CN103223755A - Plastic glass cardboard capable of being sawn and drilled with impact resistance - Google Patents
Plastic glass cardboard capable of being sawn and drilled with impact resistance Download PDFInfo
- Publication number
- CN103223755A CN103223755A CN2012100282808A CN201210028280A CN103223755A CN 103223755 A CN103223755 A CN 103223755A CN 2012100282808 A CN2012100282808 A CN 2012100282808A CN 201210028280 A CN201210028280 A CN 201210028280A CN 103223755 A CN103223755 A CN 103223755A
- Authority
- CN
- China
- Prior art keywords
- glass
- make
- plastics
- glass cloth
- glass plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a plastic glass plate, which is composed of a plastic bond glass cloth. The glass cloth has elasticity, the pulling force of the glass fiber is multiple times of that of the metal fiber, the pull resistance of the glass fiber by being born with impact force can compete with that of steel plate. The glass cloth obstructs ultraviolet ray, the encroachment on plastic by ultraviolet ray can be eliminated, an acid-base resistant plastic is selected, and thereby the plastic glass plate can be used under acid-base occasion. The proportion of the difficultly broken plastic glass plate is about 2g/cm<3>, the weight of the plastic glass plate with specification of 1 millimeter of thickness and 100 m<2> of area is 200kg; the cost of the glass cloth with thickness of 0.2 millimeters is less than 1 Yuan/m<2>, so that the cost of the plastic glass plate is low and the economic benefit is high; the plastic glass plate used for replacing metal to manufacture compartments, cabins, furniture, large workshops and exterior wall decoration has advantages. If the plastic glass plate is produced to difficultly broken foam plastic glass plate, the economic benefit can be increased by several times.
Description
Glass is not afraid of soda acid worm ant, but is afraid of bump, one bump promptly broken; If there is not bump, it's thousand pasts the life-span, makes the metallic plate self-induction be not so good as.
Present technique propose " wide surpass 10 meters be as thin as 0.3 millimeter substitute metal can saw hole do not rot mould the glass cardboard ", can solve above-mentioned glass fearness bump problem.
" wide surpass 10 meters be as thin as 0.3 millimeter substitute that metal can saw that boring do not rot mould the glass cardboard ", its beneficial effect is, the replacement metal material extends working time, weight reduction reduces cost.
" wide surpass 10 meters be as thin as 0.3 millimeter substitute that metal can saw that boring do not rot mould the glass cardboard ", the technical scheme that its technical solution problem is adopted is, form by the bonding glass cloth of plastics (1) (2), coloured or colourless plastics are heated into liquation as adhesive, make glass cloth pass through the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make after the cooling and mould glass cardboard (3), widely surpass 10 meters and be as thin as 0.3 millimeter and substitute metal and can saw the glass cardboard of moulding that do not rot of boring and moved thereby make; It is manufactured with 3 kinds:
1), make a glass cloth by the plastics liquation, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics with facility, make after the cooling be as thin as 0.3 millimeter substitute metal can saw hole do not rot mould glass paper;
2), make a glass cloth by the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make the glass cloth of several the molten slurries of parcel plastics overlapping, paste into and thickly surpass 10 meters to 2 mm wides and mould the glass plate, make after the cooling wide surpass 10 meters thick to 2 millimeters substitute that metal can saw that boring do not rot mould the glass plate;
3), make a glass cloth by the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make the glass cloth of the molten slurry of polylith parcel plastics overlapping, paste into and thickly surpass 10 meters and mould the glass plate to several centimeters wide, make after the cooling wide surpass 10 meters thick to several centimeters substitute metal can saw hole do not rot mould the glass plate.As Fig. 1
The glass plate is moulded in existing combination principle introduction:
It is reported that the pulling force of glass fibre is several times of metallic fiber pulling force; Plastics are shock-resistant not strong, destroyed by ultraviolet ray easily.
Present technique organically combines glass fibre and two kinds of materials of plastics.Make product be rich in brand-new advantage.
The glass thread that glass cloth is made up of many glass fibres is weaved into, so the glass cloth high resilience.When glass plate was subjected to impacting, plastics were passed to glass cloth with impulsive force, and whippy glass cloth just absorbs impulsive force.And along with the glass cloth number of plies increases, the impulsive force that glass plate bears constantly strengthens, until can with the steel plate trial of strength.
Because the pulling force of glass fibre is several times of the metallic fiber pulling force, so, the tensile property of glass plate, also can with the steel plate trial of strength, plastic plate can not be compared.
The anti-ultraviolet property of moulding the glass plate improves several times than plastic plate, because mould the glass plate and be made up of compound glass cloth.Wear out when the plastics of surface layer are impaired.Aging plastics can make second layer plastics avoid the ultraviolet ray infringement ultraviolet isolating.
Simultaneously, the surface layer glass cloth also can be tackled ultraviolet ray, makes second layer plastics avoid the ultraviolet ray infringement.
Mould the antiacid alkali of glass cloth.Select different antiacid alkali plastics, mould the glass plate and just can be competent at the use of soda acid occasion.Certainly, the economic benefit of moulding the glass plate is several times as much as plastic plate.
Mould the glass plate and include the whippy glass cloth of multilayer, make it flexible slightly.This specific character is a plastic plate, and steel plate is unexistent, makes it take advantage in special occasion.
Glass cloth is to make of silica sand.Plastics are to make of oil.Moulding the ratio that the glass plate contains glass cloth can make us save bulk petroleum greater than plastics, and therefore, moulding the glass plate is environment-friendly products.
Economic benefit, every square metre of glass cloth market price be less than monobasic, about 8,000 yuan one ton in plastics.
The Figure of description explanation
Fig. 1: what do not rot moulds the glass cardboard
1 plastics, 2 glass cloth, 3 mould the glass cardboard.
Claims (1)
- " wide surpass 10 meters be as thin as 0.3 millimeter substitute that metal can saw that boring do not rot mould the glass cardboard ", it is characterized in that, form by plastic bonding glass cloth (2), coloured or colourless plastics are heated into liquation as adhesive, make glass cloth pass through the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make after the cooling and mould glass cardboard (3), widely surpass 10 meters and be as thin as 0.3 millimeter and substitute metal and can saw the glass cardboard of moulding that do not rot of boring and moved thereby make; It is manufactured with 3 kinds:1), make a glass cloth by the plastics liquation, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics with facility, make after the cooling be as thin as 0.3 millimeter substitute metal can saw hole do not rot mould glass paper;2), make a glass cloth by the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make the glass cloth of several the molten slurries of parcel plastics overlapping, paste into and thickly surpass 10 meters to 2 mm wides and mould the glass plate, make after the cooling wide surpass 10 meters thick to 2 millimeters substitute that metal can saw that boring do not rot mould the glass plate;3), make a glass cloth by the plastics liquation with facility, make plastics liquation parcel glass cloth, strike off the molten slurry of unnecessary plastics, make the glass cloth of the molten slurry of polylith parcel plastics overlapping, paste into and thickly surpass 10 meters and mould the glass plate to several centimeters wide, make after the cooling wide surpass 10 meters thick to several centimeters substitute metal can saw hole do not rot mould the glass plate.