CN109837145A - A kind of aqueous fluxes in electronic industry cleaning agent and preparation method thereof - Google Patents
A kind of aqueous fluxes in electronic industry cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN109837145A CN109837145A CN201910272251.8A CN201910272251A CN109837145A CN 109837145 A CN109837145 A CN 109837145A CN 201910272251 A CN201910272251 A CN 201910272251A CN 109837145 A CN109837145 A CN 109837145A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- parts
- electronic industry
- aqueous
- fluxes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cleaning agent technical fields, more particularly to a kind of aqueous fluxes in electronic industry cleaning agent and preparation method thereof, each component is as follows by weight in the composition of raw materials of the aqueous fluxes in electronic industry cleaning agent: 50~70 parts of higher boiling alcohol ether, 20~30 parts of terpinol, 1~2 part of corrosion inhibiter, 1.5~4 parts of emulsifier, 1~2 part of bleeding agent, 1~2 part of alkali, 10~20 parts of deionized water.Novel PCB board flux cleaning agent of the invention is environmental type cleaning agent, is free of fluorocarbon solvent and halogenated hydrocarbons.Human health is not threatened.Easy to use, environmentally friendly, safe, application method is simple, after being according to demand diluted concentrate, carries out ultrasonic wave or spray cleaning.Pcb board surface welding-assistant can be effectively removed, the pcb board after the cleaning of this cleaning agent can directly carry out lower step process after rinsing and air-dry using water.
Description
Technical field
The present invention relates to cleaning agent technical field, in particular to a kind of aqueous fluxes in electronic industry cleaning agent and its preparations
Method.
Background technique
As electronic product is quickly to the development of miniaturization, high-precision and high reliability direction, in electronic manufacture
More and more pollutants are introduced in technique, such as assemble wiring board during dress connection welding, in order to ensure welding
Reliability, it is necessary to which, using the higher scaling powder of activity, these welding assisted agent residuals can etching lines plate and member on assembling wiring board
Device, while its surface insulation resistance can be reduced, especially under the condition of high temperature and high humidity, it may appear that serious corrosion and electric leakage,
Influence the reliability of complete machine.The residue assembled on wiring board is mainly the electronic weldings auxiliary material such as solder(ing) paste and scaling powder
Residue, hand perspiration, finger mark and the pollutants such as the fiber fallen in the air and dust left in operating process, these material compositions are multiple
Miscellaneous, containing the ingredient not soluble in water such as resin, grease, activating agent, there are also anions and canons and weak organic acid.Therefore in order to ensure
Electronic fabrication processes are gone on smoothly, and guarantee product quality and reliability produced, it is necessary in many links of process implementing
It imports cleaning process and uses cleaning agent.
Traditional cleaning process generally uses the ODS cleaning agent containing freon, such cleaning agent have chemical stability it is good,
Small toxicity is not burnt, many superiority such as surface tension is small and is able to maintain stronger permeability and rapid-drying properties, but ODS class
Cleaning agent has extremely strong destructive power to ozone layer, and greenhouse effects are serious, seriously endangers the ecological environment of the mankind, in addition, such as hydrogen
Chlorofluorocarbons, perfluoroparaffin and other halogenated hydrocarbon cleaning agents, it is all harmful to environment and human body.Therefore, the electronics of environmental protection is developed
Industrial flux cleaning agent is with regard to very necessary.
Chinese patent (CN102851151A) discloses a kind of used in electronic industry environment-friendly cleaning agent, including 2- methylpent
Alkane, dehydrated alcohol, ether solvent replace n-hexane using methylpentane, reduce cleaning agent to the toxicity of human body, and weld to helping
Rosin in agent has good solubility property, and ether solvent has good solubility property, anhydrous second to the organic acid in scaling powder
Alcohol plays the role of degreasing well, but the cleaning agent prepared is still toxic to human body, and moisture-free, is easy to clear
It washes device to pollute and remain, causes secondary pollution.Chinese patent (CN106635460A) discloses a kind of water-base electron work
Industry flux cleaning agent and preparation method thereof and application method, including high-boiling point alcohol ether solvent, n-methyl-2-pyrrolidone,
Ethyl alcohol, nonionic surfactant and water.Wherein higher boiling alcohol ether can prevent the volatilization of cleaning agent, reduce in cleaning process
Loss, joined water, improves its safety, while resin, scaling powder, touching of the cleaning agent to all kinds of electronic circuit plate surfaces
The purpose of Rapid Cleaning can be played by becoming agent, thickener and other pollutants, and cleaning efficiency is higher.But according to above-mentioned
The prior art develops aqueous electronics work it is found that cleaning agent water base in electronics integrated circuit board flux cleaning agent at present is less
Industry flux cleaning agent has market prospects.
