CN109971117A - A kind of flame-retardant glass fibre reinforced plastic materals - Google Patents
A kind of flame-retardant glass fibre reinforced plastic materals Download PDFInfo
- Publication number
- CN109971117A CN109971117A CN201711467289.8A CN201711467289A CN109971117A CN 109971117 A CN109971117 A CN 109971117A CN 201711467289 A CN201711467289 A CN 201711467289A CN 109971117 A CN109971117 A CN 109971117A
- Authority
- CN
- China
- Prior art keywords
- parts
- reinforced plastic
- flame
- materals
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of flame-retardant glass fibre reinforced plastic materals, and according to parts by weight, it includes, texturized glass yarn 26-39 parts of (1);(2) silicon carbide 13-26 parts;(3) epoxy modified phenolic resin 18-30 parts;(4) unsaturated polyester resin 12-19 parts;(5) methyltriethoxysilane 7-16 parts;(6) acrylic glycidol ether 2-5 parts;(7) fire retardant 3-6 parts;(8) titanium dioxide 4-9 parts;(9) magnesia 2-6 parts.The present invention is had excellent performance, good flame retardation effect, easy processing.
Description
Technical field
The invention belongs to glass fiber reinforced plastics product related fieldss, and in particular to a kind of glass-reinforced plastic material.
Background technique
Glass reinforced plastic is one kind of composite material, and glass-reinforced plastic material is because of its unique performance advantage, in aerospace, railway
Railway, decorative architecture, family's living furniture, advertising display, process gift, building materials bathroom, yacht moor a boat, sport material, sanitation project
Etc. be widely applied in related more than ten a industries, and praised deeply, become the demand favorite of new era businessman in materials industry.Glass
Glass steel part is significantly better than conventional articles on performance, purposes, service life attribute also different from traditional material product.Its easy moulding,
The characteristics of customizable, color is arbitrarily deployed, the deep favor by businessman and sellers, occupies increasing market score, prospect
It is wide.
Existing glass-reinforced plastic material, material property is general, and generally existing raw material ratio is complicated, and processing cost is high, fire-retardant
The problems such as property is poor, does not meet actual production requirement.
Summary of the invention
Goal of the invention: purpose of the invention is to overcome the shortcomings in the prior art, provides one kind and has excellent performance, fire-retardant
Effect is good, the glass fiber reinforced plastics composite material of easy processing.
Technical solution: in order to solve the above-mentioned technical problem, a kind of flame-retardant glass fibre reinforced plastic materals, according to parts by weight, it includes,
(1) texturized glass yarn 26-39 parts;
(2) silicon carbide 13-26 parts;
(3) epoxy modified phenolic resin 18-30 parts;
(4) unsaturated polyester resin 12-19 parts;
(5) methyltriethoxysilane 7-16 parts;
(6) acrylic glycidol ether 2-5 parts;
(7) fire retardant 3-6 parts;
(8) titanium dioxide 4-9 parts;
(9) magnesia 2-6 parts.
Further, a kind of flame-retardant glass fibre reinforced plastic materals, according to parts by weight, it include: 31 parts of texturized glass yarn,
17 parts of silicon carbide, 21 parts of epoxy modified phenolic resin, 15 parts of unsaturated polyester resin, 10 parts of methyltriethoxysilane, propylene
2.6 parts of base glycidol ether, 4 parts of fire retardant, 6 parts of titanium dioxide, 3.1 parts of magnesia.
The utility model has the advantages that compared with prior art, the present invention its remarkable advantage is: the present invention by accurate raw material proportioning,
It is had excellent performance finished-product material, and is matched simply, using fire retardant, the anti-flammability of product can be improved, this product uses the longevity
Life length, easy processing meet actual production requirement.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated.
Embodiment 1: a kind of flame-retardant glass fibre reinforced plastic materals, according to parts by weight, it includes, 33 parts of (1) texturized glass yarn;
(2) 22 parts of silicon carbide;(3) 25 parts of epoxy modified phenolic resin;(4) 13 parts of unsaturated polyester resin;(5) methyltriethoxy silane
8 parts of alkane;(6) 3.2 parts of acrylic glycidol ether;(7) 5.1 parts of fire retardant;(8) 7 parts of titanium dioxide;(9) 2.6 parts of magnesia.
Embodiment 2: a kind of flame-retardant glass fibre reinforced plastic materals, according to parts by weight, it includes, 31 parts of (1) texturized glass yarn;
(2) 17 parts of silicon carbide;(3) 21 parts of epoxy modified phenolic resin;(4) 15 parts of unsaturated polyester resin;(5) methyltriethoxy silane
10 parts of alkane;(6) 2.6 parts of acrylic glycidol ether;(7) 4 parts of fire retardant;(8) 6 parts of titanium dioxide;(9) 3.1 parts of magnesia.
The present invention has excellent performance finished-product material by accurate raw material proportioning, and match it is simple, using fire retardant,
The anti-flammability of product, this product long service life can be improved, easy processing meets actual production requirement.
Claims (2)
1. a kind of flame-retardant glass fibre reinforced plastic materals, it is characterised in that: according to parts by weight, it includes,
(1) texturized glass yarn 26-39 parts;
(2) silicon carbide 13-26 parts;
(3) epoxy modified phenolic resin 18-30 parts;
(4) unsaturated polyester resin 12-19 parts;
(5) methyltriethoxysilane 7-16 parts;
(6) acrylic glycidol ether 2-5 parts;
(7) fire retardant 3-6 parts;
(8) titanium dioxide 4-9 parts;
(9) magnesia 2-6 parts.
2. a kind of flame-retardant glass fibre reinforced plastic materals according to claim 1, which is characterized in that according to parts by weight, it includes: glass
31 parts of glass fibre deformation yarn, 17 parts of silicon carbide, 21 parts of epoxy modified phenolic resin, 15 parts of unsaturated polyester resin, three second of methyl
10 parts of oxysilane, 2.6 parts of acrylic glycidol ether, 4 parts of fire retardant, 6 parts of titanium dioxide, 3.1 parts of magnesia.