CN109929377A - A kind of filler - Google Patents
A kind of filler Download PDFInfo
- Publication number
- CN109929377A CN109929377A CN201711355527.6A CN201711355527A CN109929377A CN 109929377 A CN109929377 A CN 109929377A CN 201711355527 A CN201711355527 A CN 201711355527A CN 109929377 A CN109929377 A CN 109929377A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ketone resin
- aldehyde ketone
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to technical field of coatings, especially a kind of filler, is made of forming for following parts by weight: 10-30 parts of aldehyde ketone resin solution, 10-44 parts of talcum powder, 10-44 parts of transparent powder, 6-10 parts of nitrocotton liquid, 15-30 parts of solvent, 5-12 parts of mill base, 55-80 parts of solid aldehyde ketone resin, 15-20 parts of asphalt powder, 10-25 parts of calcium carbonate.A kind of filler of the invention, by aldehyde ketone resin solution, talcum powder, transparent powder, nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, asphalt powder, calcium carbonate heating be mixed be made, it is easy to use, rate of drying is fast, fillibility is good, paint dosage it is few.In any climate can be used, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Description
Technical field
The present invention relates to auxiliary agent technical field, especially a kind of filler.
Background technique
Polyvinyl chloride is one of five big synthetic resin general in the world, and dosage is maximum, extensive with superior performance
For every field such as construction industry, agricultural, daily necessities.Processing heat stability is poor when due to PVC high temperature, in its processing and forming
Heat stabilizer be must be added to maintain its performance, common heat stabilizer mainly has lead salts, organic tin, terres rares and metal
The stabilizers such as soaps.Lead salt type thermal stabilizing agent is cheap, thermostable effect is good, and dosage is bigger, but its toxicity is big, serious to endanger
Evil human health simultaneously pollutes environment.Metal soap thermal stabilizers effect limited capacity.And organic tin heat stabilizer performance efficiency,
Contamination hazard is small, but expensive, at high cost.Rare earth thermal stabilizer, exclusive use effect is less desirable, and performance needs to be mentioned
Height, but compounded with other heat stabilizers and can be realized efficient effect.Therefore it develops a kind of with efficient, nontoxic, at low cost
Heat stabilizer has very important meaning.
Summary of the invention
In order to overcome the existing unconspicuous deficiency of insulating moulding coating heat insulation, the present invention provides a kind of fillers, lead to
Aldehyde ketone resin solution, talcum powder, transparent powder, nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, asphalt powder, calcium carbonate is crossed to add
Hot mixing stirring is made.
The technical solution adopted by the present invention to solve the technical problems is: a kind of filler, by forming for following parts by weight
Be made: 10-30 parts of aldehyde ketone resin solution, 10-44 parts of talcum powder, 10-44 parts of transparent powder, 6-10 parts of nitrocotton liquid,
15-30 parts of solvent, 5-12 parts of mill base, 55-80 parts of solid aldehyde ketone resin, 15-20 parts of asphalt powder, 10-25 parts of carbon
Sour calcium.
Further, effect is best when including aldehyde ketone resin solution weight part is 10 parts.
Further, including when 10 parts of transparent powder parts by weight effect is best.
Further, effect is best when including nitrocotton liquid parts by weight are 6 parts.
A kind of filler of the invention, a kind of filler of the invention, by aldehyde ketone resin solution, talcum powder, transparent powder,
Nitrocotton liquid, solvent, mill base, solid aldehyde ketone resin, asphalt powder, calcium carbonate heating are mixed and are made, easy to use, dry speed
Degree is fast, fillibility is good, paint dosage is few.In any climate can be used, especially winter low temperature when, directly with wood grain
It scratches, priming paint will not be impacted on substrate.
Specific embodiment
A kind of filler is made of forming for following parts by weight: 10-30 parts of aldehyde ketone resin solution, 10-44 parts of talcum
Powder, 10-44 parts of transparent powder, 6-10 parts of nitrocotton liquid, 15-30 parts of solvent, 5-12 parts of mill base, 55-80 parts of solid
Aldehyde ketone resin, 15-20 parts of asphalt powder, 10-25 parts of calcium carbonate.
Column 1 are embodied: by 10 parts of aldehyde ketone resin solution, 10 parts of talcum powder, 10 parts of transparent powder, 6 parts of nitrification
Cotton liquid, 15 parts of solvent, 5 parts of mill base, 55 parts of solid aldehyde ketone resin, 15 parts of asphalt powder, 10 parts of calcium carbonate solvent
Be stirred and auxiliary agent be made, it is easy to use, rate of drying is fast, fillibility is good, paint dosage it is few.Can it make in any climate
With, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Column 2 are embodied: by 30 parts of aldehyde ketone resin solution, 44 parts of talcum powder, 44 parts of transparent powder, 10 parts of nitrification
Cotton liquid, 30 parts of solvent, 12 parts of mill base, 80 parts of solid aldehyde ketone resin, 20 parts of asphalt powder, 25 parts of calcium carbonate solvent
Be stirred and auxiliary agent be made, it is easy to use, rate of drying is fast, fillibility is good, paint dosage it is few.Can it make in any climate
With, especially winter low temperature when, directly scratch, priming paint will not be impacted on the substrate with wood grain.
Described above to be merely exemplary for the purpose of the present invention, and not restrictive, those of ordinary skill in the art understand,
In the case where not departing from spirit and scope as defined in the appended claims, many modifications, variation or equivalent can be made, but all
It will fall within the scope of protection of the present invention.
Claims (4)
1. a kind of filler, characterized in that be made of forming for following parts by weight: 10-30 parts of aldehyde ketone resin solution, 10-44
Talcum powder, 10-44 parts of the transparent powder, 6-10 parts of nitrocotton liquid, 15-30 parts of solvent, 5-12 parts of mill base, 55-80 of part
The solid aldehyde ketone resin of part, 15-20 parts of asphalt powder, 10-25 parts of calcium carbonate.
2. a kind of filler according to claim 1, characterized in that described aldehyde ketone resin solution weight part be 10 parts when
It is best to wait effect.
3. a kind of filler according to claim 1, characterized in that effect is most when 10 parts of the transparent powder parts by weight
It is good.
4. a kind of filler according to claim 1, characterized in that the nitrocotton liquid parts by weight are imitated when being 6 parts
Fruit is best.