Summary of the invention
The technical problem to be solved by the present invention is to overcome prior art disadvantage, provide a kind of aqueous fluxes in electronic industry
Cleaning agent and preparation method thereof further enriches cleaning agent type in the market.
In order to solve the above technical problems, technical solution provided by the invention are as follows: a kind of aqueous fluxes in electronic industry cleaning
Agent, each component is according to parts by weight in cleaning agent formula: 50~70 parts of higher boiling alcohol ether, 20~30 parts of terpinol, corrosion inhibiter 1~
2 parts, 1.5~4 parts of emulsifier, 1~2 part of bleeding agent, 1~2 part of alkali, 10~20 parts of deionized water.
As an improvement, the higher boiling alcohol ether is dipropylene, dipropylene glycol methyl ether, dipropylene glycol propyl ether, the third two
The combination of one or more of alcohol butyl ether.
As an improvement, the corrosion inhibiter is benzotriazole or methylbenzotriazole.
As an improvement, the emulsifier is isomeric alcohol polyethenoxy ether EH-6, octyl phenol polyoxyethylene ether OP-10 with quality
The mixture formed than 1~2:1~2.
As an improvement, the bleeding agent is one of fatty alcohol polyoxyethylene ether JFC-E, JFC-U or JFC-2.
As an improvement, the alkali is one of sodium hydroxide, potassium hydroxide or sodium carbonate.
A kind of aqueous fluxes in electronic industry cleaning agent preparation method, comprising the following steps:
S1 sequentially adds higher boiling alcohol ether, terpinol and corrosion inhibiter into reaction kettle, stirs 5~10min, speed of agitator
For 500~1000r/m;
Emulsifier and bleeding agent is added after solution clarification in S2;
S3 will be dissolved in deionized water before alkali carries, reaction kettle finally is added in aqueous alkali, stir 10~30min, and dispersion is equal
It is even;
S4, standing are cooled to room temperature, and obtain aqueous fluxes in electronic industry cleaning agent.
As an improvement, cleaning agent concentrate is diluted as needed and is heated to 50 DEG C, the pcb board for then cleaning needs
5~15min is cleaned using the method for ultrasonic wave or spray, then after pure water rinses and air-dries.
The present invention has the advantage that (1) aqueous fluxes in electronic industry cleaning agent prepared by the present invention is environmentally protective
Type cleaning agent is free of fluorocarbon solvent and halogenated hydrocarbon solvent, will not will not corrode equipment to human health and environmental concerns.
It is easy to use, safe, there can be good cleaning effect by ultrasonic wave or spray cleaning.
(2) contain high-boiling point alcohol ether solvents in aqueous fluxes in electronic industry cleaning agent prepared by the present invention in scaling powder
Organic acid have very strong cleaning action, terpinol, according to similar compatibility principle, there is rosin since its structure is similar to rosin
Good cleaning effect.
(3) mechanism of action of aqueous fluxes in electronic industry cleaning agent prepared by the present invention is simple, can with ethyl alcohol, water or
The dilution of person's ethanol water, enhances organic solvent and water directly dissolves each other effect, makes aqueous fluxes in electronic industry cleaning agent
Stability it is good, use safer.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments.
Embodiment 1
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
55 parts of dipropylene, 20 parts of terpinol, 1 part of benzotriazole, 1 part of EH-6,0.5 part of OP-10, JFC-E
1.5 parts, 1 part of sodium hydroxide, 20 parts of deionized water.
