CN110027271A - A kind of textile fabric and preparation method thereof extremely trembled with fear under environment - Google Patents
A kind of textile fabric and preparation method thereof extremely trembled with fear under environment Download PDFInfo
- Publication number
- CN110027271A CN110027271A CN201910270001.0A CN201910270001A CN110027271A CN 110027271 A CN110027271 A CN 110027271A CN 201910270001 A CN201910270001 A CN 201910270001A CN 110027271 A CN110027271 A CN 110027271A
- Authority
- CN
- China
- Prior art keywords
- fabric
- textile fabric
- water
- extremely
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the textile fabrics and preparation method thereof under a kind of extremely cold environment, belong to field of textiles, a kind of textile fabric extremely trembled with fear under environment, including fabric main body, the fabric main body is woven into fenestral fabric by horizontal line and ordinate, and the inside of fabric main body is provided with jacquard layer close to the position of upper end, the lower end outer surface of the jacquard layer is provided with waterproof layer, and the lower end outer surface of waterproof layer is provided with flax fiber layer, the lower end outer surface of the flax fiber layer is provided with polyurethane film, and the lower end outer surface of polyurethane film is provided with hygroscopic fibre, a kind of production method for the textile fabric extremely trembled with fear under environment, the following steps are included: S1: impregnating;S2: treatment fluid is prepared;S3: processing;S4: rinsing;S5: dry.Textile fabric of the invention is suitble to use under extremely cold environment, and the production method of textile fabric is simple, and cost of manufacture is lower, is suitble to be widely used.
Description
Technical field
Textile fabric the present invention relates to field of textile, under specially a kind of extremely cold environment.
The present invention relates to field of textile, the production method of the textile fabric under specially a kind of extremely cold environment.
Background technique
Textile fabric has two class of Weft knitted fabric and warp knitted fabric, Weft knitted fabric is normal by method for weaving point
With low-elasticity terylene fibre or special-shaped dacron thread, Polyamide Yarns, cotton yarn, wool yarn etc. for raw material, using plain stitch, change plain stitch,
Rib-loop plain stitch, double rib plain stitch, figured texture weave, pile stitch weave on various weft machines, existing spinning
Knitted fabric is not suitable for using under extremely cold environment, and production method is comparatively laborious, while cost of manufacture is relatively high, is not suitable for
It is widely used.
Summary of the invention
1. technical problems to be solved
Aiming at the problems existing in the prior art, the textile fabric and preparation method thereof under a kind of extremely cold environment of the present invention,
The textile fabric is suitble to use under extremely cold environment, and the production method of textile fabric is simple, and cost of manufacture is lower, is suitble to wide
General application.
2. technical solution
To solve the above problems, the present invention adopts the following technical scheme that.
To achieve the above object, the invention provides the following technical scheme: a kind of textile fabric and its system extremely trembled with fear under environment
Make method, including fabric main body, the fabric main body is woven into fenestral fabric, and the inside of fabric main body by horizontal line and ordinate
Position close to upper end is provided with jacquard layer, and the lower end outer surface of the jacquard layer is provided with waterproof layer, and the lower end of waterproof layer
Outer surface is provided with flax fiber layer, and the lower end outer surface of the flax fiber layer is provided with polyurethane film, and polyurethane film
Lower end outer surface is provided with hygroscopic fibre.
Further, the polyurethane film, flax fiber layer are together with hygroscopic fibre interlacement weave.
Further, the horizontal line is identical as the inner materials of ordinate.
Further, the horizontal line and ordinate diameter are 05-0.8mm.
A kind of production method for the textile fabric extremely trembled with fear under environment, comprising the following steps:
S1: impregnating 4~8h for textile fabric into the water, and 20~30min of steam treated is carried out after taking-up, and water is preferably gone
Ionized water, distilled water, more preferably deionized water;
S2: nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, poly alkyl alcohol are weighed
Ethylene oxide ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water mix, and are configured to fabric
Treatment fluid;
S3: the fabric in S1 is placed in the treatment fluid in S2, impregnates 1-3h, and the temperature for the treatment of fluid is maintained at 45-60
℃;
S4: taking out and place fabric, will place fabric and be placed on progress oxygen bleaching processing in clear water, and finally utilize ultrasonic cleaning,
Oxygen bleaching processing is specially to be immersed in textile fabric in 75 DEG C of the solution containing 12% hydrogen peroxide to handle 45 minutes;
S5: textile fabric is taken out, 10~20min of radiation treatment, is then dried at room temperature under ultraviolet light.
