CN110029445A - 一种抗菌抑菌水刺无纺布 - Google Patents

一种抗菌抑菌水刺无纺布 Download PDF

Info

Publication number
CN110029445A
CN110029445A CN201910392572.1A CN201910392572A CN110029445A CN 110029445 A CN110029445 A CN 110029445A CN 201910392572 A CN201910392572 A CN 201910392572A CN 110029445 A CN110029445 A CN 110029445A
Authority
CN
China
Prior art keywords
fiber
proportion
standing grain
spunlace non
antibacterial bacteriostatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910392572.1A
Other languages
English (en)
Inventor
周国敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Yikang Antibacterial Material Technology Co Ltd
Original Assignee
Nanjing Yikang Antibacterial Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Yikang Antibacterial Material Technology Co Ltd filed Critical Nanjing Yikang Antibacterial Material Technology Co Ltd
Priority to CN201910392572.1A priority Critical patent/CN110029445A/zh
Publication of CN110029445A publication Critical patent/CN110029445A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗菌抑菌水刺无纺布，一种抗菌抑菌水刺无纺布，包括布体，所述布体由禾素纤维与配比纤维共同混合制成，所述禾素纤维与配比纤维的共混比为20：80‑40：60，所述禾素纤维与配比纤维每平方米克重为20‑80克，所述禾素纤维与配比纤维经水刺烘干，且烘干温度控制在湿区至干区为110度‑88度，所述配比纤维为天丝纤维、粘胶纤维、纯棉纤维、竹纤维、莫代尔中的任意一种。本方案采用全交叉铺网的方式制成各种厚薄及花型的水刺无纺布，具有良好的抗菌抑菌作用，同时具有良好的透气性、吸湿性、柔韧性、无毒无刺激、安全又环保，可被广泛应用在面膜、口罩、婴儿尿布、成人失禁布、卫生巾等领域。

Description

一种抗菌抑菌水刺无纺布
技术领域
本发明涉及水刺无纺布技术领域，尤其涉及一种抗菌抑菌水刺无纺布。
背景技术
自我国生物基可降解PLA/PHBV禾素纤维问世以来，彻底打破了抗菌抑菌靠后整理添加技术的束博，由于禾素纤维中含带正电荷的质子化氨基能吸附细菌并与其细胞壁上的阴离子成分结合，阻碍细胞壁的生物合成，以抑制微生物的增长，禾素纤维还能阻断细胞壁的内外物质输送，使纤维具有抗菌性能而日益受到重视，均已进入产业化阶段，制品开发和市场应用已成为影响其发展的关键因素。
但是现有技术中禾素纤维也具有耐热性差，手感僵硬，难染色，可纺性差，限制了其推广应用，特别是在纤维纺织领域发展的缺点，因此需要进行改进。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种抗菌抑菌水刺无纺布。
为了实现上述目的，本发明采用了如下技术方案：
一种抗菌抑菌水刺无纺布，包括布体，所述布体由禾素纤维与配比纤维共同混合制成。
优选地，所述禾素纤维与配比纤维的共混比为20：80-40：60。
优选地，所述禾素纤维与配比纤维每平方米克重为20-80克。
优选地，所述禾素纤维与配比纤维经水刺烘干，且烘干温度控制在湿区至干区为110度-88度。
优选地，所述配比纤维为天丝纤维、粘胶纤维、纯棉纤维、竹纤维、莫代尔中的任意一种。
相比于现有技术，本发明的有益效果在于：
本方案采用全交叉铺网的方式制成各种厚薄及花型的水刺无纺布，具有良好的抗菌抑菌作用，同时具有良好的透气性、吸湿性、柔韧性、无毒无刺激、安全又环保，可被广泛应用在面膜、口罩、婴儿尿布、成人失禁布、卫生巾等领域。
具体实施方式
一种抗菌抑菌水刺无纺布，包括布体，布体由禾素纤维与配比纤维共同混合制成。
禾素纤维与配比纤维的共混比为20：80-40：60。
禾素纤维与配比纤维每平方米克重为20-80克。
禾素纤维与配比纤维经水刺烘干，且烘干温度控制在湿区至干区为110度-88度。
配比纤维为天丝纤维、粘胶纤维、纯棉纤维、竹纤维、莫代尔中的任意一种。
上述布体可参照如下方式进行制备：
将禾素纤维与配比纤维(配比限位为天丝纤维、粘胶纤维、纯棉纤维、竹纤维、莫代尔中的任意一种)分别进行开包，各按称重比例 30％与70％，称取禾素纤维20公斤，配比纤维46.5公斤分别投入粗开松混合机，将混合纤维依次经过开松混合后进入多仓混棉箱均匀混合→精开松→TMS中间棉箱储棉→气压棉箱压紧→梳理机→交叉铺网(层数越多克重越高)→牵伸机→水刺机→烘干机→卷绕→成品。
禾素纤维与配比纤维的配比为30％与70％，这样既不影响抗菌抑菌效果又能顺利开机，同时又降低成本。
水刺工艺采用交叉铺网使两种纤维混合更加均匀，并采用双层并网使成网效果更佳。
该布体克重设计在30克/平方-35克/平方，非常适合制作面膜一类面料。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (5)

1.一种抗菌抑菌水刺无纺布，包括布体，其特征在于，所述布体由禾素纤维与配比纤维共同混合制成。
2.根据权利要求1所述的一种抗菌抑菌水刺无纺布，其特征在于，所述禾素纤维与配比纤维的共混比为20：80-40：60。
3.根据权利要求1所述的一种抗菌抑菌水刺无纺布，其特征在于，所述禾素纤维与配比纤维每平方米克重为20-80克。
4.根据权利要求1所述的一种抗菌抑菌水刺无纺布，其特征在于，所述禾素纤维与配比纤维经水刺烘干，且烘干温度控制在湿区至干区为110度-88度。
5.根据权利要求1所述的一种抗菌抑菌水刺无纺布，其特征在于，所述配比纤维为天丝纤维、粘胶纤维、纯棉纤维、竹纤维、莫代尔中的任意一种。
CN201910392572.1A 2019-05-13 2019-05-13 一种抗菌抑菌水刺无纺布 Pending CN110029445A (zh)