CN109778533A - A kind of manufacture craft of seaweed fiber blending flame retardant textiles - Google Patents
A kind of manufacture craft of seaweed fiber blending flame retardant textiles Download PDFInfo
- Publication number
- CN109778533A CN109778533A CN201711109296.0A CN201711109296A CN109778533A CN 109778533 A CN109778533 A CN 109778533A CN 201711109296 A CN201711109296 A CN 201711109296A CN 109778533 A CN109778533 A CN 109778533A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- seaweed
- fire
- manufacture craft
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacture crafts of seaweed fiber blending flame retardant textiles.It is characterized by comprising following processing steps: 1) melting after drying seaweed, fire retardant is added and is copolymerized together, alginate fibre is made, the fire retardant is made of the ingredient mixing of following weight percent: calcium carbonate 13%~14%；Zinc sulphide 0.2%~0.3%；Barium hydroxide 10%~20%；Magnesium sulfate 10%~20%；Diatomite surplus；2) alginate fibre, polyamide fibre, terylene, cotton yarn are woven into flame retardant fabric；3) flame retardant fabric is carried out rolling suction processing, 75% or more liquid carrying rate in fire retardant；4) suction treated cloth will be rolled and carry out drying and processing.The beneficial effects of the present invention are: the manufacture craft of seaweed cloth of the present invention is easy to operate, operating process is easily controllable, the seaweed cloth-like texture being made is soft, it is light, have extremely strong fire-retardant and fire-proof function.
Description
Technical field
The present invention relates to a kind of manufacture crafts of seaweed fiber blending flame retardant textiles.
Background technique
Seaweed is the algae to live in the sea, is the cryptogam of plant kingdom, and algae is to generate energy with photosynthesis
Biology, they are generally considered to be simple plant, and protein needed by human, fat, carbohydrate, more is contained in seaweed
Kind vitamin and minerals, nutritive value are significantly larger than terrestrial vegetables, and under photosynthesis, seaweed is various inorganic in ocean
Object is converted into organic matter, thus more containing some compounds not having in terrestrial vegetables in seaweed body.In view of its special function
Can, China's marine algae resource is abundant in addition, and seaweed products are just being widely used in surgical dressing, pharmaceuticals industry, food preservation, spinning
Weaver's industry, paper industry, photograph etc..
Summary of the invention
Aiming at the problems existing in the prior art, the purpose of the present invention is to provide a kind of fire-retardant weavings of seaweed fiber blending
The technical solution of the manufacture craft of product.
The manufacture craft of a kind of seaweed fiber blending flame retardant textiles, it is characterised in that walked including following technique
It is rapid: 1) to be melted after drying seaweed, fire retardant is added and is copolymerized together, alginate fibre is made；2) by alginate fibre, polyamide fibre, terylene,
Cotton yarn is woven into flame retardant fabric；3) flame retardant fabric is carried out rolling suction processing, 75% or more liquid carrying rate in fire retardant；4) suction will be rolled
Treated, and cloth carries out drying and processing.
The manufacture craft of a kind of seaweed fiber blending flame retardant textiles, it is characterised in that the fire retardant is by following
The ingredient of weight percent mixes composition: calcium carbonate 13%~14%；Zinc sulphide 0.2%~0.3%；Barium hydroxide 10%~
20%；Magnesium sulfate 10%~20%；Diatomite surplus.
The manufacture craft of a kind of seaweed fiber blending flame retardant textiles, it is characterised in that miscellaneous in the alginate fibre
Matter content is lower than 5%.
The manufacture craft of a kind of seaweed fiber blending flame retardant textiles, it is characterised in that in the flame retardant fabric
Alginate fibre content is 30-40%, polyamide fibre 15-20%, terylene 15-20%, remaining be cotton yarn, the content is weight percent
Than.
The manufacture craft of a kind of seaweed fiber blending flame retardant textiles, it is characterised in that described to roll suction treatment temperature
It is maintained at 30-50 degree, described to roll the suction processing time be 40-80 minutes.
A kind of manufacture craft of seaweed fiber blending flame retardant textiles, it is characterised in that the temperature when drying and processing
Degree is 25-60 degree, and the drying and processing time is 5-25 minutes.
The beneficial effects of the present invention are: the manufacture craft of seaweed cloth of the present invention is easy to operate, operating process is easily controllable,
The seaweed cloth-like texture being made is soft, it is light, have extremely strong fire-retardant and fire-proof function.
Specific embodiment
The manufacture craft of seaweed fiber blending flame retardant textiles of the present invention, comprises the following steps that: 1) drying seaweed
After melt, be added fire retardant be copolymerized together, be made alginate fibre；2) alginate fibre, polyamide fibre, terylene, cotton yarn are woven into fire-retardant
Cloth；3) flame retardant fabric is carried out rolling suction processing, 75% or more liquid carrying rate in fire retardant；4) will roll suction treated cloth into
Row drying and processing.
Above-mentioned fire retardant is made of the ingredient mixing of following weight percent: calcium carbonate 13%~14%；Zinc sulphide 0.2%
~0.3%；Barium hydroxide 10%~20%；Magnesium sulfate 10%~20%；Diatomite surplus.
Impurity content is lower than 5% in above-mentioned alginate fibre；Alginate fibre content in flame retardant fabric is 30-40%, polyamide fibre
15-20%, terylene 15-20%, remaining be cotton yarn, the content is weight percentage；It rolls suction treatment temperature and is maintained at 30-50
Degree, it is described roll suction processing the time be 40-80 minutes；Temperature is 25-60 degree when drying and processing, and the drying and processing time is 5-25
Minute.
The beneficial effects of the present invention are: the manufacture craft of seaweed cloth of the present invention is easy to operate, operating process is easily controllable,
The seaweed cloth-like texture being made is soft, it is light, have extremely strong fire-retardant and fire-proof function.
Claims (2)
1. a kind of manufacture craft of seaweed fiber blending flame retardant textiles, it is characterised in that comprise the following steps that: 1) will be extra large
It is melted after algae drying, fire retardant is added and is copolymerized together, alginate fibre is made；2) alginate fibre, polyamide fibre, terylene, cotton yarn are weaved
At flame retardant fabric；3) flame retardant fabric is carried out rolling suction processing, 75% or more liquid carrying rate in fire retardant；4) rolling suction, treated
Cloth carries out drying and processing.
2. a kind of manufacture craft of seaweed fiber blending flame retardant textiles according to claim 1, it is characterised in that described
Fire retardant is made of the ingredient mixing of following weight percent: calcium carbonate 13%~14%；Zinc sulphide 0.2%~0.3%；Hydrogen-oxygen
Change barium 10%~20%；Magnesium sulfate 10%~20%；Diatomite surplus.