CN109929318A - A kind of oiliness filler - Google Patents
A kind of oiliness filler Download PDFInfo
- Publication number
- CN109929318A CN109929318A CN201711355521.9A CN201711355521A CN109929318A CN 109929318 A CN109929318 A CN 109929318A CN 201711355521 A CN201711355521 A CN 201711355521A CN 109929318 A CN109929318 A CN 109929318A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ketone resin
- aldehyde ketone
- oiliness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to technical field of coatings, especially a kind of oiliness filler, is made of forming for following parts by weight: 15-30 parts of aldehyde ketone resin solution, 15-44 parts of talcum powder, 15-44 parts of transparent powder, 5-10 parts of nitrocotton liquid, 10-30 parts of solvent, 8-12 parts of mill base, 45-80 parts of solid aldehyde ketone resin, 15-20 parts of paraffin, 5-20 parts of asphalt powder, 15-25 parts of calcium carbonate.A kind of oiliness filler of the invention, by aldehyde ketone resin solution, talcum powder, transparent powder, nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, paraffin, asphalt powder, 15-25 parts calcium carbonate heating be mixed be made, it is easy to use, rate of drying is fast, fillibility is good, paint dosage it is few.In any climate can be used, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Description
Technical field
The present invention relates to auxiliary agent technical field, especially a kind of oiliness filler.
Background technique
Polyvinyl chloride is one of five big synthetic resin general in the world, and dosage is maximum, extensive with superior performance
For every field such as construction industry, agricultural, daily necessities.Processing heat stability is poor when due to PVC high temperature, in its processing and forming
Heat stabilizer be must be added to maintain its performance, common heat stabilizer mainly has lead salts, organic tin, terres rares and metal
The stabilizers such as soaps.Lead salt type thermal stabilizing agent is cheap, thermostable effect is good, and dosage is bigger, but its toxicity is big, serious to endanger
Evil human health simultaneously pollutes environment.Metal soap thermal stabilizers effect limited capacity.And organic tin heat stabilizer performance efficiency,
Contamination hazard is small, but expensive, at high cost.Rare earth thermal stabilizer, exclusive use effect is less desirable, and performance needs to be mentioned
Height, but compounded with other heat stabilizers and can be realized efficient effect.Therefore it develops a kind of with efficient, nontoxic, at low cost
Heat stabilizer has very important meaning.
Summary of the invention
In order to overcome the existing unconspicuous deficiency of insulating moulding coating heat insulation, the present invention provides a kind of fillings of oiliness
Agent passes through aldehyde ketone resin solution, talcum powder, transparent powder, nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, paraffin, pitch
Powder, 15-25 parts of calcium carbonate heating, which is mixed, to be made.
The technical solution adopted by the present invention to solve the technical problems is: a kind of oiliness filler, by following parts by weight
Composition is made: 15-30 parts of aldehyde ketone resin solution, 15-44 parts of talcum powder, 15-44 parts of transparent powder, 5-10 parts of nitrocotton
Liquid, 10-30 parts of solvent, 8-12 parts of mill base, 45-80 parts of solid aldehyde ketone resin, 15-20 parts of paraffin, 5-20 parts of drip
Green powder, 15-25 parts of calcium carbonate.
Further, effect is best when including aldehyde ketone resin solution weight part is 15 parts.
Further, including when 15 parts of transparent powder parts by weight effect is best.
Further, effect is best when including nitrocotton liquid parts by weight are 5 parts.
A kind of a kind of oiliness filler of the invention, oiliness filler of the invention, passes through aldehyde ketone resin solution, talcum
Powder, transparent powder, nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, paraffin, asphalt powder, 15-25 parts of calcium carbonate heat mixing
Stirring is made, it is easy to use, rate of drying is fast, fillibility is good, paint dosage it is few.It can be used in any climate, especially
It when winter low temperature, directly scratches, priming paint will not be impacted on the substrate with wood grain.
Specific embodiment
A kind of oiliness filler, is made of forming for following parts by weight: 15-30 parts of aldehyde ketone resin solution, 15-44 parts
Talcum powder, 15-44 parts of transparent powder, 5-10 parts of nitrocotton liquid, 10-30 parts of solvent, 8-12 parts of mill base, 45-80 parts
Solid aldehyde ketone resin, 15-20 parts of paraffin, 5-20 parts of asphalt powder, 15-25 parts of calcium carbonate.
Column 1 are embodied: by 15 parts of aldehyde ketone resin solution, 15 parts of talcum powder, 15 parts of transparent powder, 5 parts of nitrification
Cotton liquid, 10 parts of solvent, 8 parts of mill base, 45 parts of solid aldehyde ketone resin, 15 parts of paraffin, 5 parts of asphalt powder, 15 parts of carbon
The stirring solvent of sour calcium is mixed and made into auxiliary agent, easy to use, rate of drying is fast, fillibility is good, paint dosage is few.In any weather
Under can be used, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Column 2 are embodied: by 30 parts of aldehyde ketone resin solution, 44 parts of talcum powder, 44 parts of transparent powder, 10 parts of nitrification
Cotton liquid, 30 parts of solvent, 12 parts of mill base, 80 parts of solid aldehyde ketone resin, 20 parts of paraffin, 20 parts of asphalt powder, 25 parts
The stirring solvent of calcium carbonate is mixed and made into auxiliary agent, easy to use, rate of drying is fast, fillibility is good, paint dosage is few.In any gas
Under time can be used, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Described above to be merely exemplary for the purpose of the present invention, and not restrictive, those of ordinary skill in the art understand,
In the case where not departing from spirit and scope as defined in the appended claims, many modifications, variation or equivalent can be made, but all
It will fall within the scope of protection of the present invention.
Claims (4)
1. a kind of oiliness filler, characterized in that be made of forming for following parts by weight: 15-30 parts of aldehyde ketone resin solution,
15-44 parts of talcum powder, 15-44 parts of transparent powder, 5-10 parts of nitrocotton liquid, 10-30 parts of solvent, 8-12 parts of mill base,
45-80 parts of solid aldehyde ketone resin, 15-20 parts of paraffin, 5-20 parts of asphalt powder, 15-25 parts of calcium carbonate.
2. a kind of oiliness filler according to claim 1, characterized in that described aldehyde ketone resin solution weight part is 15 parts
When effect it is best.
3. a kind of oiliness filler according to claim 1, characterized in that imitated when 15 parts of the transparent powder parts by weight
Fruit is best.
4. a kind of oiliness filler according to claim 1, characterized in that the nitrocotton liquid parts by weight be 5 parts when
It is best to wait effect.