CN103753889A - Sawable, drillable and unbreakable glazed glass cardboard with width of more than 10 meter and thickness of 0.3 mm capable of replacing metal - Google Patents
Sawable, drillable and unbreakable glazed glass cardboard with width of more than 10 meter and thickness of 0.3 mm capable of replacing metal Download PDFInfo
- Publication number
- CN103753889A CN103753889A CN201210032686.3A CN201210032686A CN103753889A CN 103753889 A CN103753889 A CN 103753889A CN 201210032686 A CN201210032686 A CN 201210032686A CN 103753889 A CN103753889 A CN 103753889A
- Authority
- CN
- China
- Prior art keywords
- glaze
- glass cloth
- glass
- glazed glass
- glaze slip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a sawable, drillable and unbreakable glazed glass cardboard with width of more than 10 meter and thickness of 0.3 mm capable of replacing metal, which is composed of glaze bonded glass cloth. The glaze does not combust, which can minimize fire hazard; the glass cloth is rich in elasticity, and the glaze slice also has elasticity, and the tension of the glass fibre is several times of that of the metallic fiber, so that the glazed glass plate can bear impact force and has tensile property which can compete with steel plate. The glazed glass plate has acid and alkali resistance, and thereby the product can be used in acid or alkali occasion; the specific gravity of glazed glass plate is 2g/cm<3>, and the thickness is 1mm, so 100m<2> of the product weighs 200kg, which is nearly three times lighter than the steel plate; the glass cloth of 0.2mm is cheaper than 1 yuan/m<2>, so price of the glazed glass plate is reduced by times, and the economic benefit is increased; the glass cloth is produced from silica sand, and has the advantages of more simple process than steel-making, and abundant placer millions of times more than iron ore; the glazed glass plate can replace metal sheet, because the glazed glass plate has characteristics that the steel plate does not have, and the product can be used for compartment, cabin, furniture, large workshop coverage, exterior wall finishing, etc., with great advantages. If the product is produced into an unbreakable foam glazed glass plate, the economic benefit can be increased by times.
Description
Glaze, is not afraid of soda acid worm ant, but be afraid of to clash into, one touch broken; If without shock, in thousand life-spans, make metallic plate self-induction be not so good as.
< < that this technology proposes is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and replaces metal can saw brill beating not rotten glaze glass cardboard > >, be called for short and beat not rotten glaze glass paperboard, can solve glaze and be afraid of Impact Problems.
< < is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and replaces metal can saw brill beating not rotten glaze glass cardboard > >, its beneficial effect is, replace metal material, reducing fire occurs, extend working time, weight reduction, reduces costs.
< < is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and replaces metal can saw brill beating not rotten glaze glass cardboard > >, the technical scheme that its technical solution problem adopts is to be comprised of the bonding glass cloth of glaze (1) (2); With facility, glaze slip is placed on glass cloth, and make glaze slip parcel glass cloth, and strike off unnecessary glaze slip, after being dried, put kiln into and fire, become and break not rotten glaze glass cardboard (3), thereby make widely to surpass 10 meters and be as thin as 0.3 millimeter and replace metal can saw brill breaking not rotten glaze glass cardboard and moved; It is manufactured with 3 kinds:
1), with facility, glaze slip is placed on a glass cloth, and make glaze slip parcel glass cloth, strike off unnecessary glaze slip, put kiln into after dry to fire, become and be as thin as 0.3 millimeter and replace metal can saw brill playing not rotten glaze glass paper;
2), with facility, glaze slip is placed on a glass cloth, and make glaze slip wrap up glass cloth, strike off unnecessary glaze slip, make the glass cloth of several parcel glaze slips overlapping, paste into thick to 1 mm wide can super several meters of glaze glass cloth plates, after dry, put kiln into and fire, become and widely surpass 10 meters and thickly to 1 millimeter, replace metal can saw brill breaking not rotten glaze glass plate;
3), with facility, glaze slip is placed on a glass cloth, and make glaze slip wrap up glass cloth, strike off unnecessary glaze slip, make the glass cloth of polylith parcel glaze slip overlapping, paste into thick to several centimeters wide can super several meters of glaze glass cloth plates, after dry, put kiln into and fire, become and widely surpass 10 meters and thickly to several centimeters, replace metals can saw brill breaking not rotten glaze glass plate.As Fig. 1
Not rotten glaze glass cardboard is broken in existing combination principle introduction:
It is reported, the pulling force of glass fibre is several times of metallic fiber pulling force, glass cloth high resilience; The hard fearness of glaze is clashed into, and is not afraid of soda acid worm ant.
