CN1099018A - 氧化硅结合碳化硅耐火材料 - Google Patents

氧化硅结合碳化硅耐火材料 Download PDF

Info

Publication number
CN1099018A
CN1099018A CN 93111661 CN93111661A CN1099018A CN 1099018 A CN1099018 A CN 1099018A CN 93111661 CN93111661 CN 93111661 CN 93111661 A CN93111661 A CN 93111661A CN 1099018 A CN1099018 A CN 1099018A
Authority
CN
China
Prior art keywords
silicon
furnace
burner
carborundum
refractory material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 93111661
Other languages
English (en)
Inventor
晏溶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ELECTRONIC MATERIALS FACTORY XINHUA COUNTY HUNAN PROV
Original Assignee
ELECTRONIC MATERIALS FACTORY XINHUA COUNTY HUNAN PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ELECTRONIC MATERIALS FACTORY XINHUA COUNTY HUNAN PROV filed Critical ELECTRONIC MATERIALS FACTORY XINHUA COUNTY HUNAN PROV
Priority to CN 93111661 priority Critical patent/CN1099018A/zh
Publication of CN1099018A publication Critical patent/CN1099018A/zh
Pending legal-status Critical Current

Abstract

氧化硅结合碳化硅耐火材料,是一种无粘土结合,采用SiO2结合SiC,用于有色冶炼、钢铁、化学、化工及陶瓷工业中的竖炉、保温炉内衬砖、流槽、烧嘴、锌精馏塔盘等,以及隧道窑、推板窑等热工设备关键部位的耐火砖;各种电阻炉圆形、方形管和内外丝管、炉膛、烧嘴及各种特异型制品。它具有抗氧化性强,抗渣、耐磨性能优良,热导率高,热膨胀系数小等特点。

Description

本发明涉及一种氧化硅结合碳化硅耐火材料及其制备方法,主要用于有色冶炼、钢铁、化学、化工及陶瓷工业中的竖炉、保温炉内衬砖、流槽、烧咀、锌精馏塔盘等,以及隧道窑、推板窑等热工设备关键部位的耐火砖:各种电阻炉圆形、方形管和内外丝管、炉膛、烧咀及各种特异型制品。
粘土结合碳化硅耐火材料对陶瓷行业来说,较高铝质耐火材料虽有很大突破,但在抗氧化性能、落渣、度型等方面仍有不可避免的缺陷,应用范围仍受到一定限制。
本发明的目的旨在采用SiO2结合SiC(无粘土结合),以提高制品的抗氧化性能,抗渣以及拓宽应用范围,而提供一种氧化硅结合碳化硅耐火材料及其制备方法。
本发明的技术方案是这样实现的:组成材料的配比是,SiC为90-92%,SiO2微粉为8-10%,磷酸铝溶液为3-5%(外加)。
下面提供本发明的实施例:
对碳化硅材料,配料前需用水清洗和磁选去铁以及去掉碳化硅中的其它有害物质。组成原料配料时,含水率一般以6-8%为宜,通过坯料陈腐,然后在350kg/cm2压力下半干压成型,待在80℃-100℃干燥后放入7m3倒焰窑中(燃烧值为7千大卡)烧成,烧成时间为8小时,保温时间64小时,止火温度为1450℃。
氧化硅结合碳化硅耐火材料,除制作碳化硅匣钵外,还可制作平板、砖及各种特异型制品。它具有抗氧化性强,抗渣,耐磨性能优良,热导率高,热膨胀系数小等特点,与粘土结合碳化硅耐火材料,主要理化指标比较如下:
Figure 931116619_IMG1

Claims (5)

1、氧化硅结合碳化硅耐火材料,主要组成材料为碳化硅(SiC),其特征在于:组成材料的配比是:SiC为90-92%,SiO2微粉为8-10%,磷酸铝溶液为3-5%(外加)。
2、按权利要求1所述的碳化硅耐火材料,其特征是:对碳化硅材料,配料前需用水清洗和磁选去铁以及去掉碳化硅中的其它有害杂质。
3、按权利要求1或2所述的碳化硅耐火材料,其特征是:坯料中的含水率一般以6-8%为宜。
4、按权利要求3所述的碳化硅耐火材料,其特征是:坯料在350kg/cm2压力下半干压成型。
5、按权利要求1或2所述的碳化硅耐火材料,其特征是:制品放在燃烧值为7千大卡的7m3倒焰窑中烧成,烧成时间为8小时,保温64小时,止火温度为1450℃。
CN 93111661 1993-08-14 1993-08-14 氧化硅结合碳化硅耐火材料 Pending CN1099018A (zh)