CN109912219A - Blue bottom safflower crystalline glaze and preparation method thereof - Google Patents
Blue bottom safflower crystalline glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109912219A CN109912219A CN201711326269.9A CN201711326269A CN109912219A CN 109912219 A CN109912219 A CN 109912219A CN 201711326269 A CN201711326269 A CN 201711326269A CN 109912219 A CN109912219 A CN 109912219A
- Authority
- CN
- China
- Prior art keywords
- parts
- safflower
- glaze
- crystalline
- crystalline glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of blue bottom safflower crystalline glaze, the indigo plant bottom safflower crystalline glaze each component and each component quality are as follows: 40 parts~45 parts of soda-lime glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；30 parts~35 parts of quartz；10 parts~13 parts of talcum；3 parts~5 parts of rutile；3 parts~7 parts of iron oxide；0.75 part~1 part of chromium oxide；2 parts~3 parts of cobalt oxide；The indigo plant bottom safflower crystalline glaze, it is by being fired in 1290 DEG C of down-draft kiln, it is cooled to 1130 DEG C and keeps the temperature 2 hours, blue gloss is presented in glaze, crystalline substance flower is little crystallization, by the control to kiln, with the strict demand to parameter, excellent product can be provided for crystalline glaze fan, and receive consistent favorable comment.
Description
Technical field
The invention discloses a kind of blue bottom safflower crystalline glazes and preparation method thereof.
Background technique
Currently, all kinds of furniture of life, tableware for daily use is all as enthusiasm of the people to ceramic process demand constantly increases
Gradually level off to more special fairly simple beautiful ceramic, the indigo plant bottom safflower crystalline glaze, is by 1290 DEG C
It is fired in down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours, blue gloss is presented in glaze, and crystalline substance flower is little crystallization, by kiln
The control of furnace can provide excellent product with the strict demand to parameter for crystalline glaze fan, and receive it is unanimously good
It comments.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, glazing effect is improved, keeps it more beautiful
It sees, the invention discloses a kind of blue bottom safflower crystalline glaze, the indigo plant bottom safflower crystalline glaze each component and each component quality are as follows: sodium glass
40 parts~45 parts of glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；30 parts of quartz~
35 parts；10 parts~13 parts of talcum；3 parts~5 parts of rutile；3 parts~7 parts of iron oxide；0.75 part~1 part of chromium oxide；Cobalt oxide 2
Part~3 parts.
The step of blue bottom safflower crystalline glaze production method, this method, is as follows:
A) blue bottom safflower crystalline glaze is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
C) clean green body, blueing bottom safflower crystalline glaze are taken；
D) base of above-mentioned first-class glaze is burnt into 1290 DEG C of down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours.
After above-mentioned technical proposal, by the way that blue bottom safflower crystalline glaze sintering curve, seed content carries out strict control,
Its quality is set to have greatly improved, it is deep to be liked by users.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one:
The invention discloses a kind of blue bottom safflower crystalline glazes, and the indigo plant bottom safflower crystalline glaze each component and each component quality are such as
Under: 40 parts~45 parts of soda-lime glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；Quartz
30 parts~35 parts；10 parts~13 parts of talcum；3 parts~5 parts of rutile；3 parts~7 parts of iron oxide；0.75 part~1 part of chromium oxide；Oxygen
Change 2 parts~3 parts of cobalt.
The step of blue bottom safflower crystalline glaze production method, this method, is as follows:
A) blue bottom safflower crystalline glaze is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
C) clean green body, blueing bottom safflower crystalline glaze are taken；
D) base of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours.
Embodiment two:
The invention discloses a kind of blue bottom safflower crystalline glazes, and the indigo plant bottom safflower crystalline glaze each component and each component quality are such as
Under: 40 parts~45 parts of soda-lime glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；Quartz
30 parts~35 parts；10 parts~13 parts of talcum；3 parts~5 parts of rutile；3 parts~7 parts of iron oxide；0.75 part~1 part of chromium oxide；Oxygen
Change 2 parts~3 parts of cobalt；
The step of blue bottom safflower crystalline glaze production method, this method, is as follows:
A) blue bottom safflower crystalline glaze is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
C) clean green body, blueing bottom safflower crystalline glaze are taken；
D) base of above-mentioned first-class glaze is burnt into 1290 DEG C of down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours.
Embodiment three:
The invention discloses a kind of blue bottom safflower crystalline glazes, and the indigo plant bottom safflower crystalline glaze each component and each component quality are such as
Under: 40 parts~45 parts of soda-lime glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；Quartz
30 parts~35 parts；10 parts~13 parts of talcum；1 part~3 parts of rutile；1 part~4 parts of iron oxide；0.75 part~1 part of chromium oxide；Oxygen
Change 2 parts~3 parts of cobalt.
The step of blue bottom safflower crystalline glaze production method, this method, is as follows:
A) blue bottom safflower crystalline glaze is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
C) clean green body, blueing bottom safflower crystalline glaze are taken；
D) base of above-mentioned first-class glaze is burnt into 1290 DEG C of down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours.
Conclusion: experiment one: glaze is in unglazed shape, and glaze does not reach melting.
Experiment two: meeting the purpose of this research and development, for the effect in ideal.
Experiment three: seed content addition is very few, and crystallization effect is not ideal effect.
In summary 3 points to test three as ideal developmental achievement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. the indigo plant bottom safflower crystalline glaze each component and each component quality are as follows the invention discloses a kind of blue bottom safflower crystalline glaze:
40 parts~45 parts of soda-lime glass part；20 parts~25 parts of zinc oxide；8 parts~11 parts of calcite；18 parts~23 parts of Jiepai clay；30 parts of quartz
~35 parts；10 parts~13 parts of talcum；3 parts~5 parts of rutile；3 parts~7 parts of iron oxide；0.75 part~1 part of chromium oxide；Cobalt oxide 2
Part~3 parts.
2. the step of blue bottom safflower crystalline glaze glaze production method described in, this method, is as follows:
A) blue bottom safflower crystalline glaze is stocked up according to each component and each component mass parts:
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is modulated into
51~53 Baume concentration are stand-by；
C) clean green body, blueing bottom safflower crystalline glaze are taken.
D) base of above-mentioned first-class glaze is burnt into 1290 DEG C of down-draft kiln, is cooled to 1130 DEG C and keeps the temperature 2 hours.