CN109910495A - A kind of antique imitation process of building wall - Google Patents
A kind of antique imitation process of building wall Download PDFInfo
- Publication number
- CN109910495A CN109910495A CN201910138941.4A CN201910138941A CN109910495A CN 109910495 A CN109910495 A CN 109910495A CN 201910138941 A CN201910138941 A CN 201910138941A CN 109910495 A CN109910495 A CN 109910495A
- Authority
- CN
- China
- Prior art keywords
- antique
- modelled
- layer
- parts
- building wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the processing technology fields of building wall, disclose a kind of antique imitation process of building wall, include the following steps: S1: cleaning to base course wall；S2: putty layer is formed after the putty of the surface of base's wall after clean batch；S3: paint is coated in putty layer, and sketches the contours of pattern modelled after an antique and forms layer modelled after an antique；S4: protective agent is coated on layer modelled after an antique, forms protective layer afterwards: S5: using cleaning agent, protective layer being cleaned；After S5, the work modelled after an antique of building wall is finished.Then protective agent is uniformly coated on the layer modelled after an antique after the completion of sketching the contours, so that the paint of layer modelled after an antique is completely cut off with air, so that the layer modelled after an antique made be protected, is not directly exposed to layer modelled after an antique in air, slows down the oxidation rate of layer modelled after an antique.On the other hand, prevent from beating due to solarization, wind, rain, the atrocious weathers such as thunder and lightning and layer modelled after an antique is destroyed, increase the service life of layer modelled after an antique.
Description
Technical field
The present invention relates to the processing technology fields of building wall, more specifically, it relates to a kind of antique imitation process of building wall.
Background technique
Pseudo-classic architecture has not only imitated the appearance of Chinese traditional architecture, also embody well China national style with go through
History feature, it also plays immeasurable work to the protection of Chinese traditional architecture and development while making one pleasing
With.
Wall modelled after an antique is usually to be sketched the contours after Concrete brick and cement are piled up by coating, and apparent covering with paint comes
Achieve the effect that wall decoration modelled after an antique, it is apparent to cover with paint, lacquer, colour wash, etc. to achieve the effect that wall decoration modelled after an antique.Wall modelled after an antique after finalization of the manufacture, with
Outdoor expose to wind and rain, atrocious weathers such as solarization thunder and lightning, and with the increase of use time, antique effect is gradually desalinated, nothing
Method realizes lasting wall effect naturally modelled after an antique.
Summary of the invention
The purpose of the present invention is to provide a kind of antique imitation process of building wall, by coating protective agent on layer modelled after an antique, from
And layer modelled after an antique will not be influenced by atrocious weather, increase the service life of wall modelled after an antique.
Above-mentioned technical purpose of the invention has the technical scheme that
A kind of antique imitation process of building wall, includes the following steps:
S1: base course wall is cleaned；
S2: putty layer is formed after the putty of the surface of base's wall after clean batch；
S3: paint is coated in putty layer, and sketches the contours of pattern modelled after an antique and forms layer modelled after an antique；
S4: protective agent is coated on layer modelled after an antique, forms protective layer afterwards:
S5: cleaning agent is used, protective layer is cleaned；
After S5, the work modelled after an antique of building wall is finished.
By using above-mentioned technical proposal, first base course wall is cleaned, by metope ash and other impurities it is clear
It removes, avoids the influence to subsequent step.Base course wall batch multipass flexible break resistant putty after being finished to cleaning, so that base
Progress is levelling at the bumps of layer metope, so that base course wall has good surface smoothness.Then the coating oil in putty layer
Paint, and required pattern modelled after an antique is sketched the contours of, form layer modelled after an antique.Then uniformly coating is protected on the layer modelled after an antique after the completion of sketching the contours
Shield agent, so that the layer modelled after an antique made be protected, on the one hand to imitate so that the paint of layer modelled after an antique is completely cut off with air
Ancient layer is not directly exposed in air, slows down the oxidation rate of layer modelled after an antique.On the other hand, it prevents due to solarization, wind, rain
Beat, the atrocious weathers such as thunder and lightning and layer modelled after an antique is destroyed, increase the service life of layer modelled after an antique.
