CN110066539A - A kind of UVLED three proofings environmental protection paint and preparation method thereof - Google Patents
A kind of UVLED three proofings environmental protection paint and preparation method thereof Download PDFInfo
- Publication number
- CN110066539A CN110066539A CN201910446371.5A CN201910446371A CN110066539A CN 110066539 A CN110066539 A CN 110066539A CN 201910446371 A CN201910446371 A CN 201910446371A CN 110066539 A CN110066539 A CN 110066539A
- Authority
- CN
- China
- Prior art keywords
- proofings
- environmental protection
- uvled
- protection paint
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of UVLED three proofings environmental protection paints and preparation method thereof, including organic-silicon-modified allyl resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate, special epoxy resin, photosensitizer, auxiliary agent and filler, the present invention with LED cold light source it is coating material solidified compared to more traditional heat curing coating can effectively energy conservation 95% or more, the mercury emissions for 80% or more UV photocureable coating energy conservation and the less UV lamp of comparing, the LED light is coating material solidified can to reach Diamond Search discharge.
Description
Technical field
The present invention relates to paint, printing ink manufacture fields, and in particular to a kind of UVLED three proofings environmental protection paint and preparation method thereof.
Background technique
Three-proofing coating is a kind of coating of special formulation, for protection circuit plate and its relevant device from the erosion of environment.
Three-proofing coating has good high and low temperature resistance；Its solidify after at layer of transparent protective film, there is superior insulation, moisture-proof, anti-
The performances such as electric leakage, shockproof, dust-proof, anticorrosion, anti-aging, Inverter fed motor.
Traditional coating generally uses heat cure or UV photocuring, and energy consumption is higher, is easy to produce in solidification process toxic
Gas.
Summary of the invention
The technical problem to be solved by the present invention is to a kind of UVLED three proofings environmental protection paint and preparation method thereof, rings obtained
Paint is protected, cold light source photocuring can be used, smell is low, and environment-protecting and non-poisonous, film fineness is uniform, and levelability is good, to ground after solidification
With excellent adhesive attraction, film has high hardness, gloss and good water resistance, chemical resistance.
The present invention is achieved through the following technical solutions: a kind of UVLED three proofings environmental protection paint, including following parts by weight
Each component:
As a preferred technical solution, include each component of following parts by weight:
A kind of preparation method of UVLED three proofings environmental protection paint, including following specific steps:
1), by organic-silicon-modified allyl resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate,
Special epoxy resin is sufficiently mixed 5-8min in supersonic generator, crosses the sieve of 300~450 mesh；
2) photosensitizer, auxiliary agent and filler, is added, is stirred under the speed of 800~1800r/min in 45~55 DEG C
It is even；
3) it, is separated with filtered on buchner funnel, and is cleaned 2 times with 30 DEG C of deionized waters, dried in 80 DEG C of baking ovens, using grinding
Three proofings environmental protection paint is obtained after mill equipment grinding.
The power of supersonic generator is 1.2KW~1.5KW, time 6~12 in step 1) as a preferred technical solution,
Minute, working method is service intermittent, every work 40 seconds, suspends 50 seconds.
Three proofings environmental protection paint is ground in step 3) as a preferred technical solution, to obtain 1500~2000 mesh powders.
The beneficial effects of the present invention are: 1, environmental protection: the product can achieve Diamond Search discharge, meet increasingly harsh environmental protection
Policy；
2, energy saving: the product is using cold light source (LED light solidification) solidification, compared to 90% or more traditional heat cure energy conservation,
Compared to 80% or more UV photocuring energy conservation；
3, efficiently: the product is solidified using cold light source (LED light solidification), completes solidification within light irradiation time 8-10 seconds, greatly
It has saved the cured time greatly；
4, easy to operate: the LED cold light source cured printing ink dedicated cold light source curing apparatus of cooperation easy to operate is able to achieve
Automation.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Embodiment 1
Choose organic-silicon-modified allyl resin 20%, modified polyurethane 25%, hydroxyethyl methacrylate
15%, isoborneol an aromatic plant metioned in ancient books acrylate 18%, special epoxy resin 20%, photosensitizer 6%, auxiliary agent 1%, filler 5%,
Then by organic-silicon-modified allyl resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate, Special Ring
Oxygen resin is sufficiently mixed 5min in supersonic generator, crosses the sieve of 300 mesh；Photosensitizer, auxiliary agent and filler is added, in 45
It DEG C is stirred evenly under the speed of 800r/min；It is separated with filtered on buchner funnel, and is cleaned 2 times with 30 DEG C of deionized waters, 80
It is dried in DEG C baking oven, three proofings environmental protection paint is obtained after grinding using milling apparatus.
