of printer with the preparation method of color toner, belong to the pigment field.
Background technology
The color of printing is the light of the paper reflection seen, so the three primary colors of pigment are exactly the color that can absorb RGB, is blue or green, pinkish red, yellow, and they are exactly the complementary color of RGB.As yellow uitramarine and green pigment are mixed, because yellow uitramarine absorbs blue light, therefore the green pigment absorptive red light only has green light to reflect, and Here it is, and yellow uitramarine adds that green pigment forms green reason.
The printer Yellow ink powder is one of three primary colors ink powder, and usually by solvent, colorant, surfactant, the one-tenth such as pH adjusting agent, drier and other necessary adjuvant are grouped into.Yet, the present Yellow ink powder that uses fade very fast and color relatively poor, needing to be unfavorable for long-term storage and a large amount of the printing.
Summary of the invention
The invention provides a kind of printer preparation method of color toner, this preparation method's technique is simple, easy to operate, utilize the color toner of the method preparation to adopt inorganic oxide to be pigment, gorgeous and the stable in properties of this Yellow ink powder color, long-term storage still can be stablized the performance effect, is particularly useful for a large amount of printing speeds.
A kind of printer preparation method of color toner comprises following processing step:
I. be transferred in extrusion moulding apparatus after mixing in kneading device except the raw material of silicon dioxide, carry out extrusion molding under 120 ℃ ~ 180 ℃;
II. with the coarse crushing of step I gained fragment to mean grain size 50 μ m, further pulverize as below mean grain size 5 μ m subsequently;
III. Step II gained particle is mixed with silicon dioxide, after making its mobility be at least 20%, pulverized 200 mesh sieves.
Wherein, raw material comprises yellow uitramarine, and described yellow uitramarine is comprised of following component by mass parts:
Printer of the present invention is pressed mass parts with the preferred described yellow uitramarine of preparation method of color toner, is comprised of following component:
Printer of the present invention is pressed mass parts with the preferred described yellow uitramarine of preparation method of color toner, is comprised of following component:
Printer of the present invention accounts for 0.5% ~ 5% of ink powder gross mass with the content of the preferred described yellow uitramarine of preparation method of color toner.
Printer of the present invention accounts for 2% ~ 5% of ink powder gross mass with the content of the preferred described yellow uitramarine of preparation method of color toner.
The printer of the present invention preferred described ink powder of preparation method of color toner by mass percentage, is comprised of following component:
The printer of the present invention preferred described ink powder of preparation method of color toner by mass percentage, is comprised of following component:
Printer of the present invention is water soluble resin with the preferred described resin of the preparation method of color toner.
Printer of the present invention is salicylic acid metal complex with the preferred described charge adjusting agent of the preparation method of color toner.
The invention has the beneficial effects as follows: a kind of printer preparation method of color toner, the method technique is simple, easy to operate, utilizes the color toner of the method preparation to be Yellow ink powder, and described Yellow ink powder contains yellow uitramarine, described yellow uitramarine is comprised of following component: La by mass parts
2O
3: 20 ~ 40, MoO
3: 10 ~ 40, Pr
6O
11: 5 ~ 10, Nd
1.8Sm
0.2O
3: 5 ~ 10.It is pigment that this color toner adopts inorganic oxide, the gorgeous and stable in properties of this Yellow ink powder color, and long-term storage still can be stablized the performance effect, is particularly useful for a large amount of printing speeds.
Embodiment
Following non-limiting example can make the present invention of those of ordinary skill in the art's comprehend, but does not limit the present invention in any way.
Embodiment 1
I. be transferred in extrusion moulding apparatus after mixing in kneading device except the raw material of silicon dioxide, carry out extrusion molding under 140 ℃;
Described ink powder by mass percentage, is comprised of following component:
Described yellow uitramarine by mass parts, is comprised of following component:
II. with the coarse crushing of step I gained fragment to mean grain size 20 μ m, further pulverize subsequently and be mean grain size 2 μ m;
III. Step II gained particle is mixed with silicon dioxide, after making its mobility be 20%, pulverized 200 mesh sieves.
Claims (9)
1. a printer with the preparation method of color toner, is characterized in that: comprise following processing step:
I. be transferred in extrusion moulding apparatus after mixing in kneading device except the raw material of silicon dioxide, carry out extrusion molding under 120 ℃ ~ 180 ℃;
II. with the coarse crushing of step I gained fragment to mean grain size 50 μ m, further pulverize as below mean grain size 5 μ m subsequently;
III. Step II gained particle is mixed with silicon dioxide, after making its mobility be at least 20%, pulverized 200 mesh sieves;
Wherein, raw material comprises yellow uitramarine, and described yellow uitramarine is comprised of following component by mass parts:
2. method according to claim 1 is characterized in that: described yellow uitramarine is comprised of following component by mass parts:
3. method according to claim 1 is characterized in that: described yellow uitramarine is comprised of following component by mass parts:
4. method according to claim 1, it is characterized in that: the content of described yellow uitramarine accounts for 0.5% ~ 5% of ink powder gross mass.
5. method according to claim 4, it is characterized in that: the content of described yellow uitramarine accounts for 2% ~ 5% of ink powder gross mass.
6. according to claim 1 ~ 5 described methods, it is characterized in that: described ink powder by mass percentage, is comprised of following component:
7. method according to claim 6, it is characterized in that: described ink powder by mass percentage, is comprised of following component:
8. method according to claim 6, it is characterized in that: described resin is water soluble resin.
9. method according to claim 6, it is characterized in that: described charge adjusting agent is salicylic acid metal complex.