CN109851315A - A kind of boccaro flat brick and preparation method thereof - Google Patents
A kind of boccaro flat brick and preparation method thereof Download PDFInfo
- Publication number
- CN109851315A CN109851315A CN201711234299.7A CN201711234299A CN109851315A CN 109851315 A CN109851315 A CN 109851315A CN 201711234299 A CN201711234299 A CN 201711234299A CN 109851315 A CN109851315 A CN 109851315A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- boccaro
- brick
- flat brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of boccaro flat brick and preparation method thereof, which is made of the raw material of following parts by weight: 20-25 parts of Red Stone Ware, 5-10 parts of clay, 20-25 parts of silica flour, 10-15 parts of clinker, useless 10-15 parts of brick powder, 10-15 parts of wollastonite, 10-15 parts of potassium feldspar, 10-15 parts of albite, 5-8 parts of talcum powder, 0.5-1 parts of colorant, 0.5-1 parts of brown iron oxide, 0.5-1 parts of manganese powder, 0.5-1 parts of viscosity additives, 0.5-1 parts of resin glue.Beneficial effect is: not only manufacturing cost is low for the boccaro flat brick, and heat insulation and preservation effect is good, and intensity is high, and good compactness, is not likely to produce cracking, and environmental protection has no adverse effects to human body, can purify the air of a room, complies fully with the developing direction of modern materials for wall.
Description
Technical field
The present invention relates to a kind of building decoration materials, in particular to a kind of boccaro flat brick and preparation method thereof.
Background technique
Ceramic Tiles are by clay, quartz sand and other inorganic non-metallic raw materials, through ingredient, ball milling, powder processed, molding, burning
The lamellar ceramic of the techniques such as knot production, is mainly used for the wall fitting in indoor toilets and kitchen.With economical fast
The continuous improvement of speed development and living standards of the people, requirement of the people to living environment are also higher and higher.But current ceramics
Brick product remains manufacturing cost height, and heat insulation and preservation effect is poor, and water absorption rate is high, and intensity is low, many deficiencies such as is easily cracked
Place, and without environmental protection characteristic, to human body etc., there are adverse effects, are unable to reach purification air, do not meet modern materials for wall completely
Developing direction.
Summary of the invention
Low the technical problem to be solved by the present invention is to provide a kind of manufacturing cost, heat insulation and preservation effect is good, and intensity is high
Boccaro flat brick and preparation method thereof.
To solve the above problems, the present invention adopts the following technical scheme:
A kind of boccaro flat brick, is made of the raw material of following parts by weight: 20-25 parts of Red Stone Ware, 5-10 parts of clay, and silica flour
20-25 parts, 10-15 parts of clinker, useless 10-15 parts of brick powder, 10-15 parts of wollastonite, 10-15 parts of potassium feldspar, 10-15 parts of albite,
5-8 parts of talcum powder, 0.5-1 parts of colorant, 0.5-1 parts of brown iron oxide, 0.5-1 parts of manganese powder, 0.5-1 parts of viscosity additives, resin glue
0.5-1 parts.
A kind of preparation method of boccaro flat brick, comprising steps are as follows:
1,10-15 parts of wollastonites, 10-15 parts of potassium feldspars, 10-15 parts of albites are carried out brokenly respectively using jaw crusher
Broken processing, particle size control is in 1-3mm after being crushed；
2, the raw material of following parts by weight is subjected to proportion mixing: 20-25 parts of Red Stone Ware, 5-10 parts of clay, silica flour 20-25
Part, 10-15 parts of clinker, useless 10-15 parts of brick powder, 10-15 parts of wollastonite, 10-15 parts of potassium feldspar, 10-15 parts of albite, talcum powder
5-8 parts, 0.5-1 parts of colorant, 0.5-1 parts of brown iron oxide, 0.5-1 parts of manganese powder, 0.5-1 parts of viscosity additives, resin glue 0.5-1
Part；Slurry, ground 40 mesh after sieving, drying are made using wet ball grinding；
3, it then carries out water spray granulation, after crossing 20 meshes, then carries out aging, obtain powder；Powder is passed through into half dry pressing
It is pressed into ceramic thin plate green compact；
4, ceramic thin plate green compact are put into electrical kiln and are fired, control firing temperature is 1400 DEG C, and the time is 12 hours, that is, is made
At the boccaro flat brick.
The beneficial effects of the present invention are: not only manufacturing cost is low for boccaro flat brick of the present invention, heat insulation and preservation effect
Good, intensity is high, and good compactness, is not likely to produce cracking, and environmental protection has no adverse effects to human body, can purify the air of a room, complete
Meet the developing direction of modern materials for wall entirely.