The preparation method comprises the following steps: sequentially adding dipropylene, terpinol and benzene into reaction kettle under the revolving speed of 500r/m
Parallel triazole stirs 5min, and EH-6, OP-10 and JFC-E is added after solution clarification, sodium hydroxide is dissolved in deionization in advance
Finally reaction kettle is added in aqueous alkali by water, is stirred 30min, is uniformly dispersed, is cooled to room temperature, and is stood, is obtained aqueous electronics work
Industry flux cleaning agent.
Application method 1: concentrate is diluted to 4 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 4 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Embodiment 2
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
60 parts of dipropylene glycol methyl ether, 20 parts of terpinol, 1 part of benzotriazole, 1 part of EH-6,0.5 part of OP-10, JFC-E
1.5 parts, 1 part of sodium hydroxide, 15 parts of deionized water.
The preparation method comprises the following steps: sequentially adding dipropylene glycol methyl ether, terpinol and benzene into reaction kettle under the revolving speed of 800r/m
Parallel triazole stirs 5min, and EH-6, OP-10 and JFC-E is added after solution clarification, sodium hydroxide is dissolved in deionization in advance
Finally reaction kettle is added in aqueous alkali by water, is stirred 30min, is uniformly dispersed, is cooled to room temperature, and is stood, is obtained aqueous electronics work
Industry flux cleaning agent.
Application method 1: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Embodiment 3
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
70 parts of dipropylene glycol propyl ether, 20 parts of terpinol, 1 part of benzotriazole, 1 part of EH-6,0.5 part of OP-10, JFC-E
1.5 parts, 1 part of sodium hydroxide, 10 parts of deionized water.
The preparation method comprises the following steps: under the revolving speed of 1000r/m, sequentially added into reaction kettle dipropylene glycol propyl ether, terpinol and
Benzotriazole, stir 5min, after solution clarification after be added EH-6, OP-10 and JFC-E, sodium hydroxide is dissolved in advance from
Finally reaction kettle is added in aqueous alkali by sub- water, is stirred 30min, is uniformly dispersed, is cooled to room temperature, and is stood, is obtained aqueous electronics
Industrial flux cleaning agent.
Application method 1: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Embodiment 4
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
50 parts of dipropylene glycol methyl ether, 30 parts of terpinol, 1 part of benzotriazole, 1 part of EH-6,0.5 part of OP-10, JFC-E
1.5 parts, 2 parts of sodium carbonate, 14 parts of deionized water.
The preparation method comprises the following steps: sequentially adding dipropylene glycol methyl ether, terpinol and benzene into reaction kettle under the revolving speed of 600r/m
Parallel triazole stirs 8min, and EH-6, OP-10 and JFC-E is added after solution clarification, sodium carbonate is dissolved in deionized water in advance,
Reaction kettle finally is added in aqueous alkali, 30min is stirred, is uniformly dispersed, is cooled to room temperature, stands, obtains aqueous electronics industry
Flux cleaning agent.
Application method 1: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Embodiment 5
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
55 parts of dipropylene glycol propyl ether, 20 parts of terpinol, 2 parts of methylbenzotriazole, 2 parts of EH-6,2 parts of OP-10, JFC-
2 parts of E, 2 parts of sodium hydroxide, 15 parts of deionized water.
The preparation method comprises the following steps: sequentially adding dipropylene glycol propyl ether, terpinol and first into reaction kettle under the revolving speed of 500r/m
Base benzotriazole stirs 10min, and EH-6, OP-10 and JFC-E is added after solution clarification, sodium hydroxide is dissolved in advance
Finally reaction kettle is added in aqueous alkali by ionized water, is stirred 10min, is uniformly dispersed, is cooled to room temperature, and is stood, is obtained aqueous electricity
Sub- industry flux cleaning agent.
Application method 1: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Embodiment 6
A kind of aqueous fluxes in electronic industry cleaning agent, formula in each component it is as follows by weight:
55 parts of dipropylene, 25 parts of terpinol, 1 part of benzotriazole, 1 part of EH-6,2 parts of OP-10, JFC-E 2
Part, 1 part of potassium hydroxide, 13 parts of deionized water.
