CN109971425A - A kind of environment protection snow-dissolved agent and preparation method - Google Patents
A kind of environment protection snow-dissolved agent and preparation method Download PDFInfo
- Publication number
- CN109971425A CN109971425A CN201711464969.4A CN201711464969A CN109971425A CN 109971425 A CN109971425 A CN 109971425A CN 201711464969 A CN201711464969 A CN 201711464969A CN 109971425 A CN109971425 A CN 109971425A
- Authority
- CN
- China
- Prior art keywords
- parts
- humic acid
- peat
- ammonium acetate
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of snow melt product agent described in one of claim 1-2, it is characterized in that: this method comprises the following steps: (1) collecting product liquid therein after first reacting corn stover at 70-80 DEG C with homemade catalyst, solid product, which stays, to use it for anything else;(2) it after again being mixed peat and self-control oxidant, is reacted under microwave condition, microwave power 200-300W, reaction time 10-30min, after reaction isolated Peat Humic Acid.(3) 25 parts of stalk reactant and the mixing of 15 parts of Peat Humic Acid are measured, start agitating device, control revolving speed is that 1000 ~ 1500 turns/min is advisable, then the ammonium acetate for calculating weighing is added slowly in mixer to be stirred well to and is thoroughly uniformly dispersed, excess water is added after mentioned component stirs into mixer, continue to be dispersed with stirring to solution to pack after finished product is dry, dehydration in uniform liquid.
Description
Technical field
The present invention relates to a kind of environment protection snow-dissolved agent and preparation methods.
Belong to the deicing salt product of a kind of urban road, highway, such deicing salt is substitution highway deicing
A kind of novel environment-friendly product of agent (sodium chloride) and exploitation, to the concrete and corrosivity in highway infrastructures
It is small, substantially soil and water source are not polluted, while there is good water solubility, fusing point is low, it is biodegradable the advantages that.
Background technique: deicing salt also known as changes cryosel, road antifreezing agent, is mainly used for winter airport, highway, square, parking
Field, railway, avenue etc. play snow removing and antifreeze effect, and the deicing salt type of China's exploitation at present is more, are divided by states of matter
Solid and liquid;It is divided into the mixing of inorganic matter and inorganic matter and organic matter, by composition with the mixture of inorganic matter and organic matter
It is most;Can also be by different purpose classifications, the quality for being generally used for urban road is lower, and the quality for bridge airport and other places is wanted
Ask higher, but its quality all has to comply with standard.Country's deicing salt volume of production and marketing data are counted roughly by the yield of calcium chloride at present
It calculates.Domestic deicing salt annual output is at 1,000,000 tons or so, and export volume is 1/3.Organic deicing salt does not corrode work to infrastructure
With, due to selling at exorbitant prices, now only applied on a small quantity in places such as airport, golf courses;Snow melt is answered in city, highway
With wider still chloride salt deicing salt.Villaumite Snow Agent ingredient will lead to greening and planted based on the salts such as sodium chloride, calcium chloride
It by mortality, causes highway, bridge concrete road surface heavy corrosion to destroy, can also pollute rivers, underground water, destroy ecological ring
Border.Aiming at the problem that current deicing salt, need to develop that cheap and easy to get, snow melt effect is good, low-corrosiveness, pollution-free, non-corrosive
New Kind of Solvent of Snow-melted.
Summary of the invention:
The object of the present invention is to provide a kind of New Kind of Solvent of Snow-melted and preparation method thereof of environmental protection.
Above-mentioned purpose is realized by following technical scheme: environment protection snow-dissolved agent, and composition includes: by following raw materials by weight
Measure number composition: 20~30 parts of Corn Stalk Decomposition object, 15~25 parts of Peat Humic Acid, 10-20 parts of ammonium acetate, remaining
Amount is water.The present invention is equipped with ammonium acetate etc. using Corn Stalk Decomposition object, Peat Humic Acid as main component.
The New Kind of Solvent of Snow-melted of road, the expressway etc. is made of in parts by weight following raw materials: 20 parts of corn
Straw decomposing object, 15 parts of Peat Humic Acid, 20 parts of ammonium acetate, surplus are water.
The New Kind of Solvent of Snow-melted of the road, expressway, is made of in parts by weight following raw materials: 25 parts of corn stalk
Stalk decomposition product, 20 parts of Peat Humic Acid, 15 parts of ammonium acetate, surplus are water.
The New Kind of Solvent of Snow-melted of the road, expressway, is made of in parts by weight following raw materials: 30 parts of corn stalk
Stalk decomposition product, 15 parts of Peat Humic Acid, 10 parts of ammonium acetate, surplus are water.
