CN103753893A - Sawable, drillable and unbreakable plastic glass cardboard with width of more than 10 meter and thickness of 0.5 mm capable of replacing metal - Google Patents
Sawable, drillable and unbreakable plastic glass cardboard with width of more than 10 meter and thickness of 0.5 mm capable of replacing metal Download PDFInfo
- Publication number
- CN103753893A CN103753893A CN201210028294.XA CN201210028294A CN103753893A CN 103753893 A CN103753893 A CN 103753893A CN 201210028294 A CN201210028294 A CN 201210028294A CN 103753893 A CN103753893 A CN 103753893A
- Authority
- CN
- China
- Prior art keywords
- glass
- plastic
- make
- glass cloth
- plastic melting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an unbreakable plastic glass cardboard, and the product is composed of plastic molten slurry and glass cloth which are bonded. The glass cloth is rich in elasticity, the pulling force of the glass fibre is several times of that of the metallic fiber, so that the plate can bear impact force and has tensile property which can compete with steel plate. The glass cloth can block ultraviolet ray and prevent ultraviolet ray from damaging plastic; the acid and alkali resisting plastic is selected, thereby the plastic glass plate can be used for acid and alkali occasions. The specific gravity of the plastic glass cardboard is 2g/cm<3>, and 100 m<2> of plastic glass plate of 1 mm thickness weighs less than 200 kg; glass cloth of 0.2 mm thickness is cheaper than 1 yuan/m<2>, and thereby the plastic glass plate is cheaper with high economic benefit; the plastic glass plate can replace metal, and can be used for compartment, cabin, furniture, workshop coverage, exterior wall decoration, etc., with advantages. The glass screen cloth and synthetic glass are used for producing plastic glass plate, which can replace glass at present to produce glazing with light transmittance higher than 50%, and the glass screen cloth can reflect more than 50% of sunlight, and thereby the room is more cool and refreshing, and refrigeration energy consumption is reduced, and hurt by high-altitude glazing fragmentation at present is overcome. If the product is produced into an unbreakable foam plastic glass plate, the economic benefit can be increased by times.
Description
Glass, is not afraid of soda acid worm ant, but be afraid of to clash into, one touch broken; If without shock, it's thousand pasts the life-span, makes metallic plate self-induction be not so good as.
< < that this technology proposes is wide to be surpassed 10 meters and is as thin as 0.5 millimeter and substitutes metal and can saw to hole and beat the not rotten glass cardboard > > that moulds, be called for short and break the not rotten glass cardboard of moulding, can solve above-mentioned glass fearness Impact Problems.
< < is wide to be surpassed 10 meters and is as thin as 0.5 millimeter and substitutes metal and can saw boring and beat the not rotten glass cardboard > > that moulds, its beneficial effect is that replacement metal material, extends working time, weight reduction, reduces costs.
< < is wide to be surpassed 10 meters and is as thin as 0.5 millimeter and substitutes metal and can saw boring and beat the not rotten glass cardboard > > that moulds, the technical scheme that its technical solution problem adopts is, by the bonding glass cloth of plastics (1) (2), formed, become molten slurry as adhesive coloured or colourless plastic heating, with facility, plastic melting pulp is placed on glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, after cooling, make and mould glass cardboard (3), thereby make widely to surpass 10 meters and be as thin as 0.5 millimeter and substitute metal and can saw boring and break the not rotten glass cardboard of moulding and moved, it is manufactured with 3 kinds:
1), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp parcel glass cloth, strike off unnecessary plastics and mould slurry, make after cooling and be as thin as 0.5 millimeter and substitute metal and can saw to hole and play the not rotten glass paper of moulding;
2), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, make the glass cloth of several parcel plastic melting pulps overlapping, paste into and thickly to 2 mm wides, surpass 10 meters and mould glass plate, make after cooling and widely surpass 10 meters and thickly to 2 millimeters, substitute metal and can saw boring and break the not rotten glass plate of moulding;
3), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, make the glass cloth of polylith parcel plastic melting pulp overlapping, paste into and thickly surpass 10 meters and mould glass plate to several centimeters wide, make after cooling and widely surpass 10 meters and thickly to several centimeters, substitute metal and can saw to hole and break the not rotten glass plate of moulding.As Fig. 1
The not rotten glass plate of moulding is broken in existing combination principle introduction:
It is reported, the pulling force of glass fibre is several times of metallic fiber pulling force; Plastics are shock-resistant not strong, easily by ultraviolet ray, destroyed.
