CN104312056A - Organic acid and rare earth composite heat stabilizer for PVC (polyvinyl chloride) - Google Patents
Organic acid and rare earth composite heat stabilizer for PVC (polyvinyl chloride) Download PDFInfo
- Publication number
- CN104312056A CN104312056A CN201410637717.7A CN201410637717A CN104312056A CN 104312056 A CN104312056 A CN 104312056A CN 201410637717 A CN201410637717 A CN 201410637717A CN 104312056 A CN104312056 A CN 104312056A
- Authority
- CN
- China
- Prior art keywords
- accounts
- total mass
- pvc
- composite thermal
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an organic acid and rare earth composite heat stabilizer for PVC (polyvinyl chloride). The composite heat stabilizer is prepared by chemically synthesizing a heat stabilizer, lanthanum carbonate, nitric acid, zinc stearate, cerium carbonate, a solvent, sodium hydroxide, a composite antioxidant, hexadecanol, glycerin and mineral oil. According to the composite heat stabilizer, synthesized lanthanum stearate is compounded with other heat stabilizers, so that the thermal degradation temperature of PVC can be increased, the thermal stabilization time of PVC can be prolonged, the balance torque of the PVC can be reduced, the PVC processing power can be effectively reduced, and a large amount of effective energy resources are saved.
Description
Technical field
The present invention relates to chemical field, particularly relate to a kind of PVC organic acid rare earth complex heat stabilizer.
Background technology
Polyvinyl chloride has excellent erosion resistance and very high mechanical property, again because of cheap, abundant raw material, manufacturing process is ripe, and its goods are applied to the every field that workers and peasants also produce, but, PVC adds a fatal weakness man-hour, be exactly poor heat stability, therefore, must thermo-stabilizer be added when processing PVC.
The commercial thermo-stabilizer in the whole world has reached hundreds of, and mainly contain the large class of lead salt stabilizer, metallic soap one package stabilizer, organotin stabilizer and rare-earth stabilizer four, thermo-stabilizer mainly divides tin stablizer, lead stabilizer, mixed metal stabilizer etc. at present.Lead salt stabilizer toxicity is comparatively strong, has biological accumulation, and easily produces dust; Containing heavy metal cadmium, barium etc. in metallic soap one package stabilizer, and cadmium, barium have stronger toxicity, and it is produced and causes serious impact to human health and ecotope in offal treatment process; Although organotin stabilizer performance efficiency, pollution hazard is little, expensive, and cost is high.Although rare earth thermal stabilizer stablizer stabilising effect better and have no side effect, if be used alone, can not reach desirable stabilising effect.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of PVC organic acid rare earth complex heat stabilizer, by the stearic acid lanthanum of synthesis and other thermo-stabilizer compounds, all can improve PVC thermal degradation temperature and heat-stable time, can the balancing torque of PVC decline simultaneously, effectively can reduce the power that processing PVC is, save the mass efficient energy.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of PVC organic acid rare earth complex heat stabilizer, comprise thermo-stabilizer, carbonic acid billows, nitric acid, Zinic stearas, cerous carbonate, solvent, sodium hydroxide, composite antioxidant, hexadecanol, glycerol, mineral oil, described thermo-stabilizer is the mixture of lead sulfate tribasic and rare-earth stearate, and the mass ratio of described lead sulfate tribasic and rare-earth stearate is 40 ~ 85:40 ~ 90, and the quality of described carbonic acid billows accounts for 3.5 ~ 5% of composite thermal stabilizer total mass, nitric acid accounts for 1.5 ~ 3.5% of composite thermal stabilizer total mass, Zinic stearas accounts for 8 ~ 12% of composite thermal stabilizer total mass, cerous carbonate accounts for 2 ~ 3.5% of composite thermal stabilizer total mass, solvent accounts for 2 ~ 3% of composite thermal stabilizer total mass, sodium hydroxide accounts for 3 ~ 5.5% of composite thermal stabilizer total mass, composite antioxidant accounts for 1.5 ~ 3% of composite thermal stabilizer total mass, hexadecanol accounts for 2 ~ 4.5% of composite thermal stabilizer total mass, glycerol accounts for 5 ~ 6% of composite thermal stabilizer total mass, mineral oil accounts for 1 ~ 3.5% of composite thermal stabilizer total mass.
In the present invention's preferred embodiments, described solvent is ethanol.
