CN109986055A - 砂芯铸造低压成型工艺 - Google Patents
砂芯铸造低压成型工艺 Download PDFInfo
- Publication number
- CN109986055A CN109986055A CN201711482929.2A CN201711482929A CN109986055A CN 109986055 A CN109986055 A CN 109986055A CN 201711482929 A CN201711482929 A CN 201711482929A CN 109986055 A CN109986055 A CN 109986055A
- Authority
- CN
- China
- Prior art keywords
- casting
- mold
- low pressure
- coating
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种砂芯铸造低压成型工艺，包括以下工艺过程：1)模具清理，用钢丝轮对模具表面进行打磨清理，使模具表面光滑，铸件脱模容易脱开；2)预热，模具温度一般控制在95‑105℃；3)喷专用涂料，对模具内腔表面用喷枪涂上一层专用的耐热涂料，以起到隔热和保护模具的作用。涂料喷好后还需对模具进行加热烘干，以去除涂料中的水分；4)将预先制作好的砂芯按底座定位装入低压铸造钢模腔内，并清理干净模腔内周边浮砂；5)将低压铸件的浇注温度控制在700‑720℃之间，通过降低铸件在浇注后凝固过程中不同壁厚处的温度差。本发明通过通过小批量的生产试制，明显提高了壁厚不均匀铸件的产品质量，在铸件进行探伤过程中发现铸造凝固缺陷率降低，提高了铸件的成品率。
Description
技术领域
本发明涉及一种浇注工艺，特别是涉及砂芯铸造低压成型工艺。
背景技术
现有技术中，铝合金铸件的浇注一般控制在720℃至725℃之间。这样的浇注温度，一般在铸件的壁厚均匀的情况下比较好。在铸件壁厚相差过大时，则厚大的部分明显产生铸造缺陷，说明低压浇注时的补缩情况不好。
发明内容
本发明的目的就是为克服上述现有技术存在的缺陷和不足，而提供一种砂芯铸造低压成型工艺。
采用的技术方案是：
砂芯铸造低压成型工艺，其特征在于包括以下工艺过程：
1、模具清理
用钢丝轮对模具表面进行打磨清理，使模具表面光滑，铸件脱模容易脱开。
2、预热
用液化气火焰对模具进行预热升温，模具温度一般控制在100℃左右。
3、喷专用涂料
达到温度后，对模具内腔表面用喷枪涂上一层专用的耐热涂料，以起到隔热和保护模具的作用。涂料喷好后还需对模具进行加热烘干，以去除涂料中的水分。
4、将预先制作好的砂芯按底座定位装入低压铸造钢模腔内，并清理干净模腔内周边浮砂。
5、低压铸造机需按经验或公式预先设置好相关的工艺参数，并制定工作程序。模具在低注机平台做好以上准备工作后即可进行铸造生产。将低压铸件的浇注温度由原工艺的720℃至725℃控制在700-720℃之间，并进行了小批量的生产试制。通过降低铸件在浇注后凝固过程中不同壁厚处的温度差，减小温度场分布不均匀对铸件收缩的影响。
本发明与现有技术相比具有以下优点：
通过小批量的生产试制，明显提高了壁厚不均匀铸件的产品质量，在铸件进行探伤过程中发现铸造凝固缺陷率降低，提高了铸件的成品率。
具体实施方式
砂芯铸造低压成型工艺，具体包括以下工艺过程：
1、模具清理
用钢丝轮对模具表面进行打磨清理，使模具表面光滑，铸件脱模容易脱开；
2、预热
用液化气火焰对模具进行预热升温，模具温度一般控制在95-105℃；
3、喷专用涂料
达到温度后，对模具内腔表面用喷枪涂上一层专用的耐热涂料，以起到隔热和保护模具的作用。涂料喷好后还需对模具进行加热烘干，以去除涂料中的水分；
4、将预先制作好的砂芯按底座定位装入低压铸造钢模腔内，并清理干净模腔内周边浮砂。
5、将低压铸件的浇注温度控制在700-720℃之间，通过降低铸件在浇注后凝固过程中不同壁厚处的温度差。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.砂芯铸造低压成型工艺，其特征在于包括以下工艺过程：
1)模具清理，用钢丝轮对模具表面进行打磨清理，使模具表面光滑，铸件脱模容易脱开；2)预热，用液化气火焰对模具进行预热升温，模具温度一般控制在95-105℃；3)喷专用涂料，达到温度后，对模具内腔表面用喷枪涂上一层专用的耐热涂料，以起到隔热和保护模具的作用。
2.涂料喷好后还需对模具进行加热烘干，以去除涂料中的水分；4)将预先制作好的砂芯按底座定位装入低压铸造钢模腔内，并清理干净模腔内周边浮砂；5)将低压铸件的浇注温度控制在700-720℃之间，通过降低铸件在浇注后凝固过程中不同壁厚处的温度差。