Further, the nano-antibacterial powder in the S2, nanometer titanium dioxide titanium valve, durable draining polymer, epoxy chlorine
Propane, fatty alcohol polyoxyethylene ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water ingredient ratio
Example is 2.1:1.3:0.6:0.5:3.1:2.2:1.7:4:0.3:22.
Further, steam temperature is 90~100 DEG C in the S1.
Further, textile fabric be cotton, hair, fiber crops, silk, terylene, viscose glue, polyester or acrylic fibers in any one or it is several
Kind.
3. beneficial effect
Compared with prior art, the beneficial effects of the present invention are: textile fabric of the invention is suitble to use under extremely cold environment,
And the production method of textile fabric is simple, and cost of manufacture is lower, is suitble to be widely used.
Detailed description of the invention
Fig. 1 is structure chart of the invention;
Fig. 2 is the view that horizontal line of the invention is combined with ordinate;
Fig. 3 is flow chart of the invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description;Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments, is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
In the description of the present invention, it should be noted that the instruction such as term " on ", "lower", "inner", "outside", " top/bottom end "
Orientation or positional relationship be based on the orientation or positional relationship shown in the drawings, be merely for convenience of description the present invention and simplification retouch
It states, rather than the device or element of indication or suggestion meaning must have a particular orientation, be constructed and operated in a specific orientation,
Therefore it is not considered as limiting the invention.In addition, term " first ", " second " are used for description purposes only, and cannot understand
For indication or suggestion relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " installation " " is set
Be equipped with ", " be arranged/connect ", " connection " etc., shall be understood in a broad sense, such as " connection ", may be a fixed connection, be also possible to removable
Connection is unloaded, or is integrally connected;It can be mechanical connection, be also possible to be electrically connected;It can be directly connected, it can also be in
Between medium be indirectly connected, can be the connection inside two elements.It for the ordinary skill in the art, can be specific
Situation understands the concrete meaning of above-mentioned term in the present invention.
Embodiment one
The present invention provides a kind of technical solution referring to FIG. 1-2: a kind of textile fabric and its production side extremely to tremble with fear under environment
Method, including fabric main body 1, fabric main body 1 is woven into fenestral fabric by horizontal line 7 and ordinate 8, and the inside of fabric main body 1 is leaned on
The position of nearly upper end is provided with jacquard layer 2, and the lower end outer surface of jacquard layer 2 is provided with waterproof layer 3, and outside the lower end of waterproof layer 3
Surface is provided with flax fiber layer 5, and the lower end outer surface of flax fiber layer 5 is provided with polyurethane film 4, and under polyurethane film 4
End outer surface is provided with hygroscopic fibre 6.
Referring to Fig. 3, a kind of production method of the textile fabric under extremely cold environment, comprising the following steps:
S1: impregnating 4~8h for textile fabric into the water, and 20~30min of steam treated is carried out after taking-up, and steam temperature is
90~100 DEG C, water is preferably deionized water, distilled water, more preferably deionized water;
S2: nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, poly alkyl alcohol are weighed
Ethylene oxide ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water mix, and are configured to fabric
Treatment fluid, nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, aliphatic alcohol polyethenoxy
Ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water component ratio be 2.1:1.3:0.6:
0.5:3.1:2.2:1.7:4:0.3:22;
S3: the fabric in S1 is placed in the treatment fluid in S2, impregnates 1-3h, and the temperature for the treatment of fluid is maintained at 45-60
℃;
S4: taking out and place fabric, will place fabric and be placed on progress oxygen bleaching processing in clear water, and finally utilize ultrasonic cleaning,
Oxygen bleaching processing is specially to be immersed in textile fabric in 75 DEG C of the solution containing 12% hydrogen peroxide to handle 45 minutes;
S5: textile fabric is taken out, 10~20min of radiation treatment, is then dried at room temperature under ultraviolet light.