In the present invention's preferred embodiments, described composite antioxidant is dihydroxyphenyl propane and triethyl-phosphite mixture, in mass ratio dihydroxyphenyl propane: triethyl-phosphite=1: 1.5.
The invention has the beneficial effects as follows: a kind of PVC organic acid of the present invention rare earth complex heat stabilizer, by the stearic acid lanthanum of synthesis and other thermo-stabilizer compounds, all can improve PVC thermal degradation temperature and heat-stable time, can the balancing torque of PVC decline simultaneously, effectively can reduce the power that processing PVC is, save the mass efficient energy.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A kind of PVC organic acid rare earth complex heat stabilizer, comprises thermo-stabilizer, carbonic acid billows, nitric acid, Zinic stearas, cerous carbonate, solvent, sodium hydroxide, composite antioxidant, hexadecanol, glycerol, mineral oil, described thermo-stabilizer is the mixture of lead sulfate tribasic and rare-earth stearate, and the mass ratio of described lead sulfate tribasic and rare-earth stearate is 40 ~ 85:40 ~ 90, and the quality of described carbonic acid billows accounts for 3.5 ~ 5% of composite thermal stabilizer total mass, nitric acid accounts for 1.5 ~ 3.5% of composite thermal stabilizer total mass, Zinic stearas accounts for 8 ~ 12% of composite thermal stabilizer total mass, cerous carbonate accounts for 2 ~ 3.5% of composite thermal stabilizer total mass, solvent accounts for 2 ~ 3% of composite thermal stabilizer total mass, sodium hydroxide accounts for 3 ~ 5.5% of composite thermal stabilizer total mass, composite antioxidant accounts for 1.5 ~ 3% of composite thermal stabilizer total mass, hexadecanol accounts for 2 ~ 4.5% of composite thermal stabilizer total mass, glycerol accounts for 5 ~ 6% of composite thermal stabilizer total mass, mineral oil accounts for 1 ~ 3.5% of composite thermal stabilizer total mass.
Further, described solvent is ethanol.
Further, described composite antioxidant is dihydroxyphenyl propane and triethyl-phosphite mixture, in mass ratio dihydroxyphenyl propane: triethyl-phosphite=1: 1.5.
The invention has the beneficial effects as follows: a kind of PVC organic acid of the present invention rare earth complex heat stabilizer, by the stearic acid lanthanum of synthesis and other thermo-stabilizer compounds, all can improve PVC thermal degradation temperature and heat-stable time, can the balancing torque of PVC decline simultaneously, effectively can reduce the power that processing PVC is, save the mass efficient energy.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a PVC organic acid rare earth complex heat stabilizer, is characterized in that, comprise thermo-stabilizer, carbonic acid billows, nitric acid, Zinic stearas, cerous carbonate, solvent, sodium hydroxide, composite antioxidant, hexadecanol, glycerol, mineral oil, described thermo-stabilizer is the mixture of lead sulfate tribasic and rare-earth stearate, and the mass ratio of described lead sulfate tribasic and rare-earth stearate is 40 ~ 85:40 ~ 90, and the quality of described carbonic acid billows accounts for 3.5 ~ 5% of composite thermal stabilizer total mass, nitric acid accounts for 1.5 ~ 3.5% of composite thermal stabilizer total mass, Zinic stearas accounts for 8 ~ 12% of composite thermal stabilizer total mass, cerous carbonate accounts for 2 ~ 3.5% of composite thermal stabilizer total mass, solvent accounts for 2 ~ 3% of composite thermal stabilizer total mass, sodium hydroxide accounts for 3 ~ 5.5% of composite thermal stabilizer total mass, composite antioxidant accounts for 1.5 ~ 3% of composite thermal stabilizer total mass, hexadecanol accounts for 2 ~ 4.5% of composite thermal stabilizer total mass, glycerol accounts for 5 ~ 6% of composite thermal stabilizer total mass, mineral oil accounts for 1 ~ 3.5% of composite thermal stabilizer total mass.
2. PVC organic acid rare earth complex heat stabilizer according to claim 1, is characterized in that, described solvent is ethanol.
3. PVC organic acid rare earth complex heat stabilizer according to claim 1, is characterized in that, described composite antioxidant is dihydroxyphenyl propane and triethyl-phosphite mixture, in mass ratio dihydroxyphenyl propane: triethyl-phosphite=1: 1.5.