Embodiment 2
Choose organic-silicon-modified allyl resin 25%, modified polyurethane 30%, hydroxyethyl methacrylate
17%, isoborneol an aromatic plant metioned in ancient books acrylate 19%, special epoxy resin 20%, photosensitizer 7%, auxiliary agent 1.5%, filler
8%, then by organic-silicon-modified allyl resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate, spy
Different epoxy resin is sufficiently mixed 7min in supersonic generator, crosses the sieve of 380 mesh；Photosensitizer, auxiliary agent and filler is added,
It is stirred evenly under the speed of 1300r/min in 48 DEG C；It is separated with filtered on buchner funnel, and is cleaned 2 times with 30 DEG C of deionized waters,
It is dried in 80 DEG C of baking ovens, three proofings environmental protection paint is obtained after grinding using milling apparatus.
Embodiment 3
Choose organic-silicon-modified allyl resin 30%, modified polyurethane 35%, hydroxyethyl methacrylate 18%, isoborneol
An aromatic plant metioned in ancient books acrylate 20%, special epoxy resin 20%, photosensitizer 8%, auxiliary agent 2%, filler 10%, then by organic-silicon-modified third
Olefine resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate, special epoxy resin occur in ultrasonic wave
It is sufficiently mixed 8min in device, crosses the sieve of 450 mesh；Photosensitizer, auxiliary agent and filler is added, in 45~55 DEG C 800~
It is stirred evenly under the speed of 1800r/min；It is separated with filtered on buchner funnel, and is cleaned 2 times with 30 DEG C of deionized waters, dried at 80 DEG C
It is dried in case, three proofings environmental protection paint is obtained after grinding using milling apparatus.
In Shenzhen, SMT factory is implemented, and it is 100 DEG C of degree bakings which, which originally used heat cure three-proofing coating condition of cure,
30MIN.It is moisture-proof to be changed to LED, it is mould proof, using i.e. complete using the irradiation of 395 wave band of LED 10 seconds after brush coating process after anticorrosive coating
At solidification.Parameter after the solidification of two kinds of three-proofing coatings is as follows:
Two kinds of three-proofing coating energy consumptions compare:
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.Therefore, of the invention
Protection scope should be determined by the scope of protection defined in the claims.
Claims (5)
1. a kind of UVLED three proofings environmental protection paint, which is characterized in that each component including following parts by weight:
2. UVLED three proofings environmental protection paint as described in claim 1, which is characterized in that each component including following parts by weight:
3. a kind of preparation method of UVLED three proofings environmental protection paint, which is characterized in that including following specific steps:
1), by organic-silicon-modified allyl resin, modified polyurethane, hydroxyethyl methacrylate, isoborneol an aromatic plant metioned in ancient books acrylate, special
Epoxy resin is sufficiently mixed 5-8min in supersonic generator, crosses the sieve of 300~450 mesh；
2) photosensitizer, auxiliary agent and filler, is added, is stirred evenly under the speed of 800~1800r/min in 45~55 DEG C；
3) it, is separated with filtered on buchner funnel, and is cleaned 2 times with 30 DEG C of deionized waters, dried in 80 DEG C of baking ovens, set using grinding
Three proofings environmental protection paint is obtained after standby grinding.
4. the preparation method of UVLED three proofings environmental protection paint as claimed in claim 3, it is characterised in that: ultrasonic wave is sent out in step 1)
The power of raw device is 1.2KW~1.5KW, and the time 6~12 minutes, working method was service intermittent, every work 40 seconds, pause 50
Second.
5. the preparation method of UVLED three proofings environmental protection paint as claimed in claim 3, it is characterised in that: by three proofings in step 3)
Environmental protection paint grinds to obtain 1500~2000 mesh powders.