CN109081593A - brick red metal glaze and preparation method thereof - Google Patents

brick red metal glaze and preparation method thereof Download PDF

Info

Publication number
CN109081593A
CN109081593A CN201810994096.6A CN201810994096A CN109081593A CN 109081593 A CN109081593 A CN 109081593A CN 201810994096 A CN201810994096 A CN 201810994096A CN 109081593 A CN109081593 A CN 109081593A
Authority
CN
China
Prior art keywords
parts
oxide
component
glaze
brick red
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810994096.6A
Other languages
Chinese (zh)
Inventor
王智永
文礼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Tao Hui Culture Communication Co Ltd
Original Assignee
Hunan Tao Hui Culture Communication Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan Tao Hui Culture Communication Co Ltd filed Critical Hunan Tao Hui Culture Communication Co Ltd
Priority to CN201810994096.6A priority Critical patent/CN109081593A/en
Publication of CN109081593A publication Critical patent/CN109081593A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of brick red metal glaze and preparation method thereof, the component of base glaze and each component mass parts used in brick red metal glaze are as follows: 35 parts~42 parts of frit；8 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；6 parts~9 parts of barium carbonate；7 parts~11 parts of kaolin；10~15 parts of bone ash；15~18 parts of iron oxide；Wherein each component of frit and each component mass parts are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；0.38 part of iron oxide；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.Brick red metal glaze is free of lead cadmium, and high temperature firing improves glazing effect, keeps it more beautiful, can decorate different types of type, be adapted to produce in enormous quantities, the deep favor by customers.