Specific embodiment
Embodiment 1
A kind of boccaro flat brick of the present invention, is made of following raw material: 20kg parts of Red Stone Ware, clay 5kg, silica flour
20kg, clinker 10kg, useless brick powder 10kg, wollastonite 10kg, potassium feldspar 10kg, albite 10kg, talcum powder 5kg, colorant
0.5kg, brown iron oxide 0.5kg, manganese powder 0.5kg, viscosity additives 0.5kg, resin glue 0.5kg.
A kind of preparation method of boccaro flat brick of the present invention, comprising steps are as follows:
1,10kg wollastonite, 10kg potassium feldspar, 10kg albite are subjected to break process using jaw crusher respectively, broken
Particle size control is in 1-3mm after broken；
2, the raw material is subjected to proportion mixing: slurry, ground 40 mesh after sieving, drying is made using wet ball grinding
Sieve；
3, it then carries out water spray granulation, after crossing 20 meshes, then carries out aging, obtain powder；Powder is passed through into half dry pressing
It is pressed into ceramic thin plate green compact；
4, ceramic thin plate green compact are put into electrical kiln and are fired, control firing temperature is 1400 DEG C, and the time is 12 hours, that is, is made
At the boccaro flat brick.
Embodiment 2
A kind of boccaro flat brick of the present invention, is made of following raw material: Red Stone Ware 25kg, clay 10kg, silica flour
25kg, clinker 15kg, useless brick powder 15kg, wollastonite 15kg, potassium feldspar 15kg, albite 15kg, talcum powder 8kg, colorant 1kg,
Brown iron oxide 1kg, manganese powder 1kg, viscosity additives 1kg, resin glue 1kg.
A kind of preparation method of boccaro flat brick of the present invention, comprising steps are as follows:
1,15kg wollastonite, 15kg potassium feldspar, 15kg albite are subjected to break process using jaw crusher respectively, broken
Particle size control is in 1-3mm after broken；
2, the raw material is subjected to proportion mixing: slurry, ground 40 mesh after sieving, drying is made using wet ball grinding
Sieve；
3, it then carries out water spray granulation, after crossing 20 meshes, then carries out aging, obtain powder；Powder is passed through into half dry pressing
It is pressed into ceramic thin plate green compact；
4, ceramic thin plate green compact are put into electrical kiln and are fired, control firing temperature is 1400 DEG C, and the time is 12 hours, that is, is made
At the boccaro flat brick.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details.
Claims (2)
1. a kind of boccaro flat brick, it is characterised in that be made of the raw material of following parts by weight: 20-25 parts of Red Stone Ware, clay 5-10
Part, 20-25 parts of silica flour, 10-15 parts of clinker, useless 10-15 parts of brick powder, 10-15 parts of wollastonite, 10-15 parts of potassium feldspar, albite
10-15 parts, 5-8 parts of talcum powder, 0.5-1 parts of colorant, 0.5-1 parts of brown iron oxide, 0.5-1 parts of manganese powder, viscosity additives 0.5-1
Part, 0.5-1 parts of resin glue.
2. a kind of preparation method of boccaro flat brick as described in claim 1, it is characterised in that comprising steps are as follows:
(1) 10-15 parts of wollastonites, 10-15 parts of potassium feldspars, 10-15 parts of albites are crushed respectively using jaw crusher
Processing, particle size control is in 1-3mm after being crushed；
(2) raw material of following parts by weight is subjected to proportion mixing: 20-25 parts of Red Stone Ware, 5-10 parts of clay, 20-25 parts of silica flour,
10-15 parts of clinker, useless 10-15 parts of brick powder, 10-15 parts of wollastonite, 10-15 parts of potassium feldspar, 10-15 parts of albite, talcum powder 5-8
Part, 0.5-1 parts of colorant, 0.5-1 parts of brown iron oxide, 0.5-1 parts of manganese powder, 0.5-1 parts of viscosity additives, 0.5-1 parts of resin glue；It adopts
Slurry, ground 40 mesh after sieving, drying is made with wet ball grinding；
(3) it then carries out water spray granulation, after crossing 20 meshes, then carries out aging, obtain powder；Powder is suppressed by half dry pressing
At ceramic thin plate green compact；
(4) ceramic thin plate green compact are put into electrical kiln and are fired, control firing temperature is 1400 DEG C, and the time is 12 hours, that is, is made
The boccaro flat brick.