CN104177757A - High-hardness ABS plastic - Google Patents
High-hardness ABS plastic Download PDFInfo
- Publication number
- CN104177757A CN104177757A CN201410370215.2A CN201410370215A CN104177757A CN 104177757 A CN104177757 A CN 104177757A CN 201410370215 A CN201410370215 A CN 201410370215A CN 104177757 A CN104177757 A CN 104177757A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs plastic
- hardness
- abs
- mica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-hardness ABS plastic. The plastic comprises the following substances in parts by weight: 25-36 parts of ABS resin, 15-23 parts of PP, 20-31 parts of PE, 3-9 parts of plasticizer, 9-16 parts of liquid paraffin, 3-5 parts of antistatic agent, 7-9 parts of plasticized starch, 11-24 parts of maleic anhydride grafted polyethylene, 2-8 parts of glass fibers, 3-7 parts of mica and 2-5 parts of high color black. The ABS plastic modified material has high hardness, has strong scratch resistance and is not easy to scratch in the using process, has high glossiness and black and shiny degrees and stable quality, can be directly used for assembly, improves the production efficiency, reduces the production cost, can produce great economic benefits and has good properties such as tensile strength, bending strength, impact strength, heat deformation temperature resistance and the like.
Description
Technical field
The present invention relates to a kind of high rigidity ABS plastic cement.
Background technology
ABS is one of current most widely used engineering plastics, because it has that stronger resistance to impact shock, proportion are low, good stability of the dimension, acid-proof alkaline be strong, the easy advantage such as processing, extensive in sector applications such as machinery, household electrical appliance, daily apparatus, especially in televisor, refrigerator, washing machine shell field, obtained development fast.
Along with economic fast development, improving constantly of people's living standard, people are also more and more higher to the requirement of the outward appearance of household electrical appliance, not only require it to possess higher glossiness, make the appliance shell making there is bright and new outward appearance, and its hardness is had higher requirement, so that in use reach anti-scratch technique effect.But existing ABS alloy material is in the process synthetic by polymerization methods, the refractive index of various resin materials cannot reach the degree of coupling completely, cause the glossiness of the alloy material that makes not reach the requirement of use, after completing, mold also needs to spray high gloss oil paint, make production efficiency low, improved production cost; The hardness of especially existing ABS alloy material cannot reach the requirement of scraping and wiping resistance performance, has greatly limited the application of this material in each Application Areas.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of high rigidity ABS plastic cement.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of high rigidity ABS plastic cement, the material that comprises following parts by weight: ABS resin 25-36 part, PP15-23 part, PE20-31 part, softening agent 3-9 part, liquid paraffin 9-16 part, static inhibitor 3-5 part, plasticized starch 7-9 part, maleic anhydride connects poly-second 11-24 part, glass fibre 2-8 part, mica 3-7 part, high-carbon black pigment 2-5 part.
Preferably, a kind of high rigidity ABS plastic cement, comprises the material of following parts by weight: 30 parts of ABS resin, PP20 part, PE25 part, 6 parts, softening agent, 10 parts of liquid paraffins, 4 parts, static inhibitor, 8 parts of plasticized starch, maleic anhydride connects 20 parts of poly-second, 3 parts, glass fibre, 6 parts, mica, 3 parts of high-carbon black pigments.
ABS plastic modified material of the present invention, possesses very high hardness, and in use anti-scratch performance is strong, is difficult for by scratch; Have that very high glossiness, shiny black degree are high, stay in grade, can directly assemble, improved production efficiency, reduced production cost, can produce very large economic benefit; There is the performances such as good tensile strength, flexural strength, resistance to impact shock, thermal deformation resistant temperature.
Embodiment
Embodiment 1
A kind of high rigidity ABS plastic cement, the material that comprises following parts by weight: ABS resin 25-36 part, PP15-23 part, PE20-31 part, softening agent 3-9 part, liquid paraffin 9-16 part, static inhibitor 3-5 part, plasticized starch 7-9 part, maleic anhydride connects poly-second 11-24 part, glass fibre 2-8 part, mica 3-7 part, high-carbon black pigment 2-5 part.
Embodiment 2
A kind of high rigidity ABS plastic cement according to claim 1, the material that comprises following parts by weight: 30 parts of ABS resin, PP20 part, PE25 part, 6 parts, softening agent, 10 parts of liquid paraffins, 4 parts, static inhibitor, 8 parts of plasticized starch, maleic anhydride connects 20 parts of poly-second, 3 parts, glass fibre, 6 parts, mica, 3 parts of high-carbon black pigments.
Claims (2)
1. a high rigidity ABS plastic cement, is characterized in that, comprises the material of following parts by weight: ABS resin 25-36 part, PP15-23 part, PE20-31 part, softening agent 3-9 part, liquid paraffin 9-16 part, static inhibitor 3-5 part, plasticized starch 7-9 part, maleic anhydride connects poly-second 11-24 part, glass fibre 2-8 part, mica 3-7 part, high-carbon black pigment 2-5 part.
2. a kind of high rigidity ABS plastic cement according to claim 1, is characterized in that, comprises the material of following parts by weight: 30 parts of ABS resin, PP20 part, PE25 part, 6 parts, softening agent, 10 parts of liquid paraffins, 4 parts, static inhibitor, 8 parts of plasticized starch, maleic anhydride connects 20 parts of poly-second, 3 parts, glass fibre, 6 parts, mica, 3 parts of high-carbon black pigments.