As a further improvement of the present invention, protectant each chemical composition is in parts by weight are as follows: and toluenesulfonamide/
40-45 parts of formaldehyde resin, 10-13 parts of dicetyl phosphate (changing brittleness, soft, water suction), 9-11 parts of sodium trimetaphosphate, with
And 25-30 parts of rosin.
Toluenesulfonamide/formaldehyde resin itself has viscous stickiness, enable to protective agent it is more stable be attached to building
On metope.On the other hand, there are sulfoamidos in toluenesulfonamide/formaldehyde resin molecule, have bioactivity, have to some
Pest is inhibited.Rosin is a kind of cheap Organic Ingredients, itself has volatility, in layer modelled after an antique after rosin volatilization
Surface quickly forms the firm and transparent film in side, prevents from being oxidized inside rosin, and the film formed is smooth.Rosin knot
Structure is more stable, can still keep stable chemical property under various severe natural environments.Dicetyl phosphate energy
Enough so that rosin is combined with each other transparent membrane infiltration that is stronger, and being formed in rosin with toluenesulfonamide/formaldehyde resin
Thoroughly, so as to dispersing extraneous pest.Dicetyl phosphate has good water imbibition, guarantees that layer modelled after an antique is constantly in drying
Environment, so that layer modelled after an antique be avoided to go mouldy.And sodium trimetaphosphate and dicetyl phosphate have synergistic effect, so that imitative
The protective layer that ancient layer surface is formed is more stable.
As a further improvement of the present invention, the step of being paint modelled after an antique, coating paint modelled after an antique is painted in the S3 includes:
A, 10min is gently ground using the waterproof abrasive paper of 300 mesh after completely dry to the putty layer in S2, and floating ash is swept
Only；
B, brush priming paint modelled after an antique, and to priming paint modelled after an antique it is completely dry after using the waterproof abrasive paper of 400 mesh gently grind 10min, and will
Floating ash is swept only；
C, paint modelled after an antique is brushed.
By using above-mentioned technical proposal, putty layer after the liquid honing of 300 mesh, is conducive to priming paint modelled after an antique and is adhered to,
So that the antique effect worked it out when subsequent brushing paint modelled after an antique is more life-like.Use the liquid honing of 400 mesh bottom excessively modelled after an antique
Qi Hou, then by paintbrush modelled after an antique on priming paint modelled after an antique, so that the complete rear surface of paintbrush modelled after an antique is smooth, facilitate subsequent modelled after an antique
Pattern modelled after an antique is sketched the contours on paint.
As a further improvement of the present invention, step c in the S3, to paint modelled after an antique it is completely dry after, use 400 mesh
Waterproof abrasive paper gently grinds 10min, is then needing to do old position coating attractant, and the building wall for coating attractant is exposed to
10-15h in air.
As a further improvement of the present invention, each chemical composition of the attractant is pig fat 20-25 in parts by weight
Part, 18-20 parts of glucose, 13-17 parts of fructose and 16 10-13 parts of carbon -11- olefine aldehydrs.
By using above-mentioned technical proposal, attractant is coated in building block, lures moth to damage building block, enhances block
Block does old effect.In the range of time controls 10-15h, then prevent moth from damaging to building block excessively serious；Pig fat is length
The unsaturated acids of chain provides energy for moth, moth is survived in building block；Glucose, fructose are as suction
The sweetener for drawing moth aggregation, enables to moth to be assembled；16 carbon -11- olefine aldehydr 10-13 can releasing hormone information,
Assemble in building block so that moth is large batch of, erosion speed is eaten into building block to improve, to improve old to doing for building block
Speed modelled after an antique.
As a further improvement of the present invention, it coats after the building wall of attractant exposes 10-15h in air and uses clear water
15min is rinsed, preservative is then coated with.
As a further improvement of the present invention, it is polished the building wall after coating attractant, scraping is handled.
As a further improvement of the present invention, each chemical composition of the preservative is carboxymethyl cellulose in parts by weight
15-20 parts, 25-30 parts of Arabic gum, 23-30 parts of zinc pyrithione and polysorbas20 are 12-17 parts.
Block surfaces are on the one hand made to form side and the external world by coating sealer by using above-mentioned technical proposal
The membrane structure separated, on the other hand prevent it is internal breed bacterium so that do it is old after time for saving of building block it is more permanent.