Embodiment two
Referring to Fig. 3, a kind of production method of the textile fabric under extremely cold environment, comprising the following steps:
S1: impregnating 4~8h for textile fabric into the water, and 20~30min of steam treated is carried out after taking-up, and steam temperature is
90~100 DEG C, water is preferably deionized water, distilled water, more preferably deionized water;
S2: nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, poly alkyl alcohol are weighed
Ethylene oxide ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water mix, and are configured to fabric
Treatment fluid, nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, aliphatic alcohol polyethenoxy
Ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water component ratio be 2.1:1.3:0.6:
0.5:3.1:2.2:1.7:4:0.3:1.2;
S3: the fabric in S1 is placed in the treatment fluid in S2, impregnates 1-3h, and the temperature for the treatment of fluid is maintained at 45-60
℃;
S4: taking out and place fabric, will place fabric and be placed on progress oxygen bleaching processing in clear water, and finally utilize ultrasonic cleaning,
Oxygen bleaching processing is specially to be immersed in textile fabric in 75 DEG C of the solution containing 12% hydrogen peroxide to handle 45 minutes;
S5: textile fabric is taken out, 10~20min of radiation treatment, is then dried at room temperature under ultraviolet light.
By showing that the fabric that embodiment one is prepared is than the face that embodiment two is prepared to the comparison of above-mentioned two groups of embodiments
The cold resistance of material is more preferable, and textile fabric of the invention is suitble to use under extremely cold environment, and the production method of textile fabric is simple,
Cost of manufacture is lower, is suitble to be widely used.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. the textile fabric under a kind of extremely cold environment, including fabric main body (1), it is characterised in that: the fabric main body (1) is by cross
Line (7) and ordinate (8) are woven into fenestral fabric, and the inside of fabric main body (1) is provided with jacquard layer close to the position of upper end
(2), the lower end outer surface of the jacquard layer (2) is provided with waterproof layer (3), and the lower end outer surface of waterproof layer (3) is provided with Asia
The lower end outer surface of flaxen fiber layer (5), the flax fiber layer (5) is provided with polyurethane film (4), and under polyurethane film (4)
End outer surface is provided with hygroscopic fibre (6).
2. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as described in claim 1, it is characterised in that: institute
Polyurethane film (4), flax fiber layer (5) are stated together with hygroscopic fibre (6) interlacement weave.
3. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as described in claim 1, it is characterised in that: institute
It is identical as the inner materials of ordinate (8) to state horizontal line (7).
4. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as described in claim 1, it is characterised in that: institute
It states horizontal line (7) and ordinate (8) diameter is 05-0.8mm.
5. according to a kind of production method for the textile fabric extremely trembled with fear under environment as described in claim 1, which is characterized in that including
Following steps:
S1: impregnating 4~8h for textile fabric into the water, 20~30min of steam treated is carried out after taking-up, water is preferably deionization
Water, distilled water, more preferably deionized water;
S2: nano-antibacterial powder, nanometer titanium dioxide titanium valve, durable draining polymer, epoxychloropropane, fatty alcohol polyoxy second are weighed
Alkene ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water mix, and are configured to the place of fabric
Manage liquid;
S3: the fabric in S1 is placed in the treatment fluid in S2, impregnates 1-3h, and the temperature for the treatment of fluid is maintained at 45-60 DEG C;
S4: taking out and place fabric, will place fabric and is placed on progress oxygen bleaching processing in clear water, finally utilizes ultrasonic cleaning, oxygen bleaching
Processing is specially to be immersed in textile fabric in 75 DEG C of the solution containing 12% hydrogen peroxide to handle 45 minutes;
S5: textile fabric is taken out, 10~20min of radiation treatment, is then dried at room temperature under ultraviolet light.
6. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as claimed in claim 5, it is characterised in that: institute
State nano-antibacterial powder, nanometer titanium dioxide titanium valve, the durable draining polymer, epoxychloropropane, aliphatic alcohol polyethenoxy in S2
Ether, amido silicon oil, water soluble polyurethane resin, ammonification epoxy resin, lactic acid and water component ratio be 2.1:1.3:0.6:
0.5:3.1:2.2:1.7:4:0.3:22。
7. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as claimed in claim 5, it is characterised in that: institute
Stating steam temperature in S1 is 90~100 DEG C.
8. according to a kind of textile fabric and preparation method thereof extremely trembled with fear under environment as claimed in claim 5, it is characterised in that: spin
Knitted fabric is any one or a few in cotton, hair, fiber crops, silk, terylene, viscose glue, polyester or acrylic fibers.