The road deicing salt preparation method of the road, high speed, this method comprises the following steps: (1) first by corn stalk
Stalk collects product liquid therein after reacting at 70-80 DEG C with homemade catalyst, solid product, which stays, to use it for anything else;(2) again will
After peat and self-control oxidant are mixed, reacted under microwave condition, microwave power 200-300W, reaction time 10-
30min, after reaction isolated Peat Humic Acid.(3) 25 parts of stalk reactant and 15 parts of Peat Humic Acid are measured
Agitating device is started in mixing, and control revolving speed is that 1000 ~ 1500 turns/min is advisable, and then will calculate the ammonium acetate weighed and slowly adds
Enter to be stirred well into mixer and thoroughly be uniformly dispersed, excess water is added after mentioned component stirs to mixing
In device, continue to be dispersed with stirring to solution to pack after finished product is dry, dehydration in uniform liquid.
Beneficial effects of the present invention:
This work uses Straw decomposing object and Peat Humic Acid, reduces theoretical, anti-corrosion of metal theory as foundation using freezing point, obtains one
Efficient, pollution-free, the moderate environment protection snow-dissolved agent of kind, makes stalk turn waste into wealth, has not only reached the utilization of biomass resource, but also
Reduce the pollution to environment.
The present invention is to use Straw decomposing object and Peat Humic Acid for primary raw material, and a kind of snow melt of environment-friendly high-efficiency has been made
Product has excellent snow melt and environment-friendly type.By spray pattern operation, good snow melt effect can reach.
The raw material composition of deicing salt of the present invention is safe and reliable, has many advantages, such as that environmentally friendly, degradable, dosage is small.
Specific embodiment:
Embodiment 1: a kind of highway, expressway snow melt product, composition includes: to be made of in parts by weight following raw materials: 20
The Corn Stalk Decomposition object of part, 15 parts of Peat Humic Acid, 20 parts of ammonium acetate, surplus are water.
Embodiment 2: according to the novel environment friendly deicing salt of road described in embodiment 1, in parts by weight by following raw materials
Composition: 25 parts of Corn Stalk Decomposition object, 20 parts of Peat Humic Acid, 15 parts of ammonium acetate, surplus are water.
Embodiment 3: according to the novel environment friendly deicing salt of road product described in embodiment 1, by weight by following raw materials
Number composition: 30 parts of Corn Stalk Decomposition object, 15 parts of Peat Humic Acid, 10 parts of ammonium acetate, surplus are water.
Production method is according to the following steps: (1) receiving after first reacting corn stover at 70-80 DEG C with homemade catalyst
Collect product liquid therein, solid product, which stays, to use it for anything else;(2) after again being mixed peat and self-control oxidant, in micro-strip
It is reacted under part, microwave power 200-300W, reaction time 10-30min, after reaction isolated Peat Humic Acid.
(3) 25 parts of stalk reactant and the mixing of 15 parts of Peat Humic Acid are measured, starts agitating device, control revolving speed is 1000 ~
1500 turns/min is advisable, and then will calculate the ammonium acetate weighed and be added slowly in mixer to be stirred well to and thoroughly disperse
It is even, excess water is added after mentioned component stirs into mixer, continues to be dispersed with stirring to solution in uniform liquid
Body is packed after finished product is dry, dehydration.
Claims (5)
1. a kind of environment protection snow-dissolved agent, composition includes: to be made of in parts by weight following raw materials: 20~30 parts of corn stover point
Solving object object, 15~25 parts of Peat Humic Acid, 10-20 parts of ammonium acetate, surplus is water.
2. the present invention is equipped with ammonium acetate etc. using Corn Stalk Decomposition object, Peat Humic Acid as main component.
3. environment protection snow-dissolved agent product according to claim 1, it is characterized in that: being made of in parts by weight following raw materials: 25
Corn Stalk Decomposition object, 15 parts of the Peat Humic Acid, 10 parts of ammonium acetate of part, surplus is water.
4. the preparation method of snow melt product agent described in a kind of one of claim 1-2, it is characterized in that: this method includes as follows
Step: (1) collecting product liquid therein after first reacting corn stover at 70-80 DEG C with homemade catalyst, solid produces
Object, which stays, to use it for anything else;(2) it after again being mixed peat and self-control oxidant, is reacted under microwave condition, microwave power
200-300W, reaction time 10-30min, after reaction isolated Peat Humic Acid.
25 parts of stalk reactant and the mixing of 15 parts of Peat Humic Acid 5.(3) are measured, agitating device is started, control revolving speed is
1000 ~ 1500 turns/min is advisable, and then will calculate the ammonium acetate weighed and be added slowly in mixer to be stirred well to and thoroughly divide
It dissipates uniformly, excess water is added after mentioned component stirs into mixer, continue to be dispersed with stirring to solution in equal
Even liquid is packed after finished product is dry, dehydration.