Wherein both carboxymethyl cellulose and Arabic gum combine, and as carrier, have the function of thickening；Zinc pyrithione has sterilization
Effect, prevents from breeding bacterium in building block；Polysorbas20 is as a kind of mild surfactant, so that the surface between each component
Power reduces, and to merge from each other more stable.
In conclusion the advantages of the present invention are:
1, protective agent is uniformly coated on layer modelled after an antique, so that the paint of layer modelled after an antique is completely cut off with air, thus will production
Good layer modelled after an antique is protected, and is not directly exposed to layer modelled after an antique in air, is slowed down the oxidation rate of layer modelled after an antique.
On the other hand, prevent from beating due to solarization, wind, rain, the atrocious weathers such as thunder and lightning and layer modelled after an antique is destroyed, increase modelled after an antique
The service life of layer；
2, putty layer after the liquid honing of 300 mesh, is conducive to priming paint modelled after an antique attachment, so that subsequent brush paint modelled after an antique
When the antique effect worked it out it is more life-like.Exist after the liquid honing of 400 mesh priming paint excessively modelled after an antique, then by paintbrush modelled after an antique
On priming paint modelled after an antique, so that the complete rear surface of paintbrush modelled after an antique is smooth, facilitates and subsequent sketch the contours pattern modelled after an antique on paint modelled after an antique.
Detailed description of the invention
Fig. 1 is a kind of process flow chart of the antique imitation process of building wall of the present invention.
Specific embodiment
With reference to the accompanying drawings and examples, present invention is further described in detail.
Embodiment 1:
Referring to Fig.1, a kind of antique imitation process of building wall, includes the following steps:
S1: first base course wall is cleaned.
S2: putty layer is formed after the putty of the surface of base's wall after clean batch.
Batch putty uses cement plaster, and cement plaster is made of cement, powder of lacquer putty for use on, 102 rubber powders, cellulose, ratio according to
Parts by weight mix for 15:7:5:7.
S3: coating paint modelled after an antique in putty layer, and sketches the contours of pattern modelled after an antique and form layer modelled after an antique.Wherein coat oil modelled after an antique
Paint includes the following steps:
A, after the putty layer that step S2 is formed is completely dry, using the waterproof abrasive paper of 300 mesh 10min is gently ground, it then will be greasy
The floating ash of sublayer is swept completely.
B, priming paint modelled after an antique is then brushed in putty layer, priming paint modelled after an antique is epoxy primer.To priming paint modelled after an antique it is completely dry it
10min is gently ground using the waterproof abrasive paper of 400 mesh afterwards, clears away dust.
C, paint modelled after an antique is brushed.Paint modelled after an antique is finishing coat modelled after an antique, is sketched the contours of on finishing coat modelled after an antique after having brushed finishing coat modelled after an antique
Figure modelled after an antique, to finishing coat modelled after an antique it is completely dry after, form layer modelled after an antique.
It needs to do old position in layer modelled after an antique and coats attractant, each chemical composition of attractant is in parts by weight are as follows: lard
23 parts of rouge, 19 parts of glucose, 15 parts of fructose and 16 12 parts of carbon -11- olefine aldehydrs.When configuring attractant, directly by above-mentioned three kinds
Substance is mixed evenly mutually according to parts by weight；The weight and building wall of attractant need to do the area ratio at old position
For 20g/cm2.After having coated attractant, the metope of building wall is exposed into 10-15h in air, is then rinsed using clear water
15min, then to having coated, the building wall after attractant is polished, scraping is handled.
Then to the whole coating preservative of building wall, each chemical composition of preservative is in parts by weight are as follows: carboxymethyl is fine
17 parts of dimension element, 27 parts of Arabic gum, 26 parts of zinc pyrithione and polysorbas20 are 14 parts.Weight used in preservative with draw
The weight of lure is identical.When configuring preservative, directly above-mentioned four kinds of substances are worked in coordination after mixing evenly i.e. according to parts by weight
It can.
S4: protective agent is coated on layer modelled after an antique, forms protective layer afterwards.Wherein protectant each chemical composition is in parts by weight
Are as follows: 43 parts of toluenesulfonamide/formaldehyde resin, 11 parts of dicetyl phosphate, 10 parts of sodium trimetaphosphate and 27 parts of rosin.Match
When setting protective agent, direct above-mentioned four kinds of substances are mutually added according to parts by weight, and after mixing evenly.Used in protective agent
The area ratio 17g/cm of weight and building wall2.After having coated protective agent, building wall is exposed into 8h in air.