This technology organically combines glass fibre and plastics bi-material.Make product be rich in brand-new advantage.
The glass thread that glass cloth is comprised of many glass fibres is woven into, so glass cloth high resilience.When moulding glass plate and be subject to impacting, plastics are passed to glass cloth by impulsive force, and whippy glass cloth just absorbs impulsive force.And along with the glass cloth number of plies increases, mould the impulsive force that glass plate bears and constantly strengthen, until can with steel plate trial of strength.
Because the pulling force of glass fibre is several times of metallic fiber pulling force, so, the tensile property of moulding glass plate, also can with steel plate trial of strength, plastic plate can not be compared.
The anti-ultraviolet property of moulding glass plate improves several times than plastic plate, because mould glass plate and be comprised of compound glass cloth.When the plastics of surface layer impaired aging.Aging plastics can, by ultraviolet isolating, make second layer plastics avoid ultraviolet ray infringement.Meanwhile, surface layer glass cloth also can be tackled ultraviolet ray, makes second layer plastics avoid ultraviolet ray infringement.
Mould the antiacid alkali of glass cloth.Select different antiacid alkali plastics, mould glass plate and just can be competent in soda acid occasion and use.The economic benefit of certainly, moulding glass plate is just several times as much as plastic plate.
Mould glass plate and include the whippy glass cloth of multilayer, make its slightly elasticity.This specific character is plastic plate, and steel plate is unexistent, makes it in special occasion, take advantage.
Glass cloth is to make of silica sand.Plastics are to make of oil.Mould glass plate containing the ratio of glass cloth much larger than plastics, make us save bulk petroleum, therefore, moulding glass plate is environment-friendly products.
Economic benefit, every square metre of glass cloth market price is less than monobasic, approximately 8,000 yuan one ton, plastics.
Figure of description explanation
Fig. 1: break the not rotten glass cardboard of moulding
1 plastics, 2 glass cloth, 3 mould glass cardboard.
Claims (1)
1. widely surpass 10 meters and be as thin as 0.5 millimeter and substitute metal and can saw boring and break the not rotten glass cardboard of moulding, the technical scheme that its technical solution problem adopts is, by the bonding glass cloth of plastics (1) (2), formed, become molten slurry as adhesive coloured or colourless plastic heating, with facility, plastic melting pulp is placed on glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, after cooling, make and mould glass cardboard (3), thereby make widely to surpass 10 meters and be as thin as 0.5 millimeter and substitute metal and can saw boring and break the not rotten glass cardboard of moulding and moved; It is manufactured with 3 kinds:
1), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp parcel glass cloth, strike off unnecessary plastics and mould slurry, make after cooling and be as thin as 0.5 millimeter and substitute metal and can saw to hole and play the not rotten glass paper of moulding;
2), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, make the glass cloth of several parcel plastic melting pulps overlapping, paste into and thickly to 2 mm wides, surpass 10 meters and mould glass plate, make after cooling and widely surpass 10 meters and thickly to 2 millimeters, substitute metal and can saw boring and break the not rotten glass plate of moulding;
3), with facility, plastic melting pulp is placed on a glass cloth, and make plastic melting pulp wrap up glass cloth, strike off unnecessary plastic melting pulp, make the glass cloth of polylith parcel plastic melting pulp overlapping, paste into and thickly surpass 10 meters and mould glass plate to several centimeters wide, make after cooling and widely surpass 10 meters and thickly to several centimeters, substitute metal and can saw to hole and break the not rotten glass plate of moulding.