The preparation method comprises the following steps: sequentially adding dipropylene, terpinol and benzene into reaction kettle under the revolving speed of 800r/m
Parallel triazole stirs 10min, and EH-6, OP-10 and JFC-E is added after solution clarification, sodium hydroxide is dissolved in deionization in advance
Finally reaction kettle is added in aqueous alkali by water, is stirred 10min, is uniformly dispersed, is cooled to room temperature, and is stood, is obtained aqueous electronics work
Industry flux cleaning agent.
Application method 1: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board use ultrasonic cleaning 10min, then through pure water rinse and air-dry after.
Application method 2: concentrate is diluted to 5 times (mass ratioes) of script and is heated to 50 DEG C, then will need to clean
Pcb board using spray technique clean 10min, then through pure water rinse and air-dry after.
Performance test:
Through detecting, the aqueous fluxes in electronic industry cleaning agent of Examples 1 to 6 preparation is imitated using the cleaning of application method 1
Fruit, flux cleaning rate and corrosive effect result are as follows:
Through detecting, the aqueous fluxes in electronic industry cleaning agent of Examples 1 to 6 preparation is imitated using the cleaning of application method 2
Fruit, flux cleaning rate and corrosive effect result are as follows:
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, fall within the scope of the claimed invention without departing from theon the basis of the spirit of the present invention.
Claims (8)
1. a kind of aqueous fluxes in electronic industry cleaning agent, which is characterized in that each component is according to parts by weight in cleaning agent formula:
50~70 parts of higher boiling alcohol ether, 20~30 parts of terpinol, 1~2 part of corrosion inhibiter, 1.5~4 parts of emulsifier, 1~2 part of bleeding agent, alkali
1~2 part, 10~20 parts of deionized water.
2. a kind of aqueous fluxes in electronic industry cleaning agent according to claim 1, it is characterised in that: the high-boiling point alcohol
Ether is the combination of one or more of dipropylene, dipropylene glycol methyl ether, dipropylene glycol propyl ether, propandiol butyl ether.
3. a kind of aqueous fluxes in electronic industry cleaning agent according to claim 1, it is characterised in that: the corrosion inhibiter is
Benzotriazole or methylbenzotriazole.
4. a kind of aqueous fluxes in electronic industry cleaning agent according to claim 1, it is characterised in that: the emulsifier is
The mixture that isomeric alcohol polyethenoxy ether EH-6, octyl phenol polyoxyethylene ether OP-10 are formed with mass ratio 1~2:1~2.
5. a kind of aqueous fluxes in electronic industry cleaning agent according to claim 1, it is characterised in that: the bleeding agent is
One of fatty alcohol polyoxyethylene ether JFC-E, JFC-U or JFC-2.
6. a kind of aqueous fluxes in electronic industry cleaning agent according to claim 1, it is characterised in that: the alkali is hydrogen-oxygen
Change one of sodium, potassium hydroxide or sodium carbonate.
7. a kind of aqueous fluxes in electronic industry cleaning agent preparation method according to claim 1, which is characterized in that including
Following steps:
S1 sequentially adds higher boiling alcohol ether, terpinol and corrosion inhibiter into reaction kettle, stirs 5~10min, speed of agitator 500
~1000r/m;
Emulsifier and bleeding agent is added after solution clarification in S2;
S3 will be dissolved in deionized water before alkali carries, reaction kettle finally is added in aqueous alkali, stirs 10~30min, is uniformly dispersed;
S4, standing are cooled to room temperature, and obtain aqueous fluxes in electronic industry cleaning agent.
8. a kind of aqueous fluxes in electronic industry cleaning agent preparation method according to claim 1, it is characterised in that: according to
It needs to dilute cleaning agent concentrate and is heated to 50 DEG C, then the pcb board that cleans will be needed using ultrasonic wave or spray
Method cleans 5~15min, then after pure water rinses and air-dries.