S5: cleaning agent is used, protective layer is cleaned.Cleaning agent is white using the multi-functional mouldy cleaning agent of marble platform basin
Metope wall removes mildew mildew wallpaper cleaning agent except mould.Weight used in cleaning agent and the area ratio of building wall are 38g/cm2。
After S5, the work modelled after an antique of building wall is finished.
Embodiment 2-5 the difference from embodiment 1 is that, in step S3, each chemical composition of attractant is in parts by weight such as
Shown in following table: unit: part
Embodiment 6-9 the difference from embodiment 1 is that, in step S3, each chemical composition of preservative is in parts by weight such as
Shown in following table: unit: part
Embodiment 10-13 the difference from embodiment 1 is that, in step S4, protectant each chemical composition is in parts by weight
It is as shown in the table: unit: part
Comparative example: the difference from embodiment 1 is that, unprotect agent coating.
Experimental Comparison: the mode and embodiment 1 that comparative example is recorded are by the way of；Building wall after implementation by 3 years,
After 5 years and 10 years, the damaged condition of observation construction wall in a natural environment, in the following table by observation situation record.Damage
Situation is as shown in the table:
It is found by above comparison, due to having used protective agent in embodiment 1, so most intuitively showing as up to 10
As long as year, the appearance at the layer modelled after an antique of construction wall does not receive damage still, and uses the mode in comparative example, building
Slight damage occurs when appearance at wall layer modelled after an antique is after 5 years；At 10 years, damage more serious.
On the other hand, due to having smeared preservative on construction wall, so that comparative example is modelled after an antique by the way of
Building wall is still able to maintain 3 years without the influence by environment.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of antique imitation process of building wall, characterized by the following steps:
S1: base course wall is cleaned；
S2: putty layer is formed after the putty of the surface of base's wall after clean batch；
S3: paint is coated in putty layer, and sketches the contours of pattern modelled after an antique and forms layer modelled after an antique；
S4: protective agent is coated on layer modelled after an antique, forms protective layer afterwards:
S5: cleaning agent is used, protective layer is cleaned；
After S5, the work modelled after an antique of building wall is finished.
2. a kind of antique imitation process of building wall according to claim 1, it is characterised in that: protectant each chemical group
At in parts by weight are as follows: toluenesulfonamide/40-45 parts of formaldehyde resin, 10-13 parts of dicetyl phosphate, sodium trimetaphosphate 9-
11 parts and 25-30 parts of rosin.
3. a kind of antique imitation process of building wall according to claim 1, it is characterised in that: paint is oil modelled after an antique in the S3
Paint, the step of coating paint modelled after an antique include:
A, 10min is gently ground using the waterproof abrasive paper of 300 mesh after completely dry to the putty layer in S2, and floating ash is swept only；
B, brush priming paint modelled after an antique, and to priming paint modelled after an antique it is completely dry after using the waterproof abrasive paper of 400 mesh gently grind 10min, and by floating ash
It sweeps net；
C, paint modelled after an antique is brushed.
4. a kind of antique imitation process of building wall according to claim 3, it is characterised in that: step c in the S3, to modelled after an antique
After having painted completely dry, 10min is gently ground using 400 mesh waterproof abrasive papers, is then needing to do old position coating attractant, and
The building wall for coating attractant is exposed into 10-15h in air.
5. a kind of antique imitation process of building wall according to claim 4, it is characterised in that: each chemical group of the attractant
At being in parts by weight pig fat 20-25 parts, 18-20 parts of glucose, 13-17 parts of fructose and 16 carbon -11- olefine aldehydr 10-13
Part.
6. a kind of antique imitation process of building wall according to claim 5, it is characterised in that: the building wall for coating attractant exists
15min is rinsed using clear water after exposure 10-15h in air, is then coated with preservative.
7. a kind of antique imitation process of building wall according to claim 4, it is characterised in that: to the building after coating attractant
Wall is polished, scraping is handled.
8. a kind of antique imitation process of building wall according to claim 6, it is characterised in that: each chemical group of the preservative
At being in parts by weight carboxymethyl cellulose 15-20 parts, 25-30 parts of Arabic gum, 23-30 parts of zinc pyrithione and tween
20 be 12-17 parts.