Description

Brick red metal glaze and preparation method thereof
Technical field
The present invention relates to a kind of brick red metal glaze and preparation method thereof.
Background technique
Currently, all kinds of furniture of life, tableware for daily use is all gradually as cordiality of the people to antique-collection constantly increases Level off to of an antique style, will also start a burst of trend of back-to-ancients.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of brick red metal glaze is provided, it is not Leaded cadmium, high temperature firing improve glazing effect, keep it more beautiful, can decorate different types of type, are adapted to large quantities of Amount production, the deep favor by customers.
In order to solve the above technical problems, the technical scheme is that a kind of brick red metal glaze, base glaze used in it The component and each component mass parts of material are as follows:
35 parts~42 parts of frit；8 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；6 parts~9 parts of barium carbonate；7 parts of kaolin ~11 parts；10~15 parts of bone ash；15~18 parts of iron oxide；Wherein each component of frit and each component mass parts are as follows: titanium dioxide 68.28 parts of silicon；18.35 parts of aluminium oxide；0.38 part of iron oxide；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；Oxygen Change 3.2 parts of sodium；0.22 part of titanium oxide.
The present invention also provides a kind of preparation method of brick red metal glaze, the step of method contains, is as follows:
S1: it stocks up according to each component and each component mass parts:
S2: mass ratio=1 ︰ 1.6 ︰ 0.7 of base You Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze mistake after ball milling After 200 meshes, it is stand-by to be modulated into 51~53 Baume degrees；
S3: clean green body, upper base glaze are taken.
S4: and then be burnt into 1270 DEG C of drawer kiln.
After above-mentioned technical proposal, the brick red metal glaze that the present invention is prepared is free of lead cadmium, and high temperature firing can To decorate different types of type, different decoration technologies can be done, is burnt into 1270 DEG C of drawer kiln, high-volume is adapted to Production, the deep favor by customers.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into One step detailed description.
Embodiment one
A kind of brick red metal glaze, the component and each component mass parts of base glaze used in it are as follows:
35 parts of frit；8 parts of talcum；3 parts of zinc oxide；6 parts of barium carbonate；7 parts of kaolin；10 parts of bone ash；15 parts of iron oxide；Its The each component and each component mass parts of middle frit are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；0.38 part of iron oxide； 0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.
The step of preparation method of the brick red metal glaze, method contains, is as follows:
S1: it stocks up according to each component and each component mass parts:
S2: mass ratio=1 ︰ 1.6 ︰ 0.7 of base You Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze mistake after ball milling After 200 meshes, it is stand-by to be modulated into 51~53 Baume degrees；
S3: clean green body, upper base glaze are taken.
S4: and then be burnt into 1270 DEG C of drawer kiln.
Embodiment two
A kind of brick red metal glaze, the component and each component mass parts of base glaze used in it are as follows:
42 parts of frit；16 parts of talcum；6 parts of zinc oxide；9 parts of barium carbonate；11 parts of kaolin；15 parts of bone ash；18 parts of iron oxide； Wherein each component of frit and each component mass parts are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；Iron oxide 0.38 Part；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.
The step of preparation method of the brick red metal glaze, method contains, is as follows:
S1: it stocks up according to each component and each component mass parts:
S2: mass ratio=1 ︰ 1.6 ︰ 0.7 of base You Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze mistake after ball milling After 200 meshes, it is stand-by to be modulated into 51~53 Baume degrees；
S3: clean green body, upper base glaze are taken.
S4: and then be burnt into 1270 DEG C of drawer kiln.
Embodiment three
A kind of brick red metal glaze, the component and each component mass parts of base glaze used in it are as follows:
40 parts of frit；12 parts of talcum；5 parts of zinc oxide；7 parts of barium carbonate；9 parts of kaolin；13 parts of bone ash；16 parts of iron oxide； Wherein each component of frit and each component mass parts are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；Iron oxide 0.38 Part；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.
The step of preparation method of the brick red metal glaze, method contains, is as follows:
S1: it stocks up according to each component and each component mass parts:
S2: mass ratio=1 ︰ 1.6 ︰ 0.7 of base You Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze mistake after ball milling After 200 meshes, it is stand-by to be modulated into 51~53 Baume degrees；
S3: clean green body, upper base glaze are taken.
S4: and then be burnt into 1270 DEG C of drawer kiln.
Comparative example one
A kind of brick red metal glaze, the component and each component mass parts of base glaze used in it are as follows:
30 parts of frit；8 parts of talcum；3 parts of zinc oxide；6 parts of barium carbonate；7 parts of kaolin；10 parts of bone ash；15 parts of iron oxide；Its The each component and each component mass parts of middle frit are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；0.38 part of iron oxide； 0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.
The preparation method of this comparative example one is essentially identical with embodiment one.
Comparative example two
A kind of brick red metal glaze, the component and each component mass parts of base glaze used in it are as follows:
42 parts of frit；16 parts of talcum；6 parts of zinc oxide；9 parts of barium carbonate；11 parts of kaolin；15 parts of bone ash；12 parts of iron oxide； Wherein each component of frit and each component mass parts are as follows: 68.28 parts of silica；18.35 parts of aluminium oxide；Iron oxide 0.38 Part；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；3.2 parts of sodium oxide molybdena；0.22 part of titanium oxide.
The preparation method of this comparative example one is essentially identical with embodiment one.
Comparative example one: glaze temperature is excessively high, and metallic luster is not obvious enough.
Comparative example two: metal color is partially dark, not bright-coloured enough.
Embodiment one is to embodiment three: meeting the purpose of this research and development, for the effect in ideal.
Particular embodiments described above, to the technical problems to be solved by the invention, technical scheme and beneficial effects into Further description of having gone is not used to limit it should be understood that the above is only a specific embodiment of the present invention The system present invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in Within protection scope of the present invention.

Claims (2)

1. a kind of brick red metal glaze, it is characterised in that the component and each component mass parts of base glaze used in it are as follows:
35 parts~42 parts of frit；8 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；6 parts~9 parts of barium carbonate；Kaolin 7 parts~11 Part；10~15 parts of bone ash；15~18 parts of iron oxide；Wherein each component of frit and each component mass parts are as follows: silica 68.28 parts；18.35 parts of aluminium oxide；0.38 part of iron oxide；0.3 part of calcium oxide；0.37 part of magnesia；8.9 parts of potassium oxide；Oxidation 3.2 parts of sodium；0.22 part of titanium oxide.
2. a kind of preparation method of brick red metal glaze as described in claim 1, it is characterised in that the step of method contains is as follows:
S1: it stocks up according to each component and each component mass parts:
S2: 1.6 ︰ 0.7 of mass ratio=1 ︰ of base You Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze after ball milling crossed 200 mesh After sieve, it is stand-by to be modulated into 51~53 Baume degrees；
S3: clean green body, upper base glaze are taken.
S4: and then be burnt into 1270 DEG C of drawer kiln.
CN201810994096.6A 2018-08-29 2018-08-29 brick red metal glaze and preparation method thereof Pending CN109081593A (en)