CN109912204A - Its bluegrass blueness adorns effect glaze and preparation method thereof - Google Patents
Its bluegrass blueness adorns effect glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109912204A CN109912204A CN201711326483.4A CN201711326483A CN109912204A CN 109912204 A CN109912204 A CN 109912204A CN 201711326483 A CN201711326483 A CN 201711326483A CN 109912204 A CN109912204 A CN 109912204A
- Authority
- CN
- China
- Prior art keywords
- parts
- bluegrass
- blueness
- component
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of day bluegrass blueness decorative effect glaze, the green ground coat enamel each component quality of bluegrass blueness decorations effect grass was as follows within this day: 38~40 parts of potassium feldspar；8~14 parts of wollastonite；12~15 parts of talcum；3~6 parts of zinc oxide；14~16 parts of Jiepai clay；7~11 parts of kaolin；10~12 parts of zirconium silicate；8~10 parts of titanium oxide；2~3 parts of copper oxide；The each component content of sky blue overglaze is as follows: 30~35 parts of potassium feldspar；15~20 parts of albite；10~12 parts of calcite；14~16 parts of dolomite；4~6 parts of Guizhou clay；15~16 parts of zinc oxide；10~13 parts of zirconium silicate；3~5 parts of titanium oxide；2~3 parts of cobalt oxide.This day bluegrass blueness decorations effect is the landscape design by grassland heaven bluegrass blueness, the feeling for decorating out on green body, the decorative effect is also with three kinds of coloured glazes by different technological operations, the mutual melting between three kinds of glaze is burnt out in the down-draft kiln by 1270 DEG C, the product of reaction, it is deep to be liked by the majority of consumers.
Description
Technical field
The invention discloses bluegrass blueness decorations effect glaze production in a kind of day and preparation method thereof.
Background technique
Currently, all kinds of furniture of life, tableware for daily use is all as enthusiasm of the people to ceramic process demand constantly increases
Gradually level off to more special fairly simple beautiful ceramic, bluegrass blueness decorations effect is by between three layers of glaze within this day
Mutually melting is flowed to generate special-effect, and the glaze effect is deep to be liked by the majority of consumers naturally, controllable, great artistic effect
Vigorously.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, glazing effect is improved, keeps it more beautiful
It sees, the invention discloses a kind of day bluegrass blueness decorative effect glaze, the green ground coat enamel each component of this day bluegrass blueness decorations effect grass and each component
Quality is as follows: 38 parts~40 parts of potassium feldspar；8 parts~14 parts of wollastonite；12 parts~15 parts of talcum；3 parts~6 parts of zinc oxide；Boundary's board
14 parts~16 parts of mud；7 parts~11 parts of kaolin；10 parts~12 parts of zirconium silicate；8 parts~10 parts of titanium oxide；2 parts~3 parts of copper oxide；
The each component and each component content of sky blue overglaze are as follows: 30 parts~35 parts of potassium feldspar；15 parts~20 parts of albite；Calcite 10
Part~12 parts；14 parts~16 parts of dolomite；4 parts~6 parts of Guizhou clay；15 parts~16 parts of zinc oxide；10 parts~13 parts of zirconium silicate；
3 parts~5 parts of titanium oxide；2 parts~3 parts of cobalt oxide.Yellowish rain brush glaze each component and each component quality are as follows: potassium feldspar 35 parts~40
Part；8 parts~10 parts of calcite；20 parts~25 parts of sodium glass powder；4 parts~5 parts of Guizhou clay；8 parts~11 parts of zinc oxide；Iron oxide 3
Part~4 parts；0.02 part~0.04 part of edible cellulose.
The step of day bluegrass blueness decorations effect glaze production method, this method, is as follows:
A) the green ground coat enamel of day bluegrass blueness decorations effect grass is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.5 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 52~54 Baume concentration are made；
C) the day bluegrass blueness decorations sky blue overglaze of effect is stocked up according to each component and each component mass parts；
D) 1.6 ︰ 0.6 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
E) the day bluegrass blueness decorations yellowish rain brush glaze of effect is stocked up according to each component and each component mass parts；
F) 1.6 ︰ 0.55 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes,
It is stand-by to be modulated into 53~55 Baume concentration；
G) clean green body is taken, is dried after the upper green ground coat enamel of grass, the sky blue overglaze of one third on ground coat enamel, then in ground coat enamel
The yellowish rain brush glaze of overglaze interface brush, and rain brush effect is done in suitable position；
H) the above-mentioned green body for carrying out decoration is burnt into 1270 DEG C of down-draft kiln.