This technology organically combines whippy glass cloth and hard glaze bi-material, makes product be rich in brand-new advantage.
It is reported, glaze slip just becomes hard glaze through more than 800 degree high-temperature heatings; Glaze slurry poor adhesive force, this technology addresses this problem with glass cloth.
This technology is taken the glass cloth of resistance to 1000 degree, and like this, glaze slurry is when the high temperature of degree more than 800 burns till glaze, and the glass fibre of glass cloth is not damaged, and still keeps original pulling force, and glass cloth still keeps original elasticity; Glaze slurry is through glass cloth hole, glass cloth to be wrapped up, and solves this problem of glaze slurry poor adhesive force; Utilize the mutual viscosity of glaze slurry, make multiple glaze glass paper stick into glaze glass plate.
The glass thread that glass cloth is comprised of many glass fibres is woven into, so glass cloth high resilience.When glaze glass plate is subject to impacting, glaze is passed to glass cloth by impulsive force, and whippy glass cloth just absorbs impulsive force.Glaze is used as adhesive, so glaze can be as thin as 0.02mm, makes glaze thin slice also flexible; And along with the glass cloth number of plies increases, the impulsive force that glaze glass plate bears constantly strengthens, until can with steel plate trial of strength.
Because the pulling force of glass fibre is several times of metallic fiber pulling force, so, the tensile property of glaze glass plate, also can with steel plate trial of strength.
Glaze glass plate includes the whippy glass cloth of multilayer, makes its high resilience; Glaze glass plate is not afraid of soda acid; Beat the not rotten about 2g/cm of glaze glass plate proportion
3, thick 1mm100m
2glaze glass plate 200kg, light nearly 3 times of weight ratio steel plate; 1 yuan/m of thick 0.2mm glass cloth less than
2, make glaze glass plate price reduce at double, economic benefit is high; Glass cloth is to make of silica sand, and technique is simple more a lot of than steel-making, and placer is abundant, than the many thousands of times of iron ore; These characteristics are that steel plate is unexistent, make glaze glass plate replacing metallic plate, make compartment, cabin, and furniture, the large factory building of bedding, exterior wall finishings etc. all account for and have great advantage.If be made into, break not rotten foam glaze glass plate, economic benefit promotes several times
Figure of description explanation
Fig. 1: break not rotten glaze glass cardboard
1 glaze, 2 glass cloth, 3 glaze glass cardboards.
Claims (1)
1. < < is wide surpasses 10 meters and is as thin as 0.3 millimeter and replaces metal can saw brill beating not rotten glaze glass cardboard > >, it is characterized in that, the bonding glass cloth of glaze, consist of; With facility, glaze slip is placed on glass cloth, and make glaze slip parcel glass cloth, and strike off unnecessary glaze slip, after being dried, put kiln into and fire, become and break not rotten glaze glass cardboard, thereby make widely to surpass 10 meters and be as thin as 0.3 millimeter and replace metal can saw brill breaking not rotten glaze glass cardboard and moved; It is manufactured with 3 kinds:
1), with facility, glaze slip is placed on a glass cloth, and make glaze slip parcel glass cloth, strike off unnecessary glaze slip, put kiln into after dry to fire, become and be as thin as 0.3 millimeter and replace metal can saw brill playing not rotten glaze glass paper;
2), with facility, glaze slip is placed on a glass cloth, and make glaze slip wrap up glass cloth, strike off unnecessary glaze slip, make the glass cloth of several parcel glaze slips overlapping, paste into thick to 1 mm wide can super several meters of glaze glass cloth plates, after dry, put kiln into and fire, become and widely surpass 10 meters and thickly to 1 millimeter, replace metal can saw brill breaking not rotten glaze glass plate;
3), with facility, glaze slip is placed on a glass cloth, and make glaze slip wrap up glass cloth, strike off unnecessary glaze slip, make the glass cloth of polylith parcel glaze slip overlapping, paste into thick to several centimeters wide can super several meters of glaze glass cloth plates, after dry, put kiln into and fire, become and widely surpass 10 meters and thickly to several centimeters, replace metals can saw brill breaking not rotten glaze glass plate.