CN103641404A - Art ceramic product and preparation method thereof - Google Patents
Art ceramic product and preparation method thereof Download PDFInfo
- Publication number
- CN103641404A CN103641404A CN201310675368.3A CN201310675368A CN103641404A CN 103641404 A CN103641404 A CN 103641404A CN 201310675368 A CN201310675368 A CN 201310675368A CN 103641404 A CN103641404 A CN 103641404A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- art ceramic
- ceramic products
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an art ceramic product and a preparation method thereof. The art ceramic product comprises the following components in parts by weight: 28-41 parts of SiO2, 18-32 parts of clay, 4-11 parts of cement, 8-13 parts of magnesium oxide, 12-15 parts of zinc oxide, 8-10 parts of zirconia, 2-3 parts of titanium oxide, 6-7 parts of manganese oxide, 2-3 parts of boron nitride, 0.6-1.2 parts of niobium oxide, 0.25-0.4 parts of dispersing agent and 0.4-0.5 parts of polyacrylamide.
Description
Technical field
The present invention relates to art ceramic products and preparation method thereof.
Background technology
The invention of pottery is the major contributions of Chinese to the mankind.Pottery has been subject to broad masses' attention always and has liked since invention, is integral part important in human lives.
Existing ceramic, generally need to pass through high temperature sintering in its making processes, its complex manufacturing technology, and need to consume certain energy, thereby its production cost is higher, and to environment.
Summary of the invention
Shortcoming for prior art, the invention provides a kind of art ceramic products and preparation method thereof.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
An art ceramic products, it comprises following component and weight proportion:
Si0
228～41 parts, 18～32 parts of clays, 4～11 parts of cement, 8～13 parts, magnesium oxide, 12～15 parts, zinc oxide, 8～10 parts of zirconium whites, 2～3 parts of titanium oxide, 6～7 parts of manganese oxide, 2～3 parts of boron nitride, 0.6～1.2 part of niobium oxides, 0.25～0.4 part of dispersion agent, 0.4～0.5 part of polyacrylamide.
Concrete, comprise following component and weight proportion:
Si0
233 parts, 23 parts of clays, 8 parts of cement, 10 parts, magnesium oxide, 13 parts, zinc oxide, 9 parts of zirconium whites, 2.5 parts of titanium oxide, 6.5 parts of manganese oxide, 2.5 parts of boron nitride, 0.9 part of niobium oxides, 0.3 part of dispersion agent, 0.45 part of polyacrylamide.
The present invention also provides a kind of preparation method of art ceramic products, and it comprises the following steps:
S1: described each component is prepared burden in proportion, and then mix and blend is 5～7 minutes, practices and makes mud;
S2: by mud injection technology product mould, got final product stripping forming after 3 hours;
S3: by the handicraft spontaneous curing at normal temperatures of institute's injection moulding.
The present invention is a kind of solidifying porcelain, the natural mineral matter being synthesized by multiple inanimate matter and other inanimate matter weighting material are made, its one-tenth porcelain principle is that the gelling initiator in material prescription causes jelling agent at normal temperatures, then by a series of chemical reaction, gel is crosslinking in inorganic filler mutually, through spontaneous curing, forms pottery.The prolongation of intensity set time of pottery and strengthening, finally reaches firmness degree.
In each component of the present invention, sand and clay are skeletons, and gypsum is quick dry agent, and rapid shaping effect is played in the cooperation of cement and zinc oxide, and bittern is comprehensive gelifying agent, and phosphoric acid and ferrous sulfate play mediation effect.
The present invention can be widely used in landscape art and technique Decorative Ceramics, architectural pottery, finishing material etc.Because goods are without firing, can save mass energy; Thereby there are energy-conserving and environment-protective; Starting material are easily obtained again, and manufacture craft is simple, and cost is lower.Made goods under physical environment after certain hour degradable, there is environmental protection.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
The present embodiment discloses a kind of art ceramic products, and it comprises following component and weight proportion:
Si0
228～41 parts, 18～32 parts of clays, 4～11 parts of cement, 8～13 parts, magnesium oxide, 12～15 parts, zinc oxide, 8～10 parts of zirconium whites, 2～3 parts of titanium oxide, 6～7 parts of manganese oxide, 2～3 parts of boron nitride, 0.6～1.2 part of niobium oxides, 0.25～0.4 part of dispersion agent, 0.4～0.5 part of polyacrylamide.
Concrete, comprise following component and weight proportion:
Si0
233 parts, 23 parts of clays, 8 parts of cement, 10 parts, magnesium oxide, 13 parts, zinc oxide, 9 parts of zirconium whites, 2.5 parts of titanium oxide, 6.5 parts of manganese oxide, 2.5 parts of boron nitride, 0.9 part of niobium oxides, 0.3 part of dispersion agent, 0.45 part of polyacrylamide.
The present invention also provides a kind of preparation method of art ceramic products, and it comprises the following steps:
S1: described each component is prepared burden in proportion, and then mix and blend is 5～7 minutes, practices and makes mud;
S2: by mud injection technology product mould, got final product stripping forming after 3 hours;
S3: by the handicraft spontaneous curing at normal temperatures of institute's injection moulding.
Claims (3)
1. an art ceramic products, is characterized in that, comprises following component and weight proportion:
Si0
228～41 parts, 18～32 parts of clays, 4～11 parts of cement, 8～13 parts, magnesium oxide, 12～15 parts, zinc oxide, 8～10 parts of zirconium whites, 2～3 parts of titanium oxide, 6～7 parts of manganese oxide, 2～3 parts of boron nitride, 0.6～1.2 part of niobium oxides, 0.25～0.4 part of dispersion agent, 0.4～0.5 part of polyacrylamide.
2. art ceramic products according to claim 1, is characterized in that, comprises following component and weight proportion:
Si0
233 parts, 23 parts of clays, 8 parts of cement, 10 parts, magnesium oxide, 13 parts, zinc oxide, 9 parts of zirconium whites, 2.5 parts of titanium oxide, 6.5 parts of manganese oxide, 2.5 parts of boron nitride, 0.9 part of niobium oxides, 0.3 part of dispersion agent, 0.45 part of polyacrylamide.
3. the preparation method of art ceramic products according to claim 1, is characterized in that, comprises the following steps:
S1: described each component is prepared burden in proportion, and then mix and blend is 5～7 minutes, practices and makes mud;
S2: by mud injection technology product mould, got final product stripping forming after 3 hours;
S3: by the handicraft spontaneous curing at normal temperatures of institute's injection moulding.