After above-mentioned technical proposal, the biggish promotion that all obtains of properties to day bluegrass blueness decorations effect glaze,
It is set to be more suitable for volume production, it is deep to be liked by users.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one:
The invention discloses a kind of day bluegrass blueness decorative effect glaze, the green ground coat enamel each component of this day bluegrass blueness decorations effect grass and each
Constituent mass is as follows: 38 parts~40 parts of potassium feldspar；8 parts~14 parts of wollastonite；12 parts~15 parts of talcum；3 parts~6 parts of zinc oxide；
14 parts~16 parts of Jiepai clay；7 parts~11 parts of kaolin；10 parts~12 parts of zirconium silicate；8 parts~10 parts of titanium oxide；2 parts of copper oxide
~3 parts；The each component and each component content of sky blue overglaze are as follows: 30 parts~35 parts of potassium feldspar；15 parts~20 parts of albite；Fang Xie
10 parts~12 parts of stone；14 parts~16 parts of dolomite；4 parts~6 parts of Guizhou clay；15 parts~16 parts of zinc oxide；Zirconium silicate 10 parts~13
Part；3 parts~5 parts of titanium oxide；2 parts~3 parts of cobalt oxide.Yellowish rain brush glaze each component and each component quality are as follows: 35 parts of potassium feldspar
~40 parts；8 parts~10 parts of calcite；20 parts~25 parts of sodium glass powder；4 parts~5 parts of Guizhou clay；8 parts~11 parts of zinc oxide；Oxygen
Change 3 parts~4 parts of iron；0.02 part~0.04 part of edible cellulose.
The step of day bluegrass blueness decorations effect glaze production method, this method, is as follows:
A) the green ground coat enamel of day bluegrass blueness decorations effect grass is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.5 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 52~54 Baume concentration are made；
C) the day bluegrass blueness decorations sky blue overglaze of effect is stocked up according to each component and each component mass parts；
D) 1.6 ︰ 0.6 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
E) the day bluegrass blueness decorations yellowish rain brush glaze of effect is stocked up according to each component and each component mass parts；
F) 1.6 ︰ 0.55 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 20~22 hours, after the glaze after ball milling crosses 250 meshes,
It is stand-by to be modulated into 53~55 Baume concentration；
G) clean green body is taken, is dried after the upper green ground coat enamel of grass, the sky blue overglaze of one third on ground coat enamel, then in ground coat enamel
The yellowish rain brush glaze of overglaze interface brush, and rain brush effect is done in suitable position；
H) the above-mentioned green body for carrying out decoration is burnt into 1270 DEG C of down-draft kiln.
Embodiment two:
The invention discloses a kind of day bluegrass blueness decorative effect glaze, the green ground coat enamel each component of this day bluegrass blueness decorations effect grass and each
Constituent mass is as follows: 38 parts~40 parts of potassium feldspar；8 parts~14 parts of wollastonite；12 parts~15 parts of talcum；3 parts~6 parts of zinc oxide；
14 parts~16 parts of Jiepai clay；7 parts~11 parts of kaolin；10 parts~12 parts of zirconium silicate；8 parts~10 parts of titanium oxide；2 parts of copper oxide
~3 parts；The each component and each component content of sky blue overglaze are as follows: 30 parts~35 parts of potassium feldspar；15 parts~20 parts of albite；Fang Xie
10 parts~12 parts of stone；14 parts~16 parts of dolomite；4 parts~6 parts of Guizhou clay；15 parts~16 parts of zinc oxide；Zirconium silicate 10 parts~13
Part；3 parts~5 parts of titanium oxide；2 parts~3 parts of cobalt oxide.
The step of day bluegrass blueness decorations effect glaze production method, this method, is as follows:
A) the green ground coat enamel of day bluegrass blueness decorations effect grass is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.5 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 52~54 Baume concentration are made；
C) the day bluegrass blueness decorations sky blue overglaze of effect is stocked up according to each component and each component mass parts；
D) 1.6 ︰ 0.6 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
G) clean green body is taken, is dried after the upper green ground coat enamel of grass, the sky blue overglaze of one third on ground coat enamel；
H) the above-mentioned green body for carrying out decoration is burnt into 1270 DEG C of down-draft kiln.
Experimental example three:
The invention discloses a kind of day bluegrass blueness decorative effect glaze, the green ground coat enamel each component of this day bluegrass blueness decorations effect grass and each
Constituent mass is as follows: 38 parts~40 parts of potassium feldspar；8 parts~14 parts of wollastonite；12 parts~15 parts of talcum；3 parts~6 parts of zinc oxide；
14 parts~16 parts of Jiepai clay；7 parts~11 parts of kaolin；10 parts~12 parts of zirconium silicate；8 parts~10 parts of titanium oxide；2 parts of copper oxide
~3 parts；The each component and each component content of sky blue overglaze are as follows: 30 parts~35 parts of potassium feldspar；15 parts~20 parts of albite；Fang Xie
10 parts~12 parts of stone；14 parts~16 parts of dolomite；4 parts~6 parts of Guizhou clay；15 parts~16 parts of zinc oxide；Zirconium silicate 10 parts~13
Part；3 parts~5 parts of titanium oxide；2 parts~3 parts of cobalt oxide.Yellowish rain brush glaze each component and each component quality are as follows: 35 parts of potassium feldspar
~40 parts；8 parts~10 parts of calcite；20 parts~25 parts of sodium glass powder；4 parts~5 parts of Guizhou clay；8 parts~11 parts of zinc oxide；Oxygen
Change 3 parts~4 parts of iron；0.02 part~0.04 part of edible cellulose.
The step of day bluegrass blueness decorations effect glaze production method, this method, is as follows:
A) the green ground coat enamel of day bluegrass blueness decorations effect grass is stocked up according to each component and each component mass parts；
B) 1.6 ︰ 0.5 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 52~54 Baume concentration are made；
C) the day bluegrass blueness decorations sky blue overglaze of effect is stocked up according to each component and each component mass parts；
D) 1.6 ︰ 0.6 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made；
E) the day bluegrass blueness decorations yellowish rain brush glaze of effect is stocked up according to each component and each component mass parts；
F) 1.6 ︰ 0.55 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 20~22 hours, after the glaze after ball milling crosses 250 meshes,
It is stand-by to be modulated into 53~55 Baume concentration；
G) clean green body is taken, is dried after the upper green ground coat enamel of grass, the sky blue overglaze of one third on ground coat enamel, then in ground coat enamel
The yellowish rain brush glaze of overglaze interface brush, and rain brush effect is done in suitable position；
H) the above-mentioned green body for carrying out decoration is burnt into 1270 DEG C of down-draft kiln.
Conclusion: experiment one: the fineness of yellowish rain brush glaze is inadequate, and it is unfluent to operate, and increases Ball-milling Time；
Experiment two: the effect for lacking yellowish rain brush glaze decoration is more stiff, and yellowish rain brush glaze should be added, make its more shape
As；
Experiment three: meeting the purpose of this research and development, for the effect in ideal.
In summary 3 points to test three as ideal developmental achievement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. the invention discloses a kind of day bluegrass blueness decorative effect, the green ground coat enamel each component of this day bluegrass blueness decorations effect grass and each component
Quality is as follows: 38 parts~40 parts of potassium feldspar；8 parts~14 parts of wollastonite；12 parts~15 parts of talcum；3 parts~6 parts of zinc oxide；Boundary's board
14 parts~16 parts of mud；7 parts~11 parts of kaolin；10 parts~12 parts of zirconium silicate；8 parts~10 parts of titanium oxide；2 parts~3 parts of copper oxide；
The each component and each component content of sky blue overglaze are as follows: 30 parts~35 parts of potassium feldspar；15 parts~20 parts of albite；10 parts of calcite
~12 parts；14 parts~16 parts of dolomite；4 parts~6 parts of Guizhou clay；15 parts~16 parts of zinc oxide；10 parts~13 parts of zirconium silicate；Oxidation
3 parts~5 parts of titanium；2 parts~3 parts of cobalt oxide.Yellowish rain brush glaze each component and each component quality are as follows: 35 parts~40 parts of potassium feldspar；
8 parts~10 parts of calcite；20 parts~25 parts of sodium glass powder；4 parts~5 parts of Guizhou clay；8 parts~11 parts of zinc oxide；3 parts of iron oxide~
4 parts；0.02 part~0.04 part of edible cellulose.
2. the step of day bluegrass blueness decorations effect glaze production method described in, this method, is as follows:
A) the green ground coat enamel of day bluegrass blueness decorations effect grass is stocked up according to each component and each component mass parts:
B) 1.6 ︰ 0.5 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is modulated into
52~54 Baume concentration are stand-by；
C) the day bluegrass blueness decorations sky blue overglaze of effect is stocked up according to each component and each component mass parts:
D) 1.6 ︰ 0.6 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is modulated into
51~53 Baume concentration are stand-by；
E) the day bluegrass blueness decorations yellowish rain brush glaze of effect is stocked up according to each component and each component mass parts:
F) 1.6 ︰ 0.55 of You Liao ︰ Qiu ︰ water=1 ︰, wet ball grinding 20~22 hours, after the glaze after ball milling crosses 250 meshes, modulation
It is stand-by at 53~55 Baume concentration；
G) clean green body is taken, is dried after the upper green ground coat enamel of grass, the sky blue overglaze of one third on ground coat enamel, then in ground coat enamel overglaze
The yellowish rain brush glaze of interface brush, and rain brush effect is done in suitable position；
H) the above-mentioned green body for carrying out decoration is burnt into 1270 DEG